CN105088058A - 高硬度低铬合金耐磨铸球 - Google Patents

高硬度低铬合金耐磨铸球 Download PDF

Info

Publication number
CN105088058A
CN105088058A CN201510552567.4A CN201510552567A CN105088058A CN 105088058 A CN105088058 A CN 105088058A CN 201510552567 A CN201510552567 A CN 201510552567A CN 105088058 A CN105088058 A CN 105088058A
Authority
CN
China
Prior art keywords
cast ball
resisting cast
chrome
molten iron
ball
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510552567.4A
Other languages
English (en)
Inventor
赵兵
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maanshan Yongxing Metal Component Co Ltd
Original Assignee
Maanshan Yongxing Metal Component Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Maanshan Yongxing Metal Component Co Ltd filed Critical Maanshan Yongxing Metal Component Co Ltd
Priority to CN201510552567.4A priority Critical patent/CN105088058A/zh
Publication of CN105088058A publication Critical patent/CN105088058A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高硬度低铬合金耐磨铸球，其浇筑铁水由以下质量百分数的化学成分组成：C2.2-2.5，Si0.5-1.2，Mn2.4-2.6，S0.05-0.12，P0.08-0.12，Cr1.2-1.5，Mo0.2-1.2，Cu0.1-0.15，Ni0.2-0.4，B0.02-0.05，Ti0.04-0.06，Co0.06-0.12，N0.03-0.05，余量为Fe。延长磨球的使用寿命，减少停机，降低材料和检修费用，增加生产率，使用正常的工况条件下综合球耗小于0.60kg/吨原矿，破损率≤1%。

Description

高硬度低铬合金耐磨铸球
技术领域
本发明涉及耐磨合金材料技术领域，尤其涉及一种高硬度低铬合金耐磨铸球。
背景技术
目前，国内外生产的铬系合金铸球、铸段分为三种：高铬合金铸球、铸段，中铬合金铸球、铸段，低铬合金铸球、铸段。中国专利200410041736X公布了高铬合金铸球油淬工艺，通过该工艺处理后的高铬合金铸球、铸段，硬度高，但产品性能不稳定，且高铬合金铸球、铸段的合金含量高，成本高，铬资源消耗大；低铬合金铸球、铸段合金含量低，成本低，但产品硬度低，冲击韧性低，综合机械性能较差，用户使用成本高；中铬合金铸球、铸段成本适中，但目前国内外均只是对产品进行一次低温回火处理，铸态组织得不到改变，其硬度、韧性、抗磨损等综合机械性能均不够理想。为此，须寻求一种新的热处理技术，以提高中铬合金铸球、铸段的硬度、冲击韧性及综合机械性能、降低生产成本，节约合金资源。
发明内容
为了克服上述现有技术存在的缺陷，本发明提供一种高硬度低铬合金耐磨铸球，硬度高、韧性及综合性能好，性价比高，不仅为国家节约大量的铬合金资源，也为用户降低了运行成本。
本发明的技术方案如下：
高硬度低铬合金耐磨铸球，其浇筑铁水由以下质量百分数的化学成分组成：C2.2-2.5，Si0.5-1.2，Mn2.4-2.6，S0.05-0.12，P0.08-0.12，Cr1.2-1.5，Mo0.2-1.2，Cu0.1-0.15，Ni0.2-0.4，B0.02-0.05，Ti0.04-0.06，Co0.06-0.12，N0.03-0.05，余量为Fe；其具体制备方法是将铁水温度升到1530℃～1550℃，浇铸温度控制在1490℃～1520℃；铸件温度空冷到500℃～600℃时进行水冷，水冷后经外观验收后进行热处理，热处理工艺为580-620℃回火处理，回火时间2-3h。
高硬度低铬合金耐磨铸球，其浇筑铁水由以下质量百分数的化学成分组成：C2.4，Si0.9，Mn2.5，S0.08，P0.1，Cr1.4，Mo0.7，Cu0.12，Ni0.3，B0.04，Ti0.05，Co0.09，N0.04，余量为Fe。
本发明的有益技术效果如下：
本发明的铸球硬度提高11-15HRC，韧性提高100％以上，抗疲劳冲击寿命提高150％以上，使用消耗下70％以上，碎球率极低。无裂纹，硬度达62-66HRC，抗疲劳冲击寿命高达30000次以上，心部与表面硬度差≤2HRC。
本发明的高硬度低铬合金耐磨铸球力学性能及金相组织如下：
具体实施方式
实施例1：
高硬度低铬合金耐磨铸球，其浇筑铁水由以下质量百分数的化学成分组成：C2.4，Si0.9，Mn2.5，S0.08，P0.1，Cr1.4，Mo0.7，Cu0.12，Ni0.3，B0.04，Ti0.05，Co0.09，N0.04，余量为Fe；其具体制备方法是将铁水温度升到1530℃～1550℃，浇铸温度控制在1500℃；铸件温度空冷到550℃时进行水冷，水冷后经外观验收后进行热处理，热处理工艺为600℃回火处理，回火时间2.5h。
实施例2：
高硬度低铬合金耐磨铸球，其浇筑铁水由以下质量百分数的化学成分组成：C2.5，Si01.2，Mn2.6，S0.12，P0.12，Cr1.5，Mo1.2，Cu0.15，Ni0.4，B0.05，Ti0.06，Co0.12，N0.05，余量为Fe；其具体制备方法是将铁水温度升到1550℃，浇铸温度控制在1520℃；铸件温度空冷到600℃时进行水冷，水冷后经外观验收后进行热处理，热处理工艺为620℃回火处理，回火时间3h。

Claims (2)

1.高硬度低铬合金耐磨铸球，其特征在于，其浇筑铁水由以下质量百分数的化学成分组成：C2.2-2.5，Si0.5-1.2，Mn2.4-2.6，S0.05-0.12，P0.08-0.12，Cr1.2-1.5，Mo0.2-1.2，Cu0.1-0.15，Ni0.2-0.4，B0.02-0.05，Ti0.04-0.06，Co0.06-0.12，N0.03-0.05，余量为Fe；其具体制备方法是将铁水温度升到1530℃～1550℃，浇铸温度控制在1490℃～1520℃；铸件温度空冷到500℃～600℃时进行水冷，水冷后经外观验收后进行热处理，热处理工艺为580-620℃回火处理，回火时间2-3h。
2.根据权利要求1所述的高硬度低铬合金耐磨铸球，其浇筑铁水由以下质量百分数的化学成分组成：其特征在于，C2.4，Si0.9，Mn2.5，S0.08，P0.1，Cr1.4，Mo0.7，Cu0.12，Ni0.3，B0.04，Ti0.05，Co0.09，N0.04，余量为Fe。
CN201510552567.4A 2015-08-31 2015-08-31 高硬度低铬合金耐磨铸球 Pending CN105088058A (zh)