CN105040979A - Cleaning method of building formwork capable of being repeatedly used - Google Patents
Cleaning method of building formwork capable of being repeatedly used Download PDFInfo
- Publication number
- CN105040979A CN105040979A CN201510432361.8A CN201510432361A CN105040979A CN 105040979 A CN105040979 A CN 105040979A CN 201510432361 A CN201510432361 A CN 201510432361A CN 105040979 A CN105040979 A CN 105040979A
- Authority
- CN
- China
- Prior art keywords
- cleaning
- template
- cement
- dipping form
- aluminum dipping
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a cleaning method of a building formwork capable of being repeatedly used. The cleaning method comprises a manual slag removing step, a hanging soaking and ultrasonic wave cleaning step, a hanging and cleaning agent cleaning step and a hanging and high-pressure water washing step. The method can be used for cleaning cement on the surface of the building formwork, and solves the problem that the cement on the surface of the building formwork made of composite materials cannot be cleaned, so that the building formwork can realize 100-percent recovery and utilization; the number of repeated use times of raw materials is improved; the material waste is reduced; the economic benefits are improved; the environment pollution is reduced; and environment-friendly and pollution-free effects are achieved in the cleaning process.
Description
Technical field
The present invention is specifically related to a kind of cleaning method reusing construction formwork.
Background technology
In composite material building mould board system, after an engineering uses, building shutter panel is bonded with a certain amount of cement, affects the use of construction formwork.After building site uses, construction formwork divides two kinds, and one is that surface is bonded with cement, but formwork structure is complete, continues to use after can cleaning the cement of template surface; One is that template has damaged impact continuation use, produces inserts by doing template after crushing washing.At present domestic also do not have glass fiber reinforced polypropylene composite material template clean and reuse utilize effective ways.
Summary of the invention
The technical problem to be solved in the present invention, is to provide a kind of cleaning method reusing construction formwork.
The present invention is achieved in that a kind of cleaning method reusing construction formwork, comprises the following steps:
(1) manually remove the gred: template surface small size cement block perching knife shovel falls, template surface large area cement block cement floor Plane surface grinding machine is removed, the four limit perching knives with lockhole are rooted out, cement block celt iron hammer in lockhole and reinforcing rib chamber cuts, and adopts to impact electric pick and remove when vestibule blocks completely;
(2) immersion Ultrasonic Cleaning is hung: the top hanging template, and the template that suspended on is immersed 3min in the ultrasonic cleaner that QL-999 building aluminum dipping form deslagging agent solution is housed, adopt ultrasonic wave each position to template to carry out comprehensive high-strength impact, the dissolution coordinating QL-999 to build aluminum dipping form deslagging agent solution carries out soaking and washing to the cement slurry of template surface;
(3) hang cleaning agent cleaning: utilize high pressure QL-999 to be built aluminum dipping form deslagging agent solution jet to the template surface that suspended on, carry out high-pressure spraying and rinse 2min, and from upper, left and right three direction cleaning showers template surface cement layers;
(4) hang high-pressure washing: the template surface 1min that be suspended on by high pressure tap water spray irrigation, build aluminum dipping form deslagging agent solution with the QL-999 cleaning template surface, finally drip, dry.
Further, described QL-999 builds in aluminum dipping form deslagging agent solution, and weight ratio QL-999 builds aluminum dipping form deslagging agent: water=1:0 ~ 3.
The invention has the advantages that: capable of washing fall construction formwork wash cement, solve the cement cleaning problem on composite material building mould board surface, make construction formwork can realize 100% recycling, improve and raw-materially reuse number of times, reduce the waste of material, increase economic efficiency, reduce environment pollution, and cleaning process is environment friendly and pollution-free.
Detailed description of the invention
Reuse a cleaning method for construction formwork, comprise the following steps:
(1) manually remove the gred: template surface small size cement block perching knife shovel falls, template surface large area cement block cement floor Plane surface grinding machine is removed, the four limit perching knives with lockhole are rooted out, cement block celt iron hammer in lockhole and reinforcing rib chamber cuts, and adopts to impact electric pick and remove when vestibule blocks completely;
(2) immersion Ultrasonic Cleaning is hung: the top hanging template, and the template that suspended on is immersed 3min in the ultrasonic cleaner that QL-999 building aluminum dipping form deslagging agent solution is housed, adopt ultrasonic wave each position to template to carry out comprehensive high-strength impact, the dissolution coordinating QL-999 to build aluminum dipping form deslagging agent solution carries out soaking and washing to the cement slurry of template surface;
(3) hang cleaning agent cleaning: utilize high pressure QL-999 to be built aluminum dipping form deslagging agent solution jet to the template surface that suspended on, carry out high-pressure spraying and rinse 2min, and from upper, left and right three direction cleaning showers template surface cement layers;
(4) hang high-pressure washing: the template surface 1min that be suspended on by high pressure tap water spray irrigation, build aluminum dipping form deslagging agent solution with the QL-999 cleaning template surface, finally drip, dry.
Described QL-999 builds in aluminum dipping form deslagging agent solution, and weight ratio QL-999 builds aluminum dipping form deslagging agent: water=1:0 ~ 3.
Although the foregoing describe the specific embodiment of the present invention; but be familiar with those skilled in the art to be to be understood that; specific embodiment described by us is illustrative; instead of for the restriction to scope of the present invention; those of ordinary skill in the art, in the modification of the equivalence done according to spirit of the present invention and change, should be encompassed in scope that claim of the present invention protects.
Claims (2)
1. can reuse a cleaning method for construction formwork, it is characterized in that: comprise the following steps:
(1) manually remove the gred: template surface small size cement block perching knife shovel falls, template surface large area cement block cement floor Plane surface grinding machine is removed, the four limit perching knives with lockhole are rooted out, cement block celt iron hammer in lockhole and reinforcing rib chamber cuts, and adopts to impact electric pick and remove when vestibule blocks completely;
(2) immersion Ultrasonic Cleaning is hung: the top hanging template, and the template that suspended on is immersed 3min in the ultrasonic cleaner that QL-999 building aluminum dipping form deslagging agent solution is housed, adopt ultrasonic wave each position to template to carry out comprehensive high-strength impact, the dissolution coordinating QL-999 to build aluminum dipping form deslagging agent solution carries out soaking and washing to the cement slurry of template surface;
(3) hang cleaning agent cleaning: utilize high pressure QL-999 to be built aluminum dipping form deslagging agent solution jet to the template surface that suspended on, carry out high-pressure spraying and rinse 2min, and from upper, left and right three direction cleaning showers template surface cement layers;
(4) hang high-pressure washing: the template surface 1min that be suspended on by high pressure tap water spray irrigation, build aluminum dipping form deslagging agent solution with the QL-999 cleaning template surface, finally drip, dry.
2. a kind of cleaning method reusing construction formwork as claimed in claim 1, is characterized in that: described QL-999 builds in aluminum dipping form deslagging agent solution, and weight ratio QL-999 builds aluminum dipping form deslagging agent: water=1:0 ~ 3.