CN105130353A - 一种红外高发射率涂料填料及其制备方法 - Google Patents
一种红外高发射率涂料填料及其制备方法 Download PDFInfo
- Publication number
- CN105130353A CN105130353A CN201510404091.XA CN201510404091A CN105130353A CN 105130353 A CN105130353 A CN 105130353A CN 201510404091 A CN201510404091 A CN 201510404091A CN 105130353 A CN105130353 A CN 105130353A
- Authority
- CN
- China
- Prior art keywords
- slag
- preparation
- filling material
- infrared high
- phosphogypsum
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种红外高发射率涂料填料及其制备方法,该涂料填料,以总量满足100%计,由下述质量百分比的各原料组成:硅锰渣30-60%;钡渣10-30%;磷石膏10-40%。按质量百分比取样,将硅锰渣、钡渣及磷石膏混合均匀,于400-600℃条件下焙烧1-4h,球磨3-7h即得。本发明具有性能良好、成本低廉、且可实现节能减排目的、化废为宝的特点。
Description
技术领域
本发明涉及建筑材料技术领域,具体涉及一种红外高发射率涂料填料,同时还涉及该红外高发射率涂料填料填料的制备方法。
背景技术
建筑物传统保温隔热通常采用外挂式有机或无机类保温板,但占地面积大、施工周期长且施工工艺复杂,同时还存在易燃、易起层、易脱落、易渗漏等安全隐患。
随着涂料技术的发展,建筑保温隔热涂料因具有经济、环保、使用方便和节能效果明显等优点已被用于建筑节能领域,涂刷保温隔热涂料代替外挂式外墙保温层已成为一种技术趋势。
由于各地区气候特点相差较大,不同地区建筑物对墙体结构热物性质要求不同。目前,市场上绝大多数建筑涂料主要基于阻隔反射原理,性能以反射隔热为主,通过提高对太阳光谱中可见光和红外光反射率达到降温的目的。白色涂料具有很高的反射率,但其它色系,尤其是深色系反射率急剧下降。因此,引入具有红外高发射率填料是强化涂料,尤其是深色系涂料节能的关键。
硅锰渣是冶炼硅锰合金过程中排放的一种工业废渣,结构疏松,主要由含硅锰合金元素且形状不规则的多孔非晶质颗粒组成;钡渣是以重晶石生产钡盐过程中产生的一种固体废渣,排放量大,含有丰富的硫酸钡、碳酸钡等钡盐,少量二氧化硅、氧化铝和氧化硅等金属氧化物,同时还含有极少量可溶性钡和硫离子;磷石膏是湿法磷酸生产过程中产生的一种固体废渣,主要成分硫酸钙,同时还含有少量硅、氟、铝、镁等磷酸盐和硫酸盐。这三种废渣排放量大,不及时处理将占用土地和污染环境,将其变废为宝以实现节能减排是亟待解决的问题。
发明内容
本发明的目的在于提供一种性能良好、成本低廉、且可实现节能减排目的、化废为宝的红外高发射率涂料填料。
本发明的另一目的在于提供该红外高发射率涂料填料的制备方法。
本发明的一种红外高发射率涂料填料,以总量满足100%计,由下述质量百分比的各原料组成:
硅锰渣..........30-60%;
钡渣............10-30%;
磷石膏..........10-40%。
本发明的一种红外高发射率涂料填料的制备方法,包括以下步骤:
将30-60%硅锰渣、10-30%钡渣及10-40%磷石膏混合均匀,于400-600℃条件下焙烧1-4h,球磨3-7h即得。
本发明与现有技术相比,具有明显有益效果,从以上技术方案可知:本发明中硅锰渣、钡渣及磷石膏固体废渣的利用不仅为填料的制备提供了一种方法简便、成本低廉的方法,在变废为宝的同时,还实现了节能减排的目的,拓宽了这三种固体废渣资源化利用途径;所提供的填料具有红外高发射率的特点,用于涂料中可强化涂料的节能效果。具有性能良好、成本低廉、且可实现节能减排目的、化废为宝的特点。
具体实施方式
实施例1
一种红外高发射率涂料填料,以总量满足100kg计,由下述各原料组成:
硅锰渣..........30kg;
钡渣............30kg;
磷石膏..........40kg。
该红外高发射率涂料填料的制备方法为:
将30kg硅锰渣、30kg钡渣及40kg磷石膏混合均匀,于400℃条件下焙烧4h,球磨3h即得。
采用红外发射率测试仪测得该配比填料在2.5-35μm波段的最大发射率ε为0.89。
实施例2
一种红外高发射率涂料填料,以总量满足100kg计,由下述各原料组成:
硅锰渣..........60kg;
钡渣............10kg;
磷石膏..........30kg。
该红外高发射率涂料填料的制备方法为:
将60kg硅锰渣、10kg钡渣及30kg磷石膏混合均匀,于600℃条件下焙烧1h,球磨4h即得。
采用红外发射率测试仪测得该配比填料在2.5-35μm波段的最大发射率ε为0.92。
实施例3
一种红外高发射率涂料填料,以总量满足100kg计,由下述各原料组成:
硅锰渣..........60kg;
钡渣............30kg;
磷石膏..........10kg。
该红外高发射率涂料填料的制备方法为:
将60kg硅锰渣、30kg钡渣及10kg磷石膏混合均匀,于450℃条件下焙烧2h,球磨5h即得。
采用红外发射率测试仪测得该配比填料在2.5-35μm波段的最大发射率ε为0.94。
实施例4
一种红外高发射率涂料填料,以总量满足100kg计,由下述各原料组成:
硅锰渣..........45kg;
钡渣............20kg;
磷石膏..........35kg。
该红外高发射率涂料填料的制备方法为:
将45kg硅锰渣、20kg钡渣及35kg磷石膏混合均匀,于550℃条件下焙烧3h,球磨6h即得。
采用红外发射率测试仪测得该配比填料在2.5-35μm波段的最大发射率ε为0.90。
实施例5
一种红外高发射率涂料填料,以总量满足100kg计,由下述各原料组成:
硅锰渣..........55kg;
钡渣............20kg;
磷石膏..........25kg。
该红外高发射率涂料填料的制备方法为:
将55kg硅锰渣、20kg钡渣及25kg磷石膏混合均匀,于500℃条件下焙烧2.5h,球磨7h即得。
采用红外发射率测试仪测得该配比填料在2.5-35μm波段的最大发射率ε为0.93。
以上所述,仅是本发明的较佳实施例而已,并非对本发明做任何形式上的限制,任何未脱离本发明技术方案内容,依据本发明的技术实质对以上实施例所做的任何简单修改、等同变化与修饰,均仍属于本发明技术方案的范围内。
Claims (2)
1.一种红外高发射率涂料填料,以总量满足100%计,由下述质量百分比的各原料组成:
硅锰渣..........30-60%;
钡渣............10-30%;
磷石膏..........10-40%。
2.如权利要求1所述的一种红外高发射率涂料填料的制备方法,包括以下步骤:
将30-60%硅锰渣、10-30%钡渣及10-40%磷石膏混合均匀,于400-600℃条件下焙烧1-4h,球磨3-7h即得。