CN104194526A - 一种长效防腐金属漆 - Google Patents
一种长效防腐金属漆 Download PDFInfo
- Publication number
- CN104194526A CN104194526A CN201410368011.5A CN201410368011A CN104194526A CN 104194526 A CN104194526 A CN 104194526A CN 201410368011 A CN201410368011 A CN 201410368011A CN 104194526 A CN104194526 A CN 104194526A
- Authority
- CN
- China
- Prior art keywords
- parts
- zinc
- long
- metallic paint
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种长效防腐金属漆，由以下重量份数的原料制成：水性环氧树脂8-17份，十二醇丁醚12-20份，碳酸钙3-9份，明矾粉5-7份，甲基纤维素5-10份，甲醇5-10份，银粉7-14份，磷酸锌6-12份，硬酯酸锌4-8份，三乙胺4-8份，邻苯二酚8-14份，硫酸锌5-10份，热塑性丙烯酸树脂30-50份，氟化锆7-14份，二甲氨基丙烷2-8份。本发明提供一种具有良好柔韧性、附着力、耐水性强、防腐性、耐久性，能耐酸、耐碱的长效防腐金属漆。
Description
技术领域
本发明涉及涂料技术领域，具体涉及一种长效防腐金属漆。
背景技术
随着现代工业的飞速发展，金属表面的防腐越来越受到各行各业的高度重视，采用油漆涂覆防腐是一种既经济又实效的方法，对工矿企业来说，金属腐蚀造成了经济上的巨大损失是难于估量的，约占全球钢产量的 15％～ 20％，可见，对腐蚀的防护是何等重要。防止金属腐蚀的方法很多，如在使用材料上选用耐腐蚀合金材料，虽起到防腐作用，但工程造价大，不利于有色金属资源的保护和科学经济 ；还有采用电镀和阴极保护方法，但造成排放污染，不利于环境保护。防护实践证明，采取用油漆涂层防护是最有效最经济最普遍的方法，首先是施工简便，适应性广，不受设备面积、形态大小的压缩，其次油漆防护可与其它防护措施 ( 如阴极保护等 ) 联合使用，便可获得较完善的防腐蚀体系。
我国生产油漆的企业很多，油漆品种繁多，但均属普通产品，远不能适应我国钢铁工业及金属防腐业的需要，金属的腐蚀，是金属受环境介质的化学或电化学作用而被破坏的物理化学现象。长期以来，金属设备防腐蚀最有效、最常用的方法之一是在金属表面涂刷防腐蚀涂层，以隔绝腐蚀介质与金属基体，因此，开发一种性能优异、适用于高科技金属防腐的油漆产品其意义非比寻常，迫在眉睫。
发明内容
针对现有技术的不足，本发明所要解决的技术问题是，提供一种具有良好柔韧性、附着力、耐水性强、防腐性、耐久性，能耐酸、耐碱的长效防腐金属漆。
为解决上述技术问题，本发明所采取的技术方案是：一种长效防腐金属漆，由以下重量份数的原料制成：水性环氧树脂8-17份，十二醇丁醚12-20份，碳酸钙3-9份，明矾粉5-7份，甲基纤维素5-10份，甲醇5-10份，银粉7-14份，磷酸锌6-12份，硬酯酸锌4-8份，三乙胺 4-8份，邻苯二酚8-14份，硫酸锌 5-10份，热塑性丙烯酸树脂30-50份，氟化锆7-14份，二甲氨基丙烷2-8份。
上述的长效防腐金属漆，由以下重量份数的原料制成：水性环氧树脂14份，十二醇丁醚15份，碳酸钙6份，明矾粉6份，甲基纤维素8份，甲醇8份，银粉11份，磷酸锌10份，硬酯酸锌6份，三乙胺6份，邻苯二酚12份，硫酸锌8份，热塑性丙烯酸树脂40份，氟化锆12份，二甲氨基丙烷6份。
本发明长效防腐金属漆优点是：
1、本发明长效防腐金属漆，具有良好柔韧性、附着力、耐水性强、防腐性、耐久性，能耐酸、耐碱；适用于高科技金属防腐的油漆产品其意义非比寻常，迫在眉睫。。
具体实施方式
下面结合实施例对本发明作进一步说明。
实施例1，一种长效防腐金属漆，由以下重量份数的原料制成：水性环氧树脂8份，十二醇丁醚12份，碳酸钙3份，明矾粉5份，甲基纤维素5份，甲醇5份，银粉7份，磷酸锌6份，硬酯酸锌4份，三乙胺 4份，邻苯二酚8份，硫酸锌 5份，热塑性丙烯酸树脂30份，氟化锆7份，二甲氨基丙烷2份。
实施例2，一种长效防腐金属漆，由以下重量份数的原料制成：水性环氧树脂14份，十二醇丁醚15份，碳酸钙6份，明矾粉6份，甲基纤维素8份，甲醇8份，银粉11份，磷酸锌10份，硬酯酸锌6份，三乙胺6份，邻苯二酚12份，硫酸锌8份，热塑性丙烯酸树脂40份，氟化锆12份，二甲氨基丙烷6份。
实施例3，一种长效防腐金属漆，由以下重量份数的原料制成：水性环氧树脂17份，十二醇丁醚20份，碳酸钙9份，明矾粉7份，甲基纤维素10份，甲醇10份，银粉14份，磷酸锌12份，硬酯酸锌8份，三乙胺 8份，邻苯二酚14份，硫酸锌 10份，热塑性丙烯酸树脂50份，氟化锆14份，二甲氨基丙烷8份。
当然，上述说明并非是对本发明的限制，本发明也并不限于上述举例，本技术领域的普通技术人员，在本发明的实质范围内，作出的变化、改变、添加或替换，都应属于本发明的保护范围。
Claims (2)
1.一种长效防腐金属漆，其特征在于：由以下重量份数的原料制成：水性环氧树脂8-17份，十二醇丁醚12-20份，碳酸钙3-9份，明矾粉5-7份，甲基纤维素5-10份，甲醇5-10份，银粉7-14份，磷酸锌6-12份，硬酯酸锌4-8份，三乙胺 4-8份，邻苯二酚8-14份，硫酸锌 5-10份，热塑性丙烯酸树脂30-50份，氟化锆7-14份，二甲氨基丙烷2-8份。
2.根据权利要求1所述的长效防腐金属漆，其特征在于：由以下重量份数的原料制成：水性环氧树脂14份，十二醇丁醚15份，碳酸钙6份，明矾粉6份，甲基纤维素8份，甲醇8份，银粉11份，磷酸锌10份，硬酯酸锌6份，三乙胺6份，邻苯二酚12份，硫酸锌8份，热塑性丙烯酸树脂40份，氟化锆12份，二甲氨基丙烷6份。