CN105038696A - Bonding agent for bonding optical lenses and manufacturing method of bonding agent - Google Patents
Bonding agent for bonding optical lenses and manufacturing method of bonding agent Download PDFInfo
- Publication number
- CN105038696A CN105038696A CN201510372114.3A CN201510372114A CN105038696A CN 105038696 A CN105038696 A CN 105038696A CN 201510372114 A CN201510372114 A CN 201510372114A CN 105038696 A CN105038696 A CN 105038696A
- Authority
- CN
- China
- Prior art keywords
- tackiness agent
- optical mirror
- mirror slip
- raw material
- industrial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bonding agent for bonding optical lenses. The bonding agent is prepared from the compositions of industrial rosin and industrial paraffin. Meanwhile, the invention discloses a manufacturing method of the bonding agent for bonding the optical lenses. The manufacturing method comprises the following steps of (1) mixing the industrial rosin and the industrial paraffin into a mixed raw material according to a certain mass ratio; (2) melting the mixed raw material into mixed solution; (3) cooling and solidifying the mixed solution. By adopting the bonding agent disclosed by the invention, multiple thin optical lenses can be stacked and bonded together to form a thick optical lens, so that the thick optical lens can be conveniently clamped to carry out cutting machining; after cutting machining is completed, the thick optical lens can also be divided into the multiple thin optical lenses which are subjected to cutting machining treatment, not only can the thin optical lenses be prevented from being damaged during a cutting process, but also the cutting quality and the cutting efficiency can be increased; multiple thin optical lenses can be cut at the same time during a process of cutting the thick optical lens.
Description
Technical field
The present invention relates to optical mirror slip field, particularly a kind of tackiness agent for the optical mirror slip that bonds and preparation method thereof.
Background technology
At present, some optical mirror slip thinner, when needing to clamp the thinner optical mirror slip of such Thickness Ratio and carrying out cutting processing, the optical mirror slip of monolithic is in the process of being cut by clamping, easily be caught broken or leave catcher mark on optical mirror slip, simultaneously monolithic optical mirror slip due to its thickness too thin, easily broken or occur that breach phenomenon appears in cut edge in cutting process, had a strong impact on cutting quality.
Summary of the invention
In order to solve the problem, the object of the present invention is to provide tackiness agent of a kind of optical mirror slip that can bond and preparation method thereof, optical mirror slip thinner for multi-disc Thickness Ratio overlap can be bonded together to form the thicker thick optical mirror slip of one piece of Thickness Ratio by the tackiness agent manufactured by this making method, therefore can clamp this thick optical mirror slip and carry out cutting processing, optical mirror slip is effectively prevented easily to be caught broken or to have catcher mark, also improve cutting quality simultaneously, after cutting processing, cleaner in environmental protection can be adopted to be melted by the tackiness agent be bonded on thick optical mirror slip, thus thick optical mirror slip is resolved into the thin optical mirror slip of multi-disc, and then obtain the optical mirror slip of multi-disc through cutting processing, contribute to improving cutting efficiency.
The present invention is the technical scheme that its technical problem of solution adopts:
For a tackiness agent for the optical mirror slip that bonds, the moiety of described tackiness agent is industrial rosin and industrial paraffin.
As the improvement of technique scheme, in described tackiness agent, industrial rosin and the composition quality of industrial paraffin are than being 1:8.
For a making method for the tackiness agent of the optical mirror slip that bonds, comprise the following steps:
1) mixing raw material, by the industrial rosin of solid state and industrial paraffin in mass ratio for the proportioning of 1:8 mixes and obtain required mixing raw material;
2) heat fused, puts the mixing raw material obtained in step 1) into heating tank and heats, and mixing raw material is melted completely and is mixed into together and obtains required mixing liquid;
3) cooled and solidified, by step 2) in the mixing liquid that obtains pour in container and carry out cooled and solidified, thus obtain the required tackiness agent in solid state.
Further, described step 2) in heating tank process that mixing raw material is heated, after the temperature of heating tank is to 150-160 DEG C, the temperature of heating tank remains unchanged, until mixing raw material melts completely and mixes.
Further again, mixing liquid is poured in container and is placed 4-20 hour by described step 3), and liquid naturally cooling to be mixed is frozen into solid state.
In the present invention, the container in described step 3) is a forming jig.
The invention has the beneficial effects as follows: because thin for multi-disc optical mirror slip overlap can be bonded together to form one piece of thick optical mirror slip by tackiness agent of the present invention, so that clamp thick optical mirror slip to carry out cutting processing, after completion of processing to be cut, thick optical mirror slip can be decomposed again and obtain the thin optical mirror slip of multi-disc through cutting processing process, both can prevent thin optical mirror slip from damaging in cutting process, cutting quality and cutting efficiency can be improved again, in the process of cutting one piece of thick optical mirror slip, namely can cut the thin optical mirror slip of multi-disc simultaneously.
One can be obtained quickly and easily by making method of the present invention and both thin for multi-disc optical mirror slip can be bonded together securely the thick optical mirror slip of formation, under the effect of solvating agent, thick optical mirror slip can be resolved into the tackiness agent of the thin optical mirror slip of multi-disc simultaneously.
Accompanying drawing explanation
Below in conjunction with the drawings and specific embodiments, the present invention is further detailed explanation.
Fig. 1 is the schema of making method of the present invention.
Embodiment
For a tackiness agent for the optical mirror slip that bonds, the moiety of described tackiness agent is industrial rosin and industrial paraffin.In order to make tackiness agent have enough cohesive forces and viscosity, in the present invention, preferably, in described tackiness agent, industrial rosin is 1:8 with the composition quality ratio of industrial paraffin.
With reference to Fig. 1, a kind of making method of the tackiness agent for the optical mirror slip that bonds, comprises the following steps:
1) mixing raw material, by the industrial rosin of solid state and industrial paraffin in mass ratio for the proportioning of 1:8 mixes and obtain required mixing raw material;
2) heat fused, put the mixing raw material obtained in step 1) into heating tank to heat, after the temperature of heating tank is to 150-160 DEG C, the temperature of heating tank remains unchanged, until mixing raw material melts completely and mixes and obtain required mixing liquid, in the present invention, the temperature that described heating tank heats up when heating mixing raw material is preferably 155 DEG C, after the temperature of heating tank is raised to 155 DEG C, the temperature of heating tank remains unchanged, until mixing raw material melts completely and mixes.Can mix better after melting completely to make mixing raw material, in the present invention, the solution of stirring mechanism to mixing raw material can also be adopted to stir, and the solution after mixing raw material is melted mixes more fully and forms mixing liquid;
3) cooled and solidified, by step 2) in the mixing liquid that obtains pour in container and place 4-20 hour, liquid naturally cooling to be mixed is frozen into solid state, thus obtain the required tackiness agent in solid state, in the present invention, the time that described mixing liquid places naturally cooling is in a reservoir preferably 12 hours;
4) check, the tackiness agent obtaining solid state is tested, see whether its caking ability, solubleness close symbol requirement in step 3).
In the present invention, get quantitative fetching tackiness agent to carry out bonding optical mirror slip for the ease of follow-up, preferably, the container in described step 3) is a forming jig, and is a forming jig with certain specification capacity, by by step 2) in mixing liquid pour cooled and solidified in forming jig into, the adhesive solids that one piece of block is identical in quality can be obtained, follow-up when needing to use tackiness agent, only need to calculate the quantity of tackiness agent, without the need to weighing, easy to use.
The foregoing is only preferred embodiments of the present invention, as long as the technical scheme realizing the object of the invention with basic same approach all belongs within protection scope of the present invention.
Claims (6)
1. for a tackiness agent for the optical mirror slip that bonds, it is characterized in that: the moiety of described tackiness agent is industrial rosin and industrial paraffin.
2. a kind of tackiness agent for the optical mirror slip that bonds according to claim 1, is characterized in that: in described tackiness agent, industrial rosin and the composition quality of industrial paraffin are than being 1:8.
3. make a making method for a kind of tackiness agent for the optical mirror slip that bonds described in claim 1 or 2, it is characterized in that, comprise the following steps:
1) mixing raw material, by the industrial rosin of solid state and industrial paraffin in mass ratio for the proportioning of 1:8 mixes and obtain required mixing raw material;
2) heat fused, puts the mixing raw material obtained in step 1) into heating tank and heats, and mixing raw material is melted completely and is mixed into together and obtains required mixing liquid;
3) cooled and solidified, by step 2) in the mixing liquid that obtains pour in container and carry out cooled and solidified, thus obtain the required tackiness agent in solid state.
4. the making method of a kind of tackiness agent for the optical mirror slip that bonds according to claim 3, it is characterized in that: described step 2) in heating tank process that mixing raw material is heated, after the temperature to 150 DEG C-160 DEG C of heating tank, the temperature of heating tank remains unchanged, until mixing raw material melts completely and mixes.
5. the making method of a kind of tackiness agent for the optical mirror slip that bonds according to claim 3, is characterized in that: mixing liquid is poured in container and placed 4-20 hour by described step 3), and liquid naturally cooling to be mixed is frozen into solid state.
6. the making method of a kind of tackiness agent for the optical mirror slip that bonds according to claim 3 or 4 or 5, is characterized in that: the container in described step 3) is a forming jig.