CN105111834A - Building material flame-retardant mildewproof treating agent - Google Patents
Building material flame-retardant mildewproof treating agent Download PDFInfo
- Publication number
- CN105111834A CN105111834A CN201510560468.0A CN201510560468A CN105111834A CN 105111834 A CN105111834 A CN 105111834A CN 201510560468 A CN201510560468 A CN 201510560468A CN 105111834 A CN105111834 A CN 105111834A
- Authority
- CN
- China
- Prior art keywords
- parts
- fire
- protective agent
- agent used
- mass fraction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a building material flame-retardant mildewproof treating agent which is composed of the following components in parts by mass: 44-48 parts of pentachlorophenol, 46-50 parts of ammonium polyphosphate, 42-46 parts of organosilicon quaternary ammonium salt, 46-50 parts of bamboo acetic acid, 42-46 parts of propyl p-hydroxybenzoate, 46-50 parts of nitroethane, 42-46 parts of polyglycerol, 48-52 parts of dimethylformamide, 42-46 parts of natamycin, 46-50 parts of tetrabutyl titanate, 42-46 parts of diafenthiuron, 46-50 parts of triazophos, 42-46 parts of Ailanthus altissima juice, 46-50 parts of trichloroiminocyanuric acid, 42-46 parts of naphthenic acid, 46-50 parts of diatom ooze, 42-46 parts of polyoxyethylene fatty alcohol sodium sulfate, 46-50 parts of manganese carbonate, 42-46 parts of sodium dichloro-isocyanurate, 46-50 parts of dioctyl phthalate and 42-46 parts of chloroprene rubber. The product has excellent flame retardancy, water resistance and mildew resistance, is applicable to the field of building materials, and has improved properties.
Description
Technical field
The present invention relates to a kind of material of construction fire-retardant protective agent used, belong to building material technical field.
Background technology
Material of construction buildingmaterials, the material used between floors is referred to as material of construction.The wide range that novel material of construction comprises, has lagging material, lagging material, high-strength material, the material etc. that can breathe all belongs to type material.Material of construction is the general designation of the material used in civil engineering work and construction work.The science of ecological architectural material and the definition of authority are still determining the stage.The concept of ecological architectural material comes from ecological environment material nd.The definition of ecological environment material nd is also still among determining.First its principal character is economize on resources and the energy; Next reduces environmental pollution, avoids the destruction of Global warming and ozonosphere; 3rd is easily reclaim and recycle.As ecological environment material nd important branch, by its implication ecological architectural material should refer to the production of material, use, discarded with regeneration cycle process in coordinate mutually with ecotope, meet minimum of resources and energy consumption, minimum or non-environmental-pollution, best use properties, the highest cycling and reutilization rate requires the material of construction that design is produced.Obviously such environment compatibility is relative and a develop concept.In the use of material of construction, need to adopt suitable mode stored and protect, avoid, because environmental problem, causing the infringement of material of construction.
Summary of the invention
The object of the present invention is to provide a kind of material of construction fire-retardant protective agent used, to realize the fire-retardant mildew-resistant processing capacity of material of construction better.
To achieve these goals, technical scheme of the present invention is as follows.
A kind of material of construction is fire-retardant protective agent used, be made up of the component of following mass fraction: Pentachlorophenol 44 ~ 48 parts, ammonium polyphosphate 46 ~ 50 parts, organosilicon quaternary ammonium salt 42 ~ 46 parts, bamboo vinegar 46 ~ 50 parts, propylben 42 ~ 46 parts, nitroethane 46 ~ 50 parts, Polyglycerine 42 ~ 46 parts, dimethyl formamide 48 ~ 52 parts, tennecetin 42 ~ 46 parts, tetrabutyl titanate 46 ~ 50 parts, diafenthiuron 42 ~ 46 parts, triazophos 46 ~ 50 parts, 42 ~ 46 parts, tree-of-heaven juice, trichloroisocyanuric acid 46 ~ 50 parts, naphthenic acid 42 ~ 46 parts, diatom ooze 46 ~ 50 parts, polyoxyethylenated alcohol sodium sulfate 42 ~ 46 parts, manganous carbonate 46 ~ 50 parts, Surchlor GR 60 42 ~ 46 parts, dioctyl phthalate (DOP) 46 ~ 50 parts, chloroprene rubber 42 ~ 46 parts.
Further, above-mentioned material of construction is fire-retardant protective agent used, be made up of the component of following mass fraction: Pentachlorophenol 44 parts, ammonium polyphosphate 46 parts, organosilicon quaternary ammonium salt 42 parts, bamboo vinegar 46 parts, propylben 42 parts, nitroethane 46 parts, Polyglycerine 42 parts, dimethyl formamide 48 parts, tennecetin 42 parts, tetrabutyl titanate 46 parts, diafenthiuron 42 parts, triazophos 46 parts, 42 parts, tree-of-heaven juice, trichloroisocyanuric acid 46 parts, naphthenic acid 42 parts, diatom ooze 46 parts, polyoxyethylenated alcohol sodium sulfate 42 parts, manganous carbonate 46 parts, Surchlor GR 60 42 parts, dioctyl phthalate (DOP) 46 parts, chloroprene rubber 42 parts.
Further, above-mentioned material of construction is fire-retardant protective agent used, be made up of the component of following mass fraction: Pentachlorophenol 46 parts, ammonium polyphosphate 48 parts, organosilicon quaternary ammonium salt 44 parts, bamboo vinegar 48 parts, propylben 44 parts, nitroethane 48 parts, Polyglycerine 44 parts, dimethyl formamide 50 parts, tennecetin 44 parts, tetrabutyl titanate 48 parts, diafenthiuron 44 parts, triazophos 48 parts, 44 parts, tree-of-heaven juice, trichloroisocyanuric acid 48 parts, naphthenic acid 44 parts, diatom ooze 48 parts, polyoxyethylenated alcohol sodium sulfate 44 parts, manganous carbonate 48 parts, Surchlor GR 60 44 parts, dioctyl phthalate (DOP) 48 parts, chloroprene rubber 44 parts.
Further, above-mentioned material of construction is fire-retardant protective agent used, be made up of the component of following mass fraction: Pentachlorophenol 48 parts, ammonium polyphosphate 50 parts, organosilicon quaternary ammonium salt 46 parts, bamboo vinegar 50 parts, propylben 46 parts, nitroethane 50 parts, Polyglycerine 46 parts, dimethyl formamide 52 parts, tennecetin 46 parts, tetrabutyl titanate 50 parts, diafenthiuron 46 parts, triazophos 50 parts, 46 parts, tree-of-heaven juice, trichloroisocyanuric acid 50 parts, naphthenic acid 46 parts, diatom ooze 50 parts, polyoxyethylenated alcohol sodium sulfate 46 parts, manganous carbonate 50 parts, Surchlor GR 60 46 parts, dioctyl phthalate (DOP) 50 parts, chloroprene rubber 46 parts.
Further, the fire-retardant protective agent used preparation method's step of above-mentioned material of construction is as follows:
(1) Pentachlorophenol of described mass fraction, ammonium polyphosphate, organosilicon quaternary ammonium salt, bamboo vinegar, propylben, nitroethane, Polyglycerine, dimethyl formamide, tennecetin, tetrabutyl titanate, diafenthiuron, triazophos, tree-of-heaven juice, trichloroisocyanuric acid, naphthenic acid, diatom ooze, manganous carbonate, Surchlor GR 60, chloroprene rubber are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min;
(2) add the polyoxyethylenated alcohol sodium sulfate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the dioctyl phthalate (DOP) of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix this product that rear obtained solid content is about 20 ~ 70%.
Above-mentioned each component function is as follows:
(1) Pentachlorophenol: usually used as herbicide pesticide agent, agrochemical, to most had no corrosive effect on metals.
(2) ammonium polyphosphate: nonpoisonous and tasteless, do not produce etchant gas, water absorbability is little, and thermostability is high, be a kind of non-halogen fire retardant of excellent property, be widely used in expanding fire-proof paint, polyethylene, polypropylene, urethane, epoxy resin, rubber item, fiberboard and powder extinguishing agent etc.
(3) organosilicon quaternary ammonium salt: a class Novel Cationic Surfactants, it has high temperature resistant, water-fastness, lasting effect, and scope of restraining fungi is wide, can effectively suppress gram-positive microorganism, Gram-negative bacteria, yeast and fungi.Its sterilization mechanism is using organosilicon as medium, the ammonium cation group of the energy that has microbe killing properties is adsorbed in forcefully the surface of bacterium, change the permeability of bacteria cell wall, endobacillary enzyme, coenzyme and metabolic intermediate are overflowed, cause microorganism to cease breathing function and lethal, thus reach sterilization, antibacterial effect.In leather, metal and coating, suitably add this product, except increasing flexibility, conjunctiva stability and corrosion inhibitive function, anti-mold effect is especially outstanding.
(4) bamboo vinegar: this product is in refining bamboo charcoal process, utilizes special device to reclaim and a kind of bamboo product of obtaining.
(5) propylben: white crystals or powdery, micro-have special odor.Be dissolved in ethanol, propylene glycol and sodium hydroxide, be slightly soluble in water.Be mainly used in fungicidal preservative, feed anticorrosion agent, sterilization and anticorrosion effect is greater than ethyl p-hydroxybenzoate.
(6) nitroethane: colourless oil liquid, as solvent.
(7) Polyglycerine: the hydroxyl between two or more glycerol molecule generates the polyvalent alcohol of ehter bond after dehydration, is important fine chemical product and synthetic intermediate, has purposes widely.Can emulsifying agent, dispersion agent be used as in makeup, solubilizing agent and pearling agent can be replaced, and have effect that is stable, that nurse one's health and control viscosity.
(8) dimethyl formamide: a kind of transparent liquid, can and water and majority of organic solvent dissolve each other.It is the common solvent of chemical reaction.Also the raw material of medicine and agricultural chemical insecticide is used as.
(9) tennecetin: near-white or cream yellow crystalline powder.A kind of odorless, tasteless, low dosage and the high food preservatives of security.This product is a kind of natural antifungal compound produced by streptomycete fermentation, belong to polyene macrolides, both various mould, saccharomycetic growth extensively can effectively be suppressed, again can the generation of Antifungi toxin, the fresh-keeping and antifungal therapy of food antiseptic can be widely used in.
(10) tetrabutyl titanate: colourless to light yellow transparent liquid, can be dissolved in the majority of organic solvent except ketone, is placed in air and is easily cured as transparent shred, meets water decomposition, inflammable.Be applied to coating and can improve heat resistanceheat resistant performance, can be used as high-strength polyester paint properties-correcting agent, high-temperature resistant coating additive, adhesive of medical, linking agent and condensation catalyst etc.
(11) diafenthiuron: a kind of new sulfur ureas efficient insecticide, miticide, have tag, stomach toxicity, interior suction and fumigation action.
(12) triazophos: tawny liquid, dissolves in most of organic solvent.Broad-spectrum organophosphorous pesticide, miticide, nematocides.
(13) tree-of-heaven juice: tree-of-heaven, at In Limestone Area well-grown, can make the reproducting tree species of In Limestone Area, also can do Scenery of gardens tree and shade tree.Be distributed in NORTH CHINA, east and the west and south, the southeast is to Taiwan Province.The off-odor volatilized has very strong disinfection and deinsectization effect, and can be mixed into sterilant with other materials.
(14) trichloroisocyanuric acid: organic compound, white crystalline powder or granular solids, have strong chlorine pungent taste.This product is a kind of extremely strong oxygenant and chlorizating agent, has efficient, wide spectrum, safer disinfection, has killing action, also have certain killing effect to coccidian oocyst to bacterium, virus, fungi, gemma etc.
(15) hexamethylenetetramine: under normal temperature, these product are the glossiness crystallization of white tool or crystalline powder, taste is sweet rear hardship just, irritant to skin, heating easily distils and decomposes, inflammable, soluble in water, ethanol, chloroform polar solvent, be insoluble in the non-polar solvent such as ether, aromatic hydrocarbon.Main be used as resin and the solidifying agent of plastics, the catalyzer of aminoplastics and whipping agent, the promotor of the vulcanization of rubber, the sanforzing agent etc. of textiles; As inhibiter, for slowing down the corrosion of metallic substance.
(16) naphthenic acid: dark-brown oily liquids.Be transparent faint yellow or orange liquid after refining, have special odor.Water-soluble hardly, and be dissolved in sherwood oil, ethanol, benzene and hydro carbons etc.Be used as to produce the raw material of naphthenate and coating siccative, also for timber, cable anticorrosion.
(17) diatom ooze: a kind of take diatomite as the green inner wall decoration wall material of main raw material(s), has and eliminates formaldehyde, purifies air, regulates the functions such as humidity, releasing negative oxygen ion, fire protection flame retarding, metope are self-cleaning, deodorization and sterilization.Itself without any pollution, pure natural, does not add the chemical compositions such as any gelatin substance and photocatalyst.
(18) polyoxyethylenated alcohol sodium sulfate: white or light yellow liquid are to gel lotion.Soluble in water, have excellent decontamination, emulsification, foam performance and anti-performance of hard water, gentle washing character can not injured skin.Be widely used in the washing cosmetic articles for use such as shampoo, body lotion, dish washing detergent, compound soap; For textile industry wetting agent, sanitising agent etc.Anion surfactant.
(19) manganous carbonate: this product manufactures telecommunication equipment soft magnetic ferrite, the raw material of synthesis Manganse Dioxide and other manganese salt of manufacture.As the catalyzer of desulfurization, the pigment of enamel, coating and varnish.Also fertilizer and fodder additives is used as.For medicine, welding electrode auxiliary material etc., are used as the raw material producing electrolytic metal Mn.
(20) Surchlor GR 60: white powder or granular solid, being sterilization wide spectrum, efficient, safe sterilizing agent the most in oxidizing bactericide, is also the leading product in chlorated fulminuric acid class.Can the various invasive organism such as powerful kill bacteria gemma, bacterial propagule, fungi.
(21) dioctyl phthalate (DOP): colourless transparent liquid, water insoluble, be dissolved in ethanol, ether, the most of organic solvent of mineral wet goods.This product is important universal softening agent, and have good over-all properties, good mixing property, plasticizing efficiency is high, and volatility is lower, and low-temperature pliability is better, water-fast extraction, and electric property is high, thermotolerance and weathering resistance good.Be mainly used in the processing of polyvinyl chloride (PVC) RESINS, also can be used for the processing of the superpolymer such as chemical fibre resin, acetate resin, ABS resin and rubber, also can be used for making paint, dyestuff, dispersion agent etc.
(22) chloroprene rubber: outward appearance is sheet or the block of oyster white, beige or light brown, is dissolved in toluene, dimethylbenzene, ethylene dichloride, three vanadium ethene, is slightly soluble in acetone, methylethylketone, vinyl acetic monomer, hexanaphthene, is insoluble to normal hexane, industrial naptha.There is good physical and mechanical properties, oil resistant, heat-resisting, resistance to combustion, resistance to daylight, resistance to ozone, acid and alkali-resistance, chemical-resistant reagent.Have higher tensile strength, elongation and reversible crystallinity, cementability is good, is widely used in weathering resistance product, viscose glue sole, coating and rocket fuel.
This beneficial effect of the invention is: the fire-retardant protective agent used process of preparing of this material of construction is simple, and prepared product has comparatively superior fire-resistant waterproof antimildew and antibacterial performance, is adapted at building material field and uses, improve product performance.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is described, better to understand the present invention.
embodiment 1
Material of construction in the present embodiment is fire-retardant protective agent used, be made up of the component of following mass fraction: Pentachlorophenol 44 parts, ammonium polyphosphate 46 parts, organosilicon quaternary ammonium salt 42 parts, bamboo vinegar 46 parts, propylben 42 parts, nitroethane 46 parts, Polyglycerine 42 parts, dimethyl formamide 48 parts, tennecetin 42 parts, tetrabutyl titanate 46 parts, diafenthiuron 42 parts, triazophos 46 parts, 42 parts, tree-of-heaven juice, trichloroisocyanuric acid 46 parts, naphthenic acid 42 parts, diatom ooze 46 parts, polyoxyethylenated alcohol sodium sulfate 42 parts, manganous carbonate 46 parts, Surchlor GR 60 42 parts, dioctyl phthalate (DOP) 46 parts, chloroprene rubber 42 parts.
The fire-retardant protective agent used preparation method's step of above-mentioned material of construction is as follows:
(1) Pentachlorophenol of described mass fraction, ammonium polyphosphate, organosilicon quaternary ammonium salt, bamboo vinegar, propylben, nitroethane, Polyglycerine, dimethyl formamide, tennecetin, tetrabutyl titanate, diafenthiuron, triazophos, tree-of-heaven juice, trichloroisocyanuric acid, naphthenic acid, diatom ooze, manganous carbonate, Surchlor GR 60, chloroprene rubber are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5400r/min, jitter time is 60min;
(2) add the polyoxyethylenated alcohol sodium sulfate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 5200r/min, and jitter time is 50min;
(3) add the dioctyl phthalate (DOP) of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20kHz, rate of dispersion about 4800r/min, and jitter time is 40min; Mix this product that rear obtained solid content is about 20%.
embodiment 2
Material of construction in the present embodiment is fire-retardant protective agent used, be made up of the component of following mass fraction: Pentachlorophenol 46 parts, ammonium polyphosphate 48 parts, organosilicon quaternary ammonium salt 44 parts, bamboo vinegar 48 parts, propylben 44 parts, nitroethane 48 parts, Polyglycerine 44 parts, dimethyl formamide 50 parts, tennecetin 44 parts, tetrabutyl titanate 48 parts, diafenthiuron 44 parts, triazophos 48 parts, 44 parts, tree-of-heaven juice, trichloroisocyanuric acid 48 parts, naphthenic acid 44 parts, diatom ooze 48 parts, polyoxyethylenated alcohol sodium sulfate 44 parts, manganous carbonate 48 parts, Surchlor GR 60 44 parts, dioctyl phthalate (DOP) 48 parts, chloroprene rubber 44 parts.
The fire-retardant protective agent used preparation method's step of above-mentioned material of construction is as follows:
(1) Pentachlorophenol of described mass fraction, ammonium polyphosphate, organosilicon quaternary ammonium salt, bamboo vinegar, propylben, nitroethane, Polyglycerine, dimethyl formamide, tennecetin, tetrabutyl titanate, diafenthiuron, triazophos, tree-of-heaven juice, trichloroisocyanuric acid, naphthenic acid, diatom ooze, manganous carbonate, Surchlor GR 60, chloroprene rubber are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 5200r/min, jitter time is 45min;
(2) add the polyoxyethylenated alcohol sodium sulfate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 27kHz, rate of dispersion about 5000r/min, and jitter time is 40min;
(3) add the dioctyl phthalate (DOP) of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 25kHz, rate of dispersion about 4700r/min, and jitter time is 30min; Mix this product that rear obtained solid content is about 35%.
embodiment 3
Material of construction in the present embodiment is fire-retardant protective agent used, be made up of the component of following mass fraction: Pentachlorophenol 48 parts, ammonium polyphosphate 50 parts, organosilicon quaternary ammonium salt 46 parts, bamboo vinegar 50 parts, propylben 46 parts, nitroethane 50 parts, Polyglycerine 46 parts, dimethyl formamide 52 parts, tennecetin 46 parts, tetrabutyl titanate 50 parts, diafenthiuron 46 parts, triazophos 50 parts, 46 parts, tree-of-heaven juice, trichloroisocyanuric acid 50 parts, naphthenic acid 46 parts, diatom ooze 50 parts, polyoxyethylenated alcohol sodium sulfate 46 parts, manganous carbonate 50 parts, Surchlor GR 60 46 parts, dioctyl phthalate (DOP) 50 parts, chloroprene rubber 46 parts.
The fire-retardant protective agent used preparation method's step of above-mentioned material of construction is as follows:
(1) Pentachlorophenol of described mass fraction, ammonium polyphosphate, organosilicon quaternary ammonium salt, bamboo vinegar, propylben, nitroethane, Polyglycerine, dimethyl formamide, tennecetin, tetrabutyl titanate, diafenthiuron, triazophos, tree-of-heaven juice, trichloroisocyanuric acid, naphthenic acid, diatom ooze, manganous carbonate, Surchlor GR 60, chloroprene rubber are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 40kHz, rate of dispersion 5000r/min, jitter time is 30min;
(2) add the polyoxyethylenated alcohol sodium sulfate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 35kHz, rate of dispersion 4800r/min, and jitter time is 30min;
(3) add the dioctyl phthalate (DOP) of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 30kHz, rate of dispersion about 4600r/min, and jitter time is 20min; Mix this product that rear obtained solid content is about 70%.
Carry out performance measurement for the coating in embodiment 1, embodiment 2 and embodiment 3 and certain commercial coating, measured data are as shown in table 1.Fire protection flame retarding level estimate adopts UL94 standard.
Table 1 the performance test results
Visible, material of the present invention has good fire protection flame retarding, waterproof, antibacterial and mouldproof sex change energy.
The above is the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the premise without departing from the principles of the invention; can also make some improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (5)
1. a material of construction is fire-retardant protective agent used, it is characterized in that: be made up of the component of following mass fraction: Pentachlorophenol 44 ~ 48 parts, ammonium polyphosphate 46 ~ 50 parts, organosilicon quaternary ammonium salt 42 ~ 46 parts, bamboo vinegar 46 ~ 50 parts, propylben 42 ~ 46 parts, nitroethane 46 ~ 50 parts, Polyglycerine 42 ~ 46 parts, dimethyl formamide 48 ~ 52 parts, tennecetin 42 ~ 46 parts, tetrabutyl titanate 46 ~ 50 parts, diafenthiuron 42 ~ 46 parts, triazophos 46 ~ 50 parts, 42 ~ 46 parts, tree-of-heaven juice, trichloroisocyanuric acid 46 ~ 50 parts, naphthenic acid 42 ~ 46 parts, diatom ooze 46 ~ 50 parts, polyoxyethylenated alcohol sodium sulfate 42 ~ 46 parts, manganous carbonate 46 ~ 50 parts, Surchlor GR 60 42 ~ 46 parts, dioctyl phthalate (DOP) 46 ~ 50 parts, chloroprene rubber 42 ~ 46 parts.
2. material of construction according to claim 1 is fire-retardant protective agent used, it is characterized in that: the fire-retardant protective agent used component by following mass fraction of described material of construction forms: Pentachlorophenol 44 parts, ammonium polyphosphate 46 parts, organosilicon quaternary ammonium salt 42 parts, bamboo vinegar 46 parts, propylben 42 parts, nitroethane 46 parts, Polyglycerine 42 parts, dimethyl formamide 48 parts, tennecetin 42 parts, tetrabutyl titanate 46 parts, diafenthiuron 42 parts, triazophos 46 parts, 42 parts, tree-of-heaven juice, trichloroisocyanuric acid 46 parts, naphthenic acid 42 parts, diatom ooze 46 parts, polyoxyethylenated alcohol sodium sulfate 42 parts, manganous carbonate 46 parts, Surchlor GR 60 42 parts, dioctyl phthalate (DOP) 46 parts, chloroprene rubber 42 parts.
3. fire-retardant protective agent used according to the material of construction described in claim 1 to 2, it is characterized in that: the fire-retardant protective agent used component by following mass fraction of described material of construction forms: Pentachlorophenol 46 parts, ammonium polyphosphate 48 parts, organosilicon quaternary ammonium salt 44 parts, bamboo vinegar 48 parts, propylben 44 parts, nitroethane 48 parts, Polyglycerine 44 parts, dimethyl formamide 50 parts, tennecetin 44 parts, tetrabutyl titanate 48 parts, diafenthiuron 44 parts, triazophos 48 parts, 44 parts, tree-of-heaven juice, trichloroisocyanuric acid 48 parts, naphthenic acid 44 parts, diatom ooze 48 parts, polyoxyethylenated alcohol sodium sulfate 44 parts, manganous carbonate 48 parts, Surchlor GR 60 44 parts, dioctyl phthalate (DOP) 48 parts, chloroprene rubber 44 parts.
4. the material of construction according to claims 1 to 3 is fire-retardant protective agent used, it is characterized in that: the fire-retardant protective agent used component by following mass fraction of described material of construction forms: Pentachlorophenol 48 parts, ammonium polyphosphate 50 parts, organosilicon quaternary ammonium salt 46 parts, bamboo vinegar 50 parts, propylben 46 parts, nitroethane 50 parts, Polyglycerine 46 parts, dimethyl formamide 52 parts, tennecetin 46 parts, tetrabutyl titanate 50 parts, diafenthiuron 46 parts, triazophos 50 parts, 46 parts, tree-of-heaven juice, trichloroisocyanuric acid 50 parts, naphthenic acid 46 parts, diatom ooze 50 parts, polyoxyethylenated alcohol sodium sulfate 46 parts, manganous carbonate 50 parts, Surchlor GR 60 46 parts, dioctyl phthalate (DOP) 50 parts, chloroprene rubber 46 parts.
5. the material of construction according to claim 1 or 4 is fire-retardant protective agent used, it is characterized in that: the fire-retardant protective agent used preparation method's step of described material of construction is as follows:
(1) Pentachlorophenol of described mass fraction, ammonium polyphosphate, organosilicon quaternary ammonium salt, bamboo vinegar, propylben, nitroethane, Polyglycerine, dimethyl formamide, tennecetin, tetrabutyl titanate, diafenthiuron, triazophos, tree-of-heaven juice, trichloroisocyanuric acid, naphthenic acid, diatom ooze, manganous carbonate, Surchlor GR 60, chloroprene rubber are mixed, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 40KHz, rate of dispersion about 5000 ~ 5400r/min, jitter time is 30 ~ 60min;
(2) add the polyoxyethylenated alcohol sodium sulfate of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 35KHz, rate of dispersion about 4800 ~ 5200r/min, and jitter time is 30 ~ 50min;
(3) add the dioctyl phthalate (DOP) of described mass fraction, ultrasonic high speed dispersion, ultrasonic frequency is 20 ~ 30KHz, rate of dispersion about 4600 ~ 4800r/min, and jitter time is 20 ~ 40min; Mix this product that rear obtained solid content is about 20 ~ 70%.