CN105017869A - 一种金属外表面防锈油漆 - Google Patents
一种金属外表面防锈油漆 Download PDFInfo
- Publication number
- CN105017869A CN105017869A CN201410598453.9A CN201410598453A CN105017869A CN 105017869 A CN105017869 A CN 105017869A CN 201410598453 A CN201410598453 A CN 201410598453A CN 105017869 A CN105017869 A CN 105017869A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal
- paint
- metal outer
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种金属外表面防锈油漆,按重量份计,由以下各原料组成:E-20环氧树脂20-25、质量分数40-45%的苯丙乳液33-36、三聚磷酸二氢铝6-8、亚铁氰化钾0.4-0.8、铁红2-5、氧化锌3.5-5.5、碳黑0.2-0.8、甲基异丁酮1.4-1.8、滑石粉3.2-4.6、丁基缩水甘油醚3.6-5.6、缓蚀剂1.3-1.8、水22-25;本发明成本低,适用于有锈蚀、坚实氧化皮或旧漆膜的金属表面,对无锈的金属表面也有良好的防锈作用。可用于一些难以进行表面处理的大型金属构筑物,如桥梁、交通护栏、大型机械、金属门窗等。
Description
技术领域
本发明涉及金属外表面处理领域,具体属于一种金属外表面防锈油漆。
背景技术
油漆是一种能牢固覆盖在物体表面,起保护、装饰、标志和其他特殊用途的化学混合物涂料。油漆为粘稠油性颜料,未干情况下易燃,不溶于水,微溶于脂肪,可溶于醇、醛、醚、苯、烷,易溶于汽油、煤油、柴油。
金属在潮湿、高温、氧气、二氧化硫、氯化物、尘埃的环境中容易造成外表面生锈,避免或减缓这些因素所引起的金属锈蚀作用。目前采用的防锈方法有:在金属冶炼时加入某些元素,提高金属抵抗外部介质侵蚀的能力。防锈油漆市场上种类很多,但是使用效果不佳,制作成本高。
发明内容
本发明的目的是提供一种金属外表面防锈油漆,成本低,适用于有锈蚀、坚实氧化皮或旧漆膜的金属表面,对无锈的金属表面也有良好的防锈作用。可用于一些难以进行表面处理的大型金属构筑物,如桥梁、交通护栏、大型机械、金属门窗等。
本发明采用的技术方案如下:
一种金属外表面防锈油漆,按重量份计,由以下各原料组成:
E-20环氧树脂20-25、质量分数40-45%的苯丙乳液33-36、三聚磷酸二氢铝6-8、亚铁氰化钾0.4-0.8、铁红2-5、氧化锌3.5-5.5、碳黑0.2-0.8、甲基异丁酮1.4-1.8、滑石粉3.2-4.6、丁基缩水甘油醚3.6-5.6、缓蚀剂1.3-1.8、水22-25;
其具体的制备方法如下:
具体的制备方法如下:依次向高速分散釜中加入四分之一的水、E-20环氧树脂、苯丙乳液、三聚磷酸二氢铝、亚铁氰化钾、滑石粉、缓蚀剂,85-90℃下搅拌反应40-50分钟,然后加入剩余各原料,降低至20-30℃,800-900转/分搅拌分散35-45分钟,即得该油漆。
一种金属外表面防锈油漆,按重量份计,由以下各原料组成:
E-20环氧树脂22、质量分数40-45%的苯丙乳液34、三聚磷酸二氢铝7、亚铁氰化钾0.6、铁红3、氧化锌4、碳黑0.5、甲基异丁酮1.6、滑石粉3.9、丁基缩水甘油醚4、缓蚀剂1.5、水23。
本发明采用E-20环氧树脂、亚铁氰化钾,成本低,适用于有锈蚀、坚实氧化皮或旧漆膜的金属表面,对无锈的金属表面也有良好的防锈作用。可用于一些难以进行表面处理的大型金属构筑物,如桥梁、交通护栏、大型机械、金属门窗等。
具体实施方式
一种金属外表面防锈油漆,按重量份计,由以下各原料组成:
E-20环氧树脂22、质量分数40-45%的苯丙乳液34、三聚磷酸二氢铝7、亚铁氰化钾0.6、铁红3、氧化锌4、碳黑0.5、甲基异丁酮1.6、滑石粉3.9、丁基缩水甘油醚4、缓蚀剂1.5、水23;
其具体的制备方法如下:
具体的制备方法如下:依次向高速分散釜中加入四分之一的水、E-20环氧树脂、苯丙乳液、三聚磷酸二氢铝、亚铁氰化钾、滑石粉、缓蚀剂,85-90℃下搅拌反应40-50分钟,然后加入剩余各原料,降低至20-30℃,800-900转/分搅拌分散35-45分钟,即得该油漆。
Claims (2)
1.一种金属外表面防锈油漆,按重量份计,其特征在于,由以下各原料组成:
E-20环氧树脂20-25、质量分数40-45%的苯丙乳液33-36、三聚磷酸二氢铝6-8、亚铁氰化钾0.4-0.8、铁红2-5、氧化锌3.5-5.5、碳黑0.2-0.8、甲基异丁酮1.4-1.8、滑石粉3.2-4.6、丁基缩水甘油醚3.6-5.6、缓蚀剂1.3-1.8、水22-25;
其具体的制备方法如下:
具体的制备方法如下:依次向高速分散釜中加入四分之一的水、E-20环氧树脂、苯丙乳液、三聚磷酸二氢铝、亚铁氰化钾、滑石粉、缓蚀剂,85-90℃下搅拌反应40-50分钟,然后加入剩余各原料,降低至20-30℃,800-900转/分搅拌分散35-45分钟,即得该油漆。
2.根据权利要求1所述金属外表面防锈油漆,按重量份计,其特征在于,由以下各原料组成:
E-20环氧树脂22、质量分数40-45%的苯丙乳液34、三聚磷酸二氢铝7、亚铁氰化钾0.6、铁红3、氧化锌4、碳黑0.5、甲基异丁酮1.6、滑石粉3.9、丁基缩水甘油醚4、缓蚀剂1.5、水23。