CN104952538A - 电力设施用防腐耐酸碱电缆 - Google Patents

电力设施用防腐耐酸碱电缆 Download PDF

Info

Publication number
CN104952538A
CN104952538A CN201510256582.4A CN201510256582A CN104952538A CN 104952538 A CN104952538 A CN 104952538A CN 201510256582 A CN201510256582 A CN 201510256582A CN 104952538 A CN104952538 A CN 104952538A
Authority
CN
China
Prior art keywords
parts
protective jacket
resin
anticorrosion
butyl
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510256582.4A
Other languages
English (en)
Inventor
龚灿锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510256582.4A priority Critical patent/CN104952538A/zh
Publication of CN104952538A publication Critical patent/CN104952538A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其中，内防护套由以下物质组成：邻苯二甲酸酯，羟基聚酯树脂，氯醋树脂，对羟基苯甲酸丁酯，多酮，丙二醇单醚乙酸酯，过氯乙烯树脂，正硅酸丁酯，硬脂酸钙，氯丁橡胶，钛白粉；外防护套由以下物质组成：聚硅氧烷、间苯二酚、硅树脂、纳米氧化铁、甘油三醋酸酯、高氯化聚乙烯树脂、水溶性聚氨酯树脂。该发明电缆具有更强耐候性、抗变形、拉伸强度高、延伸率大，对基层收缩和开裂变形适应性强、抗酸性、抗碱性、防腐防水性能优越，方便根据需要使用。

Description

电力设施用防腐耐酸碱电缆
技术领域
本发明涉及电力设施技术领域，具体涉及一种电力设施用防腐耐酸碱电缆。
背景技术
一般的电力电缆在安装使用过程中，受到其环境限制，当使用一段时间后，往往容易裂开，为了防止裂开，需要采用其他的包装套，而增加了制造使用成本。特别是，对于一些特殊场合传输使用的电力电缆，需要采用特别的措施，使得其能防腐抗酸碱，目前的做法是设置一些必要的防护套，以便其能满足相应的防腐抗酸碱的要求，从而增加了其使用成本。
发发明内容
本发明的目的在于提供一种电力设施用防腐耐酸碱电缆，以便实现防腐抗酸碱功能，更好地应用于实际生活应用中，延长电缆使用寿命，改善其使用效果。
为了实现上述目的，本发明的技术方案如下。
一种电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其中，内防护套由以下质量组分物质组成：邻苯二甲酸酯6～10份，羟基聚酯树脂15～30份，氯醋树脂8～16份，对羟基苯甲酸丁酯10～25份，多酮8～10份，丙二醇单醚乙酸酯4～10份，过氯乙烯树脂12～20份，正硅酸丁酯0.5～1份，硬脂酸钙0.1～0.5份，氯丁橡胶5～15份，钛白粉1～3份；外防护套由以下质量份数物质组成：聚硅氧烷60～100份、间苯二酚36～100份、硅树脂60～100份、纳米氧化铁60～100份、甘油三醋酸酯60～100份、高氯化聚乙烯树脂8～12份、水溶性聚氨酯树脂12～20份。
进一步地，上述电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其中，内防护套由以下质量组分物质组成：邻苯二甲酸酯6份，羟基聚酯树脂15份，氯醋树脂8份，对羟基苯甲酸丁酯10份，多酮8份，丙二醇单醚乙酸酯4份，过氯乙烯树脂12份，正硅酸丁酯0.5份，硬脂酸钙0.1份，氯丁橡胶5份，钛白粉1份；外防护套由以下质量份数物质组成：聚硅氧烷60份、间苯二酚36份、硅树脂60份、纳米氧化铁60份、甘油三醋酸酯60份、高氯化聚乙烯树脂8份、水溶性聚氨酯树脂12。
进一步地，上述电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其中，内防护套由以下质量组分物质组成：邻苯二甲酸酯8份，羟基聚酯树脂18份，氯醋树脂12份，对羟基苯甲酸丁酯16份，多酮9份，丙二醇单醚乙酸酯7份，过氯乙烯树脂16份，正硅酸丁酯0.8份，硬脂酸钙0.3份，氯丁橡胶10份，钛白粉2份；外防护套由以下质量份数物质组成：聚硅氧烷80份、间苯二酚66份、硅树脂80份、纳米氧化铁80份、甘油三醋酸酯80份、高氯化聚乙烯树脂10份、水溶性聚氨酯树脂16份。
进一步地，上述电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其中，内防护套由以下质量组分物质组成：邻苯二甲酸酯10份，羟基聚酯树脂30份，氯醋树脂16份，对羟基苯甲酸丁酯25份，多酮10份，丙二醇单醚乙酸酯10份，过氯乙烯树脂20份，正硅酸丁酯1份，硬脂酸钙0.5份，氯丁橡胶5份，钛白粉3份；外防护套由以下质量份数物质组成：聚硅氧烷100份、间苯二酚100份、硅树脂100份、纳米氧化铁100份、甘油三醋酸酯100份、高氯化聚乙烯树脂12份、水溶性聚氨酯树脂20份。
该发明的有益效果在于：该发明电缆具有质地柔软、耐磨耐高温、安全可靠且具有良好的散热性能，使得该传输导线可以在要求很恶劣的环境下使用，本发明具有更强耐候性、抗变形、拉伸强度高、延伸率大，对基层收缩和开裂变形适应性强、抗酸性、抗碱性、防腐防水性能优越，方便根据需要使用。
具体实施方式
下面结合实施例对本发明的具体实施方式进行描述，以便更好的理解本发明。
实施例1
本实施例中的电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其中，内防护套由以下质量组分物质组成：邻苯二甲酸酯6份，羟基聚酯树脂15份，氯醋树脂8份，对羟基苯甲酸丁酯10份，多酮8份，丙二醇单醚乙酸酯4份，过氯乙烯树脂12份，正硅酸丁酯0.5份，硬脂酸钙0.1份，氯丁橡胶5份，钛白粉1份；外防护套由以下质量份数物质组成：聚硅氧烷60份、间苯二酚36份、硅树脂60份、纳米氧化铁60份、甘油三醋酸酯60份、高氯化聚乙烯树脂8份、水溶性聚氨酯树脂12。上述内防护套和外防护套的制备方法均采用如下步骤：将上述组分物料予以分别混合，然后予以热熔，在利用设置有通孔的模具挤出制备出符合要求的内防护套和外防护套，随后予以过水冷却降温，并进行干燥处理，即获得成品。
实施例2
本实施例中的电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其中，内防护套由以下质量组分物质组成：邻苯二甲酸酯8份，羟基聚酯树脂18份，氯醋树脂12份，对羟基苯甲酸丁酯16份，多酮9份，丙二醇单醚乙酸酯7份，过氯乙烯树脂16份，正硅酸丁酯0.8份，硬脂酸钙0.3份，氯丁橡胶10份，钛白粉2份；外防护套由以下质量份数物质组成：聚硅氧烷80份、间苯二酚66份、硅树脂80份、纳米氧化铁80份、甘油三醋酸酯80份、高氯化聚乙烯树脂10份、水溶性聚氨酯树脂16份。上述内防护套和外防护套的制备方法均采用如下步骤：将上述组分物料予以分别混合，然后予以热熔，在利用设置有通孔的模具挤出制备出符合要求的内防护套和外防护套，随后予以过水冷却降温，并进行干燥处理，即获得成品。
实施例3
本实施例中的电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其中，内防护套由以下质量组分物质组成：邻苯二甲酸酯10份，羟基聚酯树脂30份，氯醋树脂16份，对羟基苯甲酸丁酯25份，多酮10份，丙二醇单醚乙酸酯10份，过氯乙烯树脂20份，正硅酸丁酯1份，硬脂酸钙0.5份，氯丁橡胶5份，钛白粉3份；外防护套由以下质量份数物质组成：聚硅氧烷100份、间苯二酚100份、硅树脂100份、纳米氧化铁100份、甘油三醋酸酯100份、高氯化聚乙烯树脂12份、水溶性聚氨酯树脂20份。上述内防护套和外防护套的制备方法均采用如下步骤：将上述组分物料予以分别混合，然后予以热熔，在利用设置有通孔的模具挤出制备出符合要求的内防护套和外防护套，随后予以过水冷却降温，并进行干燥处理，即获得成品。
针对实施例1、实施例2和实施例3中的电缆进行性能测量，所测得的数据如表1所示。
表1
以上所述是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也视为本发明的保护范围。

Claims (4)

1.一种电力设施用防腐耐酸碱电缆，包含有多根铜合金导线及内防护套，铜合金导线相互平行放置，每根铜合金导线外层均利用内防护套包覆，多个内防护套外侧利用外防护套包裹在一起，其特征在于：所述内防护套由以下质量组分物质组成：邻苯二甲酸酯6～10份，羟基聚酯树脂15～30份，氯醋树脂8～16份，对羟基苯甲酸丁酯10～25份，多酮8～10份，丙二醇单醚乙酸酯4～10份，过氯乙烯树脂12～20份，正硅酸丁酯0.5～1份，硬脂酸钙0.1～0.5份，氯丁橡胶5～15份，钛白粉1～3份；外防护套由以下质量份数物质组成：聚硅氧烷60～100份、间苯二酚36～100份、硅树脂60～100份、纳米氧化铁60～100份、甘油三醋酸酯60～100份、高氯化聚乙烯树脂8～12份、水溶性聚氨酯树脂12～20份。
2.根据权利要求1所述的电力设施用防腐耐酸碱电缆，其特征在于：所述内防护套由以下质量组分物质组成：邻苯二甲酸酯6份，羟基聚酯树脂15份，氯醋树脂8份，对羟基苯甲酸丁酯10份，多酮8份，丙二醇单醚乙酸酯4份，过氯乙烯树脂12份，正硅酸丁酯0.5份，硬脂酸钙0.1份，氯丁橡胶5份，钛白粉1份；所述外防护套由以下质量份数物质组成：聚硅氧烷60份、间苯二酚36份、硅树脂60份、纳米氧化铁60份、甘油三醋酸酯60份、高氯化聚乙烯树脂8份、水溶性聚氨酯树脂12。
3.根据权利要求1至2所述的电力设施用防腐耐酸碱电缆，其特征在于：所述内防护套由以下质量组分物质组成：邻苯二甲酸酯约8份，羟基聚酯树脂约18份，氯醋树脂约12份，对羟基苯甲酸丁酯约16份，多酮约9份，丙二醇单醚乙酸酯7份，过氯乙烯树脂16份，正硅酸丁酯0.8份，硬脂酸钙0.3份，氯丁橡胶10份，钛白粉2份；所述外防护套由以下质量份数物质组成：聚硅氧烷80份、间苯二酚66份、硅树脂80份、纳米氧化铁80份、甘油三醋酸酯80份、高氯化聚乙烯树脂10份、水溶性聚氨酯树脂16份。
4.根据权利要求1至3所述的电力设施用防腐耐酸碱电缆，其特征在于：所述内防护套由以下质量组分物质组成：邻苯二甲酸酯10份，羟基聚酯树脂30份，氯醋树脂16份，对羟基苯甲酸丁酯约25份，多酮10份，丙二醇单醚乙酸酯10份，过氯乙烯树脂20份，正硅酸丁酯1份，硬脂酸钙0.5份，氯丁橡胶约5份，钛白粉3份；所述外防护套由以下质量份数物质组成：聚硅氧烷100份、间苯二酚100份、硅树脂100份、纳米氧化铁约100份、甘油三醋酸酯约100份、高氯化聚乙烯树脂约12份、水溶性聚氨酯树脂20份。
CN201510256582.4A 2015-05-20 2015-05-20 电力设施用防腐耐酸碱电缆 Pending CN104952538A (zh)