CN104058635A - Novel building material - Google Patents
Novel building material Download PDFInfo
- Publication number
- CN104058635A CN104058635A CN201410291713.8A CN201410291713A CN104058635A CN 104058635 A CN104058635 A CN 104058635A CN 201410291713 A CN201410291713 A CN 201410291713A CN 104058635 A CN104058635 A CN 104058635A
- Authority
- CN
- China
- Prior art keywords
- parts
- building materials
- anhydrite
- phenol
- acetone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to the field of blending and preparation of building materials, particularly relates to a building material, and more particularly relates to a novel building material. The novel building material is characterized by comprising following components: magnesium chloride, phenol, acetone, a catalyst-sulfuric acid, sodium nitrite, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, polyurethane and polyethylene.
Description
Technical field
The allotment and the preparation field that the invention belongs to material of construction, be specifically related to material of construction, relates in particular to a kind of New Building Materials.
Background technology
Material of construction building materials, the material using in buildings is referred to as material of construction.The wide range that novel material of construction comprises, the material that have lagging material, lagging material, high-strength material, can breathe etc. all belongs to type material.Material of construction is the general designation of the material that uses in civil engineering work and construction work.
Structured material comprises timber, bamboo wood, stone material, cement, concrete, metal, brick and tile, pottery, glass, engineering plastics, matrix material etc.; Finishing material comprises various coating, paint, coating, veneer, ceramic tile of all kinds, has glass of special-effect etc.; Proprietary material refers to for waterproof, protection against the tide, anticorrosion, fire prevention, fire-retardant, sound insulation, heat insulation, insulation, sealing etc.
In the prior art, although the measuring body material in structured material the inside has, resistance to compression effect is not lasting, and the time has been grown material qualitative change easily occurs.
Summary of the invention
In order to solve defect of the prior art, the invention provides a kind of New Building Materials.
A kind of New Building Materials, is characterized in that component comprises: magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, urethane, polyethylene.
Described a kind of New Building Materials, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Magnesium chloride 5-10 part
Phenol 15-25 part
Acetone 10-30 part
Catalyst sulfuric acid 10-20 part
Sodium Nitrite 10-15 part
Quartz sand 5-10 part
Silicon carbide 3-5 part
Magnesium oxide 8-20 part
Calcium oxide 5-15 part
Alunite 30-55 part
Anhydrite 3-15 part
Urethane 20-25 part
Polyethylene 20-35 part.
Described a kind of New Building Materials, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
5 parts, magnesium chloride
15 parts of phenol
10 parts, acetone
10 parts of catalyst sulfuric acids
10 parts of Sodium Nitrites
5 parts of quartz sands
3 parts, silicon carbide
8 parts, magnesium oxide
5 parts, calcium oxide
30 parts of alunites
3 parts of anhydrite
20 parts of urethane
20 parts of polyethylene.
Described a kind of New Building Materials, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
10 parts, magnesium chloride
25 parts of phenol
30 parts, acetone
20 parts of catalyst sulfuric acids
15 parts of Sodium Nitrites
10 parts of quartz sands
5 parts, silicon carbide
20 parts, magnesium oxide
15 parts, calcium oxide
55 parts of alunites
15 parts of anhydrite
25 parts of urethane
35 parts of polyethylene.
The invention has the beneficial effects as follows: crushing resistance is strong, resistance to compression is effective, and the resistance to compression time length is long, and can not find qualitative change.
embodiment:
embodiment 1
A kind of New Building Materials, is characterized in that component comprises: magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, urethane, polyethylene.
Described a kind of New Building Materials, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Magnesium chloride 5-10 part
Phenol 15-25 part
Acetone 10-30 part
Catalyst sulfuric acid 10-20 part
Sodium Nitrite 10-15 part
Quartz sand 5-10 part
Silicon carbide 3-5 part
Magnesium oxide 8-20 part
Calcium oxide 5-15 part
Alunite 30-55 part
Anhydrite 3-15 part
Urethane 20-25 part
Polyethylene 20-35 part.
embodiment 2
A kind of New Building Materials, is characterized in that component comprises: magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, urethane, polyethylene.
Described a kind of New Building Materials, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
5 parts, magnesium chloride
15 parts of phenol
10 parts, acetone
10 parts of catalyst sulfuric acids
10 parts of Sodium Nitrites
5 parts of quartz sands
3 parts, silicon carbide
8 parts, magnesium oxide
5 parts, calcium oxide
30 parts of alunites
3 parts of anhydrite
20 parts of urethane
20 parts of polyethylene.
embodiment 3
A kind of New Building Materials, is characterized in that component comprises: magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, urethane, polyethylene.
Described a kind of New Building Materials, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
10 parts, magnesium chloride
25 parts of phenol
30 parts, acetone
20 parts of catalyst sulfuric acids
15 parts of Sodium Nitrites
10 parts of quartz sands
5 parts, silicon carbide
20 parts, magnesium oxide
15 parts, calcium oxide
55 parts of alunites
15 parts of anhydrite
25 parts of urethane
35 parts of polyethylene.
The invention has the beneficial effects as follows: crushing resistance is strong, resistance to compression is effective, and the resistance to compression time length is long, and can not find qualitative change.
Claims (4)
1. New Building Materials, is characterized in that component comprises: magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, magnesium oxide, calcium oxide, alunite, anhydrite, urethane, polyethylene.
2. a kind of New Building Materials according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Magnesium chloride 5-10 part
Phenol 15-25 part
Acetone 10-30 part
Catalyst sulfuric acid 10-20 part
Sodium Nitrite 10-15 part
Quartz sand 5-10 part
Silicon carbide 3-5 part
Magnesium oxide 8-20 part
Calcium oxide 5-15 part
Alunite 30-55 part
Anhydrite 3-15 part
Urethane 20-25 part
Polyethylene 20-35 part.
3. a kind of New Building Materials according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
5 parts, magnesium chloride
15 parts of phenol
10 parts, acetone
10 parts of catalyst sulfuric acids
10 parts of Sodium Nitrites
5 parts of quartz sands
3 parts, silicon carbide
8 parts, magnesium oxide
5 parts, calcium oxide
30 parts of alunites
3 parts of anhydrite
20 parts of urethane
20 parts of polyethylene.
4. a kind of New Building Materials according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
10 parts, magnesium chloride
25 parts of phenol
30 parts, acetone
20 parts of catalyst sulfuric acids
15 parts of Sodium Nitrites
10 parts of quartz sands
5 parts, silicon carbide
20 parts, magnesium oxide
15 parts, calcium oxide
55 parts of alunites
15 parts of anhydrite
25 parts of urethane
35 parts of polyethylene.