CN105113228A - Fabric non-ironing finishing liquid and method for finishing of fabric using same - Google Patents
Fabric non-ironing finishing liquid and method for finishing of fabric using same Download PDFInfo
- Publication number
- CN105113228A CN105113228A CN201510586304.5A CN201510586304A CN105113228A CN 105113228 A CN105113228 A CN 105113228A CN 201510586304 A CN201510586304 A CN 201510586304A CN 105113228 A CN105113228 A CN 105113228A
- Authority
- CN
- China
- Prior art keywords
- fabric
- concentration
- finishing
- noniron finish
- ironing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses fabric non-ironing finishing liquid. The fabric non-ironing finishing liquid is prepared from RCT with the concentration being 100-120 g/L, amino silicon oil with the concentration being 10-15 g/L, a catalyst with the concentration being 15-20 g/L, a softening agent with the concentration being 10-15 g/L and a penetrating agent with the concentration being 3-5 g/L. Meanwhile, the invention discloses a method for finishing of fabric using the finishing liquid. According to the fabric non-ironing finishing liquid and the method for finishing of the fabric using the finishing liquid, a special finishing liquid formula is adopted, it is proved by final anti-wrinkle, shrinkage, whiteness and DP grade and brute force testing experiments that the fabric finished through the method has a good non-ironing effect, the DP grade is high, and brute force meets the fabric requirement; the fabric is soft, good in handfeeling, not prone to wrinkling and free of shrinkage; good application prospects are achieved.
Description
Technical field
The present invention relates to a kind of fabric noniron finish liquid and utilize its method that silk fabrics is arranged, belonging to textile technology field.
Background technology
Along with the raising day by day of living standard, people are more and more higher for the requirement of the quality of fabric, especially to the Functional Requirement of fabric, such as, and its ironing-free performance.At present, relatively more conventional non-ironing method is for covering, filling and covalent cross-linking, and due to the situation more complicated of non-ironing mechanism, in actual use, its non-ironing effect is unsatisfactory for said method.
Summary of the invention
In order to overcome prior art problem, the object of the present invention is to provide a kind of non-ironing effective, the fabric noniron finish liquid that durability is strong and utilize its method that fabric is arranged.
For solving the problems of the technologies described above, the technical solution used in the present invention is:
A kind of fabric noniron finish liquid, is characterized in that, comprises following component and the concentration of each component is respectively:
RCT:100-120g/L;
Amido silicon oil: 10-15g/L;
Catalyst: 15-20g/L;
Softener: 10-15g/L;
Bleeding agent: 3-5g/L.
Preferably, following component is comprised and the concentration of each component is respectively:
RCT:100g/L;
Amido silicon oil: 10g/L;
Catalyst: 20g/L;
Softener: 15g/L;
Bleeding agent: 3g/L.
Further, described catalyst is triethanolamine.Described softener is cationic quaternary.Described bleeding agent is neopelex.
And the method that above-mentioned fabric noniron finish liquid arranges silk fabrics, it is characterized in that, comprise the following steps: fabric is carried out in noniron finish liquid contaminate, tie dyeing, and then fabric is baked, wash, obtain target product after drying.
Further, baking in step, temperature is 160-180 DEG C, and the time of baking is 3-5min.And in water-washing step, be first the detergent washing of 0.5% by concentration, then use clear water rinsing.
Beneficial effect of the present invention is: the present invention is by adopting special dressing liquid formula, prove through final crease-resistant, shrink, whiteness, DP grade and strength test experiment, the fabric of wherethrough reason has good non-ironing effect, DP grade is high, and brute force meets fabric requirement, and fabric sofetening, good hand touch, do not crease easily, shrink-proof, have a good application prospect.
Detailed description of the invention
The present invention is described in detail below in conjunction with specific embodiment.
embodiment 1:
(1) noniron finish liquid is prepared: by RCT:100g/L; Amido silicon oil: 10g/L; Triethanolamine: 20g/L; Ion-type quaternary ammonium salt: 15g/L; Dressing liquid is obtained after neopelex: 3g/L is uniformly mixed;
(2) fabric is arranged: fabric to be contaminated in noniron finish liquid, tie dyeing, then under the temperature conditions of 160 DEG C, 3min is baked to fabric, be 0.5%(mass percentage by concentration again) washing agent wash, then obtain target product with after clear water rinsing, drying.
embodiment 2:
(1) noniron finish liquid is prepared: by RCT:120g/L; Amido silicon oil: 15g/L; Triethanolamine: 15g/L; Ion-type quaternary ammonium salt: 10g/L; Dressing liquid is obtained after neopelex: 5g/L is uniformly mixed;
(2) fabric is arranged: fabric to be contaminated in noniron finish liquid, tie dyeing, then under the temperature conditions of 160-180 DEG C, 5min is baked to fabric, be 0.5%(mass percentage by concentration again) washing agent wash, then obtain target product with after clear water rinsing, drying.
embodiment 3:
(1) noniron finish liquid is prepared: by RCT:110g/L; Amido silicon oil: 12g/L; Triethanolamine: 18g/L; Ion-type quaternary ammonium salt: 12g/L; Dressing liquid is obtained after neopelex: 4g/L is uniformly mixed;
(2) fabric is arranged: fabric to be contaminated in noniron finish liquid, tie dyeing, then under the temperature conditions of 170 DEG C, 4min is baked to fabric, be 0.5%(mass percentage by concentration again) washing agent wash, then obtain target product with after clear water rinsing, drying.
The grey cloth of the non-ironing fabric knitted cloth prepared by above-described embodiment 1-3 carries out crease-resistant, shrink, whiteness, DP grade and strength test.Result shows: the DP grade of the cloth in three embodiments all reaches more than 3.5 grades, and broadwise tearing brute force is greater than 1.5/1bs, and ultimate strength is greater than 33.82/1bs, and shrink-proof, wrinkle resistant, and whiteness is high, soft.
The present invention is illustrated according to above-described embodiment and should be appreciated that above-described embodiment does not limit the present invention in any form, and all employings are equal to replacement or the technical scheme that obtains of equivalent transformation mode, all drop within protection scope of the present invention.
Claims (8)
1. a fabric noniron finish liquid, is characterized in that, comprises following component and the concentration of each component is respectively:
RCT:100-120g/L;
Amido silicon oil: 10-15g/L;
Catalyst: 15-20g/L;
Softener: 10-15g/L;
Bleeding agent: 3-5g/L.
2. a kind of fabric noniron finish liquid according to claim 1, is characterized in that, comprises following component and the concentration of each component is respectively:
RCT:100g/L;
Amido silicon oil: 10g/L;
Catalyst: 20g/L;
Softener: 15g/L;
Bleeding agent: 3g/L.
3. a kind of fabric noniron finish liquid according to claim 1 and 2, it is characterized in that, described catalyst is triethanolamine.
4. a kind of fabric noniron finish liquid according to claim 1 and 2, it is characterized in that, described softener is cationic quaternary.
5. a kind of fabric noniron finish liquid according to claim 1 and 2, it is characterized in that, described bleeding agent is neopelex.
6. the method utilizing the fabric noniron finish liquid described in claim 1 to arrange fabric, it is characterized in that, comprise the following steps: fabric is carried out in noniron finish liquid contaminate, tie dyeing, and then fabric is baked, wash, obtain target product after drying.
7. a kind of method utilizing dressing liquid to arrange fabric according to claim 6, is characterized in that, baking in step, temperature is 160-180 DEG C, and the time of baking is 3-5min.
8. a kind of method utilizing dressing liquid to arrange fabric according to claim 6, is characterized in that, in water-washing step, is first the detergent washing of 0.5% by concentration, then uses clear water rinsing.