CN106700622A - Dodger blue corn straw dye and production method thereof - Google Patents
Dodger blue corn straw dye and production method thereof Download PDFInfo
- Publication number
- CN106700622A CN106700622A CN201510485542.7A CN201510485542A CN106700622A CN 106700622 A CN106700622 A CN 106700622A CN 201510485542 A CN201510485542 A CN 201510485542A CN 106700622 A CN106700622 A CN 106700622A
- Authority
- CN
- China
- Prior art keywords
- parts
- maize straw
- dodge
- hyacinth
- corn straw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a dodger blue corn straw dye and a production method thereof. The dodger blue corn straw dye is prepared from the following main raw materials: corn straw, hyacinth, baphicacanthus cusia bremek, sorbaria sorbifolia, blueberries, alumen, an antimony ion compound solution and mineral water. The production method of the dodger blue corn straw dye comprises the main technological processes of selecting the materials, cutting the materials, fumigating, soaking, boiling in hot water, dyeing and carrying out fixation. The dodger blue corn straw dye is purely prepared from plants, and has the faint scent emitting by the plants; no chemical substance is added in the preparation process, so that the dodger blue corn straw dye has no harm to the human body; furthermore, the dodger blue corn straw dye is wide in material source, short in processing process and easy in processing and manufacturing.
Description
Technical field:
The present invention relates to a kind of vegetable colour, more particularly to a kind of Dodge blueness maize straw dyestuff and its production method.
Background technology:
Industrial art refer to daily living article after art up treatment, be allowed to the product with strong aesthetic value.Industrial art is typically divided into the industrial art that the practical art fine arts and furnishings are appreciated by we.The practical art fine arts are main body and the basis of whole industrial art, including clothing, food, change, row, arts and crafts, practical value is the chief value of this kind of handicraft, and aesthetic value is present as auxiliary value.This kind of handicraft is including the tea tableware by decorative processing, light fixture, wood furniture, embroidered article, careless plaited bamboo articles etc..It refers to those to furnish, view and admire the handicraft based on function that furnishings appreciate handicraft, this kind of handicraft with it is aesthetic be its primary value, manual skill is very strong, such as jadeware, jewel, ivory carving, cloisonne enamel, lacquerware, wall hanging, pottery art.
Chinese industrial art it is with a long history, be China culture treasure-house in a bright jewel, it is plain well-known in the world.Industrial art originates from the epoch that the mankind start manufacture instrument.Industrial art is mostly that working people directly creates, and the material life and cultural life with people are closely related.Its generation, often because of period of history, geographical environment, economic condition, cultural technical merit, show different style characteristics national prevailing custom is different with aesthetic standard.
Mostly it is that the method dyeed with chemical industry makes dyeing picture processed in modern technologies, therefore, it is the important content of current environment Green Development using recyclability resource, it is a long term growth direction of environmental protection, with far-reaching and realistic meaning.Stalk fibre is used as renewable resource huge on the earth; the level of sustainable use, environmental protection from resource is starting point; the recycling of stalk fibre has turned into the popular domain of research and development; the painter's paraphernalia made of stalk has natural gloss, texture and texture; the personage of making is life-like; birds and flowers, beast are remarkably true to life, very popular with third dimension.
At present, the primary raw material maize straw for making stalk picture is dyed into the blue method in Dodge has many kinds, but the Dodge blueness for dyeing impure just more, easily fade, not only not environmentally, some dyes even can produce toxic gas, the health of harmful to human during system is contaminated.
The content of the invention:
It is an object of the invention to provide a kind of pure natural, pollution-free, environmental protection, the Dodge blueness maize straw dyestuff being configured to pure plant being had no toxic side effect to the person and its production method.
The object of the present invention is achieved like this.It is that the raw material matched somebody with somebody by following weight is made,
Maize straw 25-50 parts, hyacinth 15-30 parts, acanthaceous indigo 10-22 parts, false spiraea
7-18 parts, blueberry 5-15 parts, alum 5-15 parts, 5-15 parts, mineral water 30-80 parts of antimony ion compound solution
。
Preparing blueness maize straw dyestuff preferred weight ratio range in Dodge of the present invention is, wherein the weight proportion of various raw materials is,
Maize straw 25-40 parts, hyacinth 15-25 parts, acanthaceous indigo 10-16 parts, false spiraea
7-13 parts, blueberry 5-10 parts, alum 5-10 parts, 5-10 parts, mineral water 30-70 parts of antimony ion compound solution
。
Preparing the best weight ratio scope of blueness maize straw dyestuff in Dodge of the present invention is, wherein the weight proportion of various raw materials is, it is beautiful
33 parts of stalk of rice, 20 parts of hyacinth, 13 parts of acanthaceous indigo, 10 parts of false spiraea, 8 parts of blueberry, 7 parts of alum, 7 parts of antimony ion compound solution, 60 parts of mineral water
。
Above-mentioned each component is made the production method of blueness maize straw dyestuff in Dodge of the present invention, technical process is:Sorting, blank, stifling, immersion, heat boil, dye,
Fixation
, concrete operation method follow these steps to successively:A
、
Sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried removes other branch, removes Section 1 and last 1 section, leaves and takes center section, selects and meets national health and quality standard
Hyacinth, acanthaceous indigo, false spiraea, blueberry
, alum, antimony ion compound solution, mineral water it is standby;B
, blank, maize straw knife is longitudinally cut open, it is interior inside removal
Flesh part, the stalk part outside reservation is standby;
The raw material that will be selected
Hyacinth, acanthaceous indigo, false spiraea, blueberry
, be cut into bulk respectively
It is standby
;C, it is stifling, maize straw is fumigated with sulfuric acid, the time is 10-20 minutes;D, immersion, by selected raw material be placed in the storage tank equipped with mineral water soak, temperature be 20 DEG C -25 DEG C, time 2-4 hours;E, heat are boiled, incited somebody to action
Salt and water are placed in iron pan and heat, and water temperature heating is arrived
40
°, alum is put into, it is persistently overheating to be to water temperature
70
°, it is put into
Leaching
After bubble
Hyacinth, acanthaceous indigo, false spiraea, blueberry, and be stirred continuously, it is put into
Antimony ion compound solution,
Boiling 2-3 hours, cook
Dodge is blue
Pigment solution;The pigment solution that F, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and fully absorbs maize straw
Dodge is blue
Pigment, level dyeing;
G
, fixation, the maize straw after dyeing is pulled out, stand
30
Minute, it is put into clear water
5-10
Minute, taken out after drifting out loose colour, it is put at shady and cool ventilation and dries, obtain a kind of blue maize straw dyestuff in Dodge
。
The advantage of the invention is that:1st, raw material is selected, scientific formulation, color is pure;2nd, product is made by pure plant, with the delicate fragrance that plant distributes in itself, without any chemical substance in manufacturing process, to human body without any injury;3rd, raw material sources are extensive, plus process line is short, the manufacture of product easy processing.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated:
Embodiment 1:
Preparing blueness maize straw dyestuff weight proportion scope in Dodge of the present invention is:
Maize straw 25-50 parts, hyacinth 15-30 parts, acanthaceous indigo 10-22 parts, false spiraea
7-18 parts, blueberry 5-15 parts, alum 5-15 parts, 5-15 parts, mineral water 30-80 parts of antimony ion compound solution
。
Embodiment 2:
Preparing blueness maize straw dyestuff preferred weight ratio range in Dodge of the present invention is:
Maize straw 25-40 parts, hyacinth 15-25 parts, acanthaceous indigo 10-16 parts, false spiraea
7-13 parts, blueberry 5-10 parts, alum 5-10 parts, 5-10 parts, mineral water 30-70 parts of antimony ion compound solution
。
Embodiment 3:
Preparing blueness maize straw dyestuff best weight ratio scope in Dodge of the present invention is:It is beautiful
33 parts of stalk of rice, 20 parts of hyacinth, 13 parts of acanthaceous indigo, 10 parts of false spiraea, 8 parts of blueberry, 7 parts of alum, 7 parts of antimony ion compound solution, 60 parts of mineral water
。
Above-mentioned each component is made the production method of blueness maize straw dyestuff in Dodge of the present invention, technical process is:Sorting, blank, stifling, immersion, heat boil, dye,
Fixation
, concrete operation method follow these steps to successively:A
、
Sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried removes other branch, removes Section 1 and last 1 section, leaves and takes center section, selects and meets national health and quality standard
Hyacinth, acanthaceous indigo, false spiraea, blueberry
, alum, antimony ion compound solution, mineral water it is standby;B
, blank, maize straw knife is longitudinally cut open, it is interior inside removal
Flesh part, the stalk part outside reservation is standby;
The raw material that will be selected
Hyacinth, acanthaceous indigo, false spiraea, blueberry
, be cut into bulk respectively
It is standby
;C, it is stifling, maize straw is fumigated with sulfuric acid, the time is 10-20 minutes;D, immersion, by selected raw material be placed in the storage tank equipped with mineral water soak, temperature be 20 DEG C -25 DEG C, time 2-4 hours;E, heat are boiled, incited somebody to action
Salt and water are placed in iron pan and heat, and water temperature heating is arrived
40
°, alum is put into, it is persistently overheating to be to water temperature
70
°, it is put into
Leaching
After bubble
Hyacinth, acanthaceous indigo, false spiraea, blueberry, and be stirred continuously, it is put into
Antimony ion compound solution,
Boiling 2-3 hours, cook
Dodge is blue
Pigment solution;The pigment solution that F, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and fully absorbs maize straw
Dodge is blue
Pigment, level dyeing;
G
, fixation, the maize straw after dyeing is pulled out, stand
30
Minute, it is put into clear water
5-10
Minute, taken out after drifting out loose colour, it is put at shady and cool ventilation and dries, obtain a kind of blue maize straw dyestuff in Dodge
。
Claims (4)
1. a kind of Dodge blueness maize straw dyestuff, it is characterised in that:It is that the raw material matched by following weight is made, maize straw 25-50 parts, hyacinth 15-30 parts, acanthaceous indigo 10-22 parts, false spiraea 7-18 parts, blueberry 5-15 parts, alum 5-15 parts, 5-15 parts, mineral water 30-80 parts of antimony ion compound solution.
2. a kind of Dodge blueness maize straw dyestuff, it is characterised in that:The weight proportion of wherein various raw materials is, maize straw 25-40 parts, hyacinth 15-25 parts, acanthaceous indigo 10-16 parts, false spiraea 7-13 parts, blueberry 5-10 parts, alum 5-10 parts, 5-10 parts, mineral water 30-70 parts of antimony ion compound solution.
3. a kind of Dodge blueness maize straw dyestuff, it is characterised in that:The weight proportion of wherein various raw materials is, 33 parts of maize straw, 20 parts of hyacinth, 13 parts of acanthaceous indigo, 10 parts of false spiraea, 8 parts of blueberry, 7 parts of alum, 7 parts of antimony ion compound solution, 60 parts of mineral water.
4. a kind of production method for preparing Dodge blueness maize straw dyestuff according to claim 3, it is characterised in that:Technical process is:Sorting, blank, stifling, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively:A, sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried, removes other branch, removes Section 1 and last 1 section, center section is left and taken, selects that to meet the hyacinth of national health and quality standard, acanthaceous indigo, false spiraea, blueberry, alum, antimony ion compound solution, mineral water standby;B, blank, maize straw knife is longitudinally cut open, the interior flesh part inside removal, retain outside stalk part it is standby;The raw material hyacinth that to select, acanthaceous indigo, false spiraea, blueberry, be cut into respectively it is block standby;C, it is stifling, maize straw is fumigated with sulfuric acid, the time is 10-20 minutes;D, immersion, by selected raw material be placed in the storage tank equipped with mineral water soak, temperature be 20 DEG C -25 DEG C, time 2-4 hours;E, heat boil, salt and water are placed in iron pan and are heated, water temperature heating is to 40 °, it is put into alum, it is persistently overheating to water temperature be 70 °, hyacinth, acanthaceous indigo, false spiraea, blueberry after immersion are put into, and are stirred continuously, be put into antimony ion compound solution, boiling 2-3 hours, cook Dodge blueness pigment solution;The pigment solution that F, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and maize straw is fully absorbed Dodge blue pigment, level dyeing;G, fixation, the maize straw after dyeing is pulled out, stand 30 minutes, be put into 5-10 minute in clear water, taken out after drifting out loose colour, be put at shady and cool ventilation and dry, obtain a kind of maize straw dyestuff of Dodge blueness.