CN105062371A - Bicycle polishing wax and preparing method thereof - Google Patents
Bicycle polishing wax and preparing method thereof Download PDFInfo
- Publication number
- CN105062371A CN105062371A CN201510532677.4A CN201510532677A CN105062371A CN 105062371 A CN105062371 A CN 105062371A CN 201510532677 A CN201510532677 A CN 201510532677A CN 105062371 A CN105062371 A CN 105062371A
- Authority
- CN
- China
- Prior art keywords
- parts
- bicycle
- polishing wax
- acid
- wax
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses bicycle polishing wax and a preparing method thereof. The bicycle polishing wax comprises, by weight, 3-6 parts of oxalic acid, 5-10 parts of oleic acid, 1-3 parts of stannic chloride, 2-5 parts of stearic acid, 2-6 parts of liquid paraffin, 1-4 parts of turpentine, 2-5 parts of carnauba wax, 2-5 parts of soap flakes, 0.5-2 parts of castor oil and 2-5 parts of potassium hydrogen tartrate. The preparing method includes the steps that the oxalic acid, the oleic acid, the stearic acid, the stannic chloride and the potassium hydrogen tartrate are heated to the temperature of 80 DEG C-90 DEG C, stirred evenly, and then heated to the temperature of 110 DEG C-120 DEG C, the other components are added, and the mixture is stirred at the speed of 100-120 rpm/min for 30-40 min and then naturally cooled to the room temperature. The bicycle polishing wax can be directly smeared onto the surface of a bicycle in the using process, so that a paint film on the surface of the bicycle is bright and kept new for a long time.
Description
Technical field
The invention belongs to bike care field, be specifically related to a kind of bike polishing wax and preparation method thereof.
Background technology
Polishing wax goods certain wax (or adding suitable resin) are dissolved (or emulsification) be dispersed in lotion made in suitable solvent (comprising organic solvent and water) or liquid, be applied to leather shoes, floor, furniture, behind the surfaces such as automobile, solvent evaporates loss, stay surperficial skim cere, (also have without the need to wiping polishing through to wipe polishing with soft cloth or soft brush, liquid wax as from bright type), surface just can produce gloss, seem that light is smooth, neat and artistic, and the few frayed scratch in surface can be protected, even can by some slight spots, stain, crackles etc. are wiped and are only filled.Polishing wax goods have excellent water resistance, can prevent the erosion of moisture and energy is durable in use.
Polishing wax may be used for the polishing of automobile, furniture paint film, can protect paint film, keeps gloss of film, increases its usage period and weather resistance.
Although the bike polishing wax of current use can reach good polishing effect, its less stable can not maintain long gloss after glazing, needs often to use, and brings inconvenience.
Summary of the invention
The object of the invention is to provide a kind of bike polishing wax and preparation method thereof to overcome above the deficiencies in the prior art.
The present invention is realized by following technique means:
A kind of bike polishing wax, comprises in components by weight percent: oxalic acid 3-6 part, oleic acid 5-10 part, tin chloride 1-3 part, stearic acid 2-5 part, whiteruss 2-6 part, turps 1-4 part, carnauba wax 2-5 part, soap flakes 2-5 part, Viscotrol C 0.5-2 part, tartarus 2-5 part.
Described bike polishing wax, can preferably comprise in components by weight percent: oxalic acid 3-5 part, oleic acid 6-8 part, tin chloride 1-2 part, stearic acid 3-5 part, whiteruss 3-5 part, turps 2-4 part, carnauba wax 3-4 part, soap flakes 3-5 part, Viscotrol C 0.8-1.5 part, tartarus 4-5 part.
The preparation method of the bike polishing wax described in more than one, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) by oxalic acid, oleic acid, stearic acid, tin chloride and tartarus are heated to 80-90 DEG C, stir, and are then warming up to 110-120 DEG C, add all the other components, stir 30-40 minute, then naturally cool to room temperature with the speed of 100-120 rev/min.
Directly embrocate at bicycle surface when bike polishing wax provided by the invention uses, can be bicycle surface paint film light, prolonged not old, and the few frayed scratch in surface can be protected, there is excellent water resistance simultaneously, the erosion of moisture can be prevented and energy is durable in use; Can reach after once embrocating after tested and keep surface-brightening in more than 160 days, product performance are stable lasting.
Embodiment
Embodiment 1
A kind of bike polishing wax, comprises in components by weight percent: oxalic acid 3 parts, oleic acid 5 parts, tin chloride 1 part, stearic acid 2 parts, whiteruss 2 parts, 1 part, turps, carnauba wax 2 parts, 2 parts, soap flakes, Viscotrol C 0.5 part, tartarus 2 parts.
The preparation method of above-described bike polishing wax, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) by oxalic acid, oleic acid, stearic acid, tin chloride and tartarus are heated to 80 DEG C, stir, and are then warming up to 110 DEG C, add all the other components, stir 30 minutes, then naturally cool to room temperature with the speed of 100 revs/min.
Embodiment 2
A kind of bike polishing wax, comprises in components by weight percent: oxalic acid 3 parts, oleic acid 6 parts, tin chloride 1 part, stearic acid 3 parts, whiteruss 3 parts, 2 parts, turps, carnauba wax 3 parts, 3 parts, soap flakes, Viscotrol C 0.8 part, tartarus 4 parts.
The preparation method of above-described bike polishing wax, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) by oxalic acid, oleic acid, stearic acid, tin chloride and tartarus are heated to 85 DEG C, stir, and are then warming up to 115 DEG C, add all the other components, stir 32 minutes, then naturally cool to room temperature with the speed of 105 revs/min.
Embodiment 3
A kind of bike polishing wax, comprises in components by weight percent: oxalic acid 4 parts, oleic acid 7 parts, tin chloride 2 parts, stearic acid 4 parts, whiteruss 4 parts, 3 parts, turps, carnauba wax 4 parts, 4 parts, soap flakes, Viscotrol C 1.2 parts, tartarus 5 parts.
The preparation method of above-described bike polishing wax, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) by oxalic acid, oleic acid, stearic acid, tin chloride and tartarus are heated to 86 DEG C, stir, and are then warming up to 115 DEG C, add all the other components, stir 36 minutes, then naturally cool to room temperature with the speed of 110 revs/min.
Embodiment 4
A kind of bike polishing wax, comprises in components by weight percent: oxalic acid 5 parts, oleic acid 8 parts, tin chloride 2 parts, stearic acid 5 parts, whiteruss 5 parts, 4 parts, turps, carnauba wax 4 parts, 5 parts, soap flakes, Viscotrol C 1.5 parts, tartarus 5 parts.
The preparation method of above-described bike polishing wax, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) by oxalic acid, oleic acid, stearic acid, tin chloride and tartarus are heated to 90 DEG C, stir, and are then warming up to 118 DEG C, add all the other components, stir 38 minutes, then naturally cool to room temperature with the speed of 115 revs/min.
Embodiment 5
A kind of bike polishing wax, comprises in components by weight percent: oxalic acid 6 parts, oleic acid 10 parts, tin chloride 3 parts, stearic acid 5 parts, whiteruss 6 parts, 4 parts, turps, carnauba wax 5 parts, 5 parts, soap flakes, Viscotrol C 2 parts, tartarus 5 parts.
The preparation method of above-described bike polishing wax, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) by oxalic acid, oleic acid, stearic acid, tin chloride and tartarus are heated to 90 DEG C, stir, and are then warming up to 120 DEG C, add all the other components, stir 40 minutes, then naturally cool to room temperature with the speed of 120 revs/min.
Directly embrocate at bicycle surface when bike polishing wax provided by the invention uses, can be bicycle surface paint film light, prolonged not old, and the few frayed scratch in surface can be protected, there is excellent water resistance simultaneously, the erosion of moisture can be prevented and energy is durable in use; Can reach after once embrocating after tested and keep surface-brightening in more than 160 days, product performance are stable lasting.
Claims (3)
1. a bike polishing wax, is characterized in that, comprises in components by weight percent: oxalic acid 3-6 part, oleic acid 5-10 part, tin chloride 1-3 part, stearic acid 2-5 part, whiteruss 2-6 part, turps 1-4 part, carnauba wax 2-5 part, soap flakes 2-5 part, Viscotrol C 0.5-2 part, tartarus 2-5 part.
2. bike polishing wax according to claim 1, it is characterized in that, comprise in components by weight percent: oxalic acid 3-5 part, oleic acid 6-8 part, tin chloride 1-2 part, stearic acid 3-5 part, whiteruss 3-5 part, turps 2-4 part, carnauba wax 3-4 part, soap flakes 3-5 part, Viscotrol C 0.8-1.5 part, tartarus 4-5 part.
3. a preparation method for the bike polishing wax described in claim 1 or 2, is characterized in that, be prepared according to following steps:
(1) each component is taken according to weight part;
(2) by oxalic acid, oleic acid, stearic acid, tin chloride and tartarus are heated to 80-90 DEG C, stir, and are then warming up to 110-120 DEG C, add all the other components, stir 30-40 minute, then naturally cool to room temperature with the speed of 100-120 rev/min.