CN105062056A - High-heat-radiating PA10T composite heat radiating material for LED lamp and preparation method therefor - Google Patents

Abstract

A high-heat-radiating PA10T composite heat radiating material for a LED lamp is prepared from the following raw materials in parts by weight: 40-42 parts of magnesium oxide, 20-22 parts of boron nitride, 2-3 parts of chopped glass fiber, 30-32 parts of polyamide PA10T, 7-8 parts of aluminium oxide whiskers, 2-3 parts of iron-titanium powder, 2-3 parts of flaky high-heat-conducting carbon powder, 3-4 parts of micron-scale aluminium nitride powder, 3-4 parts of methyl 2-fluoroacrylate, 1-1.5 parts of polyvinyl butyral, 6-7 parts of ethanol and 3-4 parts of SEBS. The heat conductivity coefficient and the mechanical property of the composite material are improved, and the electrical property of the material is maintained in a relatively high level; by using the iron-titanium powder, the flaky high-heat-conducting carbon powder and the micron-order aluminium nitride powder, the composite material has a good synergetic radiating effect, so that the heat radiating property of the material is greatly improved; by using methyl 2-fluoroacrylate, the toughness, the tensile property and the stain resistance of the material are improved.

Description

A kind of high-heat dissipation LED lamp PA10T composite heat dissipation material and preparation method thereof

Technical field

The present invention relates to LED heat sink material field, particularly relate to a kind of high-heat dissipation LED lamp PA10T composite heat dissipation material and preparation method thereof.

Background technology

The thermal conductivity of most metallic substance is better, but the erosion resistance of metallic substance is bad, limits the application in the fields such as its heat exchanger, heat pipe, solar water heater and water reservoir water cooler in Chemical Manufacture and wastewater treatment.Compare with metallic substance, the insulation of plastics, corrosion-resistant, chemical resistance good, and light weight, inexpensive, easy processing, shaping energy consumption are low, is widely used, such as, can be used as electronic package material in the field such as electric.

Utilize high heat-conducting ceramic as aluminium nitride, boron nitride etc. for needing the device of insulating radiation more.Because the difficulty of processing of ceramic product is high, easily break, people start to seek the good polymkeric substance of easy processing, impact resistance to prepare insulating heat-conductive matrix material.

Unbound electron and the ion of conduction current and heat energy is generally there is not in polymer molecular chain.The imperfection of polymer crystallization, also limits the conduction of phonon to heat energy, and therefore polymer materials is the poor conductor of heat mostly, even if the high density polyethylene(HDPE) that thermal conductivity is best, its thermal conductivity is also only 0.44W/mK.But polymer materials has, and quality is light, easily processing, high-performance and low price advantage, needing the numerous areas such as the electronics of product " movement " and on-the-spot " construction ", electrical equipment and information technology to have active demand to high-strength, high-ductility, light weight, easily processing and thermal conductive polymer based composites, key to improve polymer bond (completing quick heat radiating) performance.So polymer materials heat conduction functionalization becomes one of advanced subject of polymer science and engineering subject.

The insulating resin based composites that research and development have high thermal conductivity has urgent practical significance.The most convenient efficient manner of current raising macromolecular material heat conductivility carries out composite heat-conducting modification to current material.

Heat resistant polyamide PA10T is a kind of bio-based semiaromatic polyamide composition, there is excellent mechanical property, thermotolerance and processing characteristics, water-intake rate is low, the advantage such as good stability of the dimension and resistance to chemical attack, is mainly used in electric, LED, automobile and other industries.But, the thermal conductivity of heat resistant polyamide PA10T is less, thus limit its application in some fields, as junctor, motor, transformer, solenoid coil, winding around system led illuminating and heat radiating etc., be therefore necessary the modification it being carried out to heat conductivility aspect.In existing method of modifying, filling heat conductive filler and there is the advantages such as cost is low, equipment simple, applicable scale operation, being best suited for the method as improving PA10T heat conductivility.

Boron nitride has atomic crystal form and fine and close structure, and based on phonon thermal conduction, thermal conductivity is very high, and the thermal expansivity of boron nitride is minimum in pottery in addition, and high temperature insulation characteristic is very outstanding, is that good height insulate high heat conductive filler.Although magnesium oxide thermal conductivity is lower, its low price.

Above-mentioned two kinds of fillers are carried out effective compounded combination, the heat conductive insulating matrix material that thermal conductivity is high, cost is low, formability is excellent may be obtained, can be widely used in insulating requirements higher while require again the LED illumination field of radiating of excellent heat conducting performance.Adopt boron nitride microsphere powder and spherical magnesium oxide as composite heat conductive filler, a small amount of short glass fiber is as reinforcing filler, prepare the high temperature resistant PA10T matrix material of heat conductive insulating, excellent radiation performance, but mechanical property is good not, thermal diffusivity can not meet the requirement of some relatively high power equipment, and weather resistance can not be guaranteed, and needs to improve.

Summary of the invention

The object of the present invention is to provide a kind of high-heat dissipation LED lamp PA10T composite heat dissipation material, this composite heat dissipation material has good collaborative radiating effect, and thermal diffusivity is good, and toughness, tensile property and antifouling property are good.

Technical scheme of the present invention is as follows:

A kind of high-heat dissipation LED lamp PA10T composite heat dissipation material, is characterized in that being made up of the raw material of following weight part: magnesium oxide 40-42, boron nitride 20-22, short glass fiber 2-3, polymeric amide PA10T30-32, alumina whisker 7-8, ferrotitanium powder 2-3, flakey highly-conductive hot carbon powder 2-3, micron order aluminum nitride powder 3-4,2-fluoroacrylic methyl ester 3-4, polyvinyl butyral acetal 1-1.5, ethanol 6-7, SEBS3-4.

The production method of described high-heat dissipation LED lamp PA10T composite heat dissipation material, is characterized in that:

(1) polyvinyl butyral acetal is added in ethanol, be heated to 80-82 DEG C, be stirred to resin all to dissolve, add ferrotitanium powder, flakey highly-conductive hot carbon powder, micron order aluminum nitride powder again, stir, then add short glass fiber, alumina whisker stirs, dry, pulverize, obtain modified oxidized aluminium whiskers;

(2) boron nitride mixed with SEBS, 2-fluoroacrylic methyl ester, send into twin screw extruder, through melt extruding, water-cooled pelletizing, obtains pellet;

(3) polymeric amide PA10T is dry, the pellet obtained with (2) step and other remaining components mix, and enter from the main spout of parallel dual-screw extruding machine, modified oxidized aluminium whiskers enters from side spout, through melt extruding, water-cooled pelletizing obtains pellet; Forcing machine each section of temperature is respectively: 280,320,310,310 DEG C, screw speed is set as 400r/min; Then forced air drying 4-5h at 125-130 DEG C, uses injection moulding machine injection moulding, to obtain final product.

Beneficial effect of the present invention

Composite heat dissipation material of the present invention employs magnesium oxide, boron nitride, create good composite collaborative radiating effect, by using SEBS, modification is carried out to boron nitride, the notched Izod impact strength of material is improved, by using short glass fiber, alumina whisker, through modification, thermal conductivity and the mechanical property of matrix material are improved, and electrical property remains on higher level; By using ferrotitanium powder, flakey highly-conductive hot carbon powder, micron order aluminum nitride powder, there is good collaborative radiating effect, substantially increase the thermal diffusivity of material; By using 2-fluoroacrylic methyl ester, improve the toughness of material, tensile property and antifouling property.

Embodiment

A kind of high-heat dissipation LED lamp PA10T composite heat dissipation material, is made up of the raw material of following weight part (kilogram): magnesium oxide 41, boron nitride 21, short glass fiber 2.5, polymeric amide PA10T31, alumina whisker 7.5, ferrotitanium powder 2.5, flakey highly-conductive hot carbon powder 2.5, micron order aluminum nitride powder 3.5,2-fluoroacrylic methyl ester 3.5, polyvinyl butyral acetal 1.3, ethanol 6.5, SEBS3.5.

The production method of described high-heat dissipation LED lamp PA10T composite heat dissipation material, is characterized in that:

(1) polyvinyl butyral acetal is added in ethanol, be heated to 80 DEG C, be stirred to resin all to dissolve, add ferrotitanium powder, flakey highly-conductive hot carbon powder, micron order aluminum nitride powder again, stir, then add short glass fiber, alumina whisker stirs, dry, pulverize, obtain modified oxidized aluminium whiskers;

(2) boron nitride mixed with SEBS, 2-fluoroacrylic methyl ester, send into twin screw extruder, through melt extruding, water-cooled pelletizing, obtains pellet;

(3) polymeric amide PA10T is dry, the pellet obtained with (2) step and other remaining components mix, and enter from the main spout of parallel dual-screw extruding machine, modified oxidized aluminium whiskers enters from side spout, through melt extruding, water-cooled pelletizing obtains pellet; Forcing machine each section of temperature is respectively: 280,320,310,310 DEG C, screw speed is set as 400r/min; Then forced air drying 4h at 130 DEG C, uses injection moulding machine injection moulding, to obtain final product.

Experimental data: the normal direction thermal conductivity of this heat sink material is 3.69W/mK.

Claims (2)

1. a high-heat dissipation LED lamp PA10T composite heat dissipation material, is characterized in that being made up of the raw material of following weight part: magnesium oxide 40-42, boron nitride 20-22, short glass fiber 2-3, polymeric amide PA10T30-32, alumina whisker 7-8, ferrotitanium powder 2-3, flakey highly-conductive hot carbon powder 2-3, micron order aluminum nitride powder 3-4,2-fluoroacrylic methyl ester 3-4, polyvinyl butyral acetal 1-1.5, ethanol 6-7, SEBS3-4.

2. the production method of high-heat dissipation LED lamp PA10T composite heat dissipation material according to claim 1, is characterized in that:

(1) polyvinyl butyral acetal is added in ethanol, be heated to 80-82 DEG C, be stirred to resin all to dissolve, add ferrotitanium powder, flakey highly-conductive hot carbon powder, micron order aluminum nitride powder again, stir, then add short glass fiber, alumina whisker stirs, dry, pulverize, obtain modified oxidized aluminium whiskers;

(2) boron nitride mixed with SEBS, 2-fluoroacrylic methyl ester, send into twin screw extruder, through melt extruding, water-cooled pelletizing, obtains pellet;

(3) polymeric amide PA10T is dry, the pellet obtained with (2) step and other remaining components mix, and enter from the main spout of parallel dual-screw extruding machine, modified oxidized aluminium whiskers enters from side spout, through melt extruding, water-cooled pelletizing obtains pellet; Forcing machine each section of temperature is respectively: 280,320,310,310 DEG C, screw speed is set as 400r/min; Then forced air drying 4-5h at 125-130 DEG C, uses injection moulding machine injection moulding, to obtain final product.