CN104072089A - Building material - Google Patents
Building material Download PDFInfo
- Publication number
- CN104072089A CN104072089A CN201410291493.9A CN201410291493A CN104072089A CN 104072089 A CN104072089 A CN 104072089A CN 201410291493 A CN201410291493 A CN 201410291493A CN 104072089 A CN104072089 A CN 104072089A
- Authority
- CN
- China
- Prior art keywords
- parts
- construction
- phenol
- acetone
- silicon carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the fields of blending and preparation of a building material, and particularly relates to a building material which is characterized by comprising magnesium oxide, magnesium chloride, phenol, acetone, catalyst sulfuric acid, sodium nitrate, quartz sand, silicon carbide and calcium oxide.
Description
Technical field
The allotment and the preparation field that the invention belongs to material of construction, be specifically related to material of construction, relates in particular to a kind of material of construction.
Background technology
Material of construction building materials, the material using in buildings is referred to as material of construction.The wide range that novel material of construction comprises, the material that have lagging material, lagging material, high-strength material, can breathe etc. all belongs to type material.Material of construction is the general designation of the material that uses in civil engineering work and construction work.
Structured material comprises timber, bamboo wood, stone material, cement, concrete, metal, brick and tile, pottery, glass, engineering plastics, matrix material etc.; Finishing material comprises various coating, paint, coating, veneer, ceramic tile of all kinds, has glass of special-effect etc.; Proprietary material refers to for waterproof, protection against the tide, anticorrosion, fire prevention, fire-retardant, sound insulation, heat insulation, insulation, sealing etc.
In the prior art, although the measuring body material in structured material the inside has, resistance to compression effect is not lasting, and the time has been grown material qualitative change easily occurs.
Summary of the invention
In order to solve defect of the prior art, the invention provides a kind of material of construction.
A kind of material of construction, is characterized in that component comprises: magnesium oxide, magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, calcium oxide.
Described a kind of material of construction, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Magnesium oxide 10-15 part
Magnesium chloride 5-10 part
Phenol 15-25 part
Acetone 10-30 part
Catalyst sulfuric acid 10-20 part
Sodium Nitrite 10-15 part
Quartz sand 5-10 part
Silicon carbide 3-5 part
Calcium oxide 5-15 part.
Described a kind of material of construction, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
10 parts, magnesium oxide
5 parts, magnesium chloride
15 parts of phenol
10 parts, acetone
10 parts of catalyst sulfuric acids
10 parts of Sodium Nitrites
5 parts of quartz sands
3 parts, silicon carbide
5 parts, calcium oxide.
Described a kind of material of construction, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
15 parts, magnesium oxide
10 parts, magnesium chloride
25 parts of phenol
30 parts, acetone
20 parts of catalyst sulfuric acids
15 parts of Sodium Nitrites
10 parts of quartz sands
5 parts, silicon carbide
15 parts, calcium oxide.
The invention has the beneficial effects as follows: crushing resistance is strong, resistance to compression is effective, and the resistance to compression time length is long, and can not find qualitative change, and the present invention also has waterproof, the effect of leakproof.
concrete embodiment
embodiment 1:
A kind of material of construction, is characterized in that component comprises: magnesium oxide, magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, calcium oxide.
Described a kind of material of construction, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Magnesium oxide 10-15 part
Magnesium chloride 5-10 part
Phenol 15-25 part
Acetone 10-30 part
Catalyst sulfuric acid 10-20 part
Sodium Nitrite 10-15 part
Quartz sand 5-10 part
Silicon carbide 3-5 part
Calcium oxide 5-15 part.
embodiment 2:
A kind of material of construction, is characterized in that component comprises: magnesium oxide, magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, calcium oxide.
Described a kind of material of construction, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
10 parts, magnesium oxide
5 parts, magnesium chloride
15 parts of phenol
10 parts, acetone
10 parts of catalyst sulfuric acids
10 parts of Sodium Nitrites
5 parts of quartz sands
3 parts, silicon carbide
5 parts, calcium oxide.
embodiment 3:
A kind of material of construction, is characterized in that component comprises: magnesium oxide, magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, calcium oxide.
Described a kind of material of construction, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
15 parts, magnesium oxide
10 parts, magnesium chloride
25 parts of phenol
30 parts, acetone
20 parts of catalyst sulfuric acids
15 parts of Sodium Nitrites
10 parts of quartz sands
5 parts, silicon carbide
15 parts, calcium oxide.
The invention has the beneficial effects as follows: crushing resistance is strong, resistance to compression is effective, and the resistance to compression time length is long, and can not find qualitative change, and the present invention also has waterproof, the effect of leakproof.
Claims (4)
1. a material of construction, is characterized in that component comprises: magnesium oxide, magnesium chloride, phenol, acetone, catalyst sulfuric acid, Sodium Nitrite, quartz sand, silicon carbide, calcium oxide.
2. a kind of material of construction according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
Magnesium oxide 10-15 part
Magnesium chloride 5-10 part
Phenol 15-25 part
Acetone 10-30 part
Catalyst sulfuric acid 10-20 part
Sodium Nitrite 10-15 part
Quartz sand 5-10 part
Silicon carbide 3-5 part
Calcium oxide 5-15 part.
3. a kind of material of construction according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
10 parts, magnesium oxide
5 parts, magnesium chloride
15 parts of phenol
10 parts, acetone
10 parts of catalyst sulfuric acids
10 parts of Sodium Nitrites
5 parts of quartz sands
3 parts, silicon carbide
5 parts, calcium oxide.
4. a kind of material of construction according to claim 1, is characterized in that: comprise following component, be calculated as follows according to mass fraction:
15 parts, magnesium oxide
10 parts, magnesium chloride
25 parts of phenol
30 parts, acetone
20 parts of catalyst sulfuric acids
15 parts of Sodium Nitrites
10 parts of quartz sands
5 parts, silicon carbide
15 parts, calcium oxide.