CN104985363A - 一种冷焊料的激活方法 - Google Patents
一种冷焊料的激活方法 Download PDFInfo
- Publication number
- CN104985363A CN104985363A CN201510384552.1A CN201510384552A CN104985363A CN 104985363 A CN104985363 A CN 104985363A CN 201510384552 A CN201510384552 A CN 201510384552A CN 104985363 A CN104985363 A CN 104985363A
- Authority
- CN
- China
- Prior art keywords
- solder
- welding material
- cold welding
- activiation method
- cold
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种焊料的贮存与激活方法，尤其涉及一种冷焊料的激活方法。步骤包括，对冷焊料进行预热流化；将流化后的冷焊料送入焊料池进行熔融；熔融后的冷焊料放入储存罐中，即可与焊接设备对接。本发明提供的冷焊料的激活方法，且冷焊料的激活方式简单易操作，安全高。本发明提供的冷焊料的激活方法，在冷焊料激活后保证气焊料的稳定性。
Description
技术领域
本发明涉及一种焊料的贮存与激活方法，尤其涉及一种冷焊料的激活方法。
背景技术
熔焊用焊料的熔化温度通常不低于母材的固相线，其化学成分、力学、热学特性都和母材比较接近，如各种焊条、药芯焊丝等。焊缝强度常不低于母材本身；而钎料的熔化温度必须低于母材的固相线，其化学成分常与母材相去较远，钎缝纤细，尺寸精密，但钎缝强度多数不及母材本身，抗蚀性也较差。焊料在使用时如电弧焊，温度常超过母材和焊料本身许多，无软硬之分；而钎料中的硬钎料，如铜锌料（铜锌合金），银钎料（银铜合金）的钎焊接头强度较大，主要用于连接强度要求较高的金属构件，而软钎料如焊锡（锡铅为主的合金）焊成接头强度较小，主要用于连接不过分要求强度的小接头，如电子仪器、仪表、家电电子线路的接头。
焊条包括银焊条由焊条芯和药皮构成，银焊条焊芯的作用之一是作为电极导电，同时它也是形成焊缝金属的主要材料，因此焊条芯的质量直接影响焊缝的性能。焊条是一种陶质产品，他不能象钢芯那样耐冲击，所以装货和卸货时不能摔他。用纸盒包装的焊条不能用挂钩搬运。某些型号焊条如特殊烘干要求的碱性焊条涂料比正常焊条更要小心轻放。酸性焊条对水分不敏感，而有机物金红石型焊条能容许有更高的含水量。所以要根据受潮的具体情况，在70-150°烘干一小时，存储时间短且包装良好，一般使用前可不烘干。碱性低氢型焊条在使用前必须烘干，以降低焊条的含氢量，防止气孔、裂纹等缺陷产生，一般烘干温度为350°C、一小时。不可将焊条在高温炉中突然放入或突然冷却，以免要皮干裂。
露天操作时，隔夜必须将银焊条妥善保管、不允许露天存放，应该在低温箱中恒温存放，否则次日使用前必须重新烘干。
专利《一种使用液体焊料流的焊接方法》中记载内容，存在在焊料激活后造成焊料本身不稳定。户外环境对焊接的效果有影响。
发明内容
本发明提供了一种保证焊料稳定性的冷焊料的激活方法。
本发明采用如下技术方案：
本发明所述的一种冷焊料的激活方法，步骤如下：
1）、对冷焊料进行预热流化；
2）、将流化后的冷焊料送入焊料池进行熔融；
3）、将步骤2）熔融后的冷焊料放入储存罐中，即可与焊接设备对接。
本发明所述的冷焊料的激活方法，步骤1）中焊料流化在封闭式流化池中进行。
本发明所述的冷焊料的激活方法，封闭式流化池中填充有惰性气体。
本发明所述的冷焊料的激活方法，所述的焊料流化温度为220°-300°。
本发明所述的冷焊料的激活方法，所述的熔融温度为350°-600°。
本发明所述的冷焊料的激活方法，所述的焊料流化反应时间为20-30分钟。
本发明所述的冷焊料的激活方法，所述的焊料熔融反应时间为20-40分钟。
有益效果
本发明提供的冷焊料的激活方法，且冷焊料的激活方式简单易操作，安全高。
本发明提供的冷焊料的激活方法，在冷焊料激活后保证气焊料的稳定性。
具体实施方式
为使本发明实施例的目的和技术方案更加清楚，对本发明实施例的技术方案进行清楚、完整地描述。显然，所描述的实施例是本发明的一部分实施例，而不是全部的实施例。基于所描述的本发明的实施例，本领域普通技术人员在无需创造性劳动的前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例一
1、一种冷焊料的激活方法，步骤如下：
1）、对冷焊料进行预热流化；
2）、将流化后的冷焊料送入焊料池进行熔融；
3）、将步骤2）熔融后的冷焊料放入储存罐中，即可与焊接设备对接。
2、根据权利要求1所述的冷焊料的激活方法，其特征在于：步骤1）中焊料流化在封闭式流化池中进行。
作为本发明所述的冷焊料的激活方法，封闭式流化池中填充有惰性气体。
作为本发明所述的冷焊料的激活方法，所述的焊料流化温度为220°。
作为本发明所述的冷焊料的激活方法，所述的熔融温度为350°。
作为本发明所述的冷焊料的激活方法，所述的焊料流化反应时间为20分钟。
作为本发明所述的冷焊料的激活方法，所述的焊料熔融反应时间为20分钟。
实施例二
1、一种冷焊料的激活方法，步骤如下：
1）、对冷焊料进行预热流化；
2）、将流化后的冷焊料送入焊料池进行熔融；
3）、将步骤2）熔融后的冷焊料放入储存罐中，即可与焊接设备对接。
2、根据权利要求1所述的冷焊料的激活方法，其特征在于：步骤1）中焊料流化在封闭式流化池中进行。
作为本发明所述的冷焊料的激活方法，封闭式流化池中填充有惰性气体。
作为本发明所述的冷焊料的激活方法，所述的焊料流化温度为-300°。
作为本发明所述的冷焊料的激活方法，所述的熔融温度为600°。
作为本发明所述的冷焊料的激活方法，所述的焊料流化反应时间为20分钟。
作为本发明所述的冷焊料的激活方法，所述的焊料熔融反应时间为20分钟。
实施例三
1、一种冷焊料的激活方法，步骤如下：
1）、对冷焊料进行预热流化；
2）、将流化后的冷焊料送入焊料池进行熔融；
3）、将步骤2）熔融后的冷焊料放入储存罐中，即可与焊接设备对接。
2、根据权利要求1所述的冷焊料的激活方法，其特征在于：步骤1）中焊料流化在封闭式流化池中进行。
作为本发明所述的冷焊料的激活方法，封闭式流化池中填充有惰性气体。
作为本发明所述的冷焊料的激活方法，所述的焊料流化温度为270°。
作为本发明所述的冷焊料的激活方法，所述的熔融温度为550°。
作为本发明所述的冷焊料的激活方法，所述的焊料流化反应时间为30分钟。
作为本发明所述的冷焊料的激活方法，所述的焊料熔融反应时间为40分钟。
本技术领域技术人员可以理解，除非另外定义，这里使用的所有术语（包括技术术语和科学术语）具有与本发明所属领域中的普通技术人员的一般理解相同的意义。还应该理解的是，诸如通用字典中定义的那些术语应该被理解为具有与现有技术的上下文中的意义一致的意义，并且除非像这里一样定义，不会用理想化或过于正式的含义来解释。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，可轻易想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求的保护范围为准。
Claims (7)
1.一种冷焊料的激活方法，其特征在于：步骤如下：
1）、对冷焊料进行预热流化；
2）、将流化后的冷焊料送入焊料池进行熔融；
3）、将步骤2）熔融后的冷焊料放入储存罐中，即可与焊接设备对接。
2.根据权利要求1所述的冷焊料的激活方法，其特征在于：步骤1）中焊料流化在封闭式流化池中进行。
3.根据权利要求2所述的冷焊料的激活方法，其特征在于：封闭式流化池中填充有惰性气体。
4.根据权利要求1所述的冷焊料的激活方法，其特征在于：所述的焊料流化温度为220°-300°。
5.根据权利要求1所述的冷焊料的激活方法，其特征在于：所述的熔融温度为350°-600°。
6.根据权利要求1所述的冷焊料的激活方法，其特征在于：所述的焊料流化反应时间为20-30分钟。
7.根据权利要求1所述的冷焊料的激活方法，其特征在于：所述的焊料熔融反应时间为20-40分钟。