CN104961277A - 一种制革废水中铬回收利用的方法 - Google Patents

一种制革废水中铬回收利用的方法 Download PDF

Info

Publication number
CN104961277A
CN104961277A CN201510401954.8A CN201510401954A CN104961277A CN 104961277 A CN104961277 A CN 104961277A CN 201510401954 A CN201510401954 A CN 201510401954A CN 104961277 A CN104961277 A CN 104961277A
Authority
CN
China
Prior art keywords
waste water
chromium
leather
recycling
making
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510401954.8A
Other languages
English (en)
Other versions
CN104961277B (zh
Inventor
黄勇
余静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changzhou University
Original Assignee
Changzhou University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changzhou University filed Critical Changzhou University
Priority to CN201510401954.8A priority Critical patent/CN104961277B/zh
Publication of CN104961277A publication Critical patent/CN104961277A/zh
Application granted granted Critical
Publication of CN104961277B publication Critical patent/CN104961277B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公布了一种制革废水中铬回收利用的方法，属于化工废水回收利用领域。本发明通过氧化曝气的方式对制革废水进行氧化，得到游离态的铬离子，再在氧化钙的作用下，使得废水呈碱性并产生阴离子OH－加快了铬离子沉降速度，最后在二氧化硫气体作用下，将沉淀的铬盐混合物发生还原反应，有效地回收了废水中铬，同时铬回收处理后排放的废水能达到国家污水综合排放标准≤0.1000mg/L。

Description

一种制革废水中铬回收利用的方法
技术领域
本发明公布了一种制革废水中铬回收利用的方法，属于化工废水回收利用领域。
背景技术
制革废水是制革生产过程中排出的废水，通常动物皮用盐腌或用水浸泡，使其膨润，加石灰、去肉、脱碱，然后用丹宁或铬，鞣制加脂软化，最后染色加工制成皮革。制革工业生产一般包括脱脂、浸灰脱毛、软化、鞣制、染色加工、干燥、整饰等几个工段，加工过程中需要添加多种化学品，从而使得废水中含有油脂、胶原蛋白、动植物纤维、有机无机固形物、硫化物、铬、盐类、表面活性剂、染料等多种污染物质和有毒物质。
铬是银白色金属，质极硬，耐腐蚀。密度7.20g/cm3。可溶于强碱溶液。铬具有很高的耐腐蚀性，在空气中，即便是在赤热的状态下，氧化也很慢，不溶于水；尤其是六价铬为吞入性毒物/吸入性极毒物，皮肤接触可能导致敏感，更可能造成遗传性基因缺陷，吸入可能致癌，对环境有持久危险性。
从环保和可持续发展的角度出发，含铬废水中铬的无害化、减量化、资源化处理是大势所趋。国家第一个“十二五专题规划”—重金属污染综合防治“十二五”规划中，铬被纳入第一类对象，皮革及制品业列如重点防控行业，这要求各制革企业将含铬废水、废物的治理作为企业环保工作的重中之重。
发明内容
本发明主要解决的技术问题：针对于制革废水中铬再利用价值低、直接排放对环境有持久危险性的弊端，提供了一种制革废水中铬回收利用的方法，实现了铬回收，并使得废水中铬含量达标排放的目的。
为了实现上述的目的，本发明采取的具体技术方案是：一种制革废水中铬回收利用的方法，其特征在于具体步骤为：
(1)将制革废水通入废水体积为5m3蓄水池中，过虑、沉淀分离，去除制革废水中所产生的肉块和毛发，得初步分离后的废水；
(2)向上述初步分离后的废水中通入臭氧，同时加入质量浓度为30～50％双氧水进行氧化反应1～3小时，使废水中的铬盐氧化后以铬离子的形式存在；
(3)待氧化一段时间后，加入500～1000g氧化钙搅拌10～30min，并控制温度在20～40℃，停止搅拌反应2～3小时以上，沉淀，静置；
(4)将上述沉淀物和废水进行分离，得到湿润的铬盐沉淀物；
(5)向上述的铬盐沉淀物通入二氧化硫气体，在1000～1200℃的温度下，加热、烘干；
(6)将废水中回收得到的铬重新加入到制革过程中，重复利用。
本发明的应用方法为：首先将制革废水通入废水体积为5m3蓄水池中，过虑、沉淀分离，去除制革废水中所产生的肉块和毛发，得初步分离后的废水；接着向上述初步分离后的废水中通入臭氧，同时加入质量浓度为30～50％双氧水进行氧化反应1～3小时，使废水中的铬盐氧化后以铬离子的形式存在；待氧化一段时间后，加入500～1000g氧化钙搅拌10～30min，并控制温度在20～40℃，停止搅拌反应2～3小时以上，沉淀，静置；再将上述沉淀物和废水进行分离，得到湿润的铬盐沉淀物；接着向上述的铬盐沉淀物通入二氧化硫气体，在1000～1200℃的温度下，加热、烘干；最后将废水中回收得到的铬重新加入到铬鞣步骤中，重复利用。
本发明的原理是：通过氧化曝气的方式对制革废水进行氧化，得到游离态的铬离子，再在氧化钙的作用下，使得废水呈碱性并产生阴离子OH－加快了铬离子沉降速度，最后在二氧化硫气体作用下，将沉淀的铬盐混合物发生还原反应，实现了铬的回收。
本发明的有益效果是：
(1)经过多次过滤后，有效地去除了大部分皮屑、毛渣等杂质。
(2)通过加入阴离子OH－加快了沉降速度，减小了沉淀体积。
(3)铬回收处理后排放的废水能达到国家污水综合排放标准≤0.1000mg/L。
具体实施方案
一种制革废水中铬回收利用的方法，其特征在于具体步骤为：
(1)将制革废水通入废水体积为5m3蓄水池中，过虑、沉淀分离，去除制革废水中所产生的肉块和毛发，得初步分离后的废水；
(2)向上述初步分离后的废水中通入臭氧，同时加入质量浓度为30～50％双氧水进行氧化反应1～3小时，使废水中的铬盐氧化后以铬离子的形式存在；
(3)待氧化一段时间后，加入500～1000g氧化钙搅拌10～30min，并控制温度在20～40℃，停止搅拌反应2～3小时以上，沉淀，静置；
(4)将上述沉淀物和废水进行分离，得到湿润的铬盐沉淀物；
(5)向上述的铬盐沉淀物通入二氧化硫气体，在1000～1200℃的温度下，加热、烘干；
(6)将废水中回收得到的铬重新加入到制革过程中，重复利用。
实例1
首先将制革废水通入废水体积为5m3蓄水池中，过虑、沉淀分离，去除制革废水中所产生的肉块和毛发，得初步分离后的废水；接着向上述初步分离后的废水中通入臭氧，同时加入质量浓度为30％双氧水进行氧化反应1小时，使废水中的铬盐氧化后以铬离子的形式存在；待氧化一段时间后，加入500g氧化钙搅拌10min，并控制温度在20℃，停止搅拌反应2小时以上，沉淀，静置；再将上述沉淀物和废水进行分离，得到湿润的铬盐沉淀物；接着向上述的铬盐沉淀物通入二氧化硫气体，在1000℃的温度下，加热、烘干；最后将废水中回收得到的铬重新加入到铬鞣步骤中，重复利用。有效地回收了废水中铬，同时铬回收处理后排放的废水能达到国家污水综合排放标准≤0.1000mg/L。
实例2
首先将制革废水通入废水体积为5m3蓄水池中，过虑、沉淀分离，去除制革废水中所产生的肉块和毛发，得初步分离后的废水；接着向上述初步分离后的废水中通入臭氧，同时加入质量浓度为40％双氧水进行氧化反应2小时，使废水中的铬盐氧化后以铬离子的形式存在；待氧化一段时间后，加入700g氧化钙搅拌20min，并控制温度在30℃，停止搅拌反应2.5小时以上，沉淀，静置；再将上述沉淀物和废水进行分离，得到湿润的铬盐沉淀物；接着向上述的铬盐沉淀物通入二氧化硫气体，在1100℃的温度下，加热、烘干；最后将废水中回收得到的铬重新加入到铬鞣步骤中，重复利用。有效地回收了废水中铬，同时铬回收处理后排放的废水能达到国家污水综合排放标准≤0.1000mg/L。
实例3
首先将制革废水通入废水体积为5m3蓄水池中，过虑、沉淀分离，去除制革废水中所产生的肉块和毛发，得初步分离后的废水；接着向上述初步分离后的废水中通入臭氧，同时加入质量浓度为50％双氧水进行氧化反应3小时，使废水中的铬盐氧化后以铬离子的形式存在；待氧化一段时间后，加入1000g氧化钙搅拌30min，并控制温度在40℃，停止搅拌反应3小时以上，沉淀，静置；再将上述沉淀物和废水进行分离，得到湿润的铬盐沉淀物；接着向上述的铬盐沉淀物通入二氧化硫气体，在1200℃的温度下，加热、烘干；最后将废水中回收得到的铬重新加入到铬鞣步骤中，重复利用。有效地回收了废水中铬，同时铬回收处理后排放的废水能达到国家污水综合排放标准≤0.1000mg/L。

Claims (1)

1.一种制革废水中铬回收利用的方法，其特征在于具体步骤为：
(1)将制革废水通入废水体积为5m3蓄水池中，过虑、沉淀分离，去除制革废水中所产生的肉块和毛发，得初步分离后的废水；
(2)向上述初步分离后的废水中通入臭氧，同时加入质量浓度为30～50％双氧水进行氧化反应1～3小时，使废水中的铬盐氧化后以铬离子的形式存在；
(3)待氧化一段时间后，加入500～1000g氧化钙搅拌10～30min，并控制温度在20～40℃，停止搅拌反应2～3小时以上，沉淀，静置；
(4)将上述沉淀物和废水进行分离，得到湿润的铬盐沉淀物；
(5)向上述的铬盐沉淀物通入二氧化硫气体，在1000～1200℃的温度下，加热、烘干；
(6)将废水中回收得到的铬重新加入到制革过程中，重复利用。
CN201510401954.8A 2015-07-09 2015-07-09 一种制革废水中铬回收利用的方法 Active CN104961277B (zh)