CN104962351A - Wheel hub forging and stamping oil preparation method - Google Patents
Wheel hub forging and stamping oil preparation method Download PDFInfo
- Publication number
- CN104962351A CN104962351A CN201510314753.4A CN201510314753A CN104962351A CN 104962351 A CN104962351 A CN 104962351A CN 201510314753 A CN201510314753 A CN 201510314753A CN 104962351 A CN104962351 A CN 104962351A
- Authority
- CN
- China
- Prior art keywords
- parts
- forging
- stamping
- wheel hub
- oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a wheel hub forging and stamping oil preparation method. The method comprises the following steps: mixing all components according to corresponding weight parts, and processing at 60-75DEG C by using an oil refining machine to prepare required forging and stamping oil. The wheel hub forging and stamping oil preparation method can solve the defects of human body health harming, difficult storage and poor environmental protection property in the prior art in order to realize human body health benefiting, convenient storage and good environmental protection property.
Description
Technical field
The present invention relates to forging technology field, particularly, relate to the preparation method of a kind of wheel hub forging and stamping oil.
Background technology
In forging processing, there is obvious viscous deformation in blank entirety, has relatively large plastic flow; In punch process, blank is shaped mainly through changing the locus of each site area, and the plastic flow of larger distance does not appear in its inside.Forging and stamping are mainly used in processing metal product, also can be used for processing that some is nonmetal, as the shaping etc. of engineering plastics, rubber, ceramic blank, adobe and matrix material.
Rolling, draw etc. in forging and stamping and metallurgical industry all belong to plastic working, or claim press working, but forge and press mainly for the production of metallic article, and rolling, draw etc. are mainly for the production of versatility metallic substance such as sheet material, band, tubing, section bar and wire rods.Forging and stamping are forging and being collectively referred to as of punching press, and just like industrial and trade, also claim industry and trade.
Existing forging and stamping oil adopts organic solvent preparation, and such as traditional employing methylene dichloride is modulated as solvent, and this solvent is volatile, and smell is comparatively large, has larger toxicity, also should not be underestimated on the impact of environment to human body.Therefore need to develop a kind of performance requirement that both can meet cold forging pressure, again can environment-protecting asepsis cold forging force feed formula.
Realizing in process of the present invention, contriver finds at least to exist in prior art and is unfavorable for the defect such as HUMAN HEALTH, not easily storage and feature of environmental protection difference.
Summary of the invention
The object of the invention is to, for the problems referred to above, propose the preparation method of a kind of wheel hub forging and stamping oil, to realize being beneficial to the good advantage of HUMAN HEALTH, convenient storage and the feature of environmental protection.
For achieving the above object, the technical solution used in the present invention is: a kind of preparation method of wheel hub forging and stamping oil, comprising:
(1) by each component of following parts by weight proportioning:
Methyl methacrylate: 5 parts;
Ester class pour point depressant: 3 parts;
Tenox PG: 4 parts;
Soybean oil: 15 parts;
Amine carboxylic acid: 2 parts;
Mineral oil: 11 parts;
Sulfurized fatty acid amide: 3.2 parts;
Olefine sulfide: 1.5 parts;
Polymeric aliphatic ester: 0.8 part;
Sulfuration animal grease: 21 parts;
Maleic acid copolymerized ester: 10 parts;
Methyl acrylate-methyl acrylic copolymer: 6.8 parts;
(2), after each component being pressed corresponding parts by weight proportioning, under the temperature condition of 60 ~ 75 DEG C, use the required forging and stamping of oil refining device preparation oily.
The preparation method of the wheel hub forging and stamping oil of various embodiments of the present invention, owing to comprising: by each component by after corresponding parts by weight proportioning, under the temperature condition of 60 ~ 75 DEG C, uses the required forging and stamping oil of oil refining device preparation; Thus the defect being unfavorable for HUMAN HEALTH, not easily storage and feature of environmental protection difference can be overcome in prior art, to realize being conducive to the good advantage of HUMAN HEALTH, convenient storage and the feature of environmental protection.
Other features and advantages of the present invention will be set forth in the following description, and, partly become apparent from specification sheets, or understand by implementing the present invention.
Below by embodiment, technical scheme of the present invention is described in further detail.
Embodiment
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
According to the embodiment of the present invention, provide the preparation method of a kind of wheel hub forging and stamping oil, comprising:
(1) by each component of following parts by weight proportioning:
Methyl methacrylate: 5 parts;
Ester class pour point depressant: 3 parts;
Tenox PG: 4 parts;
Soybean oil: 15 parts;
Amine carboxylic acid: 2 parts;
Mineral oil: 11 parts;
Sulfurized fatty acid amide: 3.2 parts;
Olefine sulfide: 1.5 parts;
Polymeric aliphatic ester: 0.8 part;
Sulfuration animal grease: 21 parts;
Maleic acid copolymerized ester: 10 parts;
Methyl acrylate-methyl acrylic copolymer: 6.8 parts;
(2), after each component being pressed corresponding parts by weight proportioning, under the temperature condition of 60 ~ 75 DEG C, use the required forging and stamping of oil refining device preparation oily.
Empirical tests, technical solution of the present invention products obtained therefrom, can avoid using volatile, poisonous and hazardous organic solvent, can reach the main body effect of lubrication, cooling, improve the working efficiency of forging and stamping, more safety and environmental protection; Significantly can reduce the impact on operator ' s health and ecotope, and this cold forging force feed evaporation rate is fast, the requirement that serialization cold forging pressure is produced can be met.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (1)
1. a preparation method for wheel hub forging and stamping oil, is characterized in that, comprising:
(1) by each component of following parts by weight proportioning:
Methyl methacrylate: 5 parts;
Ester class pour point depressant: 3 parts;
Tenox PG: 4 parts;
Soybean oil: 15 parts;
Amine carboxylic acid: 2 parts;
Mineral oil: 11 parts;
Sulfurized fatty acid amide: 3.2 parts;
Olefine sulfide: 1.5 parts;
Polymeric aliphatic ester: 0.8 part;
Sulfuration animal grease: 21 parts;
Maleic acid copolymerized ester: 10 parts;
Methyl acrylate-methyl acrylic copolymer: 6.8 parts;
(2), after each component being pressed corresponding parts by weight proportioning, under the temperature condition of 60 ~ 75 DEG C, use the required forging and stamping of oil refining device preparation oily.