CN105056287B - 一种除螨抗菌医用绷带 - Google Patents
一种除螨抗菌医用绷带 Download PDFInfo
- Publication number
- CN105056287B CN105056287B CN201510453622.4A CN201510453622A CN105056287B CN 105056287 B CN105056287 B CN 105056287B CN 201510453622 A CN201510453622 A CN 201510453622A CN 105056287 B CN105056287 B CN 105056287B
- Authority
- CN
- China
- Prior art keywords
- gastral cavity
- modification
- minutes
- paddy gastral
- chitin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种除螨抗菌医用绷带，该医用绷带用的原料是由谷脘蛋白纤维、甲壳素纤维与棉纤维混纺而成，所述的谷脘蛋白纤维、甲壳素纤维与棉纤维原料的重量比为谷脘蛋白纤维：棉纤维=10‑15：20‑30：30‑60。采用该绷带除具有传统杀菌抑菌、洁净功能外还具有改善血液循环，促进新陈代谢，消除疲劳，醒神健脑的效果，且制得的绷带手感滑爽，柔顺舒爽，吸湿透气，更具舒适感，是一种全新型的抗菌除螨医用绷带。
Description
技术领域
本发明涉及一种除螨抗菌医用绷带。
背景技术
绷带是医疗以及日常生活中的必需品，那么选择性的在绷带加工过程中添加中药原料与有机棉、蛋白质纤维、竹纤维、抗菌材料、玉石粉混合制成，可使现有的绷带不仅在具有传统杀菌抑菌、洁净功能外还具有改善血液循环，促进新陈代谢，消除疲劳，醒神健脑，淡斑美白的效果，且制得的绷带手感滑爽，柔顺舒爽，吸湿透气，更具舒适感，是一种全新型的抗菌除螨医用绷带。中国是中医的始祖，历史悠久，药材原料种类丰富，取材范围辽阔，且因中药具有疗效明显、安全无刺激性、毒副作用在中西外前景广阔，其消费水平在百姓中也更易接受， 因此采用中草原料与绷带制备材料的有机结合的确具有很好的前景。
发明内容
本发明所要解决的技术问题在于，提供一种柔软度和抑菌性好通过改性剂制备的由谷脘蛋白纤维与棉纤维混纺而成绷带制品。采用该绷带除具有传统杀菌抑菌、洁净功能外还具有改善血液循环，促进新陈代谢，消除疲劳，醒神健脑的效果，且制得的绷带手感滑爽，柔顺舒爽，吸湿透气，更具舒适感，是一种全新型的抗菌除螨医用绷带。
本发明的技术内容为：一种除螨抗菌医用绷带，该医用绷带用的原料是由谷脘蛋白纤维、甲壳素纤维与棉纤维混纺而成，所述的谷脘蛋白纤维、甲壳素纤维与棉纤维原料的重量比为谷脘蛋白纤维：甲壳素纤维：棉纤维=10-15：20-30：30-60，制备包括以下步骤：
（1）谷脘蛋白预处理：
精选2500公支-3000公支优质谷脘蛋白纤维，将谷脘蛋白纤维均匀撕成小块后分成小堆；
（2）甲壳素改性处理：
首先，将改性液喷洒在堆置的甲壳素纤维上，改性处理12-24小时；所述改性液是由下述重量百分比的各原料组成：溴氰菊酯2-3%、烷基磷酸酯5-8%、甲基雄烯二醇2-4%、酯基季铵盐0.1-0.3%、钛酸酯偶联剂5-7%、剩余为水；
改性处理用的改性液量均为甲壳素纤维重量的8-11％；
然后，将甲壳素纤维送入蒸汽室内，蒸35-55分钟；
（3）谷脘蛋白改性处理：
首先，将甲壳素改性处理用的改性液喷洒在堆置的谷脘蛋白纤维上，改性处理12-24小时；
然后，将谷脘蛋白纤维送入蒸汽室内，蒸35-55分钟；在上述改性液中加入其体积1-2%的JFC、1-2%鼠尾草、1-2%藿香、1-2%百部、1-2%黄连、1-2%的丁香油，再进行二次改性，改性处理48-60小时；
每次改性处理用的改性液量均为谷脘蛋白纤维重量的7-9％；
（4）将改性处理后的谷脘蛋白、甲壳素与棉纤维按上述比例上槽大堆混合；
（5）按照传统工序进行梳棉、精梳、并条、纺粗纱、纺细纱、络筒、并线、倍捻即得原料混纱；
所述的医用绷带的制备方法包括以下步骤：
（1）将上述得到的原料混纱织造成绷带坯巾；
（2）将织好的坯巾浸入退煮漂联合机的热水槽中，浴比为1:20-27，先用95-100℃的水清洗25-36分钟，再降低温度5-10℃，水清洗4-8分钟，然后在水中加入整理助剂，调整水溶液温度为65-75℃，清洗40-50分钟；所述的整理助剂由下列重量份原料制成：环氧氯丙烷3-6、抗菌微胶囊7-9、1-十五醇12-14、聚六亚甲基胍0.4-0.7、海藻酸钾2.1-2.6、烷基磷酸酯5-7、脂肪醇聚氧乙烯醚6-8、纳米二氧化硅2-3等；所述抗菌微胶囊的抗菌成分是以氯苯咪唑类高分子化合物和拟除虫菊类化合物为主；
（3）再将上述坯巾用温度为90-100℃清水煮30-40分钟，再加入亲水柔软剂、纤维酶、聚丙烯酰胺和硫酸镁，在上述温度下继续煮10-20分钟；并出布，用脱水机脱水20-25分钟；
（4）烘干定型：将已脱水的坯巾经开幅机开幅，然后经烘干机在110-130℃下烘干处理18-25分钟，即得所述医用绷带。
优选地，所述的纺粗纱工艺中，工艺参数为：粗纱捻系数为100-120、粗纱锭速为600-700转/min。
优选地，所述的纺细纱工艺中，工艺参数为：细纱捻系数为800-1000、细纱锭速为8000-10000转/min。
小麦是我国主要农作物，小麦后加工和综合利用对我国国民经济的发展以及社会稳定具有重要作用。近年来由于食品、化工、生物、医药行业的发展，小麦淀粉的用途不断扩大，其产量逐年增加。作为小麦淀粉加工工业、以小麦为原料的发酵工业等副产品的谷朊粉即小麦蛋白粉，其产量逐年增加，目前中国年产量达到10万吨以上，世界年产量达到50万吨以上，来源广泛、成本低廉。谷朊粉中的蛋白质含量超过80%，其中的主要蛋白质成分为醇溶蛋白与麦谷蛋白，两者各占40%左右。醇溶蛋白分子量较小，分子间通过键能较低的氢键和疏水键相互作用；麦谷蛋白分子量较大，分子间通过二硫键相连。两种蛋白质的相互作用使得小麦蛋白比其他植物蛋白具有更好的延展性和湿热稳定性。
烷基磷酸酯能够对蛋白质、纤维素产生交联作用，且交联过程高效、无毒；环氧氯丙烷能够在碱作为催化剂的情况下与蛋白质中的氨基发生反应，对蛋白质大分子产生交联作用。
本发明所具有的优点是：本发明生产抗菌除螨医用绷带的成本低及生产工艺简单与高效；本发明生产的谷朊蛋白、甲壳素纤维与混纺纤维不仅拉伸力学性能好，而且可完全降解，生物相容性好，可应用于高品质纺织品的制造以及生物、医药、组织工程等领域；采用其制备的绷带可以有效不仅在具有传统杀菌抑菌、洁净功能外还具有改善血液循环，促进新陈代谢，消除疲劳，醒神健脑的效果，且制得的绷带手感滑爽，柔顺舒爽，吸湿透气，更具舒适感，是一种全新型的抗菌除螨医用绷带。
具体实施方式
下面结合具体实施例对本发明作进一步详细描述。
实施例1：
一种抗菌除螨医用绷带的制备方法，该医用绷带用的原料是由谷脘蛋白纤维、甲壳素纤维与棉纤维混纺而成，所述的谷脘蛋白纤维、甲壳素纤维与棉纤维原料的重量比为谷脘蛋白纤维：甲壳素纤维：棉纤维=10：20：30，制备包括以下步骤：
（1）谷脘蛋白预处理：
精选2500公支-3000公支优质谷脘蛋白纤维，将谷脘蛋白纤维均匀撕成小块后分成小堆；
（2）甲壳素改性处理：
首先，将改性液喷洒在堆置的甲壳素纤维上，改性处理12-24小时；所述改性液是由下述重量百分比的各原料组成：溴氰菊酯2%、烷基磷酸酯5%、甲基雄烯二醇2%、酯基季铵盐0.1%、钛酸酯偶联剂5%、剩余为水；
改性处理用的改性液量均为甲壳素纤维重量的8％；
然后，将甲壳素纤维送入蒸汽室内，蒸35-55分钟；
（3）谷脘蛋白改性处理：
首先，将甲壳素改性处理用的改性液喷洒在堆置的谷脘蛋白纤维上，改性处理12-24小时；
然后，将谷脘蛋白纤维送入蒸汽室内，蒸35-55分钟；在上述改性液中加入其体积1%的JFC、1%鼠尾草、1%藿香、1%百部、1%黄连、1%的丁香油，再进行二次改性，改性处理48小时；
每次改性处理用的改性液量均为谷脘蛋白纤维重量的7％；
（4）将改性处理后的谷脘蛋白、甲壳素与棉纤维按上述比例上槽大堆混合；
（5）按照传统工序进行梳棉、精梳、并条、纺粗纱、纺细纱、络筒、并线、倍捻即得原料混纱；
所述的医用绷带的制备方法包括以下步骤：
（1）将上述得到的原料混纱织造成绷带坯巾；
（2）将织好的坯巾浸入退煮漂联合机的热水槽中，浴比为1:20，先用95℃的水清洗25分钟，再降低温度5℃，水清洗4-8分钟，然后在水中加入整理助剂，调整水溶液温度为65℃，清洗40-50分钟；所述的整理助剂由下列重量份原料制成：环氧氯丙烷3、抗菌微胶囊7、1-十五醇12、聚六亚甲基胍0.4、海藻酸钾2.1、烷基磷酸酯5、脂肪醇聚氧乙烯醚6、纳米二氧化硅2；所述抗菌微胶囊的抗菌成分是以氯苯咪唑类高分子化合物和拟除虫菊类化合物为主；
（3）再将上述坯巾用温度为90℃清水煮30分钟，再加入亲水柔软剂、纤维酶、聚丙烯酰胺和硫酸镁，在上述温度下继续煮10-20分钟；并出布，用脱水机脱水20-25分钟；
（4）烘干定型：将已脱水的坯巾经开幅机开幅，然后经烘干机在110℃下烘干处理18-25分钟，即得所述医用绷带。
所述的纺粗纱工艺中，工艺参数为：粗纱捻系数为100-120、粗纱锭速为600-700转/min。所述的纺细纱工艺中，工艺参数为：细纱捻系数为800-1000、细纱锭速为8000-10000转/min。
实施例2 ：
一种抗菌除螨医用绷带的制备方法，该医用绷带用的原料是由谷脘蛋白纤维、甲壳素纤维与棉纤维混纺而成，所述的谷脘蛋白纤维、甲壳素纤维与棉纤维原料的重量比为谷脘蛋白纤维：甲壳素纤维：棉纤维=15：30：60，制备包括以下步骤：
（1）谷脘蛋白预处理：
精选2500公支-3000公支优质谷脘蛋白纤维，将谷脘蛋白纤维均匀撕成小块后分成小堆；
（2）甲壳素改性处理：
首先，将改性液喷洒在堆置的甲壳素纤维上，改性处理12-24小时；所述改性液是由下述重量百分比的各原料组成：溴氰菊酯3%、烷基磷酸酯8%、甲基雄烯二醇4%、酯基季铵盐0.3%、钛酸酯偶联剂7%、剩余为水；
改性处理用的改性液量均为甲壳素纤维重量的11％；
然后，将甲壳素纤维送入蒸汽室内，蒸35-55分钟；
（3）谷脘蛋白改性处理：
首先，将甲壳素改性处理用的改性液喷洒在堆置的谷脘蛋白纤维上，改性处理12-24小时；
然后，将谷脘蛋白纤维送入蒸汽室内，蒸35-55分钟；在上述改性液中加入其体积2%的JFC、2%鼠尾草、2%藿香、2%百部、2%黄连、2%的丁香油，再进行二次改性，改性处理48-60小时；
每次改性处理用的改性液量均为谷脘蛋白纤维重量的9％；
（4）将改性处理后的谷脘蛋白、甲壳素与棉纤维按上述比例上槽大堆混合；
（5）按照传统工序进行梳棉、精梳、并条、纺粗纱、纺细纱、络筒、并线、倍捻即得原料混纱；
所述的医用绷带的制备方法包括以下步骤：
（1）将上述得到的原料混纱织造成绷带坯巾；
（2）将织好的坯巾浸入退煮漂联合机的热水槽中，浴比为1:27，先用100℃的水清洗25-36分钟，再降低温度10℃，水清洗4-8分钟，然后在水中加入整理助剂，调整水溶液温度为75℃，清洗40-50分钟；所述的整理助剂由下列重量份原料制成：环氧氯丙烷6、抗菌微胶囊9、1-十五醇14、聚六亚甲基胍0.7、海藻酸钾2.6、烷基磷酸酯7、脂肪醇聚氧乙烯醚8、纳米二氧化硅3；所述抗菌微胶囊的抗菌成分是以氯苯咪唑类高分子化合物和拟除虫菊类化合物为主；
（3）再将上述坯巾用温度为100℃清水煮30-40分钟，再加入亲水柔软剂、纤维酶、聚丙烯酰胺和硫酸镁，在上述温度下继续煮10-20分钟；并出布，用脱水机脱水20-25分钟；
（4）烘干定型：将已脱水的坯巾经开幅机开幅，然后经烘干机在130℃下烘干处理18-25分钟，即得所述医用绷带。
所述的纺粗纱工艺中，工艺参数为：粗纱捻系数为100-120、粗纱锭速为600-700转/min。所述的纺细纱工艺中，工艺参数为：细纱捻系数为800-1000、细纱锭速为8000-10000转/min。
上述说明已经充分揭露了本发明的具体实施方式。需要指出的是，熟悉该领域的技术人员对本发明的具体实施方式所做的任何改动 均不脱离本发明的权利要求书的范围。相应地，本发明的权利要求的范围也并不仅仅局限于前述具体实施方式。
Claims (3)
1.一种除螨抗菌医用绷带，其特征在于，该医用绷带用的原料是由谷脘蛋白纤维、甲壳素纤维与棉纤维混纺而成，所述的谷脘蛋白纤维、甲壳素纤维与棉纤维原料的重量比为谷脘蛋白纤维：甲壳素纤维：棉纤维=10-15：20-30：30-60，制备包括以下步骤：
（1）谷脘蛋白预处理：
精选2500公支-3000公支优质谷脘蛋白纤维，将谷脘蛋白纤维均匀撕成小块后分成小堆；
（2）甲壳素改性处理：
首先，将改性液喷洒在堆置的甲壳素纤维上，改性处理12-24小时；所述改性液是由下述重量百分比的各原料组成：溴氰菊酯2-3%、烷基磷酸酯5-8%、甲基雄烯二醇2-4%、酯基季铵盐0.1-0.3%、钛酸酯偶联剂5-7%、剩余为水；
改性处理用的改性液量均为甲壳素纤维重量的8-11％；
然后，将甲壳素纤维送入蒸汽室内，蒸35-55分钟；
（3）谷脘蛋白改性处理：
首先，将甲壳素改性处理用的改性液喷洒在堆置的谷脘蛋白纤维上，改性处理12-24小时；
然后，将谷脘蛋白纤维送入蒸汽室内，蒸35-55分钟；在上述改性液中加入其体积1-2%的JFC、1-2%鼠尾草、1-2%藿香、1-2%百部、1-2%黄连、1-2%的丁香油，再进行二次改性，改性处理48-60小时；
每次改性处理用的改性液量均为谷脘蛋白纤维重量的7-9％；
（4）将改性处理后的谷脘蛋白、甲壳素与棉纤维按上述比例上槽大堆混合；
（5）按照传统工序进行梳棉、精梳、并条、纺粗纱、纺细纱、络筒、并线、倍捻即得原料混纱；
所述的医用绷带的制备方法包括以下步骤：
（1）将上述得到的原料混纱织造成绷带坯巾；
（2）将织好的坯巾浸入退煮漂联合机的热水槽中，浴比为1:20-27，先用95-100℃的水清洗25-36分钟，再降低温度5-10℃，水清洗4-8分钟，然后在水中加入整理助剂，调整水溶液温度为65-75℃，清洗40-50分钟；所述的整理助剂由下列重量份原料制成：环氧氯丙烷3-6、抗菌微胶囊7-9、1-十五醇12-14、聚六亚甲基胍0.4-0.7、海藻酸钾2.1-2.6、烷基磷酸酯5-7、脂肪醇聚氧乙烯醚6-8、纳米二氧化硅2-3；所述抗菌微胶囊的抗菌成分是以氯苯咪唑类高分子化合物和拟除虫菊类化合物为主；
（3）再将上述坯巾用温度为90-100℃清水煮30-40分钟，再加入亲水柔软剂、纤维酶、聚丙烯酰胺和硫酸镁，在上述温度下继续煮10-20分钟；并出布，用脱水机脱水20-25分钟；
（4）烘干定型：将已脱水的坯巾经开幅机开幅，然后经烘干机在110-130℃下烘干处理18-25分钟，即得所述医用绷带。
2.根据权利要求1所述的除螨抗菌医用绷带，其特征在于：所述的纺粗纱工艺中，工艺参数为：粗纱捻系数为100-120、粗纱锭速为600-700转/min。
3.根据权利要求1或2所述的除螨抗菌医用绷带，其特征在于：所述的纺细纱工艺中，工艺参数为：细纱捻系数为800-1000、细纱锭速为8000-10000转/min。