CN105038590B - Oiliness metallic paint and its preparation, application method and application - Google Patents
Oiliness metallic paint and its preparation, application method and application Download PDFInfo
- Publication number
- CN105038590B CN105038590B CN201510532109.4A CN201510532109A CN105038590B CN 105038590 B CN105038590 B CN 105038590B CN 201510532109 A CN201510532109 A CN 201510532109A CN 105038590 B CN105038590 B CN 105038590B
- Authority
- CN
- China
- Prior art keywords
- metallic paint
- oiliness
- oiliness metallic
- paint
- furniture
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to oiliness metallic paint technical field, specifically discloses a kind of oiliness metallic paint and its preparation, application method and application.The oiliness metallic paint includes the recipe ingredient of following parts by weight：Aromatic hydrocarbon solvent 53~70；Dispersant 0.1 1；Anti-settling agent 5~7；Wetting agent 5~10；Pigment 20~30.Described oiliness metallic paint have the characteristics that rapid draing and stably, colour saturation it is high, disclosure satisfy that demand of the European style furniture to coating.When being coated on the surface of wood substrate furniture using painting method provided by the invention, wooden texture can be retained, it is lucuriant in design so that strong third dimension and stereovision is presented in furniture.Therefore there is good application prospect in field of furniture.
Description
Technical field
The present invention relates to technical field of coatings, more particularly to a kind of oiliness metallic paint and its preparation, application method and application.
Background technology
Increasingly pursuing today of graceful quality of the life, classic European style furniture enjoys the happiness of domestic and international many consumers
Love and use.
Classic European style furniture is usually as ground material, collocation gold from deep (such as Manchurian ash) timber of wood grain
The gorgeous color such as color, silver color, and the effect coated using semi open model, to highlight the wood grain stereovision of furniture and third dimension,
By such mode, classic luxurious and modern honorable European style is showed incisively and vividly.
Therefore, researching and developing one kind can be applied on European style furniture, embody the oil of honorable ornamental decorative style
Property metallic paint has huge market prospects.
The content of the invention
The purpose of the embodiment of the present invention be to provide a kind of oiliness metallic paint that can be applied on European style furniture and
It is prepared, application method.
To achieve the above object of the invention, the technical scheme that the embodiment of the present invention uses is as follows：
A kind of oiliness metallic paint, the oiliness metallic paint include the recipe ingredient of following parts by weight：
The oiliness metallic paint is made up of the component of following parts by weight：
And a kind of preparation method of oiliness metallic paint, comprise the following steps：
The aromatic hydrocarbon solvent, dispersant, anti-settling agent, wetting agent and pigment are weighed according to recipe ingredient as described above is weighed；
The aromatic hydrocarbon solvent, dispersant, the anti-settling agent weighed is added under 300~400rpm mixing speeds, is then adjusted
Section mixing speed is 1000~1200rpm, carries out first time mixing treatment；
Adjustment mixing speed is 300~400rpm, adds the wetting agent and pigment weighed, then adjusts mixing speed
For 1000~1200rpm, second of mixing treatment is carried out.
And correspondingly, a kind of application method of oiliness metallic paint, comprise the following steps：
A, surface cleaning processing is carried out to base material to be coated；
B, finish paint spray treatment, oiliness metallic paint coating processing and polishing are carried out successively to the base material after the cleaning treatment
Processing.
Correspondingly, a kind of wood substrate furniture, the wood substrate furniture surface coating by above-mentioned oiliness metallic paint or on
The oiliness metallic paint for stating the preparation of oiliness metallic paint preparation method provides, and the wood substrate furniture surface coating is according to above-mentioned oiliness
The application method of metallic paint is formed.
The oiliness metallic paint of above-described embodiment, raw material type is few, is easy to make.With rate of drying soon and stably, color it is dense
The features such as high is spent, can meet the needs of European style furniture is to coating.
The oiliness metallic paint of above-described embodiment uses above-mentioned preparation method, only needs conventional equipment, easy to operate, production cost
It is low, it is adapted to large-scale production.Existing nigrescence phenomenon when can especially avoid the pigment from using aluminium powder.
In above-described embodiment, the application method of oiliness metallic paint, the textured pattern of base material to be coated, and can either be presented
Hole for nailing and seam are enough hidden, also makes the base material of coating that strong third dimension be presented, and it is easy for construction, grinability is good.
Wood substrate furniture in above-described embodiment, oiliness metallic paint and above-mentioned oiliness metallic paint using above-mentioned offer
Coating method decorated, furniture surface is lucuriant in design, has strong wood grain stereovision and third dimension, can show fine
European style.
Embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, following examples, the present invention is carried out
It is further described.It should be appreciated that specific embodiment described herein is not used to limit this only to explain the present invention
Invention.
The embodiments of the invention provide a kind of formula of oiliness metallic paint, the oiliness metallic paint includes following parts by weight
Recipe ingredient：
Wherein,
In any embodiment, aromatic hydrocarbon solvent is using any of dimethylbenzene, trimethylbenzene.In one embodiment, select
Use mesitylene.Mesitylene has good dissolubility and dispersiveness, can quickly dissolve other components and adjust each component
Dispersity.
In any embodiment, using electroneutral polyamide and polyester mixture as dispersant.Electroneutral polyamide with
Polyester has good dispersive property, prevents other components from precipitating using the mixture that arbitrary proportion is formed as dispersant,
Carry out whole system organic scattered.
In one embodiment, anti-settling agent uses organobentonite.The organobentonite is that inorganic mineral/organic ammonium is compound
Thing, the thixotropy of oiliness metallic paint can be improved so that the storage stability of oiliness metallic paint is improved, and is advantageous to put for a long time
Put.And cause oiliness metallic paint that there is preferable mobility, be easy to coat, paint film occurs without sagging phenomenon during coating.In addition,
Organobentonite in the present embodiment, it also may be such that other components are uniformly dispersed.
In any embodiment, wetting agent has good wetting action to solids fraction, can quick humidification solids fraction,
And realize that solids fraction merges with the acceleration of liquid composition.In any embodiment, wetting agent is using refining linseed oil, refining
Linseed oil has good wetability and construction wiping.
To realize that oiliness metallic paint color of the embodiment of the present invention shows honorable and graceful texture, in any embodiment
In, it is properly added a certain amount of pigment.The pigment is any of specific aluminium powder, copper powder.
The oiliness metallic paint that above-described embodiment provides, have the characteristics that drying quickly and stably, depth it is high
Correspondingly, on the basis of embodiments of the present invention oiliness metal paint formula, the embodiment of the present invention additionally provides
The preparation method of the oiliness metallic paint.In one embodiment, the preparation method of the oiliness metallic paint specifically comprises the following steps：
Step S01：The aromatic hydrocarbon solvent, dispersant, anti-settling agent, profit are weighed respectively according to above-mentioned oiliness metal paint formula
Humectant and pigment；
Step S02：The aromatic hydrocarbon solvent weighed, dispersant and anti-settling are added under 300~400rpm mixing speeds
Agent, it is 1000~1200rpm then to adjust mixing speed, carries out first time mixing treatment；
Step S03：Adjustment mixing speed is 300~400rpm, adds the wetting agent and pigment weighed, then adjusts
Mixing speed is 1000~1200rpm, carries out second of mixing treatment.
Specifically, when the aromatic solvent oil, dispersant are added in above-mentioned steps S03, should control in relatively low mixing speed
Lower progress, treat that the aromatic solvent oil, dispersant are added and finished, then it is 1000~1200rpm to adjust mixing speed, and stir speed
The time control for 1000~1200rpm is spent in 20~25min.
Specifically, in above-mentioned steps S03, second of mixing treatment time should be controlled between 20~25min, mixing time
It is too short it is unmixed uniformly and be likely to occur granular solids, influence paint quality；When to avoid pigment be aluminium powder simultaneously, stir for a long time
Mix and cause oiliness metallic paint to black.The preparation method for the oiliness metallic paint that above-described embodiment provides, by the time for controlling stirring
With the speed of stirring, nigrescence phenomenon caused by conventional use aluminium powder makes paint possibility as pigment, this preparation method are prevented
Easy to operate, Production Time is short, has the feasibility and practicality of operation.
Correspondingly, on the basis of embodiments of the present invention oiliness metal paint formula and preparation method, the present invention is implemented
Example additionally provides the application method of the oiliness metallic paint.In one embodiment, the application method of the oiliness metallic paint specifically includes
Following steps：
Step A, surface cleaning processing is carried out to base material to be coated；
Step B, carry out finish paint spray treatment successively to the base material after the cleaning treatment, oiliness metallic paint coating processing and
Grinding process.
Specifically, above-mentioned steps A, which carries out surface cleaning processing to base material to be coated, includes successively carrying out base material to be coated
Sand paper polishing, PU seal coats brush to brush with polishing, PU color inhibition reality colors finish paint carries out putty with polishing, to hole for nailing and seam
Fill and lead up and polish.
Specifically, in above-mentioned steps A, PU seal coats need room temperature to treat dry 4~8h after brushing, then beaten with sand paper
Mill, grinds off bur existing for base material.
Specifically, in above-mentioned steps A, PU color inhibition reality colors finish paint needs room temperature to treat dry 8~12h after brushing, then use sand paper
Polished, need to be carried out along base material grain direction during polishing.
Specifically, in above-mentioned steps A, when being filled and led up to hole for nailing and seam progress putty, it is impossible to the texture of base material is filled and led up, and it is suitable
Base material grain direction to be polished with sand paper.
Specifically, in above-mentioned steps B, spray treatment is carried out using PU color inhibition reality colors finish paint, treat dry 24 in room temperature~
48h, oiliness metallic paint is then directly coated, does not allow to polish before coating oiliness metallic paint, in order to avoid grind off texture or occur not
Smooth flour milling and influence the coating of oiliness metallic paint.
Specifically, in above-mentioned steps B, the coating of oiliness metallic paint is carried out using the mode of looping, control oiliness metallic paint is only
Stay in texture, unnecessary oiliness metallic paint can use the towel of clean dried to wipe.
Specifically, in above-mentioned steps B, room temperature is needed to treat dry 1~2h after the coating of oiliness metallic paint, then with 300~1000 mesh
Sand paper carries out being polishing to surface without bright spot without powder.
Specifically, to avoid the base material of coating oiliness metallic paint, oiliness metallic paint is worn in use, above-mentioned
Step B coats oiliness metallic paint with that after polishing, need to coat one layer from dryness thermoplastic acrylic color inhibition clear finish.
Specifically, above-mentioned process to be done, it is 60%~70% that need to keep humidity.Humidity is too low, and drying is too fast, influences enamelled coating
Adhesiving effect and paint film structure；Humidity is too high, it is not easy to dries, causes coating time long, it is often more important that easily to cause
Bottom is returned in appearance, final to influence coating effect.
Specifically, all bruting process being related in above-mentioned coating procedure, using manual grinding, avoid mechanical grinding from leading
The base material texture of cause is destroyed.
The application method for the oiliness metallic paint that above-described embodiment provides, can remain coated with the texture of base material, and can make
Obtain texture and show strong third dimension and stereovision.
Accordingly, the oiliness metallic paint or the oiliness metallic paint by above-described embodiment offer that the above embodiment of the present invention provides
The oiliness metallic paint for preparing of preparation method, using the application method that above-described embodiment provides by oiliness metallic paint coated in wooden
In base material furniture, can be good at retaining wooden texture, it is lucuriant in design so that furniture surface show good third dimension and
Stereovision.
Above-mentioned oiliness metallic paint and preparation method thereof is illustrated below by way of multiple embodiments.
Embodiment 1
A kind of oiliness metallic paint and preparation method thereof.Wherein, oiliness metallic paint includes the recipe ingredient of following parts by weight：
The preparation method of the oiliness metallic paint comprises the following steps：
First, according to embodiment 1 provide each component weight, weigh 100# aromatic solvents, electroneutral polyamide with
Polyester mixture, organobentonite, refining linseed oil and aluminium powder；Secondly, the reaction that low whipping speed is 300~400rpm is held
The 100# aromatic solvents weighed, electroneutral polyamide and polyester mixture, organobentonite are added in device, then regulation stirring
Speed is 1000~1200rpm, stirs 20min；It is 300~400rpm finally to adjust mixing speed, is added into reaction vessel
The refining linseed oil and aluminium powder weighed, adjustment mixing speed is 1000~1200rpm, continues to stir 20min.
Embodiment 2
A kind of oiliness metallic paint and preparation method thereof.Wherein, oiliness metallic paint includes the recipe ingredient of following parts by weight：
The preparation method of the oiliness metallic paint comprises the following steps：
First, according to embodiment 2 provide each component weight, weigh 100# aromatic solvents, electroneutral polyamide with
Polyester mixture, organobentonite, refining linseed oil and aluminium powder；Secondly, the reaction that low whipping speed is 300~400rpm is held
The 100# aromatic solvents weighed, electroneutral polyamide and polyester mixture, organobentonite are added in device, then regulation stirring
Speed is 1000~1200rpm, stirs 22min；It is 300~400rpm finally to adjust mixing speed, is added into reaction vessel
The refining linseed oil and aluminium powder weighed, adjustment mixing speed is 1000~1200rpm, continues to stir 25min.
Embodiment 3
A kind of oiliness metallic paint and preparation method thereof.Wherein, oiliness metallic paint includes the recipe ingredient of following parts by weight：
The preparation method of the oiliness metallic paint comprises the following steps：
First, according to embodiment 3 provide each component weight, weigh 100# aromatic solvents, electroneutral polyamide with
Polyester mixture, organobentonite, refining linseed oil and aluminium powder；Secondly, the reaction that low whipping speed is 300~400rpm is held
The 100# aromatic solvents weighed, electroneutral polyamide and polyester mixture, organobentonite are added in device, then regulation stirring
Speed is 1000~1200rpm, stirs 25min；It is 300~400rpm finally to adjust mixing speed, is added into reaction vessel
The refining linseed oil and aluminium powder weighed, adjustment mixing speed is 1000~1200rpm, continues to stir 20min.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all essences in the present invention
All any modification, equivalent and improvement made within refreshing and principle etc., should be included in the scope of the protection.
Claims (7)
- A kind of 1. oiliness metallic paint, it is characterised in that：The oiliness metallic paint is made up of the recipe ingredient of following parts by weight：The aromatic hydrocarbon solvent is any of dimethylbenzene, trimethylbenzene；The dispersant is electroneutral polyamide and polyester Mixture；The anti-settling agent is organobentonite；The wetting agent is refining linseed oil；The pigment is in aluminium powder, copper powder It is any.
- 2. a kind of preparation method of oiliness metallic paint, is comprised the following steps：The aromatic hydrocarbon solvent, dispersant, anti-settling agent, wetting agent and pigment are weighed according to recipe ingredient described in claim 1；The aromatic hydrocarbon solvent, dispersant, the anti-settling agent weighed is sequentially added under 300~400rpm mixing speeds, is then adjusted Section mixing speed is 1000~1200rpm, carries out first time mixing treatment；Adjustment mixing speed is 300~400rpm, adds the wetting agent and pigment weighed, then adjusts mixing speed and is 1000~1200rpm, carry out second of mixing treatment.
- 3. the preparation method of oiliness metallic paint as claimed in claim 2, it is characterised in that：At No. first, second batch mixing The mixing time of reason is 20~25min.
- 4. a kind of application method of oiliness metallic paint, comprises the following steps：A, surface cleaning processing is carried out to base material to be coated；B, finish paint spray treatment, oiliness metallic paint coating processing and burnishing part are carried out successively to the base material after the cleaning treatment Reason；Wherein, the medium oil metallic paints of step B are for oiliness metallic paint described in claim 1 or by any institute of claim 2~3 The oiliness metallic paint for stating method preparation provides.
- 5. the application method of oiliness metallic paint as claimed in claim 4, it is characterised in that：In the step A at surface cleaning It is resistance to that reason includes polishing base material, coating PU seal coats, polishing base material bur, coating PU color inhibition reality colors finish paint, polishing PU successively Xanthochromia reality color finish paint surface, putty full-filling hole for nailing and the processing of seam and polishing.
- 6. the application method of the oiliness metallic paint as described in claim 4~5 is any, it is characterised in that：Used in the step B PU color inhibition reality colors finish paint carries out finish paint coating processing, is directly coated in room temperature through 24~72h after dry in a manner of looping The oiliness metallic paint, it is placed in room temperature the grain direction after 1~4h along the base material to be coated and carries out manual grinding processing.
- A kind of 7. wood substrate furniture, it is characterised in that：The face coat of the wood substrate furniture is by as claimed in claim 1 Oiliness metallic paint or the oiliness metallic paint that is prepared by any oiliness metallic paint preparation method of claim 2~3 provide； And/orThe wood substrate furniture surface coating according to the oiliness metallic paint as described in claim 4~6 is any application method Formed.