CN105064641A - Membranization calcium silicate veneer and preparation method thereof - Google Patents
Membranization calcium silicate veneer and preparation method thereof Download PDFInfo
- Publication number
- CN105064641A CN105064641A CN201510566147.1A CN201510566147A CN105064641A CN 105064641 A CN105064641 A CN 105064641A CN 201510566147 A CN201510566147 A CN 201510566147A CN 105064641 A CN105064641 A CN 105064641A
- Authority
- CN
- China
- Prior art keywords
- calcium silicate
- silicate board
- coating
- membranization
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a membranization calcium silicate veneer and a preparation method thereof. The membranization calcium silicate veneer comprises a calcium silicate board. A UV coating is arranged on at least one side of the calcium silicate board. A PVC high polymeric membrane is attached to the UV coating. The calcium silicate board is further evenly provided with a plurality of vent holes. The preparation method comprises the following steps that the vent holes are punched in the calcium silicate board; 2, at least one side of the calcium silicate board with the vent holes is coated with the UV coating to obtain the calcium silicate board coated with the UV coating; 3, the PVC high polymeric membrane is attached to the calcium silicate board coated with the UV coating. Due to the fact that the PVC high polymeric membrane is additionally arranged on the calcium silicate board, the surface is smooth, and bubbles are not likely to be generated; the strength is high, abrasion and chemical corrosion are resistant, cleaning is easy, and static electricity and moisture are prevented; due to the fact that the multiple vent holes are formed in the calcium silicate board, moisture prevention and sound insulation can be achieved.
Description
Technical field
The present invention relates to a kind of decoration panel and preparation method thereof, be specifically related to a kind of membranization calcium silicates decoration panel and preparation method thereof.
Background technology
At present at architectural decoration construction field, be use the abrasive band of low mesh number to sand flat to conventional calcium silicate board surface treatment mode, then with the abrasive band polishing of high order number, effect is all undesirable, has pit or wood fiber fine hair just easily to bubble.
Summary of the invention
For solving the problems of the technologies described above, the object of the present invention is to provide a kind of membranization calcium silicates decoration panel and preparation method thereof, thus obtain with finished film calcium silicate board decoration panel, self-strength is high, area is large, lightweight, cost is low.
For achieving the above object, technical scheme of the present invention is as follows:
The invention provides a kind of membranization calcium silicates decoration panel, comprise calcium silicate board, at least side of described calcium silicate board is provided with UV coating, described UV coating is pasted with PVC polymeric membrane, described calcium silicate board is also evenly provided with multiple air-vent.
Membranization calcium silicates decoration panel of the present invention, by adding PVC polymeric membrane on calcium silicate board, smooth surface, is not easy bubble; Intensity is high, wear-resisting, resistance to chemical attack, easy cleaning, antistatic, moisture proof; And silicic acid cover plate arranges multiple air-vent, not only can prevent humidity can also sound insulation.
On the basis of technique scheme, the present invention also can make following improvement:
As preferred scheme, in described air-vent, be filled with cotton and/or artificial fiber.
Adopt preferred scheme, effect that is moistureproof and sound insulation can be strengthened further by the cotton of filling and/or artificial fiber.
As preferred scheme, described calcium silicate board and UV are coated with interlayer and are also provided with solid wood layer.
Adopt preferred scheme, by the interpolation of solid wood layer, increase the fastness of this membranization calcium silicates decoration panel.
As preferred scheme, between described solid wood layer and described calcium silicate board, be also provided with insulation layer.
Adopt preferred scheme, this membranization calcium silicates decoration panel is incubated.
As preferred scheme, described solid wood layer and described UV are coated with interlayer and are also provided with skin of paint.
Adopt preferred scheme, the setting of skin of paint can make this membranization calcium silicates decoration panel more waterproof and dampproof, and more attractive in appearance.
On the other hand, the present invention also provides a kind of preparation method of membranization calcium silicates decoration panel of the present invention, said method comprising the steps of:
1) on calcium silicate board, air-vent is beaten;
2) UV coating is smeared at least side of the calcium silicate board after beating air-vent, obtains the calcium silicate board being coated with UV coating;
3) again PVC polymeric membrane is attached to by pneumatic roll extrusion laminating machine on the calcium silicate board being coated with UV coating.
The preparation method of membranization calcium silicates decoration panel of the present invention, this coating technique is simple, and shows through test, and the membranization calcium silicates decoration panel appearance prepared by pneumatic roll extrusion laminating machine overlay film is clean and tidy, level and smooth, is not easy breakage.
On the basis of technique scheme, the present invention also can make following improvement:
As preferred scheme, in step 2) in, after obtaining being coated with the calcium silicate board of UV coating, also comprise the step of dust removal process.
Adopt preferred scheme, PVC polymeric membrane can be made more effectively to be attached on calcium silicate board by this dust removal process.
As preferred scheme, in step 3) in, PVC polymeric membrane is attached to after on the calcium silicate board being coated with UV coating, is also included in the step that 45 DEG C are carried out microwave drying.
Adopt preferred scheme, utilize microwave top energy regenerative, rationally arrange, stable conveyer chain structure, make that finished film calcium silicate board is smooth to be still on conveyer chain, finished product calcium silicate board is heated evenly, and ensure that the product shape of calcium silicate board after oven dry; Efficiently solve the problem that conventional calcium silicate board moisture content is higher, compare conventional hot blast stove (natural gas, coal, resistance) drying mode, have not yielding, temperature stabilization, the features such as dry run is reliable; And by drying at a certain temperature, more not cracky, adds application life, improves waterproof and dampproof performance.
As preferred scheme, in step 3) in, by the method that comprises the steps PVC polymeric membrane is attached on the calcium silicate board being coated with UV coating: by PVC polymeric membrane suit air inlet transmission roller press, the calcium silicate board being coated with UV coating is put into roll-in bed, again in temperature be 80 DEG C, pressure is 8.0MPa, is coated with on the calcium silicate board of UV coating described in being attached to by described PVC polymeric membrane.
Adopt preferred scheme, use the membranization calcium silicate board that pneumatic roll squeezer is produced, PVC polymeric membrane adsorptivity is strong, uniform force, surface finish is high, and ornamental perception is strong, and overlay film under specific temperature, pressure, attach more firm, coefficient of deformation is less.
As preferred scheme, in step 2) in, after being coated with the calcium silicate board of UV coating, the calcium silicate board being coated with UV coating increasing one layer of heat preservation layer, and then increase the step of one deck solid wood layer described in being also included on described insulation layer.
Accompanying drawing explanation
Fig. 1 is one of structural representation of membranization calcium silicates decoration panel of the present invention;
Fig. 2 is the structural representation two of membranization calcium silicates decoration panel of the present invention;
Wherein:
1. calcium silicate board, 2.UV coating, 3.PVC polymeric membrane, 4. air-vent, 5. solid wood layer, 6. insulation layer, 7. skin of paint.
Detailed description of the invention
The preferred embodiment of the present invention is described in detail below in conjunction with accompanying drawing.
In order to reach object of the present invention, in some embodiments, as shown in Figure 1, membranization calcium silicates decoration panel of the present invention, comprise calcium silicate board 1, the both sides of described calcium silicate board 1 are equipped with UV coating 2, and described UV coating 2 is pasted with PVC polymeric membrane 3, and described calcium silicate board 1 is also evenly provided with multiple air-vent 4.This membranization calcium silicates decoration panel, calcium silicate board adds PVC polymeric membrane, smooth surface, is not easy bubble; Intensity is high, wear-resisting, resistance to chemical attack, easy cleaning, antistatic, moisture proof; And silicic acid cover plate arranges multiple air-vent, not only can prevent humidity can also sound insulation.
In order to optimize implementation result of the present invention further, in described air-vent 4, be filled with cotton and/or artificial fiber.Effect that is moistureproof and sound insulation can be strengthened further by the cotton of filling and/or artificial fiber.
In order to optimize implementation result of the present invention further, in other embodiment, as shown in Figure 2, solid wood layer 5 is also provided with between described calcium silicate board 1 and UV coating 2.By the interpolation of solid wood layer, increase the fastness of this membranization calcium silicates decoration panel.
In order to optimize implementation result of the present invention further, between described solid wood layer 5 and calcium silicate board 1, be also provided with insulation layer 6.This membranization calcium silicates decoration panel is incubated.
In order to optimize implementation result of the present invention further, between described solid wood layer 5 and described UV coating 2, be also provided with skin of paint 7.The setting of skin of paint can make this membranization calcium silicates decoration panel more waterproof and dampproof, and more attractive in appearance.
In order to reach object of the present invention, the preparation method of membranization calcium silicates decoration panel of the present invention, said method comprising the steps of:
1) on calcium silicate board, air-vent is beaten;
2) UV coating is smeared in the both sides of the calcium silicate board after beating air-vent, obtains the calcium silicate board being coated with UV coating;
3) again PVC polymeric membrane is attached to by pneumatic roll extrusion laminating machine on the calcium silicate board being coated with UV coating.
The preparation method of this membranization calcium silicates decoration panel, this coating technique is simple, and shows through test, and the membranization calcium silicates decoration panel appearance prepared by pneumatic roll extrusion laminating machine overlay film is clean and tidy, level and smooth, is not easy breakage.
In order to optimize implementation result of the present invention further, in step 2) in, after obtaining being coated with the calcium silicate board of UV coating, also comprise the step of dust removal process.PVC polymeric membrane can be made more effectively to be attached on calcium silicate board by this dust removal process.
In order to optimize implementation result of the present invention further, in step 3) in, PVC polymeric membrane is attached to after on the calcium silicate board being coated with UV coating, is also included in the step of carrying out microwave drying in 45 DEG C.PVC polymeric membrane can be made to be attached to more firmly on calcium silicate board, not easily broken grandson, long service life.
In order to optimize implementation result of the present invention further, in step 3) in, by the method that comprises the steps PVC polymeric membrane is attached on the calcium silicate board being coated with UV coating: by PVC polymeric membrane suit air inlet transmission roller press, the calcium silicate board being coated with UV coating is put into roll-in bed, again in temperature be 45 DEG C, pressure is 8.0MPa, is coated with on the calcium silicate board of UV coating described in being attached to by described PVC polymeric membrane; Use the membranization calcium silicate board that pneumatic roll squeezer is produced, PVC polymeric membrane adsorptivity is strong, uniform force, and surface finish is high, and ornamental perception is strong, and under specific temperature, pressure overlay film, attach more firm, coefficient of deformation is less.
In order to optimize implementation result of the present invention further, in step 2) in, after being coated with the calcium silicate board of UV coating, the calcium silicate board being coated with UV coating increasing one layer of heat preservation layer, and then increase the step of one deck solid wood layer described in being also included on described insulation layer.
Below in conjunction with specific embodiment, embodiments of the present invention are described:
Embodiment 1
1) on calcium silicate board, air-vent is beaten;
2) UV coating is smeared in the both sides of the calcium silicate board after beating air-vent, obtains the calcium silicate board being coated with UV coating, then by it through dust removal process;
3) again by PVC polymeric membrane suit air inlet transmission roller press, regulate roll temperature to 80 DEG C, pressure is 8.0MPa, the calcium silicate board being coated with UV coating is put into roll-in bed, start the attaching that pneumatic roll squeezer completes PVC polymeric membrane, finally the membranization calcium silicates decoration panel completing the attaching of PVC polymeric membrane is put into microwave dryer, in 45 DEG C of oven dry; Deburring process again, to obtain final product.
Comparative example 1
Preparation method is identical with embodiment 1, and different is by vacuum plastic-absorbing machine, on the calcium silicate board adopting negative pressure of vacuum principle to be attached to by PVC polymeric membrane to be coated with UV coating.
Comparative example 2
Preparation method is identical with embodiment 1, and different is, in pneumatic roll squeezer, be 70 DEG C in temperature, pressure be 10.0MPa PVC polymeric membrane is attached to be coated with UV coating calcium silicate board on.
Comparative example 3
Preparation method is identical with embodiment 1, and different is will be pasted with the calcium silicate board of PVC polymeric membrane, at 50 DEG C, carry out microwave drying.
Membranization calcium silicates decoration panel embodiment 1 and comparative example 1 prepared uses 1 year, and observe the outward appearance of a membranization calcium silicates decoration panel at quarterly intervals, result as described in Table 1.
Table 1
Above result shows, the membranization calcium silicates decoration panel appearance that embodiment 1 is prepared by pneumatic roll extrusion laminating machine overlay film is clean and tidy, level and smooth, is not easy breakage, and PVC polymeric membrane attaches closely; And the PVC film that comparative example 1 uses vacuum plastic-absorbing machine to attach, finished product membranization membranization calcium silicates decoration panel, between film and calcium silicate board, absorption affinity is more weak, and the time one produces PVC film hardening phenomenon for a long time, easily shells; Comparative example 2 does not carry out pad pasting, cracky at specific temperature and pressure, attaches insecure, easily deformable; Comparative example 3 is not dried at 45 DEG C, be easy to damaged, attach insecure.Thus illustrate, the membranization calcium silicates decoration panel that the present invention is prepared by pneumatic roll extrusion laminating machine overlay film, PVC polymeric membrane adsorptivity is strong, and uniform force, surface finish is high, and ornamental perception is strong.
Above-described is only the preferred embodiment of the present invention, it should be pointed out that for the person of ordinary skill of the art, and without departing from the concept of the premise of the invention, can also make some distortion and improvement, these all belong to protection scope of the present invention.
Claims (10)
1. a membranization calcium silicates decoration panel, comprises calcium silicate board, it is characterized in that, described calcium silicate board at least side is provided with UV coating, described UV coating is pasted with PVC polymeric membrane, described calcium silicate board is also evenly provided with multiple air-vent.
2. membranization calcium silicates decoration panel according to claim 1, is characterized in that, be filled with cotton and/or artificial fiber in described air-vent.
3. membranization calcium silicates decoration panel according to claim 1, is characterized in that, described calcium silicate board and UV are coated with interlayer and are also provided with solid wood layer.
4. membranization calcium silicates decoration panel according to claim 3, is characterized in that, be also provided with insulation layer between described solid wood layer and described calcium silicate board.
5. the membranization calcium silicates decoration panel according to claim 3 or 4, is characterized in that, described solid wood layer and described UV are coated with interlayer and are also provided with skin of paint.
6. the preparation method of membranization calcium silicates decoration panel according to any one of claim 1 to 5, said method comprising the steps of:
1) on calcium silicate board, air-vent is beaten;
2) UV coating is smeared at least side of the calcium silicate board after beating air-vent, obtains the calcium silicate board being coated with UV coating;
3) again PVC polymeric membrane is attached to by pneumatic roll extrusion laminating machine on the calcium silicate board being coated with UV coating.
7. the preparation method of membranization calcium silicates decoration panel according to claim 6, is characterized in that, in step 2) in, after obtaining being coated with the calcium silicate board of UV coating, also comprise the step of dust removal process.
8. the preparation method of membranization calcium silicates decoration panel according to claim 6, is characterized in that, in step 3) in, PVC polymeric membrane is attached to after on the calcium silicate board being coated with UV coating, is also included in the step that 45 DEG C are carried out microwave drying.
9. the preparation method of membranization calcium silicates decoration panel according to claim 6, it is characterized in that, in step 3) in, by the method that comprises the steps PVC polymeric membrane is attached on the calcium silicate board being coated with UV coating: by PVC polymeric membrane suit air inlet transmission roller press, the calcium silicate board being coated with UV coating is put into roll-in bed, be 45 DEG C in temperature again, pressure is 8.0MPa, is attached on the calcium silicate board being coated with UV coating by PVC polymeric membrane.
10. the preparation method of the membranization calcium silicates decoration panel according to any one of claim 7 to 9, it is characterized in that, in step 2) in, after being coated with the calcium silicate board of UV coating, the calcium silicate board being coated with UV coating described in being also included in increases one layer of heat preservation layer, and then increase the step of one deck solid wood layer on described insulation layer.