CN105037758A - 一种以氮气为处理气氛提高氟硅橡胶粘接性的冷等离子体处理方法 - Google Patents
一种以氮气为处理气氛提高氟硅橡胶粘接性的冷等离子体处理方法 Download PDFInfo
- Publication number
- CN105037758A CN105037758A CN201510534832.6A CN201510534832A CN105037758A CN 105037758 A CN105037758 A CN 105037758A CN 201510534832 A CN201510534832 A CN 201510534832A CN 105037758 A CN105037758 A CN 105037758A
- Authority
- CN
- China
- Prior art keywords
- cold plasma
- trifluoropropyl siloxane
- fluorosilicone rubber
- nitrogen
- treatment method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种以氮气为处理气氛提高氟硅橡胶粘接性的冷等离子体处理方法，旨在提高氟硅橡胶粘接性能。其方法及步骤为：（1）在真空度为10~30Pa的氮气气氛中，采用冷等离子体对氟硅橡胶进行处理；（2）处理功率为120~140瓦、时间3~5分钟；（3）处理后5小时内，用开姆洛克胶黏剂CH607将氟硅橡胶与聚四氟乙烯薄膜进行粘接，并在160~170℃硫化30分钟。本发明的优点是：使氟硅橡胶与聚四氟乙烯薄膜的粘接强度从0提高到至少750牛/米，而且该处理方法并不会对氟硅橡胶的物理力学性能产生影响。
Description
技术领域
本发明涉及一种提高氟硅橡胶粘接强度的表面处理方法，尤其涉及一种用氮气为气氛的冷等离子体处理氟硅橡胶表面后，实现提高其粘接力的方法。
背景技术
氟硅橡胶的主链结构是硅氧键Si-O，侧链上具有氟烷基或者氟芳基的线性聚合物，作为特种橡胶用于高温环境下的密封。为了进一步提高氟硅橡胶的耐介质性能，可在其表面包覆一层厚度为5~20微米的聚四氟乙烯薄膜。对于粘接性能很差的氟硅橡胶，需要对其表面进行改性来提高粘接性能。
本方法采用氮气作为处理气氛，对氟硅橡胶进行冷等离子体处理，使氟硅橡胶具备了与聚四氟乙烯薄膜的粘接能力。
发明内容
本发明采用如下技术方案：一种以氮气为处理气氛提高氟硅橡胶粘接性的冷等离子体处理方法，其特征在于方法步骤如下：
（1）将准备粘接的氟硅橡胶放入冷等离子体设备的处理箱中，先抽真空至真空度小于3Pa；
（2）通入纯度99.99%的纯氮，调整真空度为10~30Pa；
（3）加载电压和电流对氟硅橡胶进行冷等离子体处理，处理功率为120~140瓦和处理时间为3~5分钟；
（4）在处理后5小时内，用开姆洛克胶黏剂CH607将冷等离子体处理后的氟硅橡胶与聚四氟乙烯进行粘接，并在160~170℃硫化30分钟。
本发明所述采用本发明方法，氟硅橡胶与聚四氟乙烯之间的粘接强度从0提高到750牛/米以上。
本发明所述采用本发明方法，不会降低氟硅橡胶的物理力学性能。
本发明的优点是：未进行冷等离子体处理的氟硅橡胶与聚四氟乙烯之间的粘接强度为零；采用本发明方法后，氟硅橡胶与聚四氟乙烯的粘接强度大于750牛/米；同时本发明方法，不会影响氟硅橡胶的物理力学性能。
具体实施方式
实施例一
（1）把准备粘接的氟硅橡胶放入冷等离子体设备的处理箱中，抽真空至真空度小于3Pa；
（2）通入纯度99.99%的纯氮，调整真空度为30Pa；
（3）加载电流和电压使氮气冷等离子体化，对氟硅橡胶进行处理，处理功率为140瓦，处理时间为5分钟；
（4）在处理后5小时以内，用开姆洛克胶黏剂CH607将已处理的氟硅橡胶和聚四氟乙烯进行粘接，并在160~170℃下硫化30分钟；
（5）氟硅橡胶与聚四氟乙烯薄膜之间的粘接强度为755牛/米。
实施例二
（1）把准备粘接的氟硅橡胶放入冷等离子体设备的处理箱中，抽真空至真空度小于3Pa；
（2）通入纯度99.99%的纯氮，调整真空度为20Pa；
（3）加载电流和电压使氮气冷等离子体化，对氟硅橡胶进行处理，处理功率为130瓦，处理时间为4分钟；
（4）在处理后5小时以内，用开姆洛克胶黏剂CH607将已处理的氟硅橡胶和聚四氟乙烯进行粘接，并在160~170℃下硫化30分钟；
（5）氟硅橡胶与聚四氟乙烯薄膜之间的粘接强度为760牛/米。
实施例三
（1）把准备粘接的氟硅橡胶放入冷等离子体设备的处理箱中，抽真空至真空度小于3Pa；
（2）通入纯度99.99%的纯氮，调整真空度为10Pa；
（3）加载电流和电压使氮气冷等离子体化，对氟硅橡胶进行处理，处理功率为120瓦，处理时间为3分钟；
（4）在处理后5小时以内，用开姆洛克胶黏剂CH607将已处理的氟硅橡胶和聚四氟乙烯进行粘接，并在160~170℃下硫化30分钟；
（5）氟硅橡胶与聚四氟乙烯薄膜之间的粘接强度为760牛/米。
注1：粘接性能的测试标准，GB/T2791—1995《胶粘剂T剥离强度试验方法挠性材料对挠性材料》。
注2：氮气的质量标准，GB/T8979-2008《纯氮、高纯氮和超纯氮》。
Claims (3)
1.一种以氮气为处理气氛提高氟硅橡胶粘接性的冷等离子体处理方法，其特征在于方法步骤如下：
（1）将准备粘接的氟硅橡胶放入冷等离子体设备的处理箱中，先抽真空至真空度小于3Pa；
（2）通入纯度99.99%的纯氮，调整真空度为10~30Pa；
（3）加载电压和电流对氟硅橡胶进行冷等离子体处理，处理功率为120~140瓦和处理时间为3~5分钟；
（4）在处理后5小时内，用开姆洛克胶黏剂CH607将冷等离子体处理后的氟硅橡胶与聚四氟乙烯进行粘接，并在160~170℃硫化30分钟。
2.根据权利1要求所述的一种以氮气为处理气氛提高氟硅橡胶粘接性的冷等离子体处理方法，其特征在于：采用本发明方法，氟硅橡胶与聚四氟乙烯之间的粘接强度从0提高到750牛/米以上。
3.根据权利1要求所述的一种以氮气为处理气氛提高氟硅橡胶粘接性的冷等离子体处理方法，其特征在于：采用本发明方法，不会降低氟硅橡胶的物理力学性能。