CN106700627A - Turquoise corn stalk dye and production method thereof - Google Patents
Turquoise corn stalk dye and production method thereof Download PDFInfo
- Publication number
- CN106700627A CN106700627A CN201510487505.XA CN201510487505A CN106700627A CN 106700627 A CN106700627 A CN 106700627A CN 201510487505 A CN201510487505 A CN 201510487505A CN 106700627 A CN106700627 A CN 106700627A
- Authority
- CN
- China
- Prior art keywords
- parts
- maize straw
- turquoise
- sericite
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a turquoise corn stalk dye and a production method thereof. The dye adopts corn stalks, Arthraxon hispidus, sericite powder, snapdragon flowers, Chinese olive, alum, an iron ion compound solution and mineral water as main raw materials. The main process flow of the production method comprises material selection, material cutting, fumigation, immersion, hot boiling, dyeing and dye fixation. The dye is made of pure plants, has the delicate fragrance emitted by the plants, and also has the advantages of no chemical substances in the making process, no harms to human bodies, wide sources of raw materials, short processing process route, and easiness in processing and manufacturing.
Description
Technical field：
The present invention relates to a kind of vegetable colour, more particularly to a kind of turquoise maize straw dyestuff and its production method.
Background technology：
Industrial art refer to daily living article after art up treatment, be allowed to the product with strong aesthetic value.Industrial art is typically divided into the industrial art that the practical art fine arts and furnishings are appreciated by we.The practical art fine arts are main body and the basis of whole industrial art, including clothing, food, change, row, arts and crafts, practical value is the chief value of this kind of handicraft, and aesthetic value is present as auxiliary value.This kind of handicraft is including the tea tableware by decorative processing, light fixture, wood furniture, embroidered article, careless plaited bamboo articles etc..It refers to those to furnish, view and admire the handicraft based on function that furnishings appreciate handicraft, this kind of handicraft with it is aesthetic be its primary value, manual skill is very strong, such as jadeware, jewel, ivory carving, cloisonne enamel, lacquerware, wall hanging, pottery art.
Chinese industrial art it is with a long history, be China culture treasure-house in a bright jewel, it is plain well-known in the world.Industrial art originates from the epoch that the mankind start manufacture instrument.Industrial art is mostly that working people directly creates, and the material life and cultural life with people are closely related.Its generation, often because of period of history, geographical environment, economic condition, cultural technical merit, show different style characteristics national prevailing custom is different with aesthetic standard.
Mostly it is that the method dyeed with chemical industry makes dyeing picture processed in modern technologies, therefore, it is the important content of current environment Green Development using recyclability resource, it is a long term growth direction of environmental protection, with far-reaching and realistic meaning.Stalk fibre is used as renewable resource huge on the earth; the level of sustainable use, environmental protection from resource is starting point; the recycling of stalk fibre has turned into the popular domain of research and development; the painter's paraphernalia made of stalk has natural gloss, texture and texture; the personage of making is life-like; birds and flowers, beast are remarkably true to life, very popular with third dimension.
At present, the method that the primary raw material maize straw for making stalk picture dyes turquoise there are into many kinds, but the turquoise for dyeing impure more, easily fade, not only not environmentally, some dyes even can produce toxic gas, the health of harmful to human during system is contaminated.
The content of the invention：
It is an object of the invention to provide a kind of pure natural, pollution-free, environmental protection, the turquoise maize straw dyestuff being configured to pure plant being had no toxic side effect to the person and its production method.
The object of the present invention is achieved like this.It is that the raw material matched somebody with somebody by following weight is made,
Maize straw 25-50 parts, hispid arthraxon 15-30 parts, sericite in powder 10-22 parts, 7-18 parts of the goldfish showy flowers of herbaceous plants, Chinese olive 5-15 parts, alum 5-15 parts, 5-15 parts, mineral water 70-100 parts of ferric ion compounds solution
。
Preparing turquoise maize straw dyestuff preferred weight ratio range of the present invention is, wherein the weight proportion of various raw materials is,
Maize straw 25-40 parts, hispid arthraxon 15-25 parts, sericite in powder 10-16 parts, 7-13 parts of the goldfish showy flowers of herbaceous plants, Chinese olive 5-10 parts, alum 5-10 parts, 5-10 parts, mineral water 70-90 parts of ferric ion compounds solution
。
Preparing the best weight ratio scope of turquoise maize straw dyestuff of the present invention is, wherein the weight proportion of various raw materials is, it is beautiful
33 parts of stalk of rice, 20 parts of hispid arthraxon, 13 parts of sericite in powder, 10 parts of the goldfish showy flowers of herbaceous plants, 8 parts of Chinese olive, 7 parts of alum, 7 parts of ferric ion compounds solution, 80 parts of mineral water
。
Above-mentioned each component is made the production method of turquoise maize straw dyestuff of the present invention, technical process is：Sorting, blank, stifling, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively：A
、
Sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried removes other branch, removes Section 1 and last 1 section, leaves and takes center section, selects and meets national health and quality standard
Hispid arthraxon, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive
, alum, ferric ion compounds solution, mineral water it is standby；B
, blank, maize straw knife is longitudinally cut open, it is interior inside removal
Flesh part, the stalk part outside reservation is standby；The raw material that will be selected
Hispid arthraxon, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive
, respectively be cut into it is block standby；C, it is stifling, maize straw is fumigated with sulfuric acid, the time is 10-20 minutes；D, immersion, by selected raw material be placed in the storage tank equipped with mineral water soak, temperature be 20 DEG C -25 DEG C, time 2-4 hours；E, heat boil, salt and water are placed in iron pan and are heated, and water temperature heating is put into alum to 40 °, and persistently overheating is 70 ° to water temperature, is put into after soaking
Hispid arthraxon, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive, and be stirred continuously, it is put into
Ferric ion compounds solution,
Boiling 2-3 hours, cook
Turquoise pigment solution；The pigment solution that F, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and maize straw is fully absorbed turquoise pigment, level dyeing；G, fixation, the maize straw after dyeing is pulled out, stand 30 minutes, be put into 5-10 minute in clear water, taken out after drifting out loose colour, be put into drying at shady and cool ventilation, obtain a kind of maize straw dyestuff of turquoise.
The advantage of the invention is that：1st, raw material is selected, scientific formulation, color is pure；2nd, product is made by pure plant, with the delicate fragrance that plant distributes in itself, without any chemical substance in manufacturing process, to human body without any injury；3rd, raw material sources are extensive, plus process line is short, the manufacture of product easy processing.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated：
Embodiment 1：
Preparing turquoise maize straw dyestuff weight proportion scope of the present invention is：
Maize straw 25-50 parts, hispid arthraxon 15-30 parts, sericite in powder 10-22 parts, 7-18 parts of the goldfish showy flowers of herbaceous plants, Chinese olive 5-15 parts, alum 5-15 parts, 5-15 parts, mineral water 70-100 parts of ferric ion compounds solution
。
Embodiment 2：
Preparing turquoise maize straw dyestuff preferred weight ratio range of the present invention is：
Maize straw 25-40 parts, hispid arthraxon 15-25 parts, sericite in powder 10-16 parts, 7-13 parts of the goldfish showy flowers of herbaceous plants, Chinese olive 5-10 parts, alum 5-10 parts, 5-10 parts, mineral water 70-90 parts of ferric ion compounds solution
。
Embodiment 3：
Preparing turquoise maize straw dyestuff best weight ratio scope of the present invention is：It is beautiful
33 parts of stalk of rice, 20 parts of hispid arthraxon, 13 parts of sericite in powder, 10 parts of the goldfish showy flowers of herbaceous plants, 8 parts of Chinese olive, 7 parts of alum, 7 parts of ferric ion compounds solution, 80 parts of mineral water
。
Above-mentioned each component is made the production method of turquoise maize straw dyestuff of the present invention, technical process is：Sorting, blank, stifling, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively：A
、
Sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried removes other branch, removes Section 1 and last 1 section, leaves and takes center section, selects and meets national health and quality standard
Hispid arthraxon, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive
, alum, ferric ion compounds solution, mineral water it is standby；B
, blank, maize straw knife is longitudinally cut open, it is interior inside removal
Flesh part, the stalk part outside reservation is standby；The raw material that will be selected
Hispid arthraxon, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive
, respectively be cut into it is block standby；C, it is stifling, maize straw is fumigated with sulfuric acid, the time is 10-20 minutes；D, immersion, by selected raw material be placed in the storage tank equipped with mineral water soak, temperature be 20 DEG C -25 DEG C, time 2-4 hours；E, heat boil, salt and water are placed in iron pan and are heated, and water temperature heating is put into alum to 40 °, and persistently overheating is 70 ° to water temperature, is put into after soaking
Hispid arthraxon, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive, and be stirred continuously, it is put into
Ferric ion compounds solution,
Boiling 2-3 hours, cook
Turquoise pigment solution；The pigment solution that F, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and maize straw is fully absorbed turquoise pigment, level dyeing；G, fixation, the maize straw after dyeing is pulled out, stand 30 minutes, be put into 5-10 minute in clear water, taken out after drifting out loose colour, be put into drying at shady and cool ventilation, obtain a kind of maize straw dyestuff of turquoise.
Claims (4)
1. a kind of turquoise maize straw dyestuff, it is characterised in that：It is by following weight match raw material be made, maize straw 25-50 parts, hispid arthraxon 15-30 parts, sericite in powder 10-22 parts, 7-18 parts of the goldfish showy flowers of herbaceous plants, Chinese olive 5-15 parts, alum 5-15 parts, 5-15 parts, mineral water 70-100 parts of ferric ion compounds solution.
2. a kind of turquoise maize straw dyestuff, it is characterised in that：The weight proportion of wherein various raw materials is, maize straw 25-40 parts, hispid arthraxon 15-25 parts, sericite in powder 10-16 parts, 7-13 parts of the goldfish showy flowers of herbaceous plants, Chinese olive 5-10 parts, alum 5-10 parts, 5-10 parts, mineral water 70-90 parts of ferric ion compounds solution.
3. a kind of turquoise maize straw dyestuff, it is characterised in that：The weight proportion of wherein various raw materials is, 33 parts of maize straw, 20 parts of hispid arthraxon, 13 parts of sericite in powder, 10 parts of the goldfish showy flowers of herbaceous plants, 8 parts of Chinese olive, 7 parts of alum, 7 parts of ferric ion compounds solution, 80 parts of mineral water.
4. a kind of production method for preparing turquoise maize straw dyestuff according to claim 3, it is characterised in that：Technical process is：Sorting, blank, stifling, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively：A, sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried, removes other branch, removes Section 1 and last 1 section, center section is left and taken, selects that to meet the hispid arthraxon of national health and quality standard, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive, alum, ferric ion compounds solution, mineral water standby；B, blank, maize straw knife is longitudinally cut open, the interior flesh part inside removal, retain outside stalk part it is standby；The raw material hispid arthraxon that to select, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive, be cut into respectively it is block standby；C, it is stifling, maize straw is fumigated with sulfuric acid, the time is 10-20 minutes；D, immersion, by selected raw material be placed in the storage tank equipped with mineral water soak, temperature be 20 DEG C -25 DEG C, time 2-4 hours；E, heat boil, salt and water are placed in iron pan and are heated, water temperature heating is to 40 °, it is put into alum, it is persistently overheating to water temperature be 70 °, hispid arthraxon, sericite in powder, the goldfish showy flowers of herbaceous plants, Chinese olive after immersion are put into, and are stirred continuously, be put into ferric ion compounds solution, boiling 2-3 hours, cook turquoise pigment solution；The pigment solution that F, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and maize straw is fully absorbed turquoise pigment, level dyeing；G, fixation, the maize straw after dyeing is pulled out, stand 30 minutes, be put into 5-10 minute in clear water, taken out after drifting out loose colour, be put into drying at shady and cool ventilation, obtain a kind of maize straw dyestuff of turquoise.