CN104991038B - 一种铝土矿正浮选矿石pH值的判别方法 - Google Patents
一种铝土矿正浮选矿石pH值的判别方法 Download PDFInfo
- Publication number
- CN104991038B CN104991038B CN201510317840.5A CN201510317840A CN104991038B CN 104991038 B CN104991038 B CN 104991038B CN 201510317840 A CN201510317840 A CN 201510317840A CN 104991038 B CN104991038 B CN 104991038B
- Authority
- CN
- China
- Prior art keywords
- value
- bauxite
- sample
- filtrate
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及铝土矿正浮选矿石pH值的判别方法,有效解决铝土矿酸碱度的判别问题,1)、低氧低碳水的制备;2)、样品制备;3)、试液制备;4)、pH值测定;5)、判别,本发明使用方便,操作简便,实用性强,效果好,本发明是根据制得液体的pH值来判别铝土矿正浮选矿石酸碱度级别,从而可快速、准确的将铝土矿分类。
Description
技术领域
本发明涉及一种铝土矿正浮选矿石pH值的判别方法。
背景技术
铝土矿正浮选工艺采用的是一精选一粗选一扫选独特的生产工艺,在正浮选过程中铝土矿是最重要的原料之一。目前,对铝土矿好坏,判断方法是铝土矿氧化铝含量、二氧化硅含量、氧化铁含量、氧化铝含量与二氧化硅含量比值这些化学指标。在实际生产过程中,铝土矿正浮选过程中,在铝土矿氧化铝含量、二氧化硅含量、氧化铁含量、氧化铝含量与二氧化硅含量比值这些化学指标基本相同的情况下,铝土矿正浮选现象及指标变化很大,经过分析测试发现,铝土矿酸碱度变化很大。而目前尚没有判别铝土矿酸碱度的方法,不利于对铝土矿正浮选矿石的指标控制,容易导致产品质量的不稳定。
发明内容
针对上述情况,为克服现有技术缺陷,本发明之目的就是提供一种铝土矿正浮选矿石pH值的判别方法,可有效解决铝土矿酸碱度的判别问题。
本发明解决的技术方案是,具体步骤如下:
1)、低氧低碳水的制备:
取蒸馏水加热至沸腾,保持8-12分钟,冷却至20-28℃,得低氧低碳水;
2)、样品制备:
A、取待测的铝土矿,经鄂式破碎机破碎至粒径小于10cm的粗颗粒,粗颗粒放入对辊破碎机内破碎,然后过孔径为1-50mm的筛网,得细颗粒;
B、将细颗粒用四分法取样,缩分1-10次,得样品;
3)、试液制备:
取低氧低碳水,加入样品,样品和低氧低碳水的重量体积比为1:1,搅拌,转速为40-60转/分,搅拌4-6分钟,停止搅拌,得混合液,混合液用定量滤纸过滤,得滤液;所述的重量体积是指固体物以g计,液体物以ml计,以下同,如样品为1g时,低氧低碳水为1ml;
4)、pH值测定:
取滤液,测定滤液的pH值;
5)、判别方法:
根据滤液的pH值的不同,将待测的铝土矿分类如下:
A、优质铝土矿:pH值6.8-7.5;
B、一般铝土矿:pH值7.6-8.0或者pH值6.3-6.7;
C、劣质铝土矿:pH值≥8.1或者pH值≤6.2。
本发明使用方便,操作简便,实用性强,效果好,本发明是根据制得液体的pH值来判别铝土矿正浮选矿石酸碱度级别,从而可快速、准确的将铝土矿分类。
具体实施方式
以下结合实施例对本发明的具体实施方式作详细说明。
实施例1:
1)、低氧低碳水的制备:
取500毫升蒸馏水于1000毫升圆底烧瓶中,电炉中加热至沸腾,保持8分钟,冷却至20℃;
2)、样品制备:
A、取待测的铝土矿3kg,经鄂式破碎机破碎至粒径小于10cm的粗颗粒,粗粒放入对辊破碎机内破碎,过孔径为20mm的筛网,得细颗粒;
B、将细颗粒用四分法取样,缩分6次,得样品;
3)、试液制备:
在烧杯中,加入40毫升低氧低碳水,再加入40g的样品,搅拌,转速为40转/分,搅拌4分钟,停止搅拌,得混合液,混合液用定量滤纸过滤,得滤液;
4)、pH值测定:
取滤液,测定滤液的pH值为6.5,即可确定待测的铝土矿为一般铝土矿。
实施例2
1)、低氧低碳水的制备:
取800毫升蒸馏水于1000毫升圆底烧瓶中,电炉中加热至沸腾,保持10分钟,冷却至25℃;
2)、样品制备:
A、取待测的铝土矿2kg,经鄂式破碎机破碎至粒径小于10cm的粗颗粒,粗粒放入对辊破碎机内破碎,过孔径为3mm的筛网,得细颗粒;
B、将细颗粒用四分法取样,缩分2次,得样品;
3)、试液制备:
在烧杯中,加入100毫升低氧低碳水,再加入100g的样品,搅拌,转速为50转/分,搅拌5分钟,停止搅拌,得混合液,混合液用定量滤纸过滤,得滤液;
4)、pH值测定:
取滤液,测定滤液的pH值为7.1,即可确定待测的铝土矿为优质铝土矿。
实施例3
1)、低氧低碳水的制备:
取900毫升蒸馏水于1000毫升圆底烧瓶中,电炉中加热至沸腾,保持12分钟,冷却至28℃;
2)、样品制备:
A、取待测的铝土矿7kg,经鄂式破碎机破碎至粒径小于10cm的粗颗粒,粗粒放入对辊破碎机内破碎,过孔径为3mm的筛网,得细颗粒;
B、将细颗粒用四分法取样,缩分8次,得样品;
3)、试液制备:
在烧杯中,加入25毫升低氧低碳水,再加入25g的样品,搅拌,转速为60转/分,搅拌6分钟,停止搅拌,得混合液,混合液用定量滤纸过滤,得滤液;
4)、pH值测定:
取滤液,测定滤液的pH值为6,即可确定待测的铝土矿为劣质铝土矿。
上述说明并非是对本发明的限制,本发明也并不仅限于上述具体实施方式,本技术领域的技术人员在本发明的实质范围内所做出的等效或等同变化、改型、添加或替换,也属于本发明的保护范围。
本发明操作简便,实用性强,全部数字化操作,重现性好,本发明的判别方法经在实际生产中应用,经过2年的实践试验,证明本发明完全能满足生产的要求,有效实现了对铝土矿正浮选矿石的指标控制,快速、准确的将铝土矿分类,且工作效率至少提高了40%,保证了产品的质量稳定,合格率提高了30%,有巨大的经济和社会效益。
Claims (4)
1.一种铝土矿正浮选矿石pH值的判别方法,其特征在于,具体步骤如下:
1)、低氧低碳水的制备:
取蒸馏水加热至沸腾,保持8-12分钟,冷却至20-28℃,得低氧低碳水;
2)、样品制备:
A、取待测的铝土矿,经鄂式破碎机破碎至粒径小于10cm的粗颗粒,粗颗粒放入对辊破碎机内破碎,然后过孔径为1-50mm的筛网,得细颗粒;
B、将细颗粒用四分法取样,缩分1-10次,得样品;
3)、试液制备:
取低氧低碳水,加入样品,样品和低氧低碳水的重量体积比为1:1,搅拌,转速为40-60转/分,搅拌4-6分钟,停止搅拌,得混合液,混合液用定量滤纸过滤,得滤液;
4)、pH值测定:
取滤液,测定滤液的pH值;
5)、判别方法:
根据滤液的pH值的不同,将待测的铝土矿分类如下:
A、优质铝土矿:pH值7.1;
B、一般铝土矿:pH值6.5;
C、劣质铝土矿:pH值6。
2.根据权利要求1所述的铝土矿正浮选矿石pH值的判别方法,其特征在于,1)、低氧低碳水的制备:
取500毫升蒸馏水于1000毫升圆底烧瓶中,电炉中加热至沸腾,保持8分钟,冷却至20℃;
2)、样品制备:
A、取待测的铝土矿3kg,经鄂式破碎机破碎至粒径小于10cm的粗颗粒,粗粒放入对辊破碎机内破碎,过孔径为20mm的筛网,得细颗粒;
B、将细颗粒用四分法取样,缩分6次,得样品;
3)、试液制备:
在烧杯中,加入40毫升低氧低碳水,再加入40g的样品,搅拌,转速为40转/分,搅拌4分钟,停止搅拌,得混合液,混合液用定量滤纸过滤,得滤液;
4)、pH值测定:
取滤液,测定滤液的pH值。
3.根据权利要求1所述的铝土矿正浮选矿石pH值的判别方法,其特征在于,
1)、低氧低碳水的制备:
取800毫升蒸馏水于1000毫升圆底烧瓶中,电炉中加热至沸腾,保持10分钟,冷却至25℃;
2)、样品制备:
A、取待测的铝土矿2kg,经鄂式破碎机破碎至粒径小于10cm的粗颗粒,粗粒放入对辊破碎机内破碎,过孔径为3mm的筛网,得细颗粒;
B、将细颗粒用四分法取样,缩分2次,得样品;
3)、试液制备:
在烧杯中,加入100毫升低氧低碳水,再加入100g的样品,搅拌,转速为50转/分,搅拌5分钟,停止搅拌,得混合液,混合液用定量滤纸过滤,得滤液;
4)、pH值测定:
取滤液,测定滤液的pH值。
4.根据权利要求1所述的铝土矿正浮选矿石pH值的判别方法,其特征在于,
1)、低氧低碳水的制备:
取900毫升蒸馏水于1000毫升圆底烧瓶中,电炉中加热至沸腾,保持12分钟,冷却至28℃;
2)、样品制备:
A、取待测的铝土矿7kg,经鄂式破碎机破碎至粒径小于10cm的粗颗粒,粗粒放入对辊破碎机内破碎,过孔径为3mm的筛网,得细颗粒;
B、将细颗粒用四分法取样,缩分8次,得样品;
3)、试液制备:
在烧杯中,加入25毫升低氧低碳水,再加入25g的样品,搅拌,转速为60转/分,搅拌6分钟,停止搅拌,得混合液,混合液用定量滤纸过滤,得滤液;
4)、pH值测定:
取滤液,测定滤液的pH值。