CN104928928A - 一种聚四氟乙烯玻璃纤维透气漆布及配方 - Google Patents
一种聚四氟乙烯玻璃纤维透气漆布及配方 Download PDFInfo
- Publication number
- CN104928928A CN104928928A CN201510253851.1A CN201510253851A CN104928928A CN 104928928 A CN104928928 A CN 104928928A CN 201510253851 A CN201510253851 A CN 201510253851A CN 104928928 A CN104928928 A CN 104928928A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- cloth
- polytetrafluoroethylene
- formula
- varnished cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种聚四氟乙烯玻璃纤维透气漆布配方,其特征在于各成分质量比如下:聚四氟乙烯含量在30 ~ 40% ;表面活性剂0.5 ~ 0.8%、余量为无离子水和经向和纬向密度为:200 根/10 厘米(±10%),厚度:0.04 毫米~ 0.06 毫米,幅宽:900 ~ 1000 毫米的无碱玻璃布;本发明的有益效果是通过定制玻璃纤维基布,改进配方和生产工艺,使聚四氟乙烯乳液均匀地涂覆、浸渍在无碱玻璃布上,配方更加合理,制作的聚四氟乙烯玻璃纤维透气漆布表面无气泡、含胶量均匀,透气性能好、生产成本低,它既具有玻璃纤维织物的耐高温、高强度性能,又具有聚四氟乙烯优良的绝缘、防粘等一系列性能。
Description
技术领域
本发明属于高分子复合材料技术领域,具体涉及到一种聚四氟乙烯玻璃纤维透气
漆布及配方。
背景技术
玻璃纤维布具有强度高、尺寸稳定、耐高温、耐腐蚀性好及过滤效率高等优点,但
玻璃纤维也有明显的缺点,即性脆、不耐折、不耐磨,容易磨损、折断,影响使用寿命。
聚四氟乙烯微孔薄膜是采用双向拉伸技术生产的,具有独特的微孔结构,透气量
大、阻力低、高微粒截留率、耐温性好,抗强酸、碱、有机溶剂和氧化剂,耐老化及不粘、不燃性和无毒、生物相容性等特点,目前聚四氟乙烯微孔膜的应用技术主要是与织物或非织造织物进行复合后使用,其工艺复杂,成本高。
玻璃纤维涂覆聚四氟乙烯后对提高过玻璃纤维布的耐折、耐磨及憎水性等性能,
延长使用寿命至关重要。玻璃纤维布在浸渍聚四氟乙烯乳液后,经过干燥、烘焙、烧结等工
序,将浸渍液烘干并使其在纤维表面成膜,达到保护纤维,使其免受化学腐蚀,并提高其耐
折、耐磨和憎水性等各项性能外,还必须具备优越的透气性能。
现有技术中(1)聚四氟乙烯微孔薄膜与玻璃纤维布复合得到的透气布配方复杂、
生产成本高、性能不稳定;(2)聚四氟乙烯乳液直接涂覆玻璃纤维布的方法,由于乳液配方
不合理,容易产生气泡,含胶量偏高,透气性能差,难以达到规定的技术要求。
发明内容
为解决上述技术问题,把发明的采用的技术方案如下:
一种聚四氟乙烯玻璃纤维透气漆布配方,各成分质量比如下:聚四氟乙烯含量在30 ~
40% ;表面活性剂0.5 ~ 0. 8%、余量为无离子水和基布。
聚四氟乙烯玻璃纤维透气漆布的基布经向和纬向密度为:200 根/10 厘米(±10%),厚度:0.04 毫米~ 0.06 毫米,幅宽:900 ~ 1000 毫米的无碱玻璃布。
优选地,各成分质量比如下:聚四氟乙烯含量在35% ;表面活性剂0.65%、余量为无
离子水和经向和纬向密度为:200 根/10 厘米,厚度:0.05 毫米,幅宽:950 毫米的无碱玻璃布。
聚四氟乙烯玻璃纤维透气漆布厚度:0.05 毫米~ 0.07 毫米,幅宽:900 ~ 1000 毫
米。
聚四氟乙烯玻璃纤维透气漆布的透气率:50Pa 时大于200mm/s、200pa 时大于
500mm/s。
本发明的有益效果:通过定制玻璃纤维基布,改进配方和生产工艺,使聚四氟乙烯
乳液均匀地涂覆、浸渍在无碱玻璃布上,配方更加合理,制作的聚四氟乙烯玻璃纤维透气漆
布表面无气泡、含胶量均匀,透气性能好、生产成本低,它既具有玻璃纤维织物的耐高温、高强度性能,又具有聚四氟乙烯优良的绝缘、防粘等一系列性能,广泛应用于耐高温、透气、防粘、抽真空、消除负压及脱模等领域,是一种高性能、多用途的高分子复合材料。
具体实施方式
下面结合具体实施例,对本发明进一步阐述:
一种聚四氟乙烯玻璃纤维透气漆布配方,各成分质量比如下:聚四氟乙烯含量在30 ~
40% ;表面活性剂0.5 ~ 0. 8%、余量为无离子水和基布。
聚四氟乙烯玻璃纤维透气漆布的基布经向和纬向密度为:200 根/10 厘米
(±10%),厚度:0.04 毫米~ 0.06 毫米,幅宽:900 ~ 1000 毫米的无碱玻璃布。
优选地,各成分质量比如下:聚四氟乙烯含量在35% ;表面活性剂0.65%、余量为无
离子水和经向和纬向密度为:200 根/10 厘米,厚度:0.05 毫米,幅宽:950 毫米的无碱玻璃布。
聚四氟乙烯玻璃纤维透气漆布的厚度:0.05 毫米~ 0.07 毫米,幅宽:900 ~ 1000
毫米,该聚四氟乙烯玻璃纤维透气漆布厚度均匀,表面无气泡、含胶量均匀。
聚四氟乙烯玻璃纤维透气漆布的透气率:50Pa 时大于200mm/s、200pa 时大于
500mm/s。,他脾气效果好,是一种高性能、多用途的高分子复合材料。
Claims (5)
1.一种聚四氟乙烯玻璃纤维透气漆布配方,其特征在于:各成分质量比如下:聚四氟
乙烯含量在30 ~ 40% ;表面活性剂0.5 ~ 0. 8%、余量为无离子水和基布。
2.根据权利要求1 所述的一种聚四氟乙烯玻璃纤维透气漆布配方,其特征在于:聚四氟
乙烯玻璃纤维透气漆布的基布经向和纬向密度为:200 根/10 厘米(±10%),厚度:0.04 毫米~ 0.06 毫米,幅宽:900 ~ 1000 毫米的无碱玻璃布。
3.根据权利要求1 所述的一种聚四氟乙烯玻璃纤维透气漆布配方,其特征在于:优选质量比如下:聚四氟乙烯含量在35% ;表面活性剂0.65%、余量为无离子水和经向和纬向密度为:200 根/10 厘米,厚度:0.05 毫米,幅宽:950 毫米的无碱玻璃布。
4.根据权利要求1、2、3 所述的聚四氟乙烯玻璃纤维透气漆布配方制得的聚四氟乙烯
玻璃纤维透气漆布,其特征在于,聚四氟乙烯玻璃纤维透气漆布厚度:0.05 毫米~ 0.07 毫米,幅宽:900 ~ 1000 毫米。
5.根据权利要求1、2、3 所述聚四氟乙烯玻璃纤维透气漆布配方制得的聚四氟乙烯玻璃纤维透气漆布,其特征在于:聚四氟乙烯玻璃纤维透气漆布的透气率:50Pa 时大于
200mm/s、200pa 时大于500mm/s。