CN105038651A - High-peel-strength hot melt adhesive particularly applicable to bonding of packing paper - Google Patents
High-peel-strength hot melt adhesive particularly applicable to bonding of packing paper Download PDFInfo
- Publication number
- CN105038651A CN105038651A CN201510462397.0A CN201510462397A CN105038651A CN 105038651 A CN105038651 A CN 105038651A CN 201510462397 A CN201510462397 A CN 201510462397A CN 105038651 A CN105038651 A CN 105038651A
- Authority
- CN
- China
- Prior art keywords
- parts
- melt adhesive
- hot melt
- resin
- add
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-peel-strength hot melt adhesive particularly applicable to bonding of packing paper. The hot melt adhesive is prepared from the following raw materials in parts by weight: 105-110 parts of EVA, 10-20 parts of modified tackifying resin, 1-2 parts of dodecyl trimethyl ammonium chloride, 10-15 parts of nanometer barite powder, 20-25 parts of nanometer bentonite, 20-30 parts of neoprene, 10-20 parts of phenolic resin, 4-5 parts of epoxy butyl oleate, 2-5 parts of triethyl acetyl citrate, 1-2 parts of urotropine and 1-2 parts of isophthalic acid. The prepared hot melt adhesive can meet the adhesive requirements of all fields, and is environment-friendly, economical, and beneficial to the environment.
Description
Technical field
The invention belongs to binding agent field, particularly relate to a kind of high-peeling strength hot melt adhesive being specially adapted to wrapping paper bonding.
Background technology
EVA hot-melt adhesive is formulated by EVA resin, tackifier, softening agent, antioxidant, filler etc.In society now, EVA hot-melt adhesive applied range, consumption are maximum.It has excellent adhesiveproperties, nearly all has hot sticky relay to various material; Excellent electric property; And its melt viscosity is low, applying glue is convenient; With the feature such as the consistency of other Synergist S-421 95s is good.EVA hot-melt adhesive has been widely used in shaping, many fields such as automobile and building materials of the bookbinding of books, bonding, ceramic etc. the reparation of the packaging, plastics etc. of food, mounting, clothes and shoes and hats.Because EVA resin is a kind of thermoplastic resin, high and low temperature resistance is limited, softening temperature is low, and main auxiliary material tackifier are all the polymkeric substance of molecular weight mostly, just play reduction melt viscosity, improve the effect of wetting ability and initial cohesiveness, itself is high-low temperature resistant not, causes the shortcoming of EVA hot-melt adhesive not high-low temperature resistant; Simultaneously also there is lower, the not resistance to fatty oil of adhesiveproperties, easily produce skinning and be not suitable for the shortcomings such as big area coating is bonding in EVA hot-melt adhesive.
At present, along with developing rapidly of PET industry, waste PET quantity also increases thereupon, thus brings serious pollution to environment.How to recycle waste PET, become one of focus of research at present.PET reclaims and mainly comprises physiochemical mutagens and chemical recovery two kinds of methods, physiochemical mutagens method cost is lower, but after physiochemical mutagens, the Mr(relative molecular mass of material) and limiting viscosity all reduce, the PET product be made up of physiochemical mutagens material can not be reused this way and recycle; Chemical recovery makes PET generate micromolecular compound by chemical reaction, and the performance of this method products therefrom is more excellent.Chemical recovery technique can be divided into hydrolysis, ammonia solution and alcoholysis etc. (wherein alcoholysis process is chemical recovery technique relatively more conventional at present), as Pereira etc. utilizes the polyester of degraded to make tensio-active agent.
Summary of the invention
The object of this invention is to provide a kind of high-peeling strength hot melt adhesive being specially adapted to wrapping paper bonding.
The present invention adopts following technical scheme to achieve these goals:
A kind of high-peeling strength hot melt adhesive being specially adapted to wrapping paper bonding, it is characterized in that, it is obtained by the raw material of following weight parts: EVA105-110, modified tacky resin 10-20, Dodecyl trimethyl ammonium chloride 1-2, nano-barite powder 10-15, nano-bentonite 20-25, chloroprene rubber 20-30, resol 10-20, epoxyoleic acid butyl ester 4-5, acetyl triethyl citrate 2-5, urotropine 1-2, m-phthalic acid 1-2;
Described modified tacky resin is obtained by the raw material of following weight parts:
Waste PET fragment 40-50, zinc acetate 3-4, thiorubber 10-15, chloroprene rubber 5-7, alkyl phenolic resin 20-30, styrene resin 5-10, trimethyloctadecyl ammonium chloride 1-2, carbide slag 10-20, gac 2-4;
The preparation method of described modified tacky resin is:
(1) by after carbide slag, gac mixing, ultraviolet irradiation 8-12h, then in concentration be 5-8% hydrochloric acid soln in soak 10-12h, solid-liquid separation is carried out to soak solution, dry, obtain the composite powder of modification for subsequent use;
(2) washing, dried waste PET fragment are joined in reactor in proportion, then add zinc acetate; Slowly be warming up to zinc acetate under nitrogen protection when dissolving completely, warming while stirring to 230-250 DEG C, insulation reaction 3-4h; Be cooled to 200-210 DEG C, then add thiorubber, chloroprene rubber, alkyl phenolic resin, styrene resin, stirring reaction 10-20min; Add the composite powder of modification and all the other raw materials again, after stirring 1-2h, discharging cooling stripping and slicing.
Described a kind of high-peeling strength hot melt adhesive being specially adapted to wrapping paper bonding, is characterized in that: preparation method comprises the following steps:
(1) nano-barite powder, Dodecyl trimethyl ammonium chloride add appropriate amount of deionized water mixing, fully disperse under 100-200 rev/min, dry after obtained compound size, then mix with chloroprene rubber, and twin screw extruder is extruded, and cools intercalation rubber mass is for subsequent use;
(2) kneader is preheated to wall temperature 190-200 DEG C, then adds EVA, resol, epoxyoleic acid butyl ester by weight, mediates 10-20min; After add surplus stock by weight, at 180-190 DEG C, mediate 30-40min, take out cool and get final product.
Beneficial effect of the present invention:
(1) through intercalation modifying, can improve the mechanical property of rubber, heat-drawn wire improves, and water-absorbent is low, use it to prepare consistency that hot melt adhesive can increase each raw material of hot melt adhesive, improves viscosity and water-repellancy.
(2) modified tacky resin batching rationally, the composite powder of modification wherein contains carbide slag, turn waste into wealth, can carbide slag sterilization be given by uv irradiation again, the hole of carbide slag, gac can be increased simultaneously, strengthen the avidity with resin, ageing-resistant, resistance to air loss is good, not only significantly improves the properties of hot melt adhesive with the composite powder of modification as the new raw material of hot melt adhesive, and has made new contribution for environmental protection.
(3) waste PET fragment by degraded after, then with all the other tackifying resins and the good melting of the composite powder of modification, obtained tackifying resin viscosity is high, and hardness strength performance satisfies the demands; Composite powder can be better dispersed in PET and remaining resin by modified, can increase the tensile strength of sizing material, hardness, nontoxic pollution-free; The present invention successfully by pet waste for the preparation of in hot melt adhesive, obtained hot melt adhesive can meet the sizing agent demand in each field, environmental protection, economy, useful environment.
embodiment,
A kind of high-peeling strength hot melt adhesive being specially adapted to wrapping paper bonding, it is obtained by the raw material of following weight (kg): EVA110, modified tacky resin 20, Dodecyl trimethyl ammonium chloride 1, nano-barite powder 10, nano-bentonite 20, chloroprene rubber 20, resol 10, epoxyoleic acid butyl ester 4, acetyl triethyl citrate 5, urotropine 1, m-phthalic acid 1;
Described modified tacky resin is obtained by the raw material of following weight (kg):
Waste PET fragment 50, zinc acetate 4, thiorubber 15, chloroprene rubber 7, alkyl phenolic resin 20, styrene resin 5, trimethyloctadecyl ammonium chloride 1, carbide slag 10, gac 2;
The preparation method of described modified tacky resin is:
(1) by after carbide slag, gac mixing, ultraviolet irradiation 9h, then in concentration be 5-8% hydrochloric acid soln in soak 10-12h, solid-liquid separation is carried out to soak solution, dry, obtain the composite powder of modification for subsequent use;
Ultraviolet light source in uv irradiation adopts power 1000W, the high voltage mercury lamp fluorescent tube of spectral range 365-450nm, peak value 365nm;
(2) washing, dried waste PET fragment are joined in reactor in proportion, then add zinc acetate; Slowly be warming up to zinc acetate under nitrogen protection when dissolving completely, warming while stirring to 230-250 DEG C, insulation reaction 3-4h; Be cooled to 200-210 DEG C, then add thiorubber, chloroprene rubber, alkyl phenolic resin, styrene resin, stirring reaction 10-20min; Add the composite powder of modification and all the other raw materials again, after stirring 1-2h, discharging cooling stripping and slicing.
Described a kind of high-peeling strength hot melt adhesive being specially adapted to wrapping paper bonding, is characterized in that: preparation method comprises the following steps:
(1) nano-barite powder, Dodecyl trimethyl ammonium chloride add appropriate amount of deionized water mixing, fully disperse under 100-200 rev/min, dry after obtained compound size, then mix with chloroprene rubber, and twin screw extruder is extruded, and cools intercalation rubber mass is for subsequent use;
(2) kneader is preheated to wall temperature 190-200 DEG C, then adds EVA, resol, epoxyoleic acid butyl ester by weight, mediates 10-20min; After add surplus stock by weight, at 180-190 DEG C, mediate 30-40min, take out cool and get final product.
The apparent viscosity of the hot melt adhesive of the present embodiment is 4800MPa.s, stripping strength 52N/2.5cm, and initial bonding strength reaches No. 5 steel balls, open hour 37s, and within 24 hours, thermally-stabilised proterties is stablized.
Claims (2)
1. one kind is specially adapted to the high-peeling strength hot melt adhesive of wrapping paper bonding, it is characterized in that, it is obtained by the raw material of following weight parts: EVA105-110, modified tacky resin 10-20, Dodecyl trimethyl ammonium chloride 1-2, nano-barite powder 10-15, nano-bentonite 20-25, chloroprene rubber 20-30, resol 10-20, epoxyoleic acid butyl ester 4-5, acetyl triethyl citrate 2-5, urotropine 1-2, m-phthalic acid 1-2;
Described modified tacky resin is obtained by the raw material of following weight parts:
Waste PET fragment 40-50, zinc acetate 3-4, thiorubber 10-15, chloroprene rubber 5-7, alkyl phenolic resin 20-30, styrene resin 5-10, trimethyloctadecyl ammonium chloride 1-2, carbide slag 10-20, gac 2-4;
The preparation method of described modified tacky resin is:
(1) by after carbide slag, gac mixing, ultraviolet irradiation 8-12h, then in concentration be 5-8% hydrochloric acid soln in soak 10-12h, solid-liquid separation is carried out to soak solution, dry, obtain the composite powder of modification for subsequent use;
(2) washing, dried waste PET fragment are joined in reactor in proportion, then add zinc acetate; Slowly be warming up to zinc acetate under nitrogen protection when dissolving completely, warming while stirring to 230-250 DEG C, insulation reaction 3-4h; Be cooled to 200-210 DEG C, then add thiorubber, chloroprene rubber, alkyl phenolic resin, styrene resin, stirring reaction 10-20min; Add the composite powder of modification and all the other raw materials again, after stirring 1-2h, discharging cooling stripping and slicing.
2. a kind of high-peeling strength hot melt adhesive being specially adapted to wrapping paper bonding according to claim 1, is characterized in that: preparation method comprises the following steps:
(1) nano-barite powder, Dodecyl trimethyl ammonium chloride add appropriate amount of deionized water mixing, fully disperse under 100-200 rev/min, dry after obtained compound size, then mix with chloroprene rubber, and twin screw extruder is extruded, and cools intercalation rubber mass is for subsequent use;
(2) kneader is preheated to wall temperature 190-200 DEG C, then adds EVA, resol, epoxyoleic acid butyl ester by weight, mediates 10-20min; After add surplus stock by weight, at 180-190 DEG C, mediate 30-40min, take out cool and get final product.