CN104961438A - Formula and preparation method for ceramic wine jar preform body capable of accelerating alcohol alcoholization - Google Patents
Formula and preparation method for ceramic wine jar preform body capable of accelerating alcohol alcoholization Download PDFInfo
- Publication number
- CN104961438A CN104961438A CN201510355180.XA CN201510355180A CN104961438A CN 104961438 A CN104961438 A CN 104961438A CN 201510355180 A CN201510355180 A CN 201510355180A CN 104961438 A CN104961438 A CN 104961438A
- Authority
- CN
- China
- Prior art keywords
- acceleration
- wine vat
- alcoholization
- kiln
- ceramic wine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of wine jar manufacture, and particularly relates to a formula and preparation method for a ceramic wine jar preform body capable of accelerating alcohol alcoholization. The formula for the ceramic wine jar preform body capable of accelerating alcohol alcoholization comprises red soil, pyrophylite, potassium feldspar, kaolin, quartz stone, limonite, medical stone, porous basalt and tourmaline. According to the wine jar prepared through the perform body, multiple pores in the inner wall of a traditional pottery are maintained, but the pores are shrunk to a non-leaking state compared with traditional pottery. Accordingly, wine in the wine bar can breathe external air and corporate with external environment through the pores, and the alcoholization speed of the wine is accelerated. When the wine jar is produced, glazing is not needed, processing is simple, and the production cost is low; through a large number of experiments, the wine jar has the effect of accelerating the alcoholization of alcohol when white wine is stored in the wine jar, and comparatively strong competitive power on the market is achieved.
Description
Technical field
The invention belongs to wine vat manufacture field, be specifically related to a kind of tool can acceleration of alcohol alcoholization ceramic wine vat blank formulation and preparation method.
Background technology
Multiple Ester can be produced depositing in process of white wine.And ester class can produce various special fragrance, " alcoholization " process that Here it is is commonly called as.Because this alcoholization process is slowly, so white wine normally can relatively goodly drink more for a long time by the shelf-time.According to brewmaster introduction, in various aromatic white spirit, hide for a long time with the high spirit optimum of pure grain brewing, the mouthfeel brought to people is enjoyed also best, and consumption value is also the highest, and meanwhile, Maotai-flavor liquor is more preferably than other aromatic white spirits stored for a long time.
Be recognized that in the industry that at present earthenware porcelain receptacle is beneficial to white wine most and stores, but ceramic ware can be subdivided into pottery and porcelain, both maximum difference are to use raw material and whether glazing.The firing temperature of pottery generally 800-1100 DEG C, the firing temperature of porcelain is generally at 1200-1400 DEG C; Porcelain can carry out glazing before the firing and pottery is divided into pottery to have not rest and rest two kinds; glaze is a kind of vitreous layer covering pottery, porcelain surface; its main object is the protection providing porcelain; glaze is firing the surface the color and luster and the surface pattern that form uniqueness that can be coated on ceramic ware equably; but the existence due to glaze can reduce the hole of porcelain greatly; the existing pottery as wine vat needs glazing, otherwise easily seeps water.Therefore, how to make wine vat by the pottery of exempting from glazing, the quality making full use of the hole lifting wine of pottery is the problem of wine vat manufacturing enterprise and brewery's extensive concern.
Summary of the invention
In order to by glaze realize plating as high gloss copper gold effect, propose tool a kind of can acceleration of alcohol alcoholization ceramic wine vat blank formulation, method of preparation and use.
Can the blank formulation of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that,
As follows according to parts by weight: laterite 45-55%, agalmatolite 8-15%, potassium felspar sand 8-15%, kaolin 5-10%, quartzite 5-10%, MUSYUSHI 5-10%, medical stone 3-5%, porous basalt 3-5%, tourmalinite 3-5%.
Optimize, can acceleration of alcohol alcoholization ceramic wine vat blank formulation, silicon oxide 65-70%, aluminum oxide 15-20%, ferric oxide 0.5-1%, calcium oxide 0.5-1%, magnesium oxide 0.5-1%, titanium oxide 0.2-0.5%, potassium oxide 1-3%, sodium oxide 0.2-0.5%, loss on ignition 3-6% in blank formulation.
Optimize, can acceleration of alcohol alcoholization ceramic wine vat blank formulation, as follows according to parts by weight: laterite 52%, agalmatolite 9%, potassium felspar sand 8%, kaolin 6%, quartzite 6%, MUSYUSHI 8%, medical stone 4%, porous basalt 4%, tourmalinite 3%.
Optimize, can acceleration of alcohol alcoholization ceramic wine vat blank formulation, as follows according to parts by weight: laterite 55%, agalmatolite 8%, potassium felspar sand 8%, kaolin 8%, quartzite 7%, MUSYUSHI 5%, medical stone 3%, porous basalt 3%, tourmalinite 3%.
Optimize, can acceleration of alcohol alcoholization ceramic wine vat blank formulation, as follows according to parts by weight: laterite 45%, agalmatolite 11%, potassium felspar sand 10%, kaolin 9%, quartzite 5%, MUSYUSHI 8%, medical stone 4%, porous basalt 4%, tourmalinite 4%.
Can the preparation method of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that, comprise the following steps:
Step one, according to blank formulation weighing and proportioning, obtained pug after first adding water for ball milling, excessively 120 mesh sieves;
Step 2, pug through filter-press dehydration, old, vacuum pugging, shaping after make wine vat base substrate;
Step 3, wine vat base substrate is put into kiln, heat up under oxidizing atmosphere, be warming up to 200-500 °, then in kiln, carbon dioxide is passed into, kiln under reducing atmosphere kiln continues to heat up, and furnace heating-up keeps temperature 1-2 hour to during 900-1000 °, and kiln continues to be warming up to 1200 °-1300 ° and burns till;
Step 4, opens kiln, obtain after naturally cooling can acceleration of alcohol alcoholization ceramic wine vat.
Further, in step 3, kiln was warming up to 200 degree through 2 hours.
Further, in step 3, kiln was warming up to 1300 degree through 9 hours.
Further, temperature is kept 2 hours during furnace heating-up to 900 ° in step 3.
Seen from the above description, provided by the invention can acceleration of alcohol alcoholization ceramic wine vat blank formulation, method of preparation and use, use the wine vat that this kind of blank is made, remain traditional pottery inner wall concrete dynamic modulus, but hole reduces the state to leaking compared with traditional pottery, make the wine wine in wine vat can be breathed with the external world by hole, mutually do with outside atmosphere, accelerate the alcoholization speed of wine; Make this kind of wine vat low without the need to glazing, water-intake rate, ne-leakage, effectively solves ceramic wine urn seepage and the extremely low bottleneck problem warp of yield rate, crosses lot of experiments, use this kind of wine vat storage white wine to have the effect of the alcoholization of acceleration of alcohol, commercially there is stronger competitive power.
Embodiment
Technical scheme for a better understanding of the present invention, further describes embodiment provided by the invention below.
The invention provides can the ceramic wine vat blank formulation of acceleration of alcohol alcoholization, can the blank formulation of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that,
As follows according to parts by weight: laterite 45-55%, agalmatolite 8-15%, potassium felspar sand 8-15%, kaolin 5-10%, quartzite 5-10%, MUSYUSHI 5-10%, medical stone 3-5%, porous basalt 3-5%, tourmalinite 3-5%; Silicon oxide 65-70%, aluminum oxide 15-20%, ferric oxide 0.5-1%, calcium oxide 0.5-1%, magnesium oxide 0.5-1%, titanium oxide 0.2-0.5%, potassium oxide 1-3%, sodium oxide 0.2-0.5%, loss on ignition 3-6% in blank formulation.
Specific embodiment one:
Can acceleration of alcohol alcoholization ceramic wine vat blank formulation, as follows according to parts by weight: laterite 52%, agalmatolite 9%, potassium felspar sand 8%, kaolin 6%, quartzite 6%, MUSYUSHI 8%, medical stone 4%, porous basalt 4%, tourmalinite 3%.
Specific embodiment two:
Can acceleration of alcohol alcoholization ceramic wine vat blank formulation, as follows according to parts by weight: laterite 55%, agalmatolite 8%, potassium felspar sand 8%, kaolin 8%, quartzite 7%, MUSYUSHI 5%, medical stone 3%, porous basalt 3%, tourmalinite 3%.
Specific embodiment three:
Can acceleration of alcohol alcoholization ceramic wine vat blank formulation, as follows according to parts by weight: laterite 45%, agalmatolite 11%, potassium felspar sand 10%, kaolin 9%, quartzite 5%, MUSYUSHI 8%, medical stone 4%, porous basalt 4%, tourmalinite 4%.
Described in specific embodiment one to three can the preparation method of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that, comprise the following steps:
Step one, according to blank formulation weighing and proportioning, obtained pug after first adding water for ball milling, excessively 120 mesh sieves;
Step 2, pug through filter-press dehydration, old, vacuum pugging, shaping after make wine vat base substrate;
Step 3, wine vat base substrate is put into kiln, heat up under oxidizing atmosphere, be warming up to 200-500 °, then in kiln, carbon dioxide is passed into, kiln under reducing atmosphere kiln continues to heat up, and furnace heating-up keeps temperature 1-2 hour to during 900-1000 °, and kiln continues to be warming up to 1200 °-1300 ° and burns till;
Step 4, opens kiln, obtain after naturally cooling can acceleration of alcohol alcoholization ceramic wine vat.
Optimize, kiln heats up under oxidizing atmosphere, is warming up to 200 degree through 2 hours, then in kiln, carbon dioxide is passed into, kiln under reducing atmosphere kiln continues to heat up, and keep temperature 2 hours when being warming up to 900 °, kiln continued to be warming up to 1300 ° and burns till through 9 hours.
Main Economic technical indicator is as follows after testing:
Water-intake rate < 0.5%, lead release≤2mg/L, quantity of cadmium release≤0.2mg/L
The wine vat using above-mentioned formula and method to make has following effect:
1, adopt plurality of raw materials as fusing assistant, the firing temperature of raw material can be reduced.Under suitable calcining system, the water-intake rate <1% of pottery storage wine jar and jar fermenter sample, wine jar sample is non-leakage;
2, lateritic materials distribution is wide, and rich reserves, belongs to regional raw material, and mining area grade is more stable, can gather materials on the spot, be conducive to stably manufactured;
3, lateritic materials, is easy to broken, saves energy consumption.No matter be rock class, sand class, pureed class, or the lateritic materials of shale class, its hardness is all lower, does not generally need coarse crushing, can direct ball milling, and the ball milling cycle is short, can save energy consumption;
4, firing temperature is low, its mineral composition of lateritic materials is to contain illitic sericite class, because illite can decompose than kaolinite and generate mullite crystalline phase under the low temperature condition of 60 DEG C ~ 80 DEG C, therefore be that the raw material of main component can sinter at a lower temperature with illite minerals, thus make the microstructure of goods more rational, improve the inner quality of goods.
The above, be only present pre-ferred embodiments, therefore can not limit scope of the invention process with this, and the equivalence namely done according to the present patent application the scope of the claims and description changes and modifies, and all should still remain within the scope of the patent.
Claims (9)
1. can the blank formulation of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that,
As follows according to parts by weight: laterite 45-55%, agalmatolite 8-15%, potassium felspar sand 8-15%, kaolin 5-10%, quartzite 5-10%, MUSYUSHI 5-10%, medical stone 3-5%, porous basalt 3-5%, tourmalinite 3-5%.
2. according to claim 1 can acceleration of alcohol alcoholization ceramic wine vat blank formulation, it is characterized in that, silicon oxide 65-70%, aluminum oxide 15-20%, ferric oxide 0.5-1%, calcium oxide 0.5-1%, magnesium oxide 0.5-1%, titanium oxide 0.2-0.5%, potassium oxide 1-3%, sodium oxide 0.2-0.5%, loss on ignition 3-6% in described blank formulation.
3. according to claim 1 can acceleration of alcohol alcoholization ceramic wine vat blank formulation, it is characterized in that, as follows according to parts by weight: laterite 52%, agalmatolite 9%, potassium felspar sand 8%, kaolin 6%, quartzite 6%, MUSYUSHI 8%, medical stone 4%, porous basalt 4%, tourmalinite 3%.
4. according to claim 1 can acceleration of alcohol alcoholization ceramic wine vat blank formulation, it is characterized in that, as follows according to parts by weight: laterite 55%, agalmatolite 8%, potassium felspar sand 8%, kaolin 8%, quartzite 7%, MUSYUSHI 5%, medical stone 3%, porous basalt 3%, tourmalinite 3%.
5. according to claim 1 can acceleration of alcohol alcoholization ceramic wine vat blank formulation, it is characterized in that, as follows according to parts by weight: laterite 45%, agalmatolite 11%, potassium felspar sand 10%, kaolin 9%, quartzite 5%, MUSYUSHI 8%, medical stone 4%, porous basalt 4%, tourmalinite 4%.
6. can the preparation method of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that, comprise the following steps:
Step one, according to blank formulation weighing and proportioning, obtained pug after first adding water for ball milling, excessively 120 mesh sieves;
Step 2, pug through filter-press dehydration, old, vacuum pugging, shaping after make wine vat base substrate;
Step 3, wine vat base substrate is put into kiln, heat up under oxidizing atmosphere, be warming up to 200-500 °, then in kiln, carbon dioxide is passed into, kiln under reducing atmosphere kiln continues to heat up, and furnace heating-up keeps temperature 1-2 hour to during 900-1000 °, and kiln continues to be warming up to 1200 °-1300 ° and burns till;
Step 4, opens kiln, obtain after naturally cooling can acceleration of alcohol alcoholization ceramic wine vat.
7. according to claim 6 can the preparation method of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that: in described step 3, kiln was warming up to 200 degree through 2 hours.
8. according to claim 6 or 7 can the preparation method of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that: in described step 3, kiln was warming up to 1300 degree through 9 hours.
9. according to claim 6 can the preparation method of ceramic wine vat of acceleration of alcohol alcoholization, it is characterized in that: in described step 3, during furnace heating-up to 900 °, keep temperature 2 hours.