CN105017914B - Method for preparing connection paint from rosin-modified acrylate - Google Patents

Method for preparing connection paint from rosin-modified acrylate Download PDF

Info

Publication number
CN105017914B
CN105017914B CN201510430020.7A CN201510430020A CN105017914B CN 105017914 B CN105017914 B CN 105017914B CN 201510430020 A CN201510430020 A CN 201510430020A CN 105017914 B CN105017914 B CN 105017914B
Authority
CN
China
Prior art keywords
paint
weight
parts
connection
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510430020.7A
Other languages
Chinese (zh)
Other versions
CN105017914A (en
Inventor
王胜龙
刘轶龙
李春光
苏雅丽
黄杰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
XIAMEN SHUANGRUI SHIPBUILDING PAINT CO Ltd
Original Assignee
XIAMEN SHUANGRUI SHIPBUILDING PAINT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by XIAMEN SHUANGRUI SHIPBUILDING PAINT CO Ltd filed Critical XIAMEN SHUANGRUI SHIPBUILDING PAINT CO Ltd
Priority to CN201510430020.7A priority Critical patent/CN105017914B/en
Publication of CN105017914A publication Critical patent/CN105017914A/en
Application granted granted Critical
Publication of CN105017914B publication Critical patent/CN105017914B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a method for preparing connection paint from rosin-modified acrylate. The method comprises putting 10-15 parts by weight of rosin-modified acrylate resin, 6-10 parts by weight of chlorinated rubber, 14-24 parts by weight of xylene and 4-8.7 parts by weight of n-butanol into a high-speed dispersion machine together, carrying out stirring to obtain a uniform mixture, putting 0.8-1.2 parts by weight of organobentonite into the high-speed dispersion machine, carrying out high-speed dispersion for 15-20min, putting 20-30 parts by weight of iron-titanium compound powder, 20-25 parts by weight of mica powder and 3-8 parts by weight of titanium dioxide into the high-speed dispersion machine, and carrying out high-speed dispersion for 30min to obtain the connection paint. A test proves that the connection paint has fineness controlled below 100 microns. The connection paint has good film-forming property, high connectivity to anti-fouling paint and anti-rust paint, prevents time interval of the connection paint coating and anti-fouling paint coating and has good connection strength.

Description

A kind of method that connection coating is prepared by Abietyl modified acrylate
Technical field
The invention belongs to technical field of coatings, the specifically present invention are a kind of preparations by Abietyl modified acrylate connect The method of coating.
Connect coating using one-component prepared by Abietyl modified acrylate and be applied to ship outer casing underwater position, be A kind of coating of transition between antirusting paint and antifouling paint.
Background technology
In order to ensure that ship outer casing underwater position, from seawater corrosion and sea organism attachment, is needed in the position application Antirusting paint and antifouling paint, but antirusting paint and antifouling paint exist different due to its property, using function etc., cause antirust Coating is different with the curing mechanism of antifouling paint.Antirusting paint mostly is epoxy double-component thermohardening lacquer, surface ratio after its solidification More smooth densification, lacks anchor point;And antifouling paint mostly is one-component thermoplastic coating, which has resin corrosion and release antifouling The characteristic of agent, therefore the intensity of antifouling paint is not typically high and has certain water imbibition.If directly coated on antirusting paint Antifouling paint, antifouling paint easily come off under seawater eroding, lose antifouling property.
The attachment issue of antifouling paint is solved, the best approach is to introduce transition zone between antirusting paint and antifouling paint, Sealing paint in the middle of connecting coating or being referred to as, connection coating must play double faced adhesive tape effect.
Chinese patent CN102964516A disclose a kind of single-component epoxy base it is acrylic resin modified and its application, this Bright mentioning uses epoxy-modified acrylic resin, and although prepared connection paint is effectively improved to antirust paint adhesive strength and antifouling Paint bonding strength, but painting interlayer failure mechanics still have 10% connection paint and priming paint interlaminar failure, 10% anti-fouling paint and connection Paint interlaminar failure, and anti-fouling paint be connected the overlay painting interval needs 7 days that paint.
In addition existing one-component connection coating also has chlorinated rubber type, and which has one to antirusting paint and antifouling paint Fixed attachment and switching performance, but it is not high to the adhesive strength of antirusting paint, and its intensity is not higher than 2.0MPa.And chlorinated rubber Differ greatly with epoxy molecule structure and polar functional group, chlorinated rubber is coated in the fine and close epoxy primer of completion of cure On adhesion property it is poor, actual application requires which to antirust paint overlay painting interval within 24h, it is seen that its intensity and application Interval still suffers from defect.
Relevant report yet there are no by the Abietyl modified method for preparing one-component connection coating into acrylic resin.
The content of the invention
For solving the above problems, the invention provides a kind of method that connection coating is prepared by Abietyl modified acrylate, The connection coating that the method is prepared is respectively provided with high-adhesion to antirusting paint and antifouling paint, most long 8 days to antirusting paint Hardening time and do not limit overlay painting interval to antifouling paint, preferably resolve connection coating adhesive strength and application between Every preparation method is simple, easy construction.
For achieving the above object, the present invention is adopted the following technical scheme that:
A kind of method for preparing connection coating by Abietyl modified acrylate, the method use Abietyl modified acrylate Resin, chlorinated rubber, thixotropic agent, color stuffing and solvent, Abietyl modified acrylic resin are methyl methacrylate, metering system The copolymer of acid butyl ester and rosin and Chemical market is on sale, the feature of the present invention are as follows:
It is required that the molecular weight Mw of Abietyl modified acrylate is controlled 50000~100000, thixotropic agent is organic bentonite Profit soil;Color stuffing is ferrotitanium powder, mica powder and titanium dioxide;Solvent is dimethylbenzene and n-butanol;
By the Abietyl modified acrylate of 10~15 weight portions, the chlorinated rubber of 6~10 weight portions, 14~24 weight The n-butanol of the dimethylbenzene and 4~8.7 weight portions of part stirs in together putting high speed dispersor into, afterwards by 0.8~1.2 weight The organobentonite of amount part is put high speed dispersor high speed into and disperses 15~20min, followed by by the ferrotitanium of 20~30 weight portions The titanium dioxide of powder, the mica powder of 20~25 weight portions and 3~8 weight portions together puts high speed dispersor high speed dispersion 30min into Connection coating can be prepared, require that the fineness of connection coating is controlled below 100 μm after testing.
As using techniques described above scheme, the present invention produces following good effect:
1st, its good film-forming property of connection coating of the invention is high to the switching performance of antirusting paint and antifouling paint.
2nd, connection coating and antifouling paint of the invention can also keep good connection intensity without overlay painting interval time restriction.
Specific embodiment
The present invention is a kind of method for preparing connection coating by Abietyl modified acrylate, present invention mainly solves connection Coating can not be provided simultaneously with the shortcoming of high intensity connection and long overlay painting interval.
The present invention with molecular weight Mw be 50000~100000 Abietyl modified acrylic resin based on base-material, with chlorination rubber Glue is auxiliary base-material, is equipped with dimethylbenzene, n-butanol, organobentonite, ferrotitanium powder, mica powder and titanium dioxide and prepares connection painting Material, the Abietyl modified acrylate for using, chlorinated rubber, dimethylbenzene, n-butanol, organobentonite, ferrotitanium powder, mica Powder, titanium dioxide are industrial raw material and Chemical market is on sale, and wherein organobentonite belongs to thixotropic agent, ferrotitanium powder, mica powder Belong to color stuffing with titanium dioxide, dimethylbenzene and n-butanol belong to solvent, and organobentonite, ferrotitanium powder and titanium dioxide are using ultra-fine Level, mica powder is fine platy.
Abietyl modified acrylic resin is formed by methyl methacrylate, butyl methacrylate and rosin copolymerization.Using Rosin aromatic ring structure and similitude and the good intermiscibility of bisphenol-A epoxy aromatic ring structure in antirusting paint, can form stronger Van der Waals force.Hydrogen bond is formed using the hydroxyl on the ester bond in acrylate and antirusting paint surface, amino etc., connection can be reached Coating is sprawled to the good wet of antirusting paint, and this Van der Waals force and hydrogen bond cooperatively form connection coating to antirusting paint High intensity attachment, while this Cooperation force receive time restriction, be capable of achieving connection longer painting of the coating to antirusting paint Dress interval.
Used as assisted resin, using its preferable bonding force, further raising connects chlorinated rubber with excellent compatibility Adhesive strength of the coating to antirusting paint is connect, connection coating densification is good, can improve the physicochemical property of film.
The thermoplasticity of Abietyl modified acrylic resin and chlorinated rubber resin is applied, it is when antifouling paint is coated, antifouling Solvent in coating is to its appropriate dissolving and winds mutually, forms firm intermolecular force, realizes high connection function, this molten Solution and mutual winding are acted on, with unconfined overlay painting interval.
The present invention can be explained in more detail by following three embodiments, this is the invention is not limited in, disclosed this Bright purpose is intended to protect all changes and improvements in the scope of the invention.
Three embodiments see the table below.
According to connection coating is prepared by upper table proportioning combination technology scheme, require the fineness of connection coating after testing Control is below 100 μm.
The performance test reference data of three embodiments see the table below.
The items of present invention connection coating are see the table below with reference to averaging index.
7 days connection coating of overlay painting interval is see the table below to the adhesive strength reference pair ratio of antirusting paint.
Type Adhesive strength/MPa
Commercially available connection coating 1.5
The connection coating of the present invention 3.5
7 days connection coating of overlay painting interval is see the table below to the bonding strength reference pair ratio of antifouling paint.
Type Bonding strength/MPa
Commercially available connection coating 1.6
The connection coating of the present invention 2.5
The bonding strength reference pair ratio of connection coating half a year interval application see the table below.
Type Bonding strength/MPa
Commercially available connection coating 1.0
The connection coating of the present invention 2.2
Above-mentioned each table is absolutely proved:The connection coating of the present invention has good film-forming property, to antirusting paint and antifouling paint Switching performance is high, can also keep good connection intensity with antifouling paint without overlay painting interval time restriction.

Claims (1)

1. a kind of to be prepared the method for connecting coating by Abietyl modified acrylate, the method uses Abietyl modified acrylate tree Fat, chlorinated rubber, thixotropic agent, color stuffing and solvent, Abietyl modified acrylic resin are methyl methacrylate, methacrylic acid The copolymer of butyl ester and rosin and Chemical market is on sale, is characterized in that:
It is required that the molecular weight Mw of Abietyl modified acrylate is controlled 50000~100000, thixotropic agent is organobentonite; Color stuffing is ferrotitanium powder, mica powder and titanium dioxide;Solvent is dimethylbenzene and n-butanol;
By the Abietyl modified acrylate of 10~15 weight portions, the chlorinated rubber of 6~10 weight portions, 14~24 weight portions The n-butanol of dimethylbenzene and 4~8.7 weight portions stirs in together putting high speed dispersor into, afterwards by 0.8~1.2 weight portion Organobentonite put into high speed dispersor high speed disperse 15~20min, followed by by the ferrotitanium powder of 20~30 weight portions, 20 The titanium dioxide of the mica powder of~25 weight portions and 3~8 weight portions is made by together putting high speed dispersor high speed dispersion 30min into It is standby to go out to connect coating, require that the fineness of connection coating is controlled below 100 μm after testing.
CN201510430020.7A 2015-07-21 2015-07-21 Method for preparing connection paint from rosin-modified acrylate Active CN105017914B (en)