CN104098965A - 一种海洋盐碱大气区水性无锌带锈重防腐漆 - Google Patents
一种海洋盐碱大气区水性无锌带锈重防腐漆 Download PDFInfo
- Publication number
- CN104098965A CN104098965A CN201310126180.3A CN201310126180A CN104098965A CN 104098965 A CN104098965 A CN 104098965A CN 201310126180 A CN201310126180 A CN 201310126180A CN 104098965 A CN104098965 A CN 104098965A
- Authority
- CN
- China
- Prior art keywords
- agent
- saline
- water
- heavy
- alkaline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种海洋盐碱大气区水性无锌带锈重防腐漆,包含以下成分:去离子水10%-26%、防霉剂0.1%、分散剂0.8%、消泡剂0.5%、成膜助剂2.5%、防冻剂2.5%、中和剂0.2%、润湿剂0.2%、抑泡剂0.2%、流平剂0.1%、锈蚀剂1%、缓蚀剂1%、抗闪锈剂2%、氧化铁红或复合铁钛粉10%、三聚磷酸铝5%-10%、金红石钛白粉1%-5%、硅灰石9%、湿法绢云母5%-10%、叔碳酸乙烯酯共聚物改良型树脂40%-60%、减溶胀增稠剂0.5%-1%。本技术方案制备的海洋盐碱大气区水性无锌带锈重防腐漆,省却了企业涂装前浩大的除锈工程,给企业节省了巨额成本,提高了防腐效果,具有很好的市场前景。
Description
技术领域
本发明涉及涂料,特别是一种水性无锌带锈重防腐漆,具体是指一种海洋盐碱大气区水性无锌带锈重防腐漆。
背景技术
水性重防腐漆是指在苛刻的腐蚀环境使用的涂料,他的使用寿命长,可适应更苛刻的环境。在化工环境和海洋盐碱环境里,水性重防腐漆可使用10年或者15年以上。水性重防腐漆的发展方向是环保、节能、高性能和功能化,是防腐涂料将来发展的主要方向,以推进我国新材料技术和产业的升级发展,可为人类社会做出重大贡献。
发明内容
本发明的目的在于提供一种海洋盐碱大气区水性无锌带锈重防腐漆,以解决现有溶剂型防腐涂料在化工企业和海洋盐碱地区环境里使用寿命过短及对环境造成污染和对人类造成危害的问题。
为实现上述目的,本发明采用的技术方案是:
一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:包括以下物质及质量份数:去离子水10%-26%、防霉剂0.1%、分散剂0.8%、消泡剂0.5%、成膜助剂2.5%、防冻剂2.5%、中和剂0.2%、润湿剂0.2%、抑泡剂0.2%、流平剂0.1%、锈蚀剂1%、缓蚀剂1%、抗闪锈剂2%、氧化铁红或复合铁钛粉10%、三聚磷酸铝5%-10%、金红石钛白粉1%-5%、硅灰石5%-10%、湿法绢云母5%、叔碳酸乙烯酯共聚物改良型树脂40%-60%、减溶胀增稠剂0.5%-1%。
所述的分散剂为211。
所述的中和剂为AMP-95。
所述的润湿剂为X-405或PE-100中的一种。
所述的抑泡剂为902W。
所述的流平剂为3580。
所述的抗闪锈剂为STAR-102。
所述的三聚磷酸铝为APW-2。
所述的叔碳酸乙烯酯共聚物改良剂树脂为Hiqua3000。
所述蚀锈剂为schwego corrit乙醇酸碱溶液。
另外,所述的防霉剂为BDBDK-1、消泡剂为202、成膜助剂为醇脂十二、防冻剂为丙二醇、氧化铁红为S130,复合钛白粉为W800、金红石钛白粉为R258、湿法绢云母为GA-2、减溶胀增稠剂分为高剪切和低剪切;高剪切为BD-21;低剪切为BD-20;缓蚀剂asconium143。
本发明相对于现有技术,本发明能在铁板表面快速变化生成一层保护膜,能有效阻止铁板与氧气、水的接触,从而达到防锈的效果,并有效抑制了铁锈的再生,并对底材不产生任何危害。
具体实施方式
以下通过具体实施方式对本发明做进一步的具体说明:
实施例1
去离子水:12%-26%;
防霉剂:BDBDK-1 0.1%;
分散剂:211 0.8%;
消泡剂:202 0.5%;
成膜助剂:醇脂十二 2.5%;
防冻剂:丙二醇 2.5%;
中和剂:AMP-95 0.2%;
润湿剂:X-405 0.2%;
抑泡剂:902W 0.2%;
流平剂:3580 0.1%;
锈蚀剂:schwego corrit(乙醇酸盐溶液)1%;
缓蚀剂:asconium143 1%;
抗闪锈剂:STAR-102 2%;
氧化铁红:S130 10%;
三聚磷酸铝:APW-2 7%;
金红石钛白粉:R258 2%;
硅灰石:9%;
湿法绢云母:GA-2 8%;
叔碳酸乙烯酯共聚物改良型树脂:Hiqua3000 40%-50%:
减溶胀增稠剂高剪切BD-21 0.4%:
减溶胀增稠剂低剪切BD-20 0.3%。
实施例2
去离子水:10%-25%;
防霉剂:BDBDK-1 0.1%:
分散剂:211 0.8%;
消泡剂:202 0.5%;
成膜助剂:醇脂十二 2.5%;
防冻剂:丙二醇 2.5%;
中和剂:AMP-95 0.2%:
润湿剂:PE-100 0.2%;
抑泡剂:902W 0.2%;
流平剂:3580 0.1%;
锈蚀剂:scnwego corrit(乙醇酸盐溶液)1%;
缓蚀剂:asconium143 1%:
抗闪锈剂:STAR-102 2%;
复合铁钛粉:W800 9%;
三聚磷酸铝:APW-2 8%:
金红石钛白粉:R258 3%;
硅灰石:9%;
湿法绢云母:GA-2 7%;
叔碳酸乙烯酯共聚物改良型树脂:Hiqua3000 45%-60%;
减溶胀增稠剂高剪切BD-21 0.4%;
减溶胀增稠剂低剪切BD-20 0.3%。
当铁板生锈时,铁板表面形成原电池,其反应方程式为,正极2H2O+O2+4e=4OH-,负极:Fe-2e=Fe2+,总反应:2Fe+2H2O+O2=2Fe(OH)2↓,然后Fe(OH)2与空气中的氧气反应生成Fe(OH)3,其反应为4Fe(OH)2+2H2O+O2=4Fe(OH)3↓,然后,2Fe(OH)3+nH2O=Fe2O3.nH2O+3H2O。此时喷涂水性带锈重防腐底漆,产品中的特种助剂与Fe2O3.nH2O迅速反应,把铁锈迅速络合生成Fe3O4.nH2O,颜色变为黑色,成为一种氧化铁防锈颜料,与防腐底漆迅速反应溶合为一体,产生相加作用,更有效的阻止铁板与氧气、水的接触,从而达到防锈的效果。产品中添加的特种助剂还能有效地抑制氧气与水的活性,有效地抑制了铁锈的再生。该水性带锈重防腐底漆在铁板的表面快速的生成一层保护膜,使铁板与外界隔绝,阻止了外界对铁板的侵蚀,因此涂刷本发明所产生的黑色物质为氧化铁黑防锈颜料,对底材是有益的,并无任何危害。
总之,本发明提供一种海洋盐碱大气区水性无锌带锈重防腐漆,本产品为低碳环保型,具有使用寿命长、防腐效果好等特点,具有良好的市场前景。
Claims (10)
1.一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:包括以下物质及质量份数:去离子水10%-26%、防霉剂0.1%、分散剂0.8%、消泡剂0.5%、成膜助剂2.5%、防冻剂2.5%、中和剂0.2%、润湿剂0.2%、抑泡剂0.2%、流平剂0.1%、锈蚀剂1%、缓蚀剂1%、抗闪锈剂2%、氧化铁红或复合铁钛粉10%、三聚磷酸铝5%-10%、金红石钛白粉1%-5%、硅灰石5%-10%、湿法绢云母5%、叔碳酸乙烯酯共聚物改良型树脂40%-60%、减溶胀增稠剂0.5%-1%。
2.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的分散剂为211。
3.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的中和剂为AMP-95。
4.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的润湿剂为X-405或PE-100中的一种。
5.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的抑泡剂为902W。
6.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的流平剂为3580。
7.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的抗闪锈剂为STAR-102。
8.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的三聚磷酸铝为APW-2。
9.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的叔碳酸乙烯酯共聚物改良型树脂为Hiqua3000。
10.根据权利要求1所述的一种海洋盐碱大气区水性无锌带锈重防腐漆,其特征在于:所述的锈蚀剂为乙醇酸碱溶液。