CN105146808B - 环保竹炭口罩及其制备方法 - Google Patents

环保竹炭口罩及其制备方法 Download PDF

Info

Publication number
CN105146808B
CN105146808B CN201510277423.2A CN201510277423A CN105146808B CN 105146808 B CN105146808 B CN 105146808B CN 201510277423 A CN201510277423 A CN 201510277423A CN 105146808 B CN105146808 B CN 105146808B
Authority
CN
China
Prior art keywords
bamboo charcoal
carbonization
microcapsule
filter layer
mask
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201510277423.2A
Other languages
English (en)
Other versions
CN105146808A (zh
Inventor
耿云花
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIAN HENGYE SILK CO Ltd
Original Assignee
HAIAN HENGYE SILK CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIAN HENGYE SILK CO Ltd filed Critical HAIAN HENGYE SILK CO Ltd
Priority to CN201510277423.2A priority Critical patent/CN105146808B/zh
Publication of CN105146808A publication Critical patent/CN105146808A/zh
Application granted granted Critical
Publication of CN105146808B publication Critical patent/CN105146808B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种环保竹炭口罩,包括内罩和外罩,内罩设有拆卸口,拆卸口内装有过滤层,其特征在于,所述过滤层包括竹炭粉,所述过滤层中的竹炭粉为纳米竹炭粉,是由毛竹炭化后研磨得到的。

Description

环保竹炭口罩及其制备方法
本申请是申请号为 2014103166649 ,申请日为 2014 7 6 日,发明名称为环保竹炭口罩及其制备方法的分案申请。
技术领域
本发明涉及医疗卫生技术领域,尤其涉及一种能抗菌除菌的环保竹炭口罩。
背景技术
当前人类的某些疾病是通过呼吸道传染的,如SARS病毒、副流感病毒、呼吸道合 胞病毒、冠状病毒、腺病毒、流行性腮腺炎病毒、麻疹病毒、风疹病毒、水痘—带状疱疹病毒等。这些病毒严重威胁着人的健康,甚至危及人的生命。很多病毒存在于病人的鼻涕、口涎、痰液等分泌物中,可借助空气、飞沫传播,另外与污染的食具也有一定关系, 给预防带来很大的难度,容易发生流行甚至世界性的大流行。在相对密闭环境 工作的人、经常处于人群密集环境中的人、大中小学学生最容易受到传染。当前对于 预防流行性传染病的主要办法就是戴口罩,另外就是经常用消毒液对环境进行消毒,有条件者接种疫苗。口罩是一种面罩,它的事业从古至今已经有2500年的历史。市场上流通的普通口罩一般是脱脂棉纱或者无纺布制作而成,阻挡空气中悬浮的灰尘颗粒,但是并不能有效的抗菌、吸湿、祛味,因此很大程度上影响了人们的身体健康。在现有技术中,化工等通过呼吸道有害人体的行业所用口罩,结构都非常复杂。传统的医用口罩基本上是采用相同品种的无菌纱布制成,由于纱布孔隙大,阻挡作用有限,为了加强阻挡效果必须用很多层,例如8-12层,在一定程度上可以起到阻挡借空气、飞沫传播的病毒进入人们呼吸道,长时间使用或热天使用会感到不舒服,影响正常呼吸。
竹炭具有特有的吸附性能,能够抗菌、吸湿、祛味、保健,可防止危害物质的侵袭,有些防止生产工作中的有害气体和物质。竹炭粉的比表面积可达到 600-800m2/g,因此几乎与活性炭一样具有强大的吸附特性。
目前竹炭功能的口罩很多都是采用竹炭纤维布,与传统的医用口罩相比,吸附功能提高不明显,而且依然采用的是很多层的结构,影响透气性。还有一种过滤口罩,一般是采用独立状态的活性炭粒或竹炭(木炭)片在纱布或滤网中使用,其较大的固态形状不仅造成使用不方便,而且,其比表面积和吸附速度也不如粉状竹炭大。
发明内容
为解决上述问题,本发明的目的是在于提供一种结构简单、具有抗菌、吸湿、祛味、保健功能、且使用寿命长、使用效果好的环保竹炭口罩。该方法以壳聚糖为囊材料,纳米竹炭为芯材料,得到的产品绿色环保、安全高效、且具有广谱抗菌作用,以蜂蜡作为粘合剂将微胶囊整理到纺织品上,具有良好的耐洗性。
为实现上述目的,本发明采用如下技术方案:
一种环保竹炭口罩,包括内罩和外罩,内罩设有拆卸口,拆卸口内装有过滤层,其中,所述过滤层包括竹炭粉。
进一步,所述过滤层中的竹炭粉为纳米竹炭粉,是由毛竹炭化后研磨得到的,将纳米竹炭粉与壳聚糖制备成微胶囊,然后将微胶囊通过蜂蜡粘合到过滤层上。
进一步,所述过滤层为多层。
进一步,所述内罩和外罩以及过滤层的基材都是由驻极体熔喷聚丙烯纤维无纺布制成,将聚丙烯熔体从喷丝孔中喷出,然后用高速热空气将其吹成超细纤维,使其飞向凝网帘而冷却粘合形成无纺布,然后经过电极放电使无纺布驻极,内罩基材的无纺布其单位面积重量为20-25g/㎡,外罩基材的无纺布其单位面积重量为30-45g/㎡,过滤层基材的无纺布其单位面积重量为40-60g/㎡,纤维纤度为0.02-0.05丹尼尔。
进一步,所述聚丙烯纤维包括电荷加强添加剂和受阻胺光稳定剂。
一种上述的环保竹炭口罩的制备方法,其中,将块状竹炭破碎成3cm大小的竹炭块、接着放入40%的硝酸溶液中浸泡5h,然后烘干,接着锤式粉碎至120目,然后经过气流磨、双向旋转球磨,得到粒径小于100nm的竹炭粉,然后将竹炭粉作为芯材,壳聚糖作为壳材,制备成微胶囊,微胶囊的囊层厚度为1μm,直径为5μm,芯囊厚度比为12:1,通过蜂蜡作为粘结剂在75℃下将微胶囊粘合到无纺布上,得到过滤层。
进一步,所述竹炭是将毛竹进行炭化得到的,其中所述的炭化采用分段炭化:以6-8℃/min的升温速率升至250-275℃,炭化3-4h,然后以10-12℃/min的升温速率升至400-450℃,再炭化2-3h,最后以15-18℃/min的升温速率升至660-720℃,并炭化处理2-3h,得到竹炭。
本发明采用分段低温炭化,一方面节省成本,另外一方面保持竹子的原有功能,可以作为吸附的载体发挥竹子功效,炭化的温度过高和过长,将破坏竹子的原有性能,这就是低温炭化的优点和长处。采用气流磨和双向旋转球磨,使竹炭粉进一步细化。由于竹炭本身具有多孔结构和较强的吸附特性,加工成粉粒状后,比表面积骤然增大,因而吸附特性猛然增强,除臭、防菌效果显著增大。
同时,本发明将竹炭粉制成微胶囊,采用壳聚糖作为囊层,而且壳聚糖也具有抗菌杀菌作用,而且作为天然材料,对人体没有任何副作用,纳米竹炭粉包覆在微胶囊内,使其缓慢发挥作用,蜂蜡作为天然的粘合剂,将微胶囊整理到纺织品上,不易被洗涤脱去,赋予口罩持久的抗菌、吸湿、祛味、保健功能。
本发明的口罩采用驻极体聚丙烯无纺布作为基材更是提供了卓越的深层过滤效果。
本申请说明书、说明书摘要、权利要求书中出现的浓度,wt%为相对于织物的重量百分比,其余为质量浓度,百分比为重量百分比。
具体实施方式
下面结合具体的实施例,进一步详细地描述本发明。应理解,这些实施例只是为了举例说明本发明,而非以任何方式限制本发明的范围。
实施例 1
将聚丙烯熔体从喷丝孔中喷出,然后用高速热空气将其吹成超细纤维,使其飞向凝网帘而冷却粘合形成无纺布,然后经过电极放电使无纺布驻极,内罩基材的无纺布其单位面积重量为20g/㎡,外罩基材的无纺布其单位面积重量为40g/㎡,过滤层基材的无纺布其单位面积重量为40g/㎡,所述聚丙烯纤维包括电荷加强添加剂和受阻胺光稳定剂,纤维纤度为0.02丹尼尔。
将毛竹进行炭化得到的,其中所述的炭化采用分段炭化:以6℃/min的升温速率升至250℃,炭化3h,然后以10℃/min的升温速率升至400℃,再炭化3h,最后以15℃/min的升温速率升至660℃,并炭化处理2h,得到竹炭。
将块状竹炭破碎成3cm大小的竹炭块、接着放入40%的硝酸溶液中浸泡5h,然后烘干,接着锤式粉碎至120目,然后经过气流磨、双向旋转球磨,得到粒径小于100nm的竹炭粉,然后将竹炭粉作为芯材,壳聚糖作为壳材,制备成微胶囊,微胶囊的囊层厚度为1μm,直径为5μm,芯囊厚度比为12:1,通过蜂蜡作为粘结剂在75℃下将微胶囊粘合到无纺布上,得到过滤层。
驻极体熔喷聚丙烯纤维无纺布制成内罩和外罩,内罩设有拆卸口,将制得的过滤层装入拆卸口内得到环保竹炭口罩。
实施例 2
将聚丙烯熔体从喷丝孔中喷出,然后用高速热空气将其吹成超细纤维,使其飞向凝网帘而冷却粘合形成无纺布,然后经过电极放电使无纺布驻极,内罩基材的无纺布其单位面积重量为20g/㎡,外罩基材的无纺布其单位面积重量为40g/㎡,过滤层基材的无纺布其单位面积重量为40g/㎡,所述聚丙烯纤维包括电荷加强添加剂和受阻胺光稳定剂,纤维纤度为0.02丹尼尔。
将毛竹进行炭化得到的,其中所述的炭化采用分段炭化:以8℃/min的升温速率升至250℃,炭化3h,然后以12℃/min的升温速率升至450℃,再炭化2h,最后以18℃/min的升温速率升至700℃,并炭化处理2h,得到竹炭。
将块状竹炭破碎成3cm大小的竹炭块、接着放入40%的硝酸溶液中浸泡5h,然后烘干,接着锤式粉碎至120目,然后经过气流磨、双向旋转球磨,得到粒径小于100nm的竹炭粉,然后将竹炭粉作为芯材,壳聚糖作为壳材,制备成微胶囊,微胶囊的囊层厚度为1μm,直径为5μm,芯囊厚度比为12:1,通过蜂蜡作为粘结剂在75℃下将微胶囊粘合到纯棉水刺无纺布上,得到过滤层。分别制作两层过滤层。
驻极体熔喷聚丙烯纤维无纺布制成内罩和外罩,内罩设有拆卸口,将制得的两层过滤层装入拆卸口内得到环保竹炭口罩。
实施例 3
将聚丙烯熔体从喷丝孔中喷出,然后用高速热空气将其吹成超细纤维,使其飞向凝网帘而冷却粘合形成无纺布,然后经过电极放电使无纺布驻极,内罩基材的无纺布其单位面积重量为20g/㎡,外罩基材的无纺布其单位面积重量为40g/㎡,过滤层基材的无纺布其单位面积重量为40g/㎡,所述聚丙烯纤维包括电荷加强添加剂和受阻胺光稳定剂,纤维纤度为0.02丹尼尔。
将毛竹进行炭化得到的,其中所述的炭化采用分段炭化:以6℃/min的升温速率升至275℃,炭化4h,然后以10℃/min的升温速率升至420℃,再炭化3h,最后以16℃/min的升温速率升至720℃,并炭化处理2h,得到竹炭。
将块状竹炭破碎成3cm大小的竹炭块、接着放入40%的硝酸溶液中浸泡5h,然后烘干,接着锤式粉碎至120目,然后经过气流磨、双向旋转球磨,得到粒径小于100nm的竹炭粉,然后将竹炭粉作为芯材,壳聚糖作为壳材,制备成微胶囊,微胶囊的囊层厚度为1μm,直径为5μm,芯囊厚度比为12:1,通过蜂蜡作为粘结剂在75℃下将微胶囊粘合到纯棉水刺无纺布上,得到过滤层。分别制成三层过滤层。
驻极体熔喷聚丙烯纤维无纺布制成内罩和外罩,内罩设有拆卸口,将制得的三层过滤层装入拆卸口内得到环保竹炭口罩。
实施例 4
将聚丙烯熔体从喷丝孔中喷出,然后用高速热空气将其吹成超细纤维,使其飞向凝网帘而冷却粘合形成无纺布,然后经过电极放电使无纺布驻极,内罩基材的无纺布其单位面积重量为20g/㎡,外罩基材的无纺布其单位面积重量为40g/㎡,过滤层基材的无纺布其单位面积重量为40g/㎡,所述聚丙烯纤维包括电荷加强添加剂和受阻胺光稳定剂,纤维纤度为0.02丹尼尔。
将毛竹进行炭化得到的,其中所述的炭化采用分段炭化:以7℃/min的升温速率升至260℃,炭化3h,然后以11℃/min的升温速率升至430℃,再炭化3h,最后以17℃/min的升温速率升至700℃,并炭化处理2h,得到竹炭。
将块状竹炭破碎成3cm大小的竹炭块、接着放入40%的硝酸溶液中浸泡5h,然后烘干,接着锤式粉碎至120目,然后经过气流磨、双向旋转球磨,得到粒径小于100nm的竹炭粉,然后将竹炭粉作为芯材,壳聚糖作为壳材,制备成微胶囊,微胶囊的囊层厚度为1μm,直径为5μm,芯囊厚度比为12:1,通过蜂蜡作为粘结剂在75℃下将微胶囊粘合到纯棉水刺无纺布上,得到过滤层。
驻极体熔喷聚丙烯纤维无纺布制成内罩和外罩,内罩设有拆卸口,将制得的过滤层装入拆卸口内得到环保竹炭口罩。

Claims (1)

1.一种环保竹炭口罩,包括内罩和外罩,内罩设有拆卸口,拆卸口内装有过滤层,其特征在于,所述环保竹炭口罩由以下方法制成:将块状竹炭破碎成3cm大小的竹炭块、接着放入质量百分比为40%的硝酸溶液中浸泡5h,然后烘干,接着锤式粉碎至120目,然后经过气流磨、双向旋转球磨,得到粒径小于100nm的竹炭粉,然后将竹炭粉作为芯材,壳聚糖作为壳材,制备成微胶囊,微胶囊的囊层厚度为1μm,直径为5μm,芯囊厚度比为12:1,通过蜂蜡作为粘结剂在75℃下将微胶囊粘合到无纺布上,得到过滤层,所述竹炭是将毛竹进行炭化得到的,其中所述的炭化采用分段炭化:以6-8℃/min的升温速率升至250-275℃,炭化3-4h,然后以10-12℃/min的升温速率升至400-450℃,再炭化2-3h,最后以15-18℃/min的升温速率升至660-720℃,并炭化处理2-3h,得到竹炭。
CN201510277423.2A 2014-07-06 2014-07-06 环保竹炭口罩及其制备方法 Expired - Fee Related CN105146808B (zh)