CN105092349A - 一种新型一系铝合金(纯铝系)待腐蚀试样的制备方法 - Google Patents
一种新型一系铝合金(纯铝系)待腐蚀试样的制备方法 Download PDFInfo
- Publication number
- CN105092349A CN105092349A CN201410211972.5A CN201410211972A CN105092349A CN 105092349 A CN105092349 A CN 105092349A CN 201410211972 A CN201410211972 A CN 201410211972A CN 105092349 A CN105092349 A CN 105092349A
- Authority
- CN
- China
- Prior art keywords
- sample
- polishing
- series
- aluminium alloy
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种新型一系铝合金(纯铝系)待腐蚀试样的制备方法,其特征在于:包含以下步骤:(1)用线切割机切取14×14×20mm的一系铝合金(纯铝系)试样,选择14×14mm表面用砂轮打磨平整;(2)用砂纸将试样表面打磨光滑,所用砂纸序号以此分别为0号、03号、05号;(3)将打磨好的试样用0号粗砂纸打磨出倒角;(4)在抛光机上进行抛光,抛光过程中,每隔40s使用0.1g抛光膏;(5)抛光过程中避免用力过大,抛光3.5min后,注入少量水,并观察试样抛光效果;(6)抛光完成,用工业酒精擦拭干净,并用清水将试样表面冲洗干净,干燥后即可。
Description
技术领域
本发明涉及一种新型一系铝合金(纯铝系)待腐蚀试样的制备方法。
背景技术
一系铝合金的金相组织很难腐蚀,即使腐蚀出来其组织也往往显示的不完全,因而通常都采用阳极覆膜加偏光来观察其金相。但这种观察方法不仅耗时,而且提高了制作成本。因此如何使一系铝合金的金相腐蚀变得与铝合金一样简单快捷是尚待解决的难题。
发明内容
本发明要解决的技术问题是:提供一种新型一系铝合金(纯铝系)待腐蚀试样的制备方法,最大程度上减小样品外形对腐蚀效果的影响。
本发明的技术方案:一种新型一系铝合金(纯铝系)待腐蚀试样的制备方法,其特征在于:包含以下步骤:
步骤一,用线切割机切取14×14×20mm的一系铝合金(纯铝系)试样,选择14×14mm表面用砂轮打磨平整;
步骤二,用砂纸将试样表面打磨光滑,所用砂纸序号以此分别为0号、03号、05号;
步骤三,将打磨好的试样用0号粗砂纸打磨出倒角;
步骤四,在抛光机上进行抛光,抛光过程中,每隔40s使用0.1g抛光膏;
步骤五,抛光过程中避免用力过大,抛光3.5min后,注入少量水,并观察试样抛光效果;
步骤六,抛光完成,用工业酒精擦拭干净,并用清水将试样表面冲洗干净,干燥后即可。
本发明的有益效果:通过本方法对样品进行处理后,在进行样品腐蚀,这样能更加清晰的观察到样品的真是腐蚀情况,避免了样品处理不恰当而带来的干扰情况。
具体实施方式
一种新型一系铝合金(纯铝系)待腐蚀试样的制备方法,其步骤包括:
步骤一,用线切割机切取14×14×20mm的一系铝合金(纯铝系)试样,选择14×14mm表面用砂轮打磨平整;
步骤二,用砂纸将试样表面打磨光滑,所用砂纸序号以此分别为0号、03号、05号,最终保证待腐蚀表面基本无肉眼可见的粗糙划痕;
步骤三,将打磨好的试样用0号粗砂纸打磨出倒角;
步骤四,在抛光机上进行抛光,抛光过程中,每隔40s使用0.1g抛光膏;
步骤五,抛光过程中避免用力过大,抛光3.5min后,注入少量水,并观察试样抛光效果;
步骤六,抛光完成,用工业酒精擦拭干净,并用清水将试样表面冲洗干净,暖风机吹干后一系铝合金(纯铝系)试样就可以进行腐蚀了。
Claims (1)
1.一种新型一系铝合金(纯铝系)待腐蚀试样的制备方法,其特征在于:包含以下步骤:
步骤一,用线切割机切取14×14×20mm的一系铝合金(纯铝系)试样,选择14×14mm表面用砂轮打磨平整;
步骤二,用砂纸将试样表面打磨光滑,所用砂纸序号以此分别为0号、03号、05号;
步骤三,将打磨好的试样用0号粗砂纸打磨出倒角;
步骤四,在抛光机上进行抛光,抛光过程中,每隔40s使用0.1g抛光膏;
步骤五,抛光过程中避免用力过大,抛光3.5min后,注入少量水,并观察试样抛光效果;
步骤六,抛光完成,用工业酒精擦拭干净,并用清水将试样表面冲洗干净,干燥后即可。