CN103194144A - Button with hammer effect and preparation method of button - Google Patents
Button with hammer effect and preparation method of button Download PDFInfo
- Publication number
- CN103194144A CN103194144A CN2013101363277A CN201310136327A CN103194144A CN 103194144 A CN103194144 A CN 103194144A CN 2013101363277 A CN2013101363277 A CN 2013101363277A CN 201310136327 A CN201310136327 A CN 201310136327A CN 103194144 A CN103194144 A CN 103194144A
- Authority
- CN
- China
- Prior art keywords
- base material
- button
- hammer
- tone effect
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a button with a hammer effect and a preparation method of the button. The button comprises a base material, and a coating with a hammer effect is sprayed onto the base material and is a mixture of hammer paint, a curing agent and a diluent with the ratio in parts by weight of 1: (0.2-0.3): 0.5. The preparation method comprises the following steps of: processing the base material: carrying out water-grinding treatment on the base material to be sprayed to guarantee that the surface of the base material is clean without pollution; spraying, wherein the viscosity of the coating is controlled for 14s-20s, and then the coating is sprayed onto the base material; and molding, namely naturally drying or stoving the base material with the coating. The button provided by the invention is strong in visual impact and decoration function, simple in preparation method and beneficial to waste reduction, and also has good performance of scratch resistance, friction resistance, shock resistance, washing durability and general chemical corrosion resistance; and the raw materials are easily available, and suitable materials are more.
Description
Technical field
The present invention relates to a kind of button and preparation method thereof, particularly relate to a kind of button with hammer tone effect and preparation method thereof.
Background technology
Hammer paint (having another name called the hammer lacquer) is the history in existing more than 60 year so far, and it has good covering decoration function to ground.This is a kind of round dot one by one that looked sunk, and as being beaten by hammer, and hand feels, and is smooth, and rugged sensation is arranged, and is extraordinary fancy paint.Hammer paint develops into self-drying type by baking-type; Kind develops into present vinylformic acid, urethane and epoxy hammer paint by amino hammer paint, or even aqueous hammer paint etc.; Constructional method is developed into present " one is coated with method " by two step or multistep processes such as initial " spattering the lacquer method ", " spattering solvent method " and " spilling the silicon method "; It is widely used in the decoration of various grounds such as instrument, instrument surface, wood furniture, plastics, cement plane and beautifies.The control of mallear stria form develops into relying on auxiliary agent to regulate by initial only relying on non-floating type aluminium powder and use the mixed solvent with very fast rate of volatilization to regulate, and this has simplified construction technology and operation easier widely, makes the mallear stria of formation have more cubic appearance.
Though hammer paint is ubiquity on market, because the coating content that the spraying of button factory is used is on the low side, color is on the high side, and this and coating factory are difficult to form interest relations, so button factory generally is difficult to obtain this coating.Then can't produce the button of needs according to customer demand, also lose the chance that obtains order.
Summary of the invention
Based on this, the invention provides a kind of button with hammer tone effect and preparation method thereof.
The technical scheme that solves the problems of the technologies described above is as follows:
A kind of button with hammer tone effect, described button comprises base material, spraying has the coating of hammer tone effect on this base material; Described coating is that weight part ratio is the mixture of hammer paint, solidifying agent and the thinner of 1:0.2-0.3:0.5.
Among some embodiment, the component of described hammer paint and weight part are therein:
Polyurethane lacquer 80-95 part,
Mallear stria auxiliary agent 0.1-0.8 part,
Un-suspension powdered aluminium 1-8 part,
Thixotropic anti-settling agent 0.1-1 part,
Mill base or colored paint 0-10 part.
Among some embodiment, the component of described hammer paint and weight part are therein:
Polyurethane lacquer 91-95 part,
Mallear stria auxiliary agent 0.55-0.65 part,
Un-suspension powdered aluminium 4-5 part,
Thixotropic anti-settling agent 0.3-0.5 part,
Mill base or colored paint 0-10 part.
Among some embodiment, described mallear stria auxiliary agent is therein: polymeric silicone compound auxiliary agent or polysiloxane auxiliary agent; Preferred polysiloxane mallear stria auxiliary agent.
Among some embodiment, described aluminium powder has floating type silver powder and non-floating type aluminium powder therein, preferred un-suspension powdered aluminium.
Among some embodiment, the granularity of described un-suspension powdered aluminium is 10-25 μ m therein.
Among some embodiment, described thixotropic anti-settling agent is castor oil derivative, organic remodeling wilkinite, metallic soap, polyethylene wax, superfine silicon dioxide or polynite organic derivative therein; Preferred polynite organic derivative anti-settling agent.
Therein among some embodiment, the material of described base material is metal, unsaturated polyester, wooden, polystyrene, shell or nut.
A kind of preparation method with button of hammer tone effect comprises the steps:
(1) processing of base material: base material to be sprayed is carried out water mill handle, guarantee that substrate surface is totally pollution-free;
(2) spraying: the viscosity of the mixture of control hammer paint, solidifying agent and thinner is 14-20 second, can spray base material;
(3) moulding: base material seasoning or oven dry that step (2) spraying is good get final product; Owing to do not add siccative in the above-mentioned hammer paint, do not use the quick-drying thinner instead, so be best with the roasting mode yet.
Among some embodiment, the temperature of the described oven dry of step (3) is 60-85 ℃ therein, and the time is 30-60min.
A kind of button with hammer tone effect of the present invention and preparation method thereof has following advantage and beneficial effect:
(1) visual impact and decoration function are strong: the button with hammer tone effect that the present invention makes, its surface irregularity, but whole smooth, each nest size depth is close, and nest and nest overlap each other, and form the decorative pattern of similar honeycomb, side seems chain of mountains rows of mountains, more beautiful things than one can take in; Also have good scratch resistance, anti-wear, shock resistance, water-fastness and general chemical corrosion resistance performance simultaneously.
(2) simple to operate: preparation method of the present invention only need add other three kinds or four kinds of chemical substances in polyurethane lacquer can obtain hammer paint, implementation method is simple, easy handling need not to use expensive professional equipment, is fit to extensive operation and operation on a small scale.
(3) raw material is easy to get: the raw material that uses among the preparation method of the present invention is common raw material on the market, obtains easily, can help button factory to break away from dependence to coating factory simultaneously, is more suitable for the personalized production demand of short run.
(4) suitable material is wide: because polyurethane lacquer has good sticking power to wide variety of substrates, therefore, utilize polyurethane lacquer optimization and the hammer paint that comes can be widely used on the buttons such as metal, unsaturated polyester, wooden, nut, shell, ABS injection moulding spraying and form good hammer tone effect.
(5) help to cut the waste: the prepared hammer paint of the present invention has extremely strong bridging effect for the laser pattern literal on button or other materials, printing pattern, slight surface imperfection, resale for after the button of having scrapped application again, can reduce the trouble that wastage of material and waste disposal are brought.
Embodiment
Because the hammer paint consumption that the spraying of button factory is used is on the low side, color is on the high side, and this and coating factory are difficult to form interest relations, so button factory generally is difficult to obtain this coating.And button factory generally is used for the polyurethane lacquer that has good quality the button spraying now, the present invention makes hammer paint by polyurethane lacquer is simply optimized accordingly, this had not only reduced obtaining difficulty but also having guaranteed control and the adjustment of button factory to the mallear stria state of raw material, had also guaranteed the supply of coating.
The principle that mallear stria of the present invention forms is as follows:
The three big major causes of impelling mallear stria to form are: formation and the surface tension effects of kalimeris lattice Buddhist nun (Marangoni) effect, Benard (Benard) nest.Kalimeris lattice Buddhist nun (Marangoni) effect refers to that natural convection weakens under microgravity, under zero gravity, ought to all disappear.But because surface tension works in liquid surface, cause a surface tension gradient, surface tension gradient surpasses viscous force, makes liquid-flow, the kapillary convection current occurs.The rate of volatilization difference of each component in the mixed solvent in liquid coating, the fast component of rate of volatilization is at first overflowed, and causes each layer concentration distribution to differ; The volatilization of solvent simultaneously reduces the temperature on top layer, causes the temperature head between bottom and top layer, and the surface tension gradient that the two acting in conjunction forms makes solvent streams in the top layer to lower floor, and lower floor's solvent streams is to the upper strata, and circulation forms circulation repeatedly.The formation of Benard nest mainly is because the imbalance of coating surface solvent evaporates, make paint film produce the skewness of solids content and temperature, thereby it is mobile to cause that surface tension difference and density difference drive, make coating surface form many little vortexs, and expansion gradually, meet and form interconnective sexangle in the border, the spitting image of honeycomb tissue, along with the evaporation of solvent, further be transformed into low, the high roundlet on every side in many centres.
Usually, button factory sprays employed polyurethane lacquer and has good levelling, anti scuffing, anti-wear, water resisting property and resistance to chemical corrosion, solid content is 50%-80% in the host, wherein main resin mostly is one or more of Synolac, Resins, epoxy, acrylic resin, and this provides the most basic condition for using polyurethane lacquer to be optimized to hammer paint.The sheet un-suspension powdered aluminium is that polyurethane lacquer is optimized to the main factor of hammer paint, after spraying into paint film, because the splash of lacquer liquid forms varnish stain, aluminium powder in the varnish stain sinks, be subjected to the influence of the whirly of solvent evaporates formation, aluminium powder is rotating sinking, so just forms the hammer nest, and each hammer nest couples together and just formed mallear stria.In order to make mallear stria more beautiful and stable, need to add the mallear stria auxiliary agent, mallear stria auxiliary agent and aluminium powder have certain repulsive interaction, so just, stereoscopic sensation and the degree of depth of hammer nest have been strengthened, in addition, most mallear stria auxiliary agent also have to reduce the capillary effect of hammer nest, reduces the levelling ability of paint film, prevents the mallear stria that formed levelling again in drying process.In order to guarantee the storage-stable of hammer paint, prevent aluminium powder sedimentation in storage process, guarantee that again aluminium powder can be heavy as to go down after spraying, so also need to add the anti-settling agent of thixotropic in the system.
Add solidifying agent (ratio of solidifying agent recomputates in former ratio according to the host amount of using) and thinner in the hammer paint of the present invention after optimization, be sprayed directly into after stirring on the button of having handled well, oven dry namely gets the mallear stria button.
Based on this, confirm that through a large amount of experiments and production add un-suspension powdered aluminium slurry, mallear stria auxiliary agent and thixotropic anti-settling agent in polyurethane lacquer, according to the weight part preparation hammer paint of disclosure of the Invention, formed hammer tone effect is best.
Among the following embodiment, polyurethane lacquer: supplier is Northwest fine chemistry industry;
9526 un-suspension powdered aluminiums slurry: supplier is the outstanding pigment of Shenzhen fame company limited;
SP-903 polysiloxane auxiliary agent: sincere chemical industry is won in the supplier Dongguan;
DC-61 silicone compounds auxiliary agent: city far away, Wuhan Lion Rock chemistry painting industry factory;
Bentone SD-2 polynite organic derivative thixotropic anti-settling agent: this moral of supplier's hamming is modest;
Self-drying type nitro alkyd varnish: supplier is coating company limited of state nation;
Silicon-dioxide anti-settling agent: the prosperous brightness chemical industry of Qingyuan City company limited.
Below in conjunction with specific embodiment the present invention is further elaborated.
Embodiment 1 silver color mallear stria unsaturated polyester button
A kind of silver color mallear stria unsaturated polyester button, described button comprises base material, also is coated with the coating of silver color hammer tone effect on the described base material.
The preparation method of silver color mallear stria unsaturated polyester button comprises the steps:
(1) processing of base material: unsaturated polyester base material to be sprayed is carried out water mill handled 40 minutes, guarantee that substrate surface is totally pollution-free;
(2) spraying: with hammer paint, solidifying agent and thinner by weight than mix for 1:0.25:0.5 compo, the viscosity of controlling compo with rock field cup is 17 seconds, can spray base material; The method of described spraying base material is: adopt 1.5mm bore spray gun, about 300ml/min, air pressure adjustment is to the 0.6MPa with flow control, and from being 25cm, spraying swath is adjusted to medium the rifle mouth from the knob identity distance, sprays a cross and gets final product;
The component of above-mentioned hammer paint and weight part are:
94.6 parts of polyurethane lacquers;
0.6 part of SP-903 polysiloxane auxiliary agent;
4.2 parts of 9526 un-suspension powdered aluminiums;
0.4 part of Bentone SD-2 polynite organic derivative thixotropic anti-settling agent;
0.2 part of black color paste, (because aluminium powder directly is added in opacifying power deviation in the varnish, so generally need add a small amount of black or white colorant for increasing opacifying power, this belongs to the toning category);
The preparation method of described hammer paint: by above-mentioned weight part, earlier polyurethane lacquer and Bentone SD-2 polynite organic derivative thixotropic anti-settling agent are mixed, be that the homogenizer of 2000r/min stirs 5 minutes to being uniformly dispersed with rotating speed, add 9526 un-suspension powdered aluminiums and black color paste again, be that the homogenizer of 2000r/min stirs 10 minutes to being uniformly dispersed with rotating speed, add SP-903 polysiloxane auxiliary agent at last, continuation is stirred to make in 2 minutes and is uniformly dispersed;
(3) moulding: the unsaturated polyester base material after will spraying is put into 80 ℃ of baking ovens and is toasted 40min, and cooling gets final product.
Embodiment 2 peak green mallear stria unsaturated polyester buttons
A kind of peak green mallear stria unsaturated polyester button, described button comprises base material, also sprays the coating of silver color hammer tone effect on this base material.
A kind of preparation method of peak green mallear stria unsaturated polyester button comprises the steps:
(1) processing of base material: unsaturated polyester base material to be sprayed is carried out water mill handled 40 minutes, guarantee that substrate surface is totally pollution-free;
(2) spraying: with hammer paint, solidifying agent and thinner by weight than mix for 1:0.25:0.5 compo, the viscosity of controlling compo with rock field cup is 17 seconds, can spray base material; The method of described spraying base material is: adopt 1.5mm bore spray gun, about 300ml/min, air pressure adjustment is to the 0.6MPa with flow control, and from being 25cm, spraying swath is adjusted to medium the rifle mouth from the knob identity distance, sprays a cross and gets final product;
The component of above-mentioned hammer paint and weight part are:
91.8 parts of polyurethane lacquers;
0.6 part of SP-903 polysiloxane auxiliary agent;
4.2 parts of 9526 un-suspension powdered aluminiums;
0.4 part of Bentone SD-2 polynite organic derivative thixotropic anti-settling agent;
3 parts of blue-greenish colour mill bases;
The preparation method of described hammer paint: by above-mentioned weight part, earlier polyurethane lacquer and Bentone SD-2 polynite organic derivative thixotropic anti-settling agent are mixed, be that the homogenizer of 2000r/min stirs 5 minutes to being uniformly dispersed with rotating speed, add 9526 un-suspension powdered aluminiums and blue-greenish colour mill base again, be that the homogenizer of 2000r/min stirs 10 minutes to being uniformly dispersed with rotating speed, add SP-903 polysiloxane auxiliary agent at last, continuation is stirred to make in 2 minutes and is uniformly dispersed;
(3) moulding: the unsaturated polyester base material after will spraying is put into 80 ℃ of baking ovens and is toasted 40min, and cooling gets final product.
Embodiment 3 rose mallear stria copper buttons
A kind of rose mallear stria copper button, described button comprises base material, also sprays the coating of silver color hammer tone effect on this base material.
A kind of preparation method of rose mallear stria copper button comprises the steps:
(1) processing of base material: the slight water mill of copper base material to be sprayed was handled 10 minutes, guaranteed that substrate surface is totally pollution-free;
(2) spraying: with hammer paint, solidifying agent and thinner by weight than mix for 1:0.25:0.5 compo, the viscosity of controlling compo with rock field cup is 17 seconds, can spray base material; The method of described spraying base material is: adopt 1.5mm bore spray gun, about 300ml/min, air pressure adjustment is to the 0.6MPa with flow control, and from being 25cm, spraying swath is adjusted to medium the rifle mouth from the knob identity distance, sprays a cross and gets final product;
The component of the above hammer paint and weight part thereof are:
91.3 parts of polyurethane lacquers;
0.6 part of SP-903 polysiloxane auxiliary agent;
4.2 parts of 9526 un-suspension powdered aluminiums;
0.4 part of Bentone SD-2 polynite organic derivative thixotropic anti-settling agent;
3.5 parts of red mill bases;
The preparation method of described hammer paint: by above-mentioned weight part, earlier polyurethane lacquer and Bentone SD-2 polynite organic derivative thixotropic anti-settling agent are mixed, be that the homogenizer of 2000r/min stirs 5 minutes to being uniformly dispersed with rotating speed, add 9526 un-suspension powdered aluminiums and red mill base again, be that the homogenizer of 2000r/min stirs 10 minutes to being uniformly dispersed with rotating speed, add SP-903 polysiloxane auxiliary agent at last, continuation is stirred to make in 2 minutes and is uniformly dispersed;
(3) moulding: the copper base material after will spraying is put into 80 ℃ of baking ovens and is toasted 40min, and cooling gets final product.
Embodiment 4 black mallear stria injection moulding polystyrene buttons
A kind of black mallear stria injection moulding polystyrene button, described button comprises base material, also sprays the coating of silver color hammer tone effect on this base material.
A kind of preparation method of black mallear stria injection moulding polystyrene button comprises the steps:
(1) processing of base material: the slight water mill of injection moulding polystyrene base material to be sprayed was handled 10 minutes, guaranteed that substrate surface is totally pollution-free;
(2) spraying: with hammer paint, solidifying agent and thinner by weight than mix for 1:0.25:0.5 compo, the viscosity of controlling compo with rock field cup is 17 seconds, can spray base material; The method of described spraying base material is: adopt 1.5mm bore spray gun, about 300ml/min, air pressure adjustment is to the 0.6MPa with flow control, and from being 25cm, spraying swath is adjusted to medium the rifle mouth from the knob identity distance, sprays a cross and gets final product;
The component of the above hammer paint and weight part thereof are:
92.3 parts of polyurethane lacquers;
0.6 part of SP-903 polysiloxane auxiliary agent;
4.2 parts of 9526 un-suspension powdered aluminiums;
0.4 part of Bentone SD-2 polynite organic derivative thixotropic anti-settling agent;
2.5 parts of black color pastes;
The preparation method of described hammer paint: by above-mentioned weight part, earlier polyurethane lacquer and Bentone SD-2 polynite organic derivative thixotropic anti-settling agent are mixed, be that the homogenizer of 2000r/min stirs 5 minutes to being uniformly dispersed with rotating speed, add 9526 un-suspension powdered aluminiums and black color paste again, be that the homogenizer of 2000r/min stirs 10 minutes to being uniformly dispersed with rotating speed, add SP-903 polysiloxane auxiliary agent at last, continuation is stirred to make in 2 minutes and is uniformly dispersed;
(3) moulding: the injection moulding polystyrene button after will spraying is put into 80 ℃ of baking ovens and is toasted 40min, and cooling gets final product.
For embodying the functional of the prepared button with hammer tone effect of the present invention, be described further below by the contrast experiment.
Testing method and equipment:
1, friction resistant performance test: test the experimental installation model according to standard A ATCC 116: TNH06 manufacturer: Dongguan City east inscription Instr Ltd..
2, Washing performance test: ATCC61-1A tests according to standard A, the experimental installation model: SW-12 manufacturer: Laizhou Electron Instrument Co., Ltd..
3, adhesion performance test: 2409-2007 tests according to standard ISO, the experimental installation model: A-5123 manufacturer: German BYK company.
4, family's water-cleaning appearance test: test the experimental installation model according to standard A ATCC 135: XC7001VIS manufacturer: U.S. Whirlpool.
5, store test: test the experimental installation model according to standard A ATCC 163: XMTD-8222 manufacturer: go up the grand experimental installation of Nereid company limited.
6, Commerical dryclean: experimental installation model: the international laundry of K120QD manufacturer: UCC group.
7, press boiling hot test: ATCC-133 tests according to standard A, the experimental installation model: YG-605 manufacturer: Laizhou Electron Instrument Co., Ltd..
Comparative Examples 1
This Comparative Examples 1 described button with hammer tone effect, the preparation method is substantially the same manner as Example 1, and different is: do not contain un-suspension powdered aluminium in the hammer paint, the weight part of polyurethane lacquer is 98.8 parts.
The result shows: only there is oily nest in Comparative Examples 1 prepared button, there is no beautiful mallear stria.
Comparative Examples 2
This Comparative Examples 2 described buttons with hammer tone effect, the preparation method is substantially the same manner as Example 1, and different is: do not contain the polysiloxane auxiliary agent in the hammer paint, the weight part of polyurethane lacquer host is 95 parts.
The result shows: Comparative Examples 2 prepared button mallear strias are tiny and easily by levelling again, hammer nest skewness.
Comparative Examples 3
This Comparative Examples 3 described buttons with hammer tone effect, the preparation method is substantially the same manner as Example 1, and different is: make polyurethane lacquer host into self-drying type nitro alkyd varnish.
Tests such as boiling hot are washed, dry-clean, rub, pressed to this Comparative Examples 3 with embodiment 1～4, and comparing result is as shown in the table:
The hammer paint performance comparison of the different lacquer base of table 1 preparation
* annotate: AATCC/ISO represents method and the standard of testing; 4.5/0 the standard of expression grading, AATCC to be being qualified more than 4.0 grades, is qualified with the 0-1 level among the ISO.
Though in the actually operating, use self-drying type nitro alkyd varnish better as the hammer tone effect that the lacquer base forms than using polyurethane lacquer as the lacquer base, but from the test result of last table as can be known, the moisture-proof friction of the hammer paint that self-drying type nitro alkyd paint obtains for the optimization of lacquer base, anti-Commerical dryclean, colour fasteness to dry cleaning than polyurethane lacquer as coating with lacquer basis, be that self-drying type nitro alkyd paint washable and wearable is poor than polyurethanes type hammer paint, can't be up to standard.
Comparative Examples 4
This Comparative Examples 4 described buttons with hammer tone effect, the preparation method is substantially the same manner as Example 1, and different is that SP-903 polysiloxane auxiliary agent is modified to DC-61 silicone compounds auxiliary agent.
The result shows: use the mallear stria hammer nest of DC-61 silicone compounds auxiliary agent too small, mallear stria is levelling more easily, and the mallear stria whole structure is effective not as SP-903.
Comparative Examples 5
This Comparative Examples 5 described buttons with hammer tone effect, the preparation method is substantially the same manner as Example 1, and different is that SD-2 polynite organic derivative anti-settling agent is modified to the silicon-dioxide anti-settling agent.
The result shows: though use silicon-dioxide anti-settling agent and polynite organic derivative anti-settling agent all to have thixotropy, but during the long-time placement after dilution, the anti-heavy effect in this individual system of silicon-dioxide is anti-heavy effective not as the polynite organic derivative.
The above embodiment has only expressed several embodiment of the present invention, and it describes comparatively concrete and detailed, but can not therefore be interpreted as the restriction to claim of the present invention.Should be pointed out that for the person of ordinary skill of the art without departing from the inventive concept of the premise, can also make some distortion and improvement, these all belong to protection scope of the present invention.Therefore, the protection domain of patent of the present invention should be as the criterion with claims.
Claims (9)
1. button with hammer tone effect, described button comprises base material, it is characterized in that, also is coated with the coating with hammer tone effect on the described base material; Described coating is that weight part ratio is the mixture of hammer paint, solidifying agent and the thinner of 1:0.2-0.3:0.5.
2. the button with hammer tone effect according to claim 1 is characterized in that, the component of described hammer paint and weight part are:
Polyurethane lacquer 80-95 part,
Mallear stria auxiliary agent 0.1-0.8 part,
Un-suspension powdered aluminium 1-8 part,
Thixotropic anti-settling agent 0.1-1 part,
Mill base or colored paint 0-10 part.
3. the button with hammer tone effect according to claim 2 is characterized in that, the component of described hammer paint and weight part are:
Polyurethane lacquer 91-95 part,
Mallear stria auxiliary agent 0.55-0.65 part,
Un-suspension powdered aluminium 4-5 part,
Thixotropic anti-settling agent 0.3-0.5 part,
Mill base or colored paint 0-10 part.
4. according to claim 2 or 3 described buttons with hammer tone effect, it is characterized in that described mallear stria auxiliary agent is: polymeric silicone compound auxiliary agent or polysiloxane auxiliary agent.
5. according to claim 2 or 3 described buttons with hammer tone effect, it is characterized in that the granularity of described un-suspension powdered aluminium is 10-25 μ m.
6. according to claim 2 or 3 described buttons with hammer tone effect, it is characterized in that described thixotropic anti-settling agent is castor oil derivative, organic remodeling wilkinite, metallic soap, polyethylene wax, superfine silicon dioxide or polynite organic derivative.
7. the button with hammer tone effect according to claim 1 is characterized in that, the material of described base material is metal, unsaturated polyester, wooden, polystyrene, shell or nut.
8. one kind as each described preparation method with button of hammer tone effect of claim 1-7, it is characterized in that, comprises the steps:
(1) processing of base material: base material to be sprayed is carried out water mill handle, guarantee that substrate surface is totally pollution-free;
(2) spraying: the viscosity of the mixture of control hammer paint, solidifying agent and thinner is 14-20 second, can spray base material;
(3) moulding: base material seasoning or oven dry that step (2) spraying is good get final product.
9. the preparation method with button of hammer tone effect according to claim 8 is characterized in that, the temperature of the described oven dry of step (3) is 60-85 ℃, and the time is 30-60min.