CN105064641B - Membranization calcium silicates decoration panel and preparation method thereof - Google Patents
Membranization calcium silicates decoration panel and preparation method thereof Download PDFInfo
- Publication number
- CN105064641B CN105064641B CN201510566147.1A CN201510566147A CN105064641B CN 105064641 B CN105064641 B CN 105064641B CN 201510566147 A CN201510566147 A CN 201510566147A CN 105064641 B CN105064641 B CN 105064641B
- Authority
- CN
- China
- Prior art keywords
- silicate board
- calcium silicate
- coatings
- calcium
- membranization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of membranization calcium silicates decoration panel and preparation method thereof, the membranization calcium silicates decoration panel includes calcium silicate board, the at least side of the calcium silicate board is provided with UV coatings, and the UV coatings are pasted with PVC polymeric membranes, the calcium silicate board and are also uniformly provided with multiple air-vents；The preparation method comprises the following steps：1) air-vent is beaten on calcium silicate board；2) UV coatings are smeared at least side of the calcium silicate board after air-vent is beaten, and obtain being coated with the calcium silicate board of UV coatings；3) PVC polymeric membranes are attached to again and be coated with the calcium silicate board of UV coatings；By adding PVC polymeric membranes on calcium silicate board, surface is smooth, it is not easy to bubble；Intensity is high, wear-resisting, resistant to chemical etching, easy cleaning, antistatic, moisture proof；And multiple air-vents are set on silicic acid cover plate, not only can protection against the tide can also sound insulation.
Description
Technical field
The present invention relates to a kind of decoration panel and preparation method thereof, and in particular to a kind of membranization calcium silicates decoration panel and its preparation
Method.
Background technology
It is the abrasive band sand using low mesh number to conventional calcium silicate board surface treatment mode at present in building decoration construction field
It is flat, then with the abrasive band polishing of high mesh number, effect is all undesirable, has pit or wood-fibred fine hair to be easy for foaming.
The content of the invention
In order to solve the above technical problems, it is an object of the invention to provide a kind of membranization calcium silicates decoration panel and its preparation side
Method, with finished film calcium silicate board decoration panel obtained from, self-strength is high, area is big, lightweight, low cost.
To reach above-mentioned purpose, technical scheme is as follows：
The present invention provides a kind of membranization calcium silicates decoration panel, including calcium silicate board, and at least side of the calcium silicate board is set
Have to be pasted with PVC polymeric membranes, the calcium silicate board on UV coatings, the UV coatings and be also uniformly provided with multiple air-vents.
The membranization calcium silicates decoration panel of the present invention, by adding PVC polymeric membranes on calcium silicate board, surface is smooth, no
Easy bubble；Intensity is high, wear-resisting, resistant to chemical etching, easy cleaning, antistatic, moisture proof；And set multiple on silicic acid cover plate
Stomata, is not only able to prevent humidity can also sound insulation.
On the basis of above-mentioned technical proposal, the present invention can also make following improvement：
As preferred scheme, cotton and/or staple fibre are filled with the air-vent.
Using preferred scheme, moistureproof and sound insulation can be further enhanced by the cotton of filling and/or staple fibre
Effect.
As preferred scheme, the calcium silicate board and UV apply interlayer and are additionally provided with solid wood layer.
Using preferred scheme, by the addition of solid wood layer, increase the fastness of the membranization calcium silicates decoration panel.
As preferred scheme, heat-insulation layer is additionally provided between the solid wood layer and the calcium silicate board.
Using preferred scheme, the membranization calcium silicates decoration panel is set to be incubated.
As preferred scheme, the solid wood layer and the UV apply interlayer and are additionally provided with skin of paint.
Using preferred scheme, the setting of skin of paint can make the membranization calcium silicates decoration panel more waterproof and dampproof, and more
To be attractive in appearance.
On the other hand, the present invention also provides a kind of preparation method of membranization calcium silicates decoration panel of the invention, methods described
Comprise the following steps：
1) air-vent is beaten on calcium silicate board；
2) UV coatings are smeared at least side of the calcium silicate board after air-vent is beaten, and obtain being coated with the calcium silicates of UV coatings
Plate；
3) PVC polymeric membranes are attached to by pneumatic rolling laminating machine again and be coated with the calcium silicate board of UV coatings.
The preparation method of the membranization calcium silicates decoration panel of the present invention, the coating technique is simple, and shows through overtesting, leads to
The membranization calcium silicates decoration panel appearance for crossing pneumatic rolling laminating machine overlay film preparation is clean and tidy, smooth, it is not easy to damaged.
On the basis of above-mentioned technical proposal, the present invention can also make following improvement：
As preferred scheme, in step 2) in, obtain being coated with after the calcium silicate board of UV coatings, in addition to dust removal process
The step of.
Using preferred scheme, by the dust removal process PVC polymeric membranes can be made more effectively to be attached to calcium silicate board
On.
As preferred scheme, in step 3) in, PVC polymeric membranes are attached to and are coated with the calcium silicate board of UV coatings
Afterwards, the step of being also included in 45 DEG C of progress microwave dryings.
Using preferred scheme, using energy regenerative at the top of microwave, rationally arrangement, stable transport chain structure makes finished product membranization
Calcium silicate board is smooth to be still on conveyer chain, and finished product calcium silicate board is heated evenly, and the product shape of calcium silicate board is ensure that after drying；Have
Effect solves the problem of conventional calcium silicate board moisture content is higher, compared to conventional hot blast stove (natural gas, coal, resistance) drying mode,
It is unlikely to deform, temperature stabilization, the features such as drying process is reliable；And by drying at a certain temperature, less cracky increases
Add service life, improve waterproof and dampproof performance.
As preferred scheme, in step 3) in, PVC polymeric membranes are attached to by painting by the method that comprises the following steps
On the calcium silicate board for being covered with UV coatings：PVC polymeric membranes are set with air inlet transmission roller press, the calcium silicate board of UV coatings is coated with
Roll-in bed is put into, is 80 DEG C then at temperature, pressure is 8.0MPa, the PVC polymeric membranes are attached into the UV that is coated with applies
On the calcium silicate board of layer.
Using preferred scheme, the membranization calcium silicate board produced using pneumatic roll squeezer, PVC polymeric membrane adsorptivities
By force, uniform force, surface smoothness is high, and ornamental perception is strong, and the overlay film under specific temperature, pressure, attaches more firm
Gu, deformation coefficient is smaller.
As preferred scheme, in step 2) in, after the calcium silicate board for being coated with UV coatings, it is additionally included in described be coated with
Increase one layer of heat preservation layer, the step of then increasing by one layer of solid wood layer on the heat-insulation layer again on the calcium silicate board of UV coatings.
Brief description of the drawings
Fig. 1 is one of structural representation of membranization calcium silicates decoration panel of the present invention；
Fig. 2 is the two of the structural representation of the membranization calcium silicates decoration panel of the present invention；
Wherein：
1. calcium silicate board, 2. UV coatings, 3. PVC polymeric membranes, 4. air-vents, 5. solid wood layers, 6. heat-insulation layers, 7. paint
Layer.
Embodiment
The preferred embodiment that the invention will now be described in detail with reference to the accompanying drawings.
In order to reach the purpose of the present invention, in some embodiments, as shown in figure 1, the membranization calcium silicates decorations of the present invention
Panel, including calcium silicate board 1, the both sides of the calcium silicate board 1 are equipped with UV coatings 2, the UV coatings 2 that to be pasted with PVC high
Multiple air-vents 4 are also uniformly provided with molecular film 3, the calcium silicate board 1.The membranization calcium silicates decoration panel, on calcium silicate board
PVC polymeric membranes are added, surface is smooth, it is not easy to bubble；Intensity is high, wear-resisting, resistant to chemical etching, easy cleaning, antistatic, protection against the tide
It is wet；And multiple air-vents are set on silicic acid cover plate, are not only able to prevent humidity can also sound insulation.
Cotton and/or artificial fibre are filled with the implementation result of the present invention, the air-vent 4 in order to further optimize
Dimension.The effect of moistureproof and sound insulation can be further enhanced by the cotton of filling and/or staple fibre.
In order to further optimize the implementation result of the present invention, in other embodiment, as shown in Fig. 2 described
Solid wood layer 5 is additionally provided between calcium silicate board 1 and UV coatings 2.By the addition of solid wood layer, increase the jail of the membranization calcium silicates decoration panel
Solidity.
In order to further optimize the implementation result of the present invention, heat-insulation layer is additionally provided between the solid wood layer 5 and calcium silicate board 1
6.The membranization calcium silicates decoration panel is set to be incubated.
In order to further optimize the implementation result of the present invention, paint is additionally provided between the solid wood layer 5 and the UV coatings 2
Layer 7.The setting of skin of paint can make the membranization calcium silicates decoration panel more waterproof and dampproof and more aesthetically pleasing.
In order to reach the purpose of the present invention, the preparation method of membranization calcium silicates decoration panel of the invention, methods described includes
Following steps：
1) air-vent is beaten on calcium silicate board；
2) UV coatings are smeared in the both sides of the calcium silicate board after air-vent is beaten, and obtain being coated with the calcium silicate board of UV coatings；
3) PVC polymeric membranes are attached to by pneumatic rolling laminating machine again and be coated with the calcium silicate board of UV coatings.
The preparation method of the membranization calcium silicates decoration panel, the coating technique is simple, and shows through overtesting, by pneumatic
The membranization calcium silicates decoration panel appearance for rolling the preparation of laminating machine overlay film is clean and tidy, smooth, it is not easy to damaged.
In order to further optimize the implementation result of the present invention, in step 2) in, obtain being coated with the calcium silicates of UV coatings
After plate, in addition to the step of dust removal process.By the dust removal process PVC polymeric membranes can be made more effectively to be attached to calcium silicates
On plate.
In order to further optimize the implementation result of the present invention, in step 3) in, PVC polymeric membranes are attached to and are coated with
After on the calcium silicate board of UV coatings, also it is included in the step of microwave drying is carried out for 45 DEG C.PVC polymeric membranes can be made more firm
Ground is attached on calcium silicate board, and not fragile grandson, service life is long.
In order to further optimize the implementation result of the present invention, in step 3) in, will by the method comprised the following steps
PVC polymeric membranes, which are attached to, to be coated with the calcium silicate board of UV coatings：PVC polymeric membranes are set with air inlet transmission roller press, will be applied
The calcium silicate board for being covered with UV coatings puts into roll-in bed, is 45 DEG C then at temperature, pressure is 8.0MPa, by the PVC polymeric membranes
It is attached to described be coated with the calcium silicate board of UV coatings；The membranization calcium silicate board produced using pneumatic roll squeezer, PVC is high
Molecular film adsorptivity is strong, uniform force, and surface smoothness is high, and ornamental perception is strong, and is covered under specific temperature, pressure
Film, attaching is more firm, and deformation coefficient is smaller.
In order to further optimize the implementation result of the present invention, in step 2) in, after the calcium silicate board for being coated with UV coatings,
Being additionally included in described be coated with the calcium silicate board of UV coatings increases one layer of heat preservation layer, then increases by one on the heat-insulation layer again
The step of layer solid wood layer.
Embodiments of the present invention are illustrated below in conjunction with specific embodiment：
Embodiment 1
1) air-vent is beaten on calcium silicate board；
2) UV coatings are smeared in the both sides of the calcium silicate board after air-vent is beaten, and obtain being coated with the calcium silicate board of UV coatings,
Dust removal process is passed it through again；
3) PVC polymeric membranes are set with air inlet transmission roller press again, regulation roll temperature is to 80 DEG C, and pressure is 8.0MPa, will
The calcium silicate board for being coated with UV coatings puts into roll-in bed, starts the attaching that pneumatic roll squeezer completes PVC polymeric membranes, finally by
The membranization calcium silicates decoration panel for completing the attaching of PVC polymeric membranes is put into microwave dryer, in 45 DEG C of drying；Deburring is handled again, i.e.,
.
Comparative example 1
Preparation method is same as Example 1, it is different be by vacuum plastic-absorbing machine, it is using negative pressure of vacuum principle that PVC is high
Molecular film, which is attached to, to be coated with the calcium silicate board of UV coatings.
Comparative example 2
Preparation method is same as Example 1, and it is 70 DEG C in temperature, pressure is in pneumatic roll squeezer that different, which is,
PVC polymeric membranes are attached to and are coated with the calcium silicate board of UV coatings by 10.0MPa.
Comparative example 3
Preparation method is same as Example 1, and different is the calcium silicate board of PVC polymeric membranes will to be pasted with, at 50 DEG C
Carry out microwave drying.
Membranization calcium silicates decoration panel prepared by embodiment 1 and comparative example 1 is used 1 year, and a membranization is observed at quarterly intervals
The outward appearance of calcium silicates decoration panel, as a result as described in Table 1.
Table 1
Result above shows, the membranization calcium silicates decoration panel appearance that embodiment 1 is prepared by pneumatic rolling laminating machine overlay film
Neatly, smoothly, it is not easy to damaged, PVC polymeric membranes attach close；And the PVC film that comparative example 1 is attached using vacuum plastic-absorbing machine,
Finished product membranization membranization calcium silicates decoration panel, absorption affinity is weaker between film and calcium silicate board, and it is existing that the time one produces PVC film hardening long
As easily shelling；Comparative example 2 does not carry out pad pasting at specific temperature and pressure, and cracky is attached insecure, it is easy to deform；
Comparative example 3 is dried not at 45 DEG C, it is easy to which damaged, attaching is insecure.So as to illustrate, the present invention passes through pneumatic rolling laminating machine
Membranization calcium silicates decoration panel prepared by overlay film, PVC polymeric membranes adsorptivity is strong, uniform force, and surface smoothness is high, and dicoration is seen
It is perceptual strong.
Above-described is only the preferred embodiment of the present invention, it is noted that for one of ordinary skill in the art
For, without departing from the concept of the premise of the invention, various modifications and improvements can be made, these belong to the present invention
Protection domain.
Claims (4)
1. a kind of membranization calcium silicates decoration panel, including calcium silicate board, it is characterised in that the calcium silicate board at least side is provided with UV
It is pasted with coating, the UV coatings on PVC polymeric membranes, the calcium silicate board and is also uniformly provided with multiple air-vents, the silicon
Sour calcium plate and UV apply interlayer and are additionally provided with solid wood layer, and heat-insulation layer, the solid wood are additionally provided between the solid wood layer and the calcium silicate board
Layer applies interlayer with the UV and is additionally provided with skin of paint；
Membranization calcium silicates decoration panel preparation method comprises the following steps：
1) air-vent is beaten on calcium silicate board；
2) UV coatings are smeared at least side of the calcium silicate board after air-vent is beaten, and obtain being coated with the calcium silicate board of UV coatings；
3) PVC polymeric membranes are attached to by pneumatic rolling laminating machine again and be coated with the calcium silicate board of UV coatings；Its step
Method is：PVC polymeric membranes are set with air inlet transmission roller press, the calcium silicate board for being coated with UV coatings puts into roll-in bed, then at
Temperature is 45 DEG C, and pressure is 8.0MPa, PVC polymeric membranes is attached to after being coated with the calcium silicate board of UV coatings, in addition to
The step of microwave drying is carried out for 45 DEG C.
2. membranization calcium silicates decoration panel according to claim 1, it is characterised in that cotton is filled with the air-vent
And/or staple fibre.
3. the preparation method of membranization calcium silicates decoration panel according to claim 1, it is characterised in that in step 2) in, obtain
To being coated with after the calcium silicate board of UV coatings, in addition to the step of dust removal process.
4. membranization calcium silicates decoration panel according to claim 1, it is characterised in that in step 2) in, it is coated with UV coatings
Calcium silicate board after, being additionally included in described be coated with the calcium silicate board of UV coatings increases one layer of heat preservation layer, then again described
The step of increasing by one layer of solid wood layer on heat-insulation layer.