CN105062095A - Glass fiber rigid communication tubing - Google Patents
Glass fiber rigid communication tubing Download PDFInfo
- Publication number
- CN105062095A CN105062095A CN201510476454.0A CN201510476454A CN105062095A CN 105062095 A CN105062095 A CN 105062095A CN 201510476454 A CN201510476454 A CN 201510476454A CN 105062095 A CN105062095 A CN 105062095A
- Authority
- CN
- China
- Prior art keywords
- parts
- glass fibre
- raw material
- following raw
- tubing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a glass fiber rigid communication tubing, which comprises the following raw materials by weight part: 36-40 parts of benzoin resin, 35-38 parts of water-soluble urea-formaldehyde resin glue, 4-6 parts of calcium plumbite, 4.5-6.5 parts of titanate coupling agent, 12.5-14.5 parts of glass fibre, 1.2-1.4 parts of antioxidant, 2.5-3 parts of solvent naphtha, 2.5-4.5 parts of plasticizer, 0.6-1.4 parts of cobaltous naphthenate and 4-6 parts of color masterbatch. The PVC tubing formula can greatly increase the antioxidation performance of the PVC tubing, cost is low, compared with prior art, the PVC tubing is suitable for popularization and application. The PVC tubing has the advantages of high intensity and high-toughness, strong impact resistance capability, low cost of product components and large market competition.
Description
Technical field
The present invention relates to architectural decoration coating material field, specifically belong to a kind of glass fibre rigidity communication tubing.
Background technology
As everyone knows, the cable work pipe used in the market, mostly adopt CPVC, VPVC and Glass Steel Tube, the defect such as CPVC pipe rigidity is low, the flexible distortion of insufficient strength, heat-drawn wire are low, had a strong impact on the expansion of its range of application, Glass Steel Tube conduit volume is large, material is heavy, be not easy to install and use, again because pipeline is firmly crisp, work-ing life of easily breaking is short; And above-mentioned pipeline when wearing cable and conductive cable contacts face large, friction resistance is large, and cable skin easily damages, and its insulating property are poor, and radiating effect is poor, has been not suitable with cable and has mated formation the demand of industry development.
Summary of the invention
The object of this invention is to provide a kind of glass fibre rigidity communication tubing, not only greatly can improve the antioxidant property of PVC, and become lower, be applicable to applying compared with prior art, the present invention's obtained PVC of filling a prescription has the advantages that high strength and high tenacity lay equal stress on, strong shock resistance, and product component is cheap, the market competitiveness is large.
The technical solution used in the present invention is as follows:
A kind of glass fibre rigidity communication tubing, by weight, be made up of following raw material: the resin 36-40 that rests in peace, water-soluble urea-formaldehyde resin glue 35-38, calcium plumbite 4-6, titanate coupling agent 4.5-6.5, glass fibre 12.5-14.5, anti-aging agent 1.2-1.4, solvent oil 2.5-3, softening agent 2.5-4.5, cobalt naphthenate 0.6-1.4, colour batch 4-6;
Its concrete preparation method is as follows: first mixed by the raw material of above-mentioned weight part, then carries out vacuum, boosting, constant temperature and pressure stage, and the parameter in each stage and process are: vacuum: 0.01 ~ 0.02MPa, and the pumpdown time is 0.4 ~ 0.6h; Boosting: 0.02 ~ 1.2MPa, pressure rising time is 0.9 ~ 1.2h; Constant temperature and pressure: 1.0MPa, constant voltage time is 1 ~ 2h, thermostat temperature is 85 ~ 90 DEG C, finally adds single screw extrusion machine, at 190-200 DEG C of plasticizing forming, the pipe of extrusion moulding, enter in the forming mould of rotation through longitudinal stretching, then through vacuum forming, namely cross directional stretch is shaping obtains rigidity communication tubing, its longitudinal stretching is than being 1.2-1.3, and cross directional stretch is than being 1.4-1.6.
A kind of glass fibre rigidity communication tubing, by weight, be made up of following raw material: be made up of following raw material: resin 38 of resting in peace, water-soluble urea-formaldehyde resin glue 36, calcium plumbite 5, titanate coupling agent 5.5, glass fibre 13.5, anti-aging agent 1.3, solvent oil 2.7, softening agent 3.5, cobalt naphthenate 1, colour batch 5.
PVC formula of the present invention not only can improve the antioxidant property of PVC greatly, and become lower, be applicable to applying compared with prior art, the present invention's obtained PVC of filling a prescription has the advantages that high strength and high tenacity lay equal stress on, strong shock resistance, and product component is cheap, the market competitiveness is large.
Embodiment
A kind of glass fibre rigidity communication tubing, by weight, be made up of following raw material: be made up of following raw material: resin 38 of resting in peace, water-soluble urea-formaldehyde resin glue 36, calcium plumbite 5, titanate coupling agent 5.5, glass fibre 13.5, anti-aging agent 1.3, solvent oil 2.7, softening agent 3.5, cobalt naphthenate 1, colour batch 5;
Its concrete preparation method is as follows: first mixed by the raw material of above-mentioned weight part, then carries out vacuum, boosting, constant temperature and pressure stage, and the parameter in each stage and process are: vacuum: 0.01 ~ 0.02MPa, and the pumpdown time is 0.4 ~ 0.6h; Boosting: 0.02 ~ 1.2MPa, pressure rising time is 0.9 ~ 1.2h; Constant temperature and pressure: 1.0MPa, constant voltage time is 1 ~ 2h, thermostat temperature is 85 ~ 90 DEG C, finally adds single screw extrusion machine, at 190-200 DEG C of plasticizing forming, the pipe of extrusion moulding, enter in the forming mould of rotation through longitudinal stretching, then through vacuum forming, namely cross directional stretch is shaping obtains rigidity communication tubing, its longitudinal stretching is than being 1.2-1.3, and cross directional stretch is than being 1.4-1.6.
Glass fibre rigidity communication pipe performance experimental data of the present invention:
80 DEG C, under 165h condition, hydrostatic test Zernike annular polynomial is 5.4Mpa;
80 DEG C, hydrostatic test Zernike annular polynomial is 5.0Mpa under 1000h condition.
Claims (2)
1. a glass fibre rigidity communication tubing, by weight, it is characterized in that, be made up of following raw material: the resin 36-40 that rests in peace, water-soluble urea-formaldehyde resin glue 35-38, calcium plumbite 4-6, titanate coupling agent 4.5-6.5, glass fibre 12.5-14.5, anti-aging agent 1.2-1.4, solvent oil 2.5-3, softening agent 2.5-4.5, cobalt naphthenate 0.6-1.4, colour batch 4-6;
Its concrete preparation method is as follows: first mixed by the raw material of above-mentioned weight part, then carries out vacuum, boosting, constant temperature and pressure stage, and the parameter in each stage and process are: vacuum: 0.01 ~ 0.02MPa, and the pumpdown time is 0.4 ~ 0.6h; Boosting: 0.02 ~ 1.2MPa, pressure rising time is 0.9 ~ 1.2h; Constant temperature and pressure: 1.0MPa, constant voltage time is 1 ~ 2h, thermostat temperature is 85 ~ 90 DEG C, finally adds single screw extrusion machine, at 190-200 DEG C of plasticizing forming, the pipe of extrusion moulding, enter in the forming mould of rotation through longitudinal stretching, then through vacuum forming, namely cross directional stretch is shaping obtains rigidity communication tubing, its longitudinal stretching is than being 1.2-1.3, and cross directional stretch is than being 1.4-1.6.
2. glass fibre rigidity communication tubing according to claim 1, by weight, it is characterized in that, be made up of following raw material: be made up of following raw material: resin 38 of resting in peace, water-soluble urea-formaldehyde resin glue 36, calcium plumbite 5, titanate coupling agent 5.5, glass fibre 13.5, anti-aging agent 1.3, solvent oil 2.7, softening agent 3.5, cobalt naphthenate 1, colour batch 5.