CN105038646A - Anti-bacterial hot melt adhesive containing nanometer titanium dioxide - Google Patents
Anti-bacterial hot melt adhesive containing nanometer titanium dioxide Download PDFInfo
- Publication number
- CN105038646A CN105038646A CN201510461960.2A CN201510461960A CN105038646A CN 105038646 A CN105038646 A CN 105038646A CN 201510461960 A CN201510461960 A CN 201510461960A CN 105038646 A CN105038646 A CN 105038646A
- Authority
- CN
- China
- Prior art keywords
- parts
- melt adhesive
- hot melt
- titanium dioxide
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-bacterial hot melt adhesive containing nanometer titanium dioxide. The hot melt adhesive is prepared from the following raw materials in parts by weight: 65-70 parts of EVA, 10-20 parts of modified tackifying resin, 20-30 parts of butyl rubber, 1-2 parts of dodecyl trimethyl ammonium chloride, 1-2 parts of aluminum oxide, 1-2 parts of calcium oxide, 1-2 parts of zinc oxide, 3-6 parts of 2402 resin, 2-6 parts of oxhide gelatin, 1.5-2.9 parts of paraffin, 3-5 parts of epoxy butyl oleate, 20-25 parts of bauxite powder, 1-3 parts of naphthenic oil and 10-20 parts of nanometer titanium dioxide. The hot melt adhesive contains anti-bacterial components such as zinc oxide and nanometer titanium dioxide; through composition of the anti-bacterial components and other raw materials, the hot melt adhesive has the characteristics of being high in adhesive strength and anti-bacterial capability, short in open time, and high in curing speed.
Description
Technical field
The invention belongs to binding agent field, particularly relate to a kind of Antibacterial hot melt adhesive containing nanometer titanium dioxide.
Background technology
EVA hot-melt adhesive is formulated by EVA resin, tackifier, softening agent, antioxidant, filler etc.In society now, EVA hot-melt adhesive applied range, consumption are maximum.It has excellent adhesiveproperties, nearly all has hot sticky relay to various material; Excellent electric property; And its melt viscosity is low, applying glue is convenient; With the feature such as the consistency of other Synergist S-421 95s is good.EVA hot-melt adhesive has been widely used in shaping, many fields such as automobile and building materials of the bookbinding of books, bonding, ceramic etc. the reparation of the packaging, plastics etc. of food, mounting, clothes and shoes and hats.Because EVA resin is a kind of thermoplastic resin, high and low temperature resistance is limited, softening temperature is low, and main auxiliary material tackifier are all the polymkeric substance of molecular weight mostly, just play reduction melt viscosity, improve the effect of wetting ability and initial cohesiveness, itself is high-low temperature resistant not, causes the shortcoming of EVA hot-melt adhesive not high-low temperature resistant; Simultaneously also there is lower, the not resistance to fatty oil of adhesiveproperties, easily produce skinning and be not suitable for the shortcomings such as big area coating is bonding in EVA hot-melt adhesive.
At present, along with developing rapidly of PET industry, waste PET quantity also increases thereupon, thus brings serious pollution to environment.How to recycle waste PET, become one of focus of research at present.PET reclaims and mainly comprises physiochemical mutagens and chemical recovery two kinds of methods, physiochemical mutagens method cost is lower, but after physiochemical mutagens, the Mr(relative molecular mass of material) and limiting viscosity all reduce, the PET product be made up of physiochemical mutagens material can not be reused this way and recycle; Chemical recovery makes PET generate micromolecular compound by chemical reaction, and the performance of this method products therefrom is more excellent.Chemical recovery technique can be divided into hydrolysis, ammonia solution and alcoholysis etc. (wherein alcoholysis process is chemical recovery technique relatively more conventional at present), as Pereira etc. utilizes the polyester of degraded to make tensio-active agent.
Summary of the invention
The object of this invention is to provide a kind of Antibacterial hot melt adhesive containing nanometer titanium dioxide.
The present invention adopts following technical scheme to achieve these goals:
A kind of Antibacterial hot melt adhesive containing nanometer titanium dioxide, it is characterized in that, it is obtained by the raw material of following weight parts: EVA65-70, modified tacky resin 10-20, isoprene-isobutylene rubber 20-30, Dodecyl trimethyl ammonium chloride 1-2, aluminum oxide 1-2, calcium oxide 1-2, zinc oxide 1-2,2402 resin 3-6, carpenter's glue 2-6, paraffin 1.5-2.9, epoxyoleic acid butyl ester 3-5, bauxite powder 20-25, naphthenic oil 1-3, nanometer titanium dioxide 10-20;
Described modified tacky resin is obtained by the raw material of following weight parts:
Waste PET fragment 40-50, zinc acetate 3-4, thiorubber 10-15, chloroprene rubber 5-7, alkyl phenolic resin 20-30, styrene resin 5-10, trimethyloctadecyl ammonium chloride 1-2, carbide slag 10-20, gac 2-4;
The preparation method of described modified tacky resin is:
(1) by after carbide slag, gac mixing, ultraviolet irradiation 8-12h, then in concentration be 5-8% hydrochloric acid soln in soak 10-12h, solid-liquid separation is carried out to soak solution, dry, obtain the composite powder of modification for subsequent use;
(2) washing, dried waste PET fragment are joined in reactor in proportion, then add zinc acetate; Slowly be warming up to zinc acetate under nitrogen protection when dissolving completely, warming while stirring to 260 DEG C, insulation reaction 3-4h; Be cooled to 200-210 DEG C, then add thiorubber, chloroprene rubber, alkyl phenolic resin, styrene resin, stirring reaction 10-20min; Add the composite powder of modification and all the other raw materials again, after stirring 1-2h, discharging cooling stripping and slicing.
Described a kind of Antibacterial hot melt adhesive containing nanometer titanium dioxide, is characterized in that: preparation method comprises the following steps:
(1) attapulgite, Dodecyl trimethyl ammonium chloride add appropriate amount of deionized water mixing, fully disperse under 300-400 rev/min, dry after obtained compound size, then mix with isoprene-isobutylene rubber, and twin screw extruder is extruded, and cools to obtain intercalation rubber mass;
(2) kneader is preheated to wall temperature 180-190 DEG C, then adds EVA, aluminum oxide, calcium oxide, zinc oxide by weight, mediates 10-20min;
(3) add intercalation rubber mass and surplus stock by weight after, at 180-190 DEG C, mediate 10-20min, take out and cool and get final product.
Beneficial effect of the present invention:
(1) the present invention contain zinc oxide, nanometer titanium dioxide etc. antimicrobial component, composite with all the other raw materials, it is large that gained hot melt adhesive has bonding strength, the feature that antibacterial ability is good, and the open hour are short, curing speed is fast;
Through intercalation modifying, can improve the mechanical property of nylon, heat-drawn wire improves, and water-absorbent is low, use it to prepare consistency that hot melt adhesive can increase each raw material of hot melt adhesive, improves viscosity and water-repellancy.
(2) modified tacky resin batching rationally, the composite powder of modification wherein contains carbide slag, turn waste into wealth, can carbide slag sterilization be given by uv irradiation again, the hole of carbide slag, gac can be increased simultaneously, strengthen the avidity with resin, ageing-resistant, resistance to air loss is good, not only significantly improves the properties of hot melt adhesive with the composite powder of modification as the new raw material of hot melt adhesive, and has made new contribution for environmental protection.
(3) waste PET fragment by degraded after, then with all the other tackifying resins and the good melting of the composite powder of modification, obtained tackifying resin viscosity is high, and hardness strength performance satisfies the demands; Composite powder can be better dispersed in PET and remaining resin by modified, can increase the tensile strength of sizing material, hardness, nontoxic pollution-free; The present invention successfully by pet waste for the preparation of in hot melt adhesive, obtained hot melt adhesive can meet the sizing agent demand in each field, environmental protection, economy, useful environment.
Embodiment
A kind of Antibacterial hot melt adhesive containing nanometer titanium dioxide, it is obtained by the raw material of following weight (kg): EVA65, modified tacky resin 20, isoprene-isobutylene rubber 30, Dodecyl trimethyl ammonium chloride 2, aluminum oxide 1, calcium oxide 1, zinc oxide 1,2402 resin 3, carpenter's glue 2, paraffin 1.9, epoxyoleic acid butyl ester 5, bauxite powder 25, naphthenic oil 1, nanometer titanium dioxide 20;
Described modified tacky resin is obtained by the raw material of following weight (kg):
Waste PET fragment 40, zinc acetate 3, thiorubber 15, chloroprene rubber 5, alkyl phenolic resin 20, styrene resin 10, trimethyloctadecyl ammonium chloride 1, carbide slag 10, gac 2;
The preparation method of described modified tacky resin is:
(1) by after carbide slag, gac mixing, ultraviolet irradiation 12h, then in concentration be 5% hydrochloric acid soln in soak 10h, solid-liquid separation is carried out to soak solution, dry, obtain the composite powder of modification for subsequent use;
Ultraviolet light source in uv irradiation adopts power 1000W, the high voltage mercury lamp fluorescent tube of spectral range 365-450nm, peak value 365nm;
(2) washing, dried waste PET fragment are joined in reactor in proportion, then add zinc acetate; Slowly be warming up to zinc acetate under nitrogen protection when dissolving completely, warming while stirring to 260 DEG C, insulation reaction 3h; Be cooled to 210 DEG C, then add thiorubber, chloroprene rubber, alkyl phenolic resin, styrene resin, stirring reaction 20min; Add the composite powder of modification and all the other raw materials again, after stirring 2h, discharging cooling stripping and slicing.
Described a kind of Antibacterial hot melt adhesive containing nanometer titanium dioxide, preparation method comprises the following steps:
(1) attapulgite, Dodecyl trimethyl ammonium chloride add appropriate amount of deionized water mixing, fully disperse under 400 revs/min, dry after obtained compound size, then mix with isoprene-isobutylene rubber, and twin screw extruder is extruded, and cools to obtain intercalation rubber mass;
(2) kneader is preheated to wall temperature 180 DEG C, then adds EVA, aluminum oxide, calcium oxide, zinc oxide by weight, mediates 15min;
(3) add intercalation rubber mass and surplus stock by weight after, at 180 DEG C, mediate 20min, take out and cool and get final product.
The apparent viscosity of the hot melt adhesive of the present embodiment is 5300MPa.s, stripping strength 51N/2.5cm, and initial bonding strength reaches No. 5 steel balls, open hour 36s, and within 24 hours, thermally-stabilised proterties is stablized.
Claims (2)
1. the Antibacterial hot melt adhesive containing nanometer titanium dioxide, it is characterized in that, it is obtained by the raw material of following weight parts: EVA65-70, modified tacky resin 10-20, isoprene-isobutylene rubber 20-30, Dodecyl trimethyl ammonium chloride 1-2, aluminum oxide 1-2, calcium oxide 1-2, zinc oxide 1-2,2402 resin 3-6, carpenter's glue 2-6, paraffin 1.5-2.9, epoxyoleic acid butyl ester 3-5, bauxite powder 20-25, naphthenic oil 1-3, nanometer titanium dioxide 10-20;
Described modified tacky resin is obtained by the raw material of following weight parts:
Waste PET fragment 40-50, zinc acetate 3-4, thiorubber 10-15, chloroprene rubber 5-7, alkyl phenolic resin 20-30, styrene resin 5-10, trimethyloctadecyl ammonium chloride 1-2, carbide slag 10-20, gac 2-4;
The preparation method of described modified tacky resin is:
(1) by after carbide slag, gac mixing, ultraviolet irradiation 8-12h, then in concentration be 5-8% hydrochloric acid soln in soak 10-12h, solid-liquid separation is carried out to soak solution, dry, obtain the composite powder of modification for subsequent use;
(2) washing, dried waste PET fragment are joined in reactor in proportion, then add zinc acetate; Slowly be warming up to zinc acetate under nitrogen protection when dissolving completely, warming while stirring to 260 DEG C, insulation reaction 3-4h; Be cooled to 200-210 DEG C, then add thiorubber, chloroprene rubber, alkyl phenolic resin, styrene resin, stirring reaction 10-20min; Add the composite powder of modification and all the other raw materials again, after stirring 1-2h, discharging cooling stripping and slicing.
2. a kind of Antibacterial hot melt adhesive containing nanometer titanium dioxide according to claim 1, is characterized in that: preparation method comprises the following steps:
(1) attapulgite, Dodecyl trimethyl ammonium chloride add appropriate amount of deionized water mixing, fully disperse under 300-400 rev/min, dry after obtained compound size, then mix with isoprene-isobutylene rubber, and twin screw extruder is extruded, and cools to obtain intercalation rubber mass;
(2) kneader is preheated to wall temperature 180-190 DEG C, then adds EVA, aluminum oxide, calcium oxide, zinc oxide by weight, mediates 10-20min;
(3) add intercalation rubber mass and surplus stock by weight after, at 180-190 DEG C, mediate 10-20min, take out and cool and get final product.