CN105001670A - Dark green color corn straw dye and production method thereof - Google Patents
Dark green color corn straw dye and production method thereof Download PDFInfo
- Publication number
- CN105001670A CN105001670A CN201510487464.4A CN201510487464A CN105001670A CN 105001670 A CN105001670 A CN 105001670A CN 201510487464 A CN201510487464 A CN 201510487464A CN 105001670 A CN105001670 A CN 105001670A
- Authority
- CN
- China
- Prior art keywords
- maize straw
- paleturquoise
- parts
- broad
- babei
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a dark green color corn straw dye and a production method thereof. Corn straw, globe artichoke, barbiere roots, osmanthus asiaticus nakai, broad-leaved epuphyllum, alumen, an ionic compound solution and alkaline mineral water are taken as main raw materials, and the main technological process of the production method of the dark green color corn straw dye comprises the steps of material selecting, material cutting, fuming, steeping, hot boiling, dyeing and color fixing. The dark green color corn straw dye is made of pure plants and has the faint scent diffused by the plants, no chemical matter is added in the manufacturing process, and no harm is caused on the human body; furthermore, the raw materials are wide in source, the processing technological route is short, and the product is easy to process and manufacture.
Description
technical field:
the present invention relates to a kind of vegetable dye, particularly relates to a kind of paleturquoise maize straw dyestuff and production method thereof.
background technology:
industrial art refers to that daily living article is after art up process, makes it the product with strong aesthetic value.We are generally the industrial art that industrial art is divided into the practical art fine arts and furnishings to appreciate.The practical art fine arts are main body and the basis of whole industrial art, comprise clothing, food, change, row, arts and crafts, practical value is the chief value of this kind of artwork, and aesthetic value exists as auxiliary value.This kind of artwork comprises tea tableware, light fixture, wood furniture, embroidered article, careless plaited bamboo articles etc. through decorative processing.Furnishings are appreciated artwork and are referred to that those are based on ornaments, the artwork viewing and admiring function, and this kind of artwork is primarily worth for it with aesthetic, and manual skill is very strong, as jadeware, jewel, ivory carving, cloisonne, lacquerware, wall hanging, pottery art etc.
china's industrial art with a long history is a bright jewel in China's culture treasure-house, plain well-known in the world.Industrial art originates from the epoch that the mankind start fabrication tool.Industrial art is that working people directly creates mostly, and the material life with people is closely related with cultural life.Its generation, often because of period of history, geographical environment, economic condition, cultural state of the art, national prevailing custom is different with aesthetic standard and show different style characteristics.
in modern technologies, be mostly to make dyeing picture processed with the method for chemical industry dyeing, therefore, utilize recyclability resource to be the important content of current environment Green Development, be a long term growth direction of protection of the environment, there is far-reaching and realistic meaning.Stalk fibre is as renewable resources huge on the earth; be starting point from the level of the sustainable use of resource, protection of the environment; the recycling of stalk fibre has become the popular domain of research and development; natural gloss, texture and texture is had with the painter's paraphernalia that stalk makes; the personage made is life-like; birds and flowers, beast is remarkably true to life, has stereoscopic sensation, very popular.
at present, the method that the main raw material maize straw making stalk picture dyes paleturquoise is had a variety of, but the paleturquoise that polychromatophilia goes out is impure, easily fade, not only not environmentally, some dyes even can produce toxic gas, the health of harmful to human in the process of dye system.
summary of the invention:
the object of the present invention is to provide a kind of pure natural, pollution-free, environmental protection, the paleturquoise maize straw dyestuff be mixed with natural plant that the person is had no side effect and production method thereof.
the object of the present invention is achieved like this.It is that the raw material of being joined by following weight is made, maize straw 25-50 part, choke 15-30 part, BABEI profit root 10-22 part, silver-colored osmanthus 7-18 part, broad-leaved epiphyllum 5-15 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 70-100 part.
preparing paleturquoise maize straw dyestuff preferred weight ratio range of the present invention is, wherein the weight proportion of various raw material is, maize straw 25-40 part, choke 15-25 part, BABEI profit root 10-16 part, silver-colored osmanthus 7-13 part, broad-leaved epiphyllum 5-10 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 70-90 part.
the optimum weight ratio range preparing paleturquoise maize straw dyestuff of the present invention is, wherein the weight proportion of various raw material is, maize straw 33 parts, choke 20 parts, BABEI profit root 13 parts, 10 parts, silver-colored osmanthus, broad-leaved epiphyllum 8 parts, alum 7 parts, ferric ion compounds solution 7 parts, mineral water 80 parts.
above-mentioned each component is made the production method of paleturquoise maize straw dyestuff of the present invention, technical process is: select materials, blank, stifling, soak, heat is boiled, dye, fixation, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, choose the maize straw of complete drying, remove other branch, remove Section 1 and last 1 joint, leave and take middle portion, select the choke, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, maize straw knife longitudinally to be cut open, remove the interior flesh part of the inside, retain outside stalk part for subsequent use; By the raw material choke selected, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, be respectively cut into block for subsequent use; C, stifling, maize straw sulfuric acid is fumigated, the time is 10-20 minute; D, immersion, selected raw material is placed in the storage tank that mineral water is housed soaks, temperature is 20 DEG C-25 DEG C, time 2-4 hour; E, heat are boiled, salt and water are placed in iron pan and heat, water temp. heating is to 40 °, put into alum, persistently overheating to water temperature be 70 °, put into the choke after immersion, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, and constantly stir, put into ferric ion compounds solution, boiling 2-3 hour, cooks paleturquoise pigment solution; The pigment solution that F, dyeing, extraction boiling go out, puts in pottery, puts into the maize straw after immersion, and boiling 1-2 hour, period constantly stirs, and makes maize straw fully absorb paleturquoise pigment, level dyeing; G, fixation, the maize straw after dyeing to be pulled out, leave standstill 30 minutes, put into clear water 5-10 minute, take out after drifting out loose colour, be put into shady and cool ventilation place dry, obtain a kind of maize straw dyestuff of paleturquoise.
the invention has the advantages that: 1, select raw material, scientific formulation, color is pure; 2, product is made by pure plant, has the delicate fragrance that plant itself is distributed, and does not add any chemical substance in making processes, to human body without any injury; 3, raw material sources are extensive, add process line short, the easy processing and manufacturing of product.
Embodiment
below in conjunction with specific embodiment, the present invention is further illustrated:
embodiment 1:
preparing paleturquoise maize straw dyestuff weight proportion scope of the present invention is: maize straw 25-50 part, choke 15-30 part, BABEI profit root 10-22 part, silver-colored osmanthus 7-18 part, broad-leaved epiphyllum 5-15 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 70-100 part.
embodiment 2:
preparing paleturquoise maize straw dyestuff preferred weight ratio range of the present invention is: maize straw 25-40 part, choke 15-25 part, BABEI profit root 10-16 part, silver-colored osmanthus 7-13 part, broad-leaved epiphyllum 5-10 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 70-90 part.
embodiment 3:
preparing paleturquoise maize straw dyestuff optimum weight ratio range of the present invention is: maize straw 33 parts, choke 20 parts, BABEI profit root 13 parts, 10 parts, silver-colored osmanthus, broad-leaved epiphyllum 8 parts, alum 7 parts, ferric ion compounds solution 7 parts, mineral water 80 parts.
above-mentioned each component is made the production method of paleturquoise maize straw dyestuff of the present invention, technical process is: select materials, blank, stifling, soak, heat is boiled, dye, fixation, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, choose the maize straw of complete drying, remove other branch, remove Section 1 and last 1 joint, leave and take middle portion, select the choke, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, maize straw knife longitudinally to be cut open, remove the interior flesh part of the inside, retain outside stalk part for subsequent use; By the raw material choke selected, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, be respectively cut into block for subsequent use; C, stifling, maize straw sulfuric acid is fumigated, the time is 10-20 minute; D, immersion, selected raw material is placed in the storage tank that mineral water is housed soaks, temperature is 20 DEG C-25 DEG C, time 2-4 hour; E, heat are boiled, salt and water are placed in iron pan and heat, water temp. heating is to 40 °, put into alum, persistently overheating to water temperature be 70 °, put into the choke after immersion, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, and constantly stir, put into ferric ion compounds solution, boiling 2-3 hour, cooks paleturquoise pigment solution; The pigment solution that F, dyeing, extraction boiling go out, puts in pottery, puts into the maize straw after immersion, and boiling 1-2 hour, period constantly stirs, and makes maize straw fully absorb paleturquoise pigment, level dyeing; G, fixation, the maize straw after dyeing to be pulled out, leave standstill 30 minutes, put into clear water 5-10 minute, take out after drifting out loose colour, be put into shady and cool ventilation place dry, obtain a kind of maize straw dyestuff of paleturquoise.
Claims (4)
1. a paleturquoise maize straw dyestuff, it is characterized in that: it is made up of the raw material of following weight proportioning, maize straw 25-50 part, choke 15-30 part, BABEI profit root 10-22 part, silver-colored osmanthus 7-18 part, broad-leaved epiphyllum 5-15 part, alum 5-15 part, ferric ion compounds solution 5-15 part, mineral water 70-100 part.
2. a paleturquoise maize straw dyestuff, it is characterized in that: wherein the weight proportion of various raw material is, maize straw 25-40 part, choke 15-25 part, BABEI profit root 10-16 part, silver-colored osmanthus 7-13 part, broad-leaved epiphyllum 5-10 part, alum 5-10 part, ferric ion compounds solution 5-10 part, mineral water 70-90 part.
3. a paleturquoise maize straw dyestuff, it is characterized in that: wherein the weight proportion of various raw material is, maize straw 33 parts, choke 20 parts, BABEI profit root 13 parts, 10 parts, silver-colored osmanthus, broad-leaved epiphyllum 8 parts, alum 7 parts, ferric ion compounds solution 7 parts, mineral water 80 parts.
4. a kind of production method preparing paleturquoise maize straw dyestuff according to claim 3, it is characterized in that: technical process is: select materials, blank, stifling, soak, heat is boiled, dye, fixation, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, choose the maize straw of complete drying, remove other branch, remove Section 1 and last 1 joint, leave and take middle portion, select the choke, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, alum, ferric ion compounds solution, the mineral water that meet national health and quality standard for subsequent use; B, blank, maize straw knife longitudinally to be cut open, remove the interior flesh part of the inside, retain outside stalk part for subsequent use; By the raw material choke selected, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, be respectively cut into block for subsequent use; C, stifling, maize straw sulfuric acid is fumigated, the time is 10-20 minute; D, immersion, selected raw material is placed in the storage tank that mineral water is housed soaks, temperature is 20 DEG C-25 DEG C, time 2-4 hour; E, heat are boiled, salt and water are placed in iron pan and heat, water temp. heating is to 40 °, put into alum, persistently overheating to water temperature be 70 °, put into the choke after immersion, BABEI profit root, silver-colored osmanthus, broad-leaved epiphyllum, and constantly stir, put into ferric ion compounds solution, boiling 2-3 hour, cooks paleturquoise pigment solution; The pigment solution that F, dyeing, extraction boiling go out, puts in pottery, puts into the maize straw after immersion, and boiling 1-2 hour, period constantly stirs, and makes maize straw fully absorb paleturquoise pigment, level dyeing; G, fixation, the maize straw after dyeing to be pulled out, leave standstill 30 minutes, put into clear water 5-10 minute, take out after drifting out loose colour, be put into shady and cool ventilation place dry, obtain a kind of maize straw dyestuff of paleturquoise.