CN105019167A - Production technology rope ring-dyeing dark-blue weaving fabric - Google Patents
Production technology rope ring-dyeing dark-blue weaving fabric Download PDFInfo
- Publication number
- CN105019167A CN105019167A CN201410166505.5A CN201410166505A CN105019167A CN 105019167 A CN105019167 A CN 105019167A CN 201410166505 A CN201410166505 A CN 201410166505A CN 105019167 A CN105019167 A CN 105019167A
- Authority
- CN
- China
- Prior art keywords
- padding machine
- machine pressure
- staining bath
- oxidation frame
- oxidation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of a rope ring-dyeing dark-blue weaving fabric. The production technology comprises that (1), the vehicle velocity V is 20.0-30m/min; (2), blooming and boiling are conducted for one process at the temperature of 60-90 DEG C; hot water rinsing is conducted for one process at the temperature of 60-80 DEG C; water rinsing is conducted for one process; dying is conducted by using indigo blue for 14-16 processes; water rinsing is conducted for three processes; softening is conducted for one process at the temperature of 60-80 DEG C and drying; (3), a dying groove contains 0.9-3.0g/L of indigo blue, 2.0-3.52g/L of NaOH, 0.8-2.5g/L of sodium hydrosulfite, 8-10g/L of boiled material, 80-120g/L of a softening agent, 3-10g/L of amino silicon oil and 11-12g/L of pH; the electric potential is 740-760; and (4), the padder pressure is 5.5MPa-6.5MPa. The bundle-type ring-dyeing dark-blue yarn dyed fabric is modified based on an existing Morrison beam dyeing machine, high dye-uptake of jean cloth is achieved, and the requirement of dark-blue jean cloth is met.
Description
Technical field
The present invention relates to the dye transformation of special dark blue equipment color-woven fabric of a kind of pencil ring and production technology, particularly a kind of pencil ring contaminates the production technology of special navy blue knitted fabric especially denim.
Background technology
Denim is woven color-woven fabric after a kind of first yarn dyeing, and yarn dyeing mainly adopts indigo dyeing, indigoly belongs to reducing dye, and dyeing exists Four processes: reducing dyes, leuco compound contaminate, leuco compound oxidation, dye post processing.The affinity of bipseudoindoxyl dye to cotton fiber is poor, low, the upper dye difficulty of dye temperature, the warp dyeing of denim, and low dense, the low temperature of general employing, the continuous dyeing method repeatedly soaking, roll, be oxidized, can reach required dyefastness through six to eight staining baths.According to the dyeing property of bipseudoindoxyl dye, denim adopts special dyeing equipment: 1, ball warp (pencil) dyeing; 2, sheet dyeing; 3 floated dyeing three kinds.
Along with the raising day by day of people's life, require more and more higher to the quality of denim and COLOR FASTNESS.Conventional 6-11 groove dye can not meet the requirement of special dark blue denim completely.For this reason, need reequip Morrison's pencil dyeing machine, oxidation frame installs cord roller additional, point fasces 24 is restrainted, when yarn bundle from staining bath after contaminating roll compacting, after oxidation frame oxidation, return staining bath from oxidation frame upper strata cord roller, then contaminate after roll compacting through staining bath, after oxidation, enter next staining bath.If need interval open loop to contaminate 3-5 groove, staining bath is made to reach 13-16.Meet the requirement of special dark blue denim.
Restraint because of ring dye staining bath 12 and out enter oxidation frame afterwards from staining bath, directly do not enter next staining bath, but enter same staining bath from oxidation frame through returning dye deflector roll.Therefore pencil car becomes 24 bundles from 12 bundles, and Shu Liancheng sheet of restricting, then causes and twine yarn.Solution: repeatedly layering is carried out to 24 bundles, thus solves strand and phenomenon.
Summary of the invention
Invention is transformed based on former Morrison's pencil dyeing machine, makes denim have higher dye-uptake.The object of this invention is to provide a kind of special dark blue, textile, chemical fibre, sticky cotton and blended yarn-dyed fabric kind, the production technology of especially special dark blue denim.
For achieving the above object, the technical solution used in the present invention is:
Pencil ring contaminates a production technology for special navy blue knitted fabric, it is characterized in that:
(1) vehicle velocity V: 20.0-30m/min; (2) technological process: breaking down boiling-off, 1 road 60-90 DEG C; Hot water wash, 1 road 60-80 DEG C; Washing, 1 road; Indigo, 14-16 road; Washing, 3 roads; Softness, 1 road 60-80 DEG C; Dry; (3) staining bath content: indigo: 0.9-3.0g/L; NaOH:2.0-3.52g/L; Sodium hydrosulfite: 0.8-2.5g/L; Boiling-off: 8-10g/L; Softener: 80--120g/L; Amido silicon oil: 3--10g/L; PH:11-12g/L; Current potential: 740-760; (4) padding machine pressure 5.5Mpa-6.5Mpa.
Contaminate the production technology of special navy blue knitted fabric according to described a kind of pencil ring, it is characterized in that:
The speed of a motor vehicle: 20m/min; Textile R20, RING SPINNING;
Technological process:
(1) ball warp axle; (2) boiling-off alkali, 60-90 DEG C of padding machine pressure 0.4Mpa; (3) hot water wash, 60-80 DEG C of padding machine pressure 0.5Mpa; (4) cold wash, 1 padding machine pressure 0.5Mpa; (5) staining bath 1, padding machine pressure 0.5Mpa; (6) oxidation frame; (7) staining bath 2, padding machine pressure 0.5Mpa; (8) oxidation frame; (9) staining bath 3, padding machine pressure 0.5Upa; (10) oxidation frame; (11) staining bath 4, padding machine pressure 0.5Mpa; (12) oxidation frame; (13) staining bath 5, padding machine pressure 0.5Mpa; (14) oxidation frame; (15) staining bath 6, padding machine pressure 0.5Mpa; (16) oxidation frame; (17) staining bath 7, padding machine pressure 0.5Mpa; (18) oxidation frame; (19) staining bath 8 is contaminated, padding machine pressure 0.5Mpa; (20) oxidation frame; (21) staining bath 9, padding machine pressure 0.5Mpa; (22) oxidation frame; (23) staining bath 10, padding machine pressure 0.5Mpa; (24) oxidation frame; (25) staining bath 11, padding machine pressure 0.6Mpa; (26) oxidation frame; (27) indigo rear cold wash, 3 padding machine pressure 0.5Mpa; (28) softener, 70-90 DEG C, padding machine pressure 0.4Mpa; (29) oven dry is doffed; (30) lease making; (31) sizing beam of a loom; Ring dye 2#, 8# groove;
Staining bath content: indigo: 0.97-1.0g/L; NaOH:2.0-3.52g/L; Sodium hydrosulfite: 0.8-2.5g/L; Boiling-off: 8-10g/L; Softener: 80--120g/L; Amido silicon oil: 3--10g/L; PH:11-12g/L; Current potential: 740-760;
Reference flow: 10 seconds/66 milliliters; Scale value: 170-175; Benefit abandons scale value: 100-120.
According to the production technology of the special dark blue denim of described pencil ring dye, it is characterized in that:
The speed of a motor vehicle: 24M/min; OE10, open-end spinning;
Technological process: (1) ball warp axle; (2) boiling-off alkali, 60-90 DEG C of padding machine pressure 0.4Mpa; (3) hot water wash, 60-80 DEG C of padding machine pressure 0.5Mpa; (4) cold wash, 1 padding machine pressure 0.5Mpa; (5) staining bath 1, padding machine pressure 0.5Mpa; (6) oxidation frame; (7) staining bath 2, padding machine pressure 0.5Mpa; (8) oxidation frame; (9) staining bath 2, padding machine pressure 0.5Mpa; (10) oxidation frame (11); Staining bath 3, padding machine pressure 0.5Mpa; (12) oxidation frame; (13) staining bath 4, padding machine pressure 0.5Mpa; 14) oxidation frame; (15) staining bath 5, padding machine pressure 0.5Mpa; (16) oxidation frame; (17) staining bath 5, padding machine pressure 0.5Mpa; (18) oxidation frame; (19) staining bath 6, padding machine pressure 0.5Mpa; (20) oxidation frame; (21) staining bath 7, padding machine pressure 0.5Mpa; (22) oxidation frame; (23) staining bath 8 is contaminated, padding machine pressure 0.5Mpa; (24) oxidation frame (25) staining bath 8, padding machine pressure 0.5Mpa; (26) oxidation frame; (27) staining bath 9, padding machine pressure 0.5Mpa; (28) oxidation frame; (29) staining bath 10, padding machine pressure 0.5Mpa; (30) oxidation frame; (31) staining bath 11, padding machine pressure 0.6Mpa; (32) oxidation frame; (33) indigo rear cold wash, 3 padding machine pressure 0.5Mpa; (34) softener, 70-90 DEG C, padding machine pressure 0.4Mpa; (35) oven dry is doffed; (36) lease making; (37) sizing beam of a loom; Ring dye 2#, 5#, 8# groove;
Staining bath content: indigo: 1.9-2.1g/L; NaOH:2.8-3.5g/L; Sodium hydrosulfite: 1.2-2.2g/L; Boiling-off: 8-10g/L; Softener: 80--120g/L; Amido silicon oil: 3--10g/L; PH:11-12g/L; Current potential: 740-760;
Reference flow: 8 seconds/66 milliliters; Scale value: 200-210; Benefit abandons scale value: 110-130.
According to the production technology of the special dark blue denim of described pencil ring dye, it is characterized in that:
The speed of a motor vehicle: 24m/min; RSB12 RING SPINNING ring;
Technological process: ball warp axle-boiling-off alkali, 60-90 DEG C of padding machine pressure 0.4Mpa;-hot water wash, 60-80 DEG C of padding machine pressure 0.5Mpa;-cold wash, 1 padding machine pressure 0.5Mpa;--staining bath 1, padding machine pressure 0.5Mpa;--oxidation frame--staining bath 2, padding machine pressure 0.5Upa;-oxidation frame--staining bath 2, padding machine pressure 0.5Mpa;--oxidation frame-staining bath 3, padding machine pressure 0.5Mpa;-oxidation frame--staining bath 4, padding machine pressure 0.5Mpa;-oxidation frame-staining bath 5, padding machine pressure 0.5Mpa; Oxidation frame-staining bath 5, padding machine pressure 0.5Mpa;--oxidation frame-staining bath 6, padding machine pressure 0.5Mpa,--oxidation frame-staining bath 7, padding machine pressure 0.5Mpa;--oxidation frame-dye staining bath 8, padding machine pressure 0.5Mpa;--oxidation frame-staining bath 8, padding machine pressure 0.5Mpa;--oxidation frame--staining bath 9, padding machine pressure 0.5Mpa;--oxidation frame-staining bath 10, padding machine pressure 0.5Mpa;-oxidation frame-staining bath 11, padding machine pressure 0.6Mpa;-oxidation frame-indigo rear cold wash, 3 padding machine pressure 0.5Mpa;-softener, 70-90 DEG C of padding machine pressure 0.4Mpa dries--lease making--sizing beam of a loom that doffs; Ring dye 2#, 5#, 8# groove;
Staining bath content: indigo: 2.0-2.3g/L; NaOH:2.5-3.3g/L; Sodium hydrosulfite: 1.0-2.0g/L; Boiling-off: 8-10g/L; Softener: 80--120g/L; Amido silicon oil: 3--10g/L; PH:11-12g/L; Current potential: 740-760;
Reference flow: 7.5 seconds/66 milliliters; Scale value: 205-220; Benefit abandons scale value: 115-135.
The present invention transforms based on former Morrison's pencil dyeing machine, makes denim have higher dye-uptake.Meet the requirement of special dark blue denim.
Accompanying drawing explanation
Fig. 1 is process chart of the present invention.
Detailed description of the invention
Below in conjunction with the drawings and specific embodiments, the invention will be further described:
As shown in Figure 1, pencil ring contaminates special dark blue scrap build and production technology, and its production technology feature is as follows in the present invention:
Ball beam - alkali scouring (60-90 ℃ rolling pressure 0.4 Mpa) - hot water to wash the car (60-80 ℃ rolling pressure 0.5 Mpa) - cold water to wash the car (1 only rolling pressure 0.5 Mpa) - dye VAT (1 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (2 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (3 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (4 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (5 car rolling pressure 0.5 Mpa) oxidation - dyed grooves (6 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (7 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (8 car rolling pressure 0.5 Mpa) - frame - dye VAT - oxide (9 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (10 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (11 car rolling pressure 0.6 Mpa) - oxidation frame - cold water bath after the indigo (3 car rolling pressure 0.5 Mpa) - softener (70-90 ℃ rolling pressure 0.4 Mpa) drying doffing, lease, sizing weaving shaft.
Above 1-11 staining bath all can make ring dye staining bath.
Technical solution of the present invention elaborates
To the object of the invention is based on former Morrison's pencil dyeing machine transformation and adapt to the higher dye-uptake of denim, special dark blue, textile, chemical fibre, sticky cotton and the scrap build of blending kind and production technology.
1, vehicle velocity V: 20.0-30m/min;
2, technological process: breaking down boiling-off (1 road 60-90 DEG C), hot water wash (1 road 60-80 DEG C), washing (1 road) indigo (14-16 road), washing (3 road), soft (1 road 60-80 DEG C), oven dry.
3, staining bath content: indigo: 0.9-3.0g/L; NaOH:2.0-3.52g/L;
Sodium hydrosulfite: 0.8-2.5g/L; Boiling-off: 8-10g/L;
Softener: 80--120g/L; Amido silicon oil: 3--10g/L
PH:11-12g/L; Current potential: 740-760.
4, padding machine pressure 5.5Mpa-6.5Mpa.
Embodiment 1
1, the speed of a motor vehicle: 20m/min, textile R20 (RING SPINNING);
2, technological process: the ball beam - alkali scouring (60-90 ℃ rolling pressure 0.4 Mpa) - hot water to wash the car (60-80 ℃ rolling pressure 0.5 Mpa) - cold water to wash the car (1 only rolling pressure 0.5 Mpa) - dye VAT (1 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (2, rolling car pressure 0.5 Mpa) - oxidation - dye grooves (2 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (3 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (4 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (5 car rolling pressure 0.5 Mpa) oxidation - dyed grooves (6 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (7 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (8 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (8 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (9 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (10 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (11 car rolling pressure 0.6 Mpa) - oxidation frame - cold water bath after the indigo (3 car rolling pressure 0.5 Mpa) - softener (70-90 ℃ rolling pressure 0.4 Mpa) drying doffing, lease, sizing weaving shaft.
(ring dye 2#, 8# groove)
3, staining bath content: indigo: 0.97-1.0g/L; NaOH:2.0-3.52g/L;
Sodium hydrosulfite: 0.8-2.5g/L; Boiling-off: 8-10g/L;
Softener: 80--120g/L; Amido silicon oil: 3--10g/L;
PH:11-12g/L; Current potential: 740-760.
4, reference flow: 10 seconds/66 milliliters (left and right); Scale value: 170-175; Benefit abandons scale value: 100-120.
Embodiment 2
1, the speed of a motor vehicle: 24M/min; OE10 (open-end spinning)
2, technological process: the ball beam - alkali scouring (60-90 ℃ rolling pressure 0.4 Mpa) - hot water to wash the car (60-80 ℃ rolling pressure 0.5 Mpa) - cold water to wash the car (1 only rolling pressure 0.5 Mpa) - dye VAT (1 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (2, rolling car pressure 0.5 Mpa) - oxidation - dye grooves (2 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (3 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (4 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (5 car rolling pressure 0.5 Mpa) oxidation frame - dye VAT (5 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (6 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (7 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (8 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (8 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (9 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (10 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (11 car rolling pressure 0.6 Mpa) - oxidation frame - cold water bath after the indigo (3 car rolling pressure 0.5 Mpa) - softener (70-90 ℃ rolling pressure 0.4 Mpa) drying doffing, lease, sizing weaving shaft.
(ring dye 2#, 5#, 8# groove)
3, staining bath content: indigo: 1.9-2.1g/L; NaOH:2.8-3.5g/L;
Sodium hydrosulfite: 1.2-2.2g/L; Boiling-off: 8-10g/L;
Softener: 80--120g/L; Amido silicon oil: 3--10g/L;
PH:11-12g/L; Current potential: 740-760.
4, reference flow: 8 seconds/66 milliliters (left and right); Scale value: 200-210; Benefit abandons scale value: 110-130.
Embodiment 3
1, the speed of a motor vehicle: 24m/min; RSB12 (RING SPINNING ring)
2, technological process: the ball beam - alkali scouring (60-90 ℃ rolling pressure 0.4 Mpa) - hot water to wash the car (60-80 ℃ rolling pressure 0.5 Mpa) - cold water to wash the car (1 only rolling pressure 0.5 Mpa) - dye VAT (1 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (2, rolling car pressure 0.5 Mpa) - oxidation - dye grooves (2 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (3 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (4 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (5 car rolling pressure 0.5 Mpa) oxidation frame - dye VAT (5 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (6 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (7 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (8 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (8 car rolling pressure 0.5 Mpa) - oxidation - dye grooves (9 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (10 car rolling pressure 0.5 Mpa) - oxidation - dyed grooves (11 car rolling pressure 0.6 Mpa) - oxidation frame - cold water bath after the indigo (3 car rolling pressure 0.5 Mpa) - softener (70-90 ℃ rolling pressure 0.4 Mpa) drying doffing, lease, sizing weaving shaft.
(ring dye 2#, 5#, 8# groove)
3, staining bath content: indigo: 2.0-2.3g/L; NaOH:2.5-3.3g/L;
Sodium hydrosulfite: 1.0-2.0g/L; Boiling-off: 8-10g/L;
Softener: 80--120g/L; Amido silicon oil: 3--10g/L;
PH:11-12g/L; Current potential: 740-760.
4, reference flow: 7.5 seconds/66 milliliters (left and right); Scale value: 205-220; Benefit abandons scale value: 115-135.
Embodiment recited above is only be described the preferred embodiment of the present invention; not design of the present invention and protection domain are limited; under the prerequisite not departing from design concept of the present invention; the various modification that in this area, common engineers and technicians make technical scheme of the present invention and improvement, all should fall into protection scope of the present invention.
Claims (4)
1. pencil ring contaminates a production technology for special navy blue knitted fabric, it is characterized in that:
(1) vehicle velocity V: 20.0-30m/min; (2) technological process: breaking down boiling-off, 1 road 60-90 DEG C; Hot water wash, 1 road 60-80 DEG C; Washing, 1 road; Indigo, 14-16 road; Washing, 3 roads; Softness, 1 road 60-80 DEG C; Dry; (3) staining bath content: indigo: 0.9-3.0g/L; NaOH:2.0-3.52g/L; Sodium hydrosulfite: 0.8-2.5g/L; Boiling-off: 8-10g/L; Softener: 80--120g/L; Amido silicon oil: 3--10g/L; PH:11-12g/L; Current potential: 740-760; (4) padding machine pressure 5.5Mpa-6.5Mpa.
2. a kind of pencil ring according to claim 1 contaminates the production technology of special navy blue knitted fabric, it is characterized in that:
The speed of a motor vehicle: 20m/min; Textile R20, RING SPINNING;
Technological process:
(1) ball warp axle; (2) boiling-off alkali, 60-90 DEG C of padding machine pressure 0.4Mpa; (3) hot water wash, 60-80 DEG C of padding machine pressure 0.5Mpa; (4) cold wash, 1 padding machine pressure 0.5Mpa; (5) staining bath 1, padding machine pressure 0.5Mpa; (6) oxidation frame; (7) staining bath 2, padding machine pressure 0.5Mpa; (8) oxidation frame; (9) staining bath 3, padding machine pressure 0.5Mpa; (10) oxidation frame; (11) staining bath 4, padding machine pressure 0.5Mpa; (12) oxidation frame; (13) staining bath 5, padding machine pressure 0.5Mpa; (14) oxidation frame; (15) staining bath 6, padding machine pressure 0.5Mpa; (16) oxidation frame; (17) staining bath 7, padding machine pressure 0.5Mpa; (18) oxidation frame; (19) staining bath 8 is contaminated, padding machine pressure 0.5Mpa; (20) oxidation frame; (21) staining bath 9, padding machine pressure 0.5Mpa; (22) oxidation frame; (23) staining bath 10, padding machine pressure 0.5Mpa; (24) oxidation frame; (25) staining bath 11, padding machine pressure 0.6Mpa; (26) oxidation frame; (27) indigo rear cold wash, 3 padding machine pressure 0.5Mpa; (28) softener, 70-90 DEG C, padding machine pressure 0.4Mpa; (29) oven dry is doffed; (30) lease making; (31) sizing beam of a loom; Ring dye 2#, 8# groove;
Staining bath content: indigo: 0.97-1.0g/L; NaOH:2.0-3.52g/L; Sodium hydrosulfite: 0.8-2.5g/L; Boiling-off: 8-10g/L; Softener: 80--120g/L; Amido silicon oil: 3--10g/L; PH:11-12g/L; Current potential: 740-760.
3. a kind of pencil ring according to claim 1 contaminates the production technology of special navy blue knitted fabric, it is characterized in that:
The speed of a motor vehicle: 24M/min; OE10, open-end spinning;
Technological process: (1) ball warp axle; (2) boiling-off alkali, 60-90 DEG C of padding machine pressure 0.4Mpa; (3) hot water wash, 60-80 DEG C of padding machine pressure 0.5Mpa; (4) cold wash, 1 padding machine pressure 0.5Mpa; (5) staining bath 1, padding machine pressure 0.5Mpa; (6) oxidation frame; (7) staining bath 2, padding machine pressure 0.5Mpa; (8) oxidation frame; (9) staining bath 2, padding machine pressure 0.5Mpa; (10) oxidation frame (11); Staining bath 3, padding machine pressure 0.5Mpa; (12) oxidation frame; (13) staining bath 4, padding machine pressure 0.5Mpa; 14) oxidation frame; (15) staining bath 5, padding machine pressure 0.5Mpa; (16) oxidation frame; (17) staining bath 5, padding machine pressure 0.5Mpa; (18) oxidation frame; (19) staining bath 6, padding machine pressure 0.5Mpa; (20) oxidation frame; (21) staining bath 7, padding machine pressure 0.5Mpa; (22) oxidation frame; (23) staining bath 8 is contaminated, padding machine pressure 0.5Mpa; (24) oxidation frame (25) staining bath 8, padding machine pressure 0.5Mpa; (26) oxidation frame; (27) staining bath 9, padding machine pressure 0.5Mpa; (28) oxidation frame; (29) staining bath 10, padding machine pressure 0.5Mpa; (30) oxidation frame; (31) staining bath 11, padding machine pressure 0.6Mpa; (32) oxidation frame; (33) indigo rear cold wash, 3 padding machine pressure 0.5Mpa; (34) softener, 70-90 DEG C, padding machine pressure 0.4Mpa; (35) oven dry is doffed; (36) lease making; (37) sizing beam of a loom; Ring dye 2#, 5#, 8# groove;
Staining bath content: indigo: 1.9-2.1g/L; NaOH:2.8-3.5g/L; Sodium hydrosulfite: 1.2-2.2g/L; Boiling-off: 8-10g/L; Softener: 80--120g/L; Amido silicon oil: 3--10g/L; PH:11-12g/L; Current potential: 740-760.
4. a kind of pencil ring according to claim 1 contaminates the production technology of special navy blue knitted fabric, it is characterized in that:
The speed of a motor vehicle: 24m/min; RSB12 RING SPINNING ring;
Technological process: ball warp axle-boiling-off alkali, 60-90 DEG C of padding machine pressure 0.4Mpa;-hot water wash, 60-80 DEG C of padding machine pressure 0.5Mpa;-cold wash, 1 padding machine pressure 0.5Mpa;--staining bath 1, padding machine pressure 0.5Mpa;--oxidation frame--staining bath 2, padding machine pressure 0.5Mpa;-oxidation frame--staining bath 2, padding machine pressure 0.5Mpa;--oxidation frame-staining bath 3, padding machine pressure 0.5Mpa;-oxidation frame--staining bath 4, padding machine pressure 0.5Mpa;-oxidation frame-staining bath 5, padding machine pressure 0.5Mpa; Oxidation frame-staining bath 5, padding machine pressure 0.5Mpa;--oxidation frame-staining bath 6, padding machine pressure 0.5Mpa,--oxidation frame-staining bath 7, padding machine pressure 0.5Mpa;--oxidation frame-dye staining bath 8, padding machine pressure 0.5Mpa;--oxidation frame-staining bath 8, padding machine pressure 0.5Mpa;--oxidation frame--staining bath 9, padding machine pressure 0.5Mpa;--oxidation frame-staining bath 10, padding machine pressure 0.5Mpa;-oxidation frame-staining bath 11, padding machine pressure 0.6Mpa;-oxidation frame-indigo rear cold wash, 3 padding machine pressure 0.5Mpa;-softener, 70-90 DEG C of padding machine pressure 0.4Mpa dries--lease making--sizing beam of a loom that doffs; Ring dye 2#, 5#, 8# groove;
Staining bath content: indigo: 2.0-2.3g/L; NaOH:2.5-3.3g/L; Sodium hydrosulfite: 1.0-2.0g/L; Boiling-off: 8-10g/L; Softener: 80--120g/L; Amido silicon oil: 3--10g/L; PH:11-12g/L; Current potential: 740-760.