CN105086076A - 一种添加废旧塑料的环保电缆护套料及其制备方法 - Google Patents

一种添加废旧塑料的环保电缆护套料及其制备方法 Download PDF

Info

Publication number
CN105086076A
CN105086076A CN201510511904.5A CN201510511904A CN105086076A CN 105086076 A CN105086076 A CN 105086076A CN 201510511904 A CN201510511904 A CN 201510511904A CN 105086076 A CN105086076 A CN 105086076A
Authority
CN
China
Prior art keywords
parts
minutes
mixed
speed
nano
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510511904.5A
Other languages
English (en)
Inventor
许义彬
赵欣泰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JING FENG GROUP
Original Assignee
JING FENG GROUP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JING FENG GROUP filed Critical JING FENG GROUP
Priority to CN201510511904.5A priority Critical patent/CN105086076A/zh
Publication of CN105086076A publication Critical patent/CN105086076A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种添加废旧塑料的环保电缆护套料，由下列重量份的原料制成：高密度聚乙烯70-72、回收聚乙烯塑料14-16、十溴联苯醚15-17、三氧化二锑7-9、茂金属聚乙烯2-3、纳米氢氧化镁2-3、环己烷4-5、γ-氨丙基三乙氧基硅烷0.2-0.3、EVA树脂12-15、滑石粉8-10、堇青石粉4-6、二甲基硅油2-3、十二烷基硫酸钠0.8-1、硅烷偶联剂kh560？1-1.2、水适量。本发明在基料上添加适量的回收聚乙烯塑料，通过一系列的工艺处理，同样能够达到新料的要求，而且降低了材料成本，经济效益显著，同时制成的产品具有耐高温、耐磨、高强度、高阻燃、抗击穿、流动性好等优良的综合性能。

Description

一种添加废旧塑料的环保电缆护套料及其制备方法
技术领域
本发明涉及高分子材料技术领域，尤其涉及一种添加废旧塑料的环保电缆护套料及其制备方法。
背景技术
聚氯乙烯(PVC)是一种用途非常广泛的通用塑料，根据添加增塑剂的量不同，可以制成硬质、半硬质和软质制品，还可以与其他聚合物共混进行改性，做成种类繁多、性能各异的制品，用量非常大，是世界五大通用塑料之一。在全球范围内PVC树脂的需求量和聚乙烯、聚丙烯位列前三位，而在中国其消费量已经升至第一位。聚氯乙烯本身也是本质阻燃材料，其氧指数很高，阻燃效果很好，但纯的PVC是刚性链段，在90℃以上就开始分解，加工就必须加入增塑剂，增塑剂都是易燃物，所以软质PVC须加入阻燃剂才有阻燃效果。而且聚氯乙烯在燃烧时会产生氯化氢气体，具有很大的毒性和腐蚀性，且浓烟较多。随着环保要求的提高，DOP等邻苯类增塑剂已经被禁止，所以说就要进一步发挥聚乙烯电缆料的各项优点。
聚乙烯(PE)是目前产量最大的通用塑料之一，具有耐化学腐蚀性、质轻、电绝缘性、无毒、易加工、价格低廉等特点，广泛应用于电器、化工、包装、食品、交通、建筑等行业。然而PE的氧指数只有17.5%，属于易燃材料，因此需要对其进行阻燃改性处理以扩大其应用范围。还有为了提高聚乙烯电缆料的介电特性，如空间电荷集聚、体积电阻率和击穿强度等，目前高压直流电缆一般采用传统方法来改性聚乙烯绝缘料。其中共混技术是提高聚乙烯介电性能使用最多的一种方法，但是不同组分的共混会形成两相结构的微观界面，甚至出现向材料表面渗透和分离现象，影响共混物的其他介电性能，如共混可能会导致介电强度降低。因此，最好的方法是使用两种化学结构相似、相容性好的组分来进行共混，从而消除两种材料的微观界面的不良影响。
在电缆的生产过程中，约有8-10%的废品，还有大部分已经使用过的废旧电缆料或废旧塑料，没有经过合理的二次利用，造成资源的浪费以及资金的浪费。本发明拟将废旧回收聚乙烯塑料，通过一系列的工艺，添加到电缆料的生产中，不仅能够具有上述优点，同时能够节约资源，降低生产成本。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种添加废旧塑料的环保电缆护套料及其制备方法。
本发明是通过以下技术方案实现的：
一种添加废旧塑料的环保电缆护套料，由下列重量份的原料制成：高密度聚乙烯70-72、回收聚乙烯塑料14-16、十溴联苯醚15-17、三氧化二锑7-9、茂金属聚乙烯2-3、纳米氢氧化镁2-3、环己烷4-5、γ-氨丙基三乙氧基硅烷0.2-0.3、EVA树脂12-15、滑石粉8-10、堇青石粉4-6、二甲基硅油2-3、十二烷基硫酸钠0.8-1、硅烷偶联剂kh5601-1.2、水适量。
所述一种添加废旧塑料的环保电缆护套料，由以下具体步骤制成：
（1）将十溴联苯醚、三氧化二锑加入到高速混合机中，在80-90℃下混合15-20分钟，然后将一半量的高密度聚乙烯加入到高速混合机中，90-100℃下混合10-15分钟，最后将混合好的物料置于开炼机中，在145℃下塑炼8-10分钟出片，粉碎后放入烘箱中干燥5-6小时，即得到阻燃母料；
（2）将纳米氢氧化铝与茂金属聚乙烯分别放在80℃电热恒温干燥箱内热处理6小时待用；将干燥后的纳米氢氧化铝超声分散于环己烷中，形成悬浮液，然后加入γ-氨丙基三乙氧基硅烷，超声分散20分钟后将悬浮液倒入器皿中，放入烘箱中，在60℃的温度下烘干24小时，得到表面改性的纳米粉；干燥后的茂金属聚乙烯与表面改性的纳米粉放入混料机中，以140℃的温度混料30分钟，然后在双螺杆挤出机中挤出造粒，制成抗击穿改性母料；
（3）将回收聚乙烯塑料清洗表面赃物后，放入烘箱中，以80℃的温度烘干，冷却后放入塑料粉碎机中粉碎成粉末状；将硅烷偶联剂kh560溶于20倍量的水中形成溶液，将滑石粉、堇青石粉放入溶液中，以500转/分的速度搅拌分散均匀，继续加入二甲基硅油、十二烷基硫酸钠，以800转/分的速度搅拌20分钟后静置，过滤，将沉淀物烘干待用；将回收聚乙烯塑料粉末与烘干的沉淀物混合，送入高速混合机混合，6分钟后分钟后将物料送入挤出温度为135-145℃的挤出机中挤出造粒，得到混合物料；
（4）将阻燃母料、抗击穿改性母料、混合物料、剩余的高密度聚乙烯以及其余剩余成分放入高速混合机中，在温度为160℃，500转/分的速度下混合15分钟，再以2000转/分的速度混合10分钟下料，然后放入双螺杆挤出机挤出造粒，最后将粒料在80℃烘箱中干燥24小时即得。
本发明的优点是：本发明通过配方与工艺的改性，添加纳米氢氧化铝与茂金属聚乙烯等成分，这些成分的引入显著地减少了空间电荷的注入和聚集，改善了空间电荷特性，提高了直流击穿电场强度，同时由于含有少量的茂金属聚乙烯，提高了电缆料的拉伸强度以及综合性能。添加十溴联苯醚与三氧化二锑，协同作用，减少了可燃气体的生成量，改变了聚合物的分解模式，使材料的热稳定性得到了提高。同时反应分解出SbBr3，能较长时间停留在燃烧区域，具有稀释和隔离作用，进一步提高阻燃性能。
本发明在基料上添加适量的回收聚乙烯塑料，通过一系列的工艺处理，同样能够达到新料的要求，而且降低了材料成本，经济效益显著，同时制成的产品具有耐高温、耐磨、高强度、高阻燃、抗击穿、流动性好等优良的综合性能。
具体实施方式
一种添加废旧塑料的环保电缆护套料，由下列重量份（公斤）的原料制成：高密度聚乙烯70、回收聚乙烯塑料14、十溴联苯醚15、三氧化二锑7、茂金属聚乙烯2、纳米氢氧化镁2、环己烷4、γ氨丙基三乙氧基硅烷0.2、EVA树脂12、滑石粉8、堇青石粉4、二甲基硅油2、十二烷基硫酸钠0.8、硅烷偶联剂kh5601、水适量。
所述一种添加废旧塑料的环保电缆护套料，由以下具体步骤制成：
（1）将十溴联苯醚、三氧化二锑加入到高速混合机中，在80℃下混合15分钟，然后将一半量的高密度聚乙烯加入到高速混合机中，90℃下混合10分钟，最后将混合好的物料置于开炼机中，在145℃下塑炼8分钟出片，粉碎后放入烘箱中干燥5小时，即得到阻燃母料；
（2）将纳米氢氧化铝与茂金属聚乙烯分别放在80℃电热恒温干燥箱内热处理6小时待用；将干燥后的纳米氢氧化铝超声分散于环己烷中，形成悬浮液，然后加入γ氨丙基三乙氧基硅烷，超声分散20分钟后将悬浮液倒入器皿中，放入烘箱中，在60℃的温度下烘干24小时，得到表面改性的纳米粉；干燥后的茂金属聚乙烯与表面改性的纳米粉放入混料机中，以140℃的温度混料30分钟，然后在双螺杆挤出机中挤出造粒，制成抗击穿改性母料；
（3）将回收聚乙烯塑料清洗表面赃物后，放入烘箱中，以80℃的温度烘干，冷却后放入塑料粉碎机中粉碎成粉末状；将硅烷偶联剂kh560溶于20倍量的水中形成溶液，将滑石粉、堇青石粉放入溶液中，以500转/分的速度搅拌分散均匀，继续加入二甲基硅油、十二烷基硫酸钠，以800转/分的速度搅拌20分钟后静置，过滤，将沉淀物烘干待用；将回收聚乙烯塑料粉末与烘干的沉淀物混合，送入高速混合机混合，6分钟后分钟后将物料送入挤出温度为135℃的挤出机中挤出造粒，得到混合物料；
（4）将阻燃母料、抗击穿改性母料、混合物料、剩余的高密度聚乙烯以及其余剩余成分放入高速混合机中，在温度为160℃，500转/分的速度下混合15分钟，再以2000转/分的速度混合10分钟下料，然后放入双螺杆挤出机挤出造粒，最后将粒料在80℃烘箱中干燥24小时即得。
将本发明电缆料应用于电缆的生产，电缆产品经检测，达到的指标如下：抗张强度≥16MPa，断裂伸张率≥280%，断裂伸长率变化率为15.5%，氧指数≥28%，介电强度≥30MV/m。

Claims (2)

1.一种添加废旧塑料的环保电缆护套料，其特征在于，由下列重量份的原料制成：高密度聚乙烯70-72、回收聚乙烯塑料14-16、十溴联苯醚15-17、三氧化二锑7-9、茂金属聚乙烯2-3、纳米氢氧化镁2-3、环己烷4-5、γ-氨丙基三乙氧基硅烷0.2-0.3、EVA树脂12-15、滑石粉8-10、堇青石粉4-6、二甲基硅油2-3、十二烷基硫酸钠0.8-1、硅烷偶联剂kh5601-1.2、水适量。
2.根据权利要求1所述一种添加废旧塑料的环保电缆护套料，其特征在于，由以下具体步骤制成：
（1）将十溴联苯醚、三氧化二锑加入到高速混合机中，在80-90℃下混合15-20分钟，然后将一半量的高密度聚乙烯加入到高速混合机中，90-100℃下混合10-15分钟，最后将混合好的物料置于开炼机中，在145℃下塑炼8-10分钟出片，粉碎后放入烘箱中干燥5-6小时，即得到阻燃母料；
（2）将纳米氢氧化铝与茂金属聚乙烯分别放在80℃电热恒温干燥箱内热处理6小时待用；将干燥后的纳米氢氧化铝超声分散于环己烷中，形成悬浮液，然后加入γ-氨丙基三乙氧基硅烷，超声分散20分钟后将悬浮液倒入器皿中，放入烘箱中，在60℃的温度下烘干24小时，得到表面改性的纳米粉；干燥后的茂金属聚乙烯与表面改性的纳米粉放入混料机中，以140℃的温度混料30分钟，然后在双螺杆挤出机中挤出造粒，制成抗击穿改性母料；
（3）将回收聚乙烯塑料清洗表面赃物后，放入烘箱中，以80℃的温度烘干，冷却后放入塑料粉碎机中粉碎成粉末状；将硅烷偶联剂kh560溶于20倍量的水中形成溶液，将滑石粉、堇青石粉放入溶液中，以500转/分的速度搅拌分散均匀，继续加入二甲基硅油、十二烷基硫酸钠，以800转/分的速度搅拌20分钟后静置，过滤，将沉淀物烘干待用；将回收聚乙烯塑料粉末与烘干的沉淀物混合，送入高速混合机混合，6分钟后分钟后将物料送入挤出温度为135-145℃的挤出机中挤出造粒，得到混合物料；
（4）将阻燃母料、抗击穿改性母料、混合物料、剩余的高密度聚乙烯以及其余剩余成分放入高速混合机中，在温度为160℃，500转/分的速度下混合15分钟，再以2000转/分的速度混合10分钟下料，然后放入双螺杆挤出机挤出造粒，最后将粒料在80℃烘箱中干燥24小时即得。
CN201510511904.5A 2015-08-20 2015-08-20 一种添加废旧塑料的环保电缆护套料及其制备方法 Pending CN105086076A (zh)