CN105018941A - 一种金属防锈缓蚀剂及其制备方法 - Google Patents

一种金属防锈缓蚀剂及其制备方法 Download PDF

Info

Publication number
CN105018941A
CN105018941A CN201510510199.7A CN201510510199A CN105018941A CN 105018941 A CN105018941 A CN 105018941A CN 201510510199 A CN201510510199 A CN 201510510199A CN 105018941 A CN105018941 A CN 105018941A
Authority
CN
China
Prior art keywords
parts
sodium
hexamethylenetetramine
mercaptobenzothiazole
furfural
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510510199.7A
Other languages
English (en)
Inventor
杨洋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510510199.7A priority Critical patent/CN105018941A/zh
Publication of CN105018941A publication Critical patent/CN105018941A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种金属防锈缓蚀剂及其制备方法，其中防锈缓蚀剂包括：硅酸钠、聚丙烯酸钠、巯基苯并噻唑、苯并三氮唑、三聚磷酸钠、六次甲基四胺、咪唑啉、烷胺基醇、糠醛、聚磷酸盐、乙醇胺、硼酸钠和乙醇；其制备方法为先将硅酸钠、聚丙烯酸钠、巯基苯并噻唑、苯并三氮唑、三聚磷酸钠、六次甲基四胺、咪唑啉、烷胺基醇、糠醛、乙醇胺和乙醇混合液加热至50～60℃，再加入聚磷酸盐和硼酸钠，继续加热至85～90℃，并保温2～3小时后，放冷即得。本发明的防锈缓蚀剂与各材料的相容性好，防锈时间长，可达4-6个月，并对铜、铝材料有较好的适应性，本发明可以缓释防锈的同时在金属表面成膜，从而延长防锈时间。

Description

一种金属防锈缓蚀剂及其制备方法
技术领域
本发明属于金属防腐技术领域，具体涉及一种金属防锈缓蚀剂及其制备方法。
背景技术
缓蚀剂是一种以适当的浓度和形式存在于环境中时，可以防止或减缓金属表面腐蚀的化学物质或几种化学物质的混合物。目前，所使用的缓蚀剂有无机化合物缓蚀剂和有机化合物缓蚀剂。已知的缓蚀剂大多功能单一，只能够用于防止或减缓单一金属的锈蚀，即只对于铁、钢、铜等其中一种金属起主要作用，，用途单一，只适用于一种介质；另外，除延缓金属锈蚀之外，不能作为润滑剂、软化剂、保湿剂、防冻剂或导热剂使用；缓蚀剂多溶入各种有机溶剂，有的有毒性，使用会给环境造成一定的危害。到目前，尚未见到有能适用于多种介质，同时对多种金属起缓蚀作用的缓蚀剂。当然，也有采用几种化学物质的缓释剂混合使用的，但其功能和用途也不能够囊括各种金属或多种介质，并当作除缓蚀剂之外的其他助剂使用。
发明内容
本发明的目的是提供一种金属防锈缓蚀剂及其制备方法。
一种金属防锈缓蚀剂以重量份计包括：硅酸钠6-10份，聚丙烯酸钠3-8份，巯基苯并噻唑2-7份，苯并三氮唑0.7-4.6份，六次甲基四胺0.2-1.6份，咪唑啉0.6-2.1份，糠醛0.4-1.5份，乙醇胺1.1-4.6份，硼酸钠1.6-4.5份，乙醇10-15份。
进一步的方案，还包括烷胺基醇0.6-4.3份。
进一步的方案，还包括烷聚磷酸盐3-6份。
进一步的方案，还包括烷三聚磷酸钠0.3-2.6份。
更进一步的方案，以重量份计包括：硅酸钠6份，聚丙烯酸钠4份，巯基苯并噻唑2份，苯并三氮唑1.2份，三聚磷酸钠0.5份，六次甲基四胺0.4份，咪唑啉0.8份，烷胺基醇1.0份，糠醛0.5份，聚磷酸盐3份，乙醇胺1.5份，硼酸钠1.8份，乙醇10份。
更进一步的方案，以重量份计包括：硅酸钠7份，聚丙烯酸钠5份，巯基苯并噻唑3份，苯并三氮唑2.1份，三聚磷酸钠0.8份，六次甲基四胺0.6份，咪唑啉1.0份，烷胺基醇1.5份，糠醛0.7份，聚磷酸盐4份，乙醇胺2.1份，硼酸钠2.5份，乙醇12份。
更进一步的方案，以重量份计包括：硅酸钠9份，聚丙烯酸钠6份，巯基苯并噻唑5份，苯并三氮唑3.2份，三聚磷酸钠1.4份，六次甲基四胺1.1份，咪唑啉1.3份，烷胺基醇2.0份，糠醛1.0份，聚磷酸盐5份，乙醇胺3.1份，硼酸钠3.6份，乙醇14份。
更进一步的方案，以重量份计包括：硅酸钠10份，聚丙烯酸钠8份，巯基苯并噻唑7份，苯并三氮唑4.0份，三聚磷酸钠2.6份，六次甲基四胺1.6份，咪唑啉2.1份，烷胺基醇4.0份，糠醛1.5份，聚磷酸盐6份，乙醇胺4.2份，硼酸钠4.2份，乙醇15份。
上述金属防锈缓蚀剂的制备方法，具体步骤为：
（1）先将硅酸钠、聚丙烯酸钠、巯基苯并噻唑、苯并三氮唑、三聚磷酸钠、六次甲基四胺、咪唑啉、烷胺基醇、糠醛、乙醇胺和乙醇混合液加热至50～60℃；
（2）再加入聚磷酸盐和硼酸钠，继续加热至85～90℃，并保温2～3小时后，放冷即得。
本发明的防锈缓蚀剂与各材料的相容性好，防锈时间长，可达4-6个月，并对铜、铝材料有较好的适应性，本发明可以缓释防锈的同时在金属表面成膜，从而延长防锈时间。
具体实施方式
实施例1
一金属防锈缓蚀剂，以重量份计包括：硅酸钠6份，聚丙烯酸钠4份，巯基苯并噻唑2份，苯并三氮唑1.2份，三聚磷酸钠0.5份，六次甲基四胺0.4份，咪唑啉0.8份，烷胺基醇1.0份，糠醛0.5份，聚磷酸盐3份，乙醇胺1.5份，硼酸钠1.8份，乙醇10份。
制备步骤如下：
（1）先将硅酸钠、聚丙烯酸钠、巯基苯并噻唑、苯并三氮唑、三聚磷酸钠、六次甲基四胺、咪唑啉、烷胺基醇、糠醛、乙醇胺和乙醇混合液加热至50～60℃；
（2）再加入聚磷酸盐和硼酸钠，继续加热至85～90℃，并保温2～3小时后，放冷即得。
实施例2
一种金属防锈缓蚀剂，以重量份计包括：硅酸钠7份，聚丙烯酸钠5份，巯基苯并噻唑3份，苯并三氮唑2.1份，三聚磷酸钠0.8份，六次甲基四胺0.6份，咪唑啉1.0份，烷胺基醇1.5份，糠醛0.7份，聚磷酸盐4份，乙醇胺2.1份，硼酸钠2.5份，乙醇12份。
制备步骤如下：
（1）先将硅酸钠、聚丙烯酸钠、巯基苯并噻唑、苯并三氮唑、三聚磷酸钠、六次甲基四胺、咪唑啉、烷胺基醇、糠醛、乙醇胺和乙醇混合液加热至50～60℃；
（2）再加入聚磷酸盐和硼酸钠，继续加热至85～90℃，并保温2～3小时后，放冷即得。
实施例3
一种金属防锈缓蚀剂，其特征在于，以重量份计包括：硅酸钠9份，聚丙烯酸钠6份，巯基苯并噻唑5份，苯并三氮唑3.2份，三聚磷酸钠1.4份，六次甲基四胺1.1份，咪唑啉1.3份，烷胺基醇2.0份，糠醛1.0份，聚磷酸盐5份，乙醇胺3.1份，硼酸钠3.6份，乙醇14份。
制备步骤如下：
（1）先将硅酸钠、聚丙烯酸钠、巯基苯并噻唑、苯并三氮唑、三聚磷酸钠、六次甲基四胺、咪唑啉、烷胺基醇、糠醛、乙醇胺和乙醇混合液加热至50～60℃；
（2）再加入聚磷酸盐和硼酸钠，继续加热至85～90℃，并保温2～3小时后，放冷即得。
实施例4
一种金属防锈缓蚀剂，以重量份计包括：硅酸钠10份，聚丙烯酸钠8份，巯基苯并噻唑7份，苯并三氮唑4.0份，三聚磷酸钠2.6份，六次甲基四胺1.6份，咪唑啉2.1份，烷胺基醇4.0份，糠醛1.5份，聚磷酸盐6份，乙醇胺4.2份，硼酸钠4.2份，乙醇15份。
制备步骤如下：
（1）先将硅酸钠、聚丙烯酸钠、巯基苯并噻唑、苯并三氮唑、三聚磷酸钠、六次甲基四胺、咪唑啉、烷胺基醇、糠醛、乙醇胺和乙醇混合液加热至50～60℃；
（2）再加入聚磷酸盐和硼酸钠，继续加热至85～90℃，并保温2～3小时后，放冷即得。
将上述实施例所得样品与市售防锈剂进行对比试验，结果如下：
  实施例1 实施例2 实施例3 实施例4 市售样品
样品浓度% 1.2 1.2 1.2 1.2 1.2
稀溶液pH值 8.4 8.2 8.4 8 8.7
高低温稳定性 稳定 稳定 稳定 稳定 稳定
湿热防锈（天） 15 19 17 16 8
腐蚀性H62铜2h 0级 0级 0级 0级 0级
腐蚀性LY12铝合金2h 0级 0级 0级 0级 0级
室内挂片（月） 6 6 5 5 2
封存防锈（月） 10 9 11 12 7
残留% 38 37 37 38 38
本发明的防锈缓蚀剂与各材料的相容性好，防锈时间长，可达4-6个月，并对铜、铝材料有较好的适应性，本发明可以缓释防锈的同时在金属表面成膜，从而延长防锈时间。

Claims (9)

1.一种金属防锈缓蚀剂，其特征在于，以重量份计包括：硅酸钠6-10份，聚丙烯酸钠3-8份，巯基苯并噻唑2-7份，苯并三氮唑0.7-4.6份，六次甲基四胺0.2-1.6份，咪唑啉0.6-2.1份，糠醛0.4-1.5份，乙醇胺1.1-4.6份，硼酸钠1.6-4.5份，乙醇10-15份。
2.根据权利要求1所述的金属防锈缓蚀剂，其特征在于，还包括烷胺基醇0.6-4.3份。
3.根据权利要求2所述的金属防锈缓蚀剂，其特征在于，还包括烷聚磷酸盐3-6份。
4.根据权利要求3所述的金属防锈缓蚀剂，其特征在于，还包括烷三聚磷酸钠0.3-2.6份。
5.根据权利要求4所述的金属防锈缓蚀剂，其特征在于，以重量份计包括：硅酸钠6份，聚丙烯酸钠4份，巯基苯并噻唑2份，苯并三氮唑1.2份，三聚磷酸钠0.5份，六次甲基四胺0.4份，咪唑啉0.8份，烷胺基醇1.0份，糠醛0.5份，聚磷酸盐3份，乙醇胺1.5份，硼酸钠1.8份，乙醇10份。
6.根据权利要求4所述的金属防锈缓蚀剂，其特征在于，以重量份计包括：硅酸钠7份，聚丙烯酸钠5份，巯基苯并噻唑3份，苯并三氮唑2.1份，三聚磷酸钠0.8份，六次甲基四胺0.6份，咪唑啉1.0份，烷胺基醇1.5份，糠醛0.7份，聚磷酸盐4份，乙醇胺2.1份，硼酸钠2.5份，乙醇12份。
7.根据权利要求4所述的金属防锈缓蚀剂，其特征在于，以重量份计包括：硅酸钠9份，聚丙烯酸钠6份，巯基苯并噻唑5份，苯并三氮唑3.2份，三聚磷酸钠1.4份，六次甲基四胺1.1份，咪唑啉1.3份，烷胺基醇2.0份，糠醛1.0份，聚磷酸盐5份，乙醇胺3.1份，硼酸钠3.6份，乙醇14份。
8.根据权利要求4所述的金属防锈缓蚀剂，其特征在于，以重量份计包括：硅酸钠10份，聚丙烯酸钠8份，巯基苯并噻唑7份，苯并三氮唑4.0份，三聚磷酸钠2.6份，六次甲基四胺1.6份，咪唑啉2.1份，烷胺基醇4.0份，糠醛1.5份，聚磷酸盐6份，乙醇胺4.2份，硼酸钠4.2份，乙醇15份。
9.权利要求5-8所述的金属防锈缓蚀剂的制备方法，其特征在于：具体步骤为：
（1）先将硅酸钠、聚丙烯酸钠、巯基苯并噻唑、苯并三氮唑、三聚磷酸钠、六次甲基四胺、咪唑啉、烷胺基醇、糠醛、乙醇胺和乙醇混合液加热至50～60℃；
（2）再加入聚磷酸盐和硼酸钠，继续加热至85～90℃，并保温2～3小时后，放冷即得。
CN201510510199.7A 2015-08-19 2015-08-19 一种金属防锈缓蚀剂及其制备方法 Pending CN105018941A (zh)