CN104926269A - Wash basin made of burn-free ceramic and preparation method of wash basin - Google Patents
Wash basin made of burn-free ceramic and preparation method of wash basin Download PDFInfo
- Publication number
- CN104926269A CN104926269A CN201510377776.XA CN201510377776A CN104926269A CN 104926269 A CN104926269 A CN 104926269A CN 201510377776 A CN201510377776 A CN 201510377776A CN 104926269 A CN104926269 A CN 104926269A
- Authority
- CN
- China
- Prior art keywords
- wash basin
- free ceramic
- preparation
- washbowl
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a wash basin made of burn-free ceramic and a preparation method of the wash basin. The wash basin made of the burn-free ceramic, disclosed by the invention, comprises the following components in percentage by weight: 40%-55% of magnesium oxide, 41%-50% of sodium chloride, 3%-6% of talcum powder, 2%-4% of quartz powder, 0.1%-0.2% of glass fibers and 2%-4% of rubberlith. According to the wash basin made of the burn-free ceramic and the preparation method of the wash basin, disclosed by the invention, the wash basin is manufactured by inorganic materials by adopting a scientific formula and has the advantages that the water basin can be solidified at normal atmospheric temperature, is energy-saving and environment-friendly, is simple in fabrication process, is high in strength, is light in weight, is not frangible, is high in plasticity, shortens the production cycle of ceramic products, improves the production efficiency, and has the function of radiation resistance. The wash basin products release negative oxygen ions unvaryingly.
Description
Technical field
The present invention relates to a kind of ceramic washbasin and preparation method thereof, washbowl of especially a kind of baking-free ceramic and preparation method thereof.
Background technology
Traditional pottery washbowl product are first through idiosome processing, then form through stove high-temperature calcination, and product has the deficiencies such as waste resource, contaminate environment, product are heavy, frangible.
Baking-free ceramic washbowl in the market, based on traditional ceramics goods, by the calcining finished product that fetches earth, causes huge pollution to environment in making processes, causes soil erosion and atmospheric pollution.
Summary of the invention
The invention provides washbowl of a kind of baking-free ceramic and preparation method thereof, energy-saving and emission-reduction, economize on resources, lightweight, intensity good, nontoxic, without obnoxious flavour, nonpollution environment, making is simple, cost is low, production efficiency is high.
Realize the washbowl of the baking-free ceramic of the object of the invention, comprise the composition of following part by weight:
Magnesium oxide: 40% ~ 55%;
Sodium-chlor: 41% ~ 50%;
Talcum powder: 3% ~ 6%;
Silica powder: 2% ~ 4%;
Glass fibre: 0.1% ~ 0.2%;
Zinc sulfide white: 2% ~ 4%.
Realize the preparation method of the washbowl of the baking-free ceramic of the object of the invention two, comprise the steps:
(1) the washbowl material of above-mentioned baking-free ceramic is carried out mix and blend;
(2) slurry be stirred is carried out in product mold whitewash and filling, remove mould after 24 hours, formed product;
(3) the unburned enamel priming paint of spary and finish paint is carried out at product surface.
The finish paint thickness of described step (3) is 1 ~ 2mm.
In described step (3) after the unburned enamel priming paint of spary and finish paint, air-dry 24 hours of product.
The beneficial effect of the washbowl of baking-free ceramic of the present invention and preparation method thereof is as follows:
Washbowl of baking-free ceramic of the present invention and preparation method thereof, utilizes inorganic materials to be made through scientific formula, has ambient cure, energy-conserving and environment-protective, manufacture craft is simple, product strength is high, lightweight, non-friable, plasticity-is strong; And shorten the production cycle of ceramic, improve production efficiency; The permanent releasing negative oxygen ion of product, has the advantages such as radiation proof function.
Embodiment
Embodiment 1
The washbowl of baking-free ceramic of the present invention, comprises the composition of following part by weight:
Magnesium oxide: 40%;
Sodium-chlor: 50%;
Talcum powder: 5.9%;
Silica powder: 2%;
Glass fibre: 0.1%;
Zinc sulfide white: 2%.
Embodiment 2
The washbowl of baking-free ceramic of the present invention, comprises the composition of following part by weight:
Magnesium oxide: 50.7%;
Sodium-chlor: 41%;
Talcum powder: 3%;
Silica powder: 2.1%;
Glass fibre: 0.2%;
Zinc sulfide white: 3%.
Embodiment 3
The washbowl of baking-free ceramic of the present invention, comprises the composition of following part by weight:
Magnesium oxide: 40.9%;
Sodium-chlor: 45%;
Talcum powder: 6%;
Silica powder: 4%;
Glass fibre: 0.1%;
Zinc sulfide white: 4%.
Washbowl of baking-free ceramic of the present invention and preparation method thereof, comprises the steps:
(1) the washbowl material of baking-free ceramic is carried out mix and blend;
(2) slurry be stirred is carried out in product mold whitewash and filling, remove mould after 24 hours, formed product;
(3) after product surface carries out the unburned enamel priming paint of spary and finish paint, air-dry 24 hours of product, finish paint thickness is 1 ~ 2mm.
Existing ceramic washbasin must form through calcining, the present invention utilizes magnesium oxide to combine with sodium-chlor, after fully reflecting, produce high-strength adhesive power, solve heavy, the frangible problem of product and permanent releasing negative oxygen ion can be produced by 100% chemistry reflection, there is the advantages such as radiation proof function.Product surface is through the spary of unburned ceramic glaze paint, play glittering and translucent, waterproof and dampproof effect, just the same through calcining the effect played with traditional ceramics, solve that traditional ceramics goods need to calcine, this problem of environmental pollution, owing to calcining, the present invention only needs 24 hours at shaping time, traditional burning ceramics needs 48 hours, so improve output.
The washbowl of baking-free ceramic of the present invention carries out test result according to regulation in magnesite art general technical specifications GB/T 17657-1999:
Surface halide accumulation resistance:
Being stood up by test specimen or hang into relative humidity is 90% ~ 95%, and temperature is in the thermostat container of 40 DEG C ± 2 DEG C.Enough intervals should be had, to ensure the circulation of air between test specimen.Take out after 72h and observe each surface of artwork.
Apparent density:
According in GB/T 17657-1999 4.2 regulation carry out, using the arithmetical av of 3 test specimens as measurement result, be accurately 0.1g/cm3.
Water-intake rate
Should under test conditions, according in B/T 17657-1999 4.6 regulation carry out, with using the arithmetical av of 3 test specimens as measurement result, be accurately 0.1%.
Water ratio
Should under test conditions, according in B/T 17657-1999 4.3 regulation carry out, with using the arithmetical av of 3 test specimens as measurement result, be accurately 0.1%.
Chlorion stripping quantity
The method that should specify by JG/T 301 free chlorine ion content is carried out.
Film adhesive
With sharp blade and scale steel ruler, cut in the direction in length and breadth of test specimen the cut channel that 11 stripe pitch are 1mm, cut channel intersects 100 pros in length and breadth.During cutting, blade face must be vertical with base plate, blade becomes 10 ° ~ 20 ° angles with bottom surface, firmly will will penetrate the surface of film to base material by evenly all otch, each sharp mouth of blade can only do single test to keep the sharp of blade, and the different sites of same test specimen does three tests.After cutting with banister brush gently along foursquare two diagonal lines each brush 5 times back and forth, and observe with 4 times of magnifying glasses and come off with or without grid, with the test-results that secondary is close, as final test-results.
Intensity
Adopt the actual slip of craft articles, cast, vibratory compaction 40mm × 40mm × 160mm prism test specimen 2 groups totally 6 pieces.Be 20 DEG C ± 5 DEG C in temperature, form removal after maintenance 1d in the indoor environment of relative humidity (60 ± 10) %, continues maintenance with this understanding afterwards to 28d, and wherein 1 group for measuring ultimate compression strength and folding strength, and measuring method carries out according to the regulation of GB/T 17657.
Coefficient of softening
Test specimen should temperature 20 DEG C ± 5 DEG C, maintenance 28d in the indoor environment of relative humidity (60 ± 10) %, test specimen is immersed in the water that temperature is (20 ± 5) DEG C, spacing between test specimen is not less than 20mm, the submerged depth of time upper surface and the water surface is not less than 20mm, take out after soaking 24h, wipe the moisture of surface of test piece with towel away.According to the regulation immersion folding strength below of GB/T 17671, the ratio of the folding strength before what the folding strength and 6.10 calculated after water inlet measured do not soak is test-results, is accurately 0.1.
Freezing and thawing test
At room temperature soak test specimen 24h, takes out and wipe swimming of surface, put into the Hanging Basket of the cryogenic freezing case being cooled to-20 DEG C ± 2 DEG C in advance, freezing 4h, takes out the clear water putting into 20 DEG C ± 5 DEG C, melts 4h, for once circulating.Multigelation 28 times, needs to dry before putting into cryogenic freezing case at every turn, observes the surface of test specimen with or without damaged, cracking phenomena.
Embodiment recited above is only be described the preferred embodiment of the present invention; not scope of the present invention is limited; do not departing under the present invention designs spiritual prerequisite; the various distortion that the common engineering technical personnel in this area make technical solution of the present invention and improvement, all should fall in protection domain that claims of the present invention determine.
Claims (4)
1. a washbowl for baking-free ceramic, comprises the composition of following part by weight:
Magnesium oxide: 40% ~ 55%;
Sodium-chlor: 41% ~ 50%;
Talcum powder: 3% ~ 6%;
Silica powder: 2% ~ 4%;
Glass fibre: 0.1% ~ 0.2%;
Zinc sulfide white: 2% ~ 4%.
2. a preparation method for the washbowl of baking-free ceramic according to claim 1, comprises the steps:
(1) the washbowl material of above-mentioned baking-free ceramic is carried out mix and blend;
(2) slurry be stirred is carried out in product mold whitewash and filling, remove mould after 24 hours, formed product;
(3) the unburned enamel priming paint of spary and finish paint is carried out at product surface.
3. the preparation method of the washbowl of baking-free ceramic according to claim 2, is characterized in that: the finish paint thickness of described step (3) is 1 ~ 2mm.
4. the preparation method of the washbowl of the baking-free ceramic according to Claims 2 or 3, is characterized in that: in described step (3) after the unburned enamel priming paint of spary and finish paint, air-dry 24 hours of product.