CN105000860A - Flame-retardant building material - Google Patents
Flame-retardant building material Download PDFInfo
- Publication number
- CN105000860A CN105000860A CN201510403078.2A CN201510403078A CN105000860A CN 105000860 A CN105000860 A CN 105000860A CN 201510403078 A CN201510403078 A CN 201510403078A CN 105000860 A CN105000860 A CN 105000860A
- Authority
- CN
- China
- Prior art keywords
- parts
- building material
- cement
- retardant building
- alunite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of blending and preparation of building materials, and particularly relates to the building materials, in particular to a flame-retardant building material. The flame-retardant building material is characterized by comprising the following components: cement, aluminum hydroxide, magnesium chloride, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite and polyurethane.
Description
Technical field
The invention belongs to allotment and the preparation field of material of construction, be specifically related to material of construction, particularly relate to a kind of flame retardant building material.
Background technology
Material of construction building materials, the material used between floors is referred to as material of construction.The wide range that novel material of construction comprises, has lagging material, lagging material, high-strength material, the material etc. that can breathe all belongs to type material.Material of construction is the general designation of the material used in civil engineering work and construction work.
Structured material comprises timber, bamboo wood, stone material, cement, concrete, metal, brick and tile, pottery, glass, engineering plastics, matrix material etc.; Finishing material comprises various coating, paint, coating, veneer, assorted ceramic tile, has the glass etc. of special-effect; Proprietary material refers to for waterproof, protection against the tide, anticorrosion, fire prevention, fire-retardant, sound insulation, heat insulation, insulation, sealing etc.
In the prior art, although inside structured material there be measuring body material, resistance to compression effect is not lasting, and the time has been grown material and easily qualitative change occurred.
Summary of the invention
in order to solve defect of the prior art, the invention provides a kind of flame retardant building material.
A kind of flame retardant building material, is characterized in that component comprises: cement, aluminium hydroxide, magnesium chloride, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, urethane.
Described a kind of flame retardant building material, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 100-150 part
Aluminium hydroxide 60-95 part
Magnesium chloride 5-10 part
Quartz sand 55-150 part
Silicon carbide 55-70 part
Magnesium oxide 15-20 part
Calcium oxide 25-35 part
Alunite 30-55 part
Anhydrite 10-15 part
Urethane 25-35 part.
Described a kind of flame retardant building material, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 150 parts
95 parts, aluminium hydroxide
10 parts, magnesium chloride
Quartz sand 150 parts
70 parts, silicon carbide
20 parts, magnesium oxide
35 parts, calcium oxide
Alunite 55 parts
Anhydrite 15 parts
Urethane 35 parts.
Described a kind of flame retardant building material, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 100 parts
60 parts, aluminium hydroxide
5 parts, magnesium chloride
Quartz sand 55 parts
55 parts, silicon carbide
15 parts, magnesium oxide
25 parts, calcium oxide
Alunite 30 parts
Anhydrite 10 parts
Urethane 25 parts.
the invention has the beneficial effects as follows: crushing resistance is strong, and can find qualitative change, good flame resistance, this invention simultaneously also has the good feature of sound insulation.
embodiment:
embodiment 1
A kind of flame retardant building material, is characterized in that component comprises: cement, aluminium hydroxide, magnesium chloride, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, urethane.
Described a kind of flame retardant building material, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 100-150 part
Aluminium hydroxide 60-95 part
Magnesium chloride 5-10 part
Quartz sand 55-150 part
Silicon carbide 55-70 part
Magnesium oxide 15-20 part
Calcium oxide 25-35 part
Alunite 30-55 part
Anhydrite 10-15 part
Urethane 25-35 part.
embodiment 2
Described a kind of flame retardant building material, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 150 parts
95 parts, aluminium hydroxide
10 parts, magnesium chloride
Quartz sand 150 parts
70 parts, silicon carbide
20 parts, magnesium oxide
35 parts, calcium oxide
Alunite 55 parts
Anhydrite 15 parts
Urethane 35 parts.
embodiment 3
Described a kind of flame retardant building material, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 100 parts
60 parts, aluminium hydroxide
5 parts, magnesium chloride
Quartz sand 55 parts
55 parts, silicon carbide
15 parts, magnesium oxide
25 parts, calcium oxide
Alunite 30 parts
Anhydrite 10 parts
Urethane 25 parts.
the invention has the beneficial effects as follows: crushing resistance is strong, and can find qualitative change, good flame resistance, this invention simultaneously also has the good feature of sound insulation.
Claims (4)
1. a flame retardant building material, is characterized in that component comprises: cement, aluminium hydroxide, magnesium chloride, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, urethane.
2. a kind of flame retardant building material according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 100-150 part
Aluminium hydroxide 60-95 part
Magnesium chloride 5-10 part
Quartz sand 55-150 part
Silicon carbide 55-70 part
Magnesium oxide 15-20 part
Calcium oxide 25-35 part
Alunite 30-55 part
Anhydrite 10-15 part
Urethane 25-35 part.
3. a kind of flame retardant building material according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 150 parts
95 parts, aluminium hydroxide
10 parts, magnesium chloride
Quartz sand 150 parts
70 parts, silicon carbide
20 parts, magnesium oxide
35 parts, calcium oxide
Alunite 55 parts
Anhydrite 15 parts
Urethane 35 parts.
4. a kind of flame retardant building material according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Cement 100 parts
60 parts, aluminium hydroxide
5 parts, magnesium chloride
Quartz sand 55 parts
55 parts, silicon carbide
15 parts, magnesium oxide
25 parts, calcium oxide
Alunite 30 parts
Anhydrite 10 parts
Urethane 25 parts.