CN104912272A - Teflon fireproof self-cleaning wall cloth membrane material - Google Patents
Teflon fireproof self-cleaning wall cloth membrane material Download PDFInfo
- Publication number
- CN104912272A CN104912272A CN201510256360.2A CN201510256360A CN104912272A CN 104912272 A CN104912272 A CN 104912272A CN 201510256360 A CN201510256360 A CN 201510256360A CN 104912272 A CN104912272 A CN 104912272A
- Authority
- CN
- China
- Prior art keywords
- ptfe
- layer
- polytetrafluoroethylene
- teflon
- cleaning wall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a Teflon fireproof self-cleaning wall cloth membrane material, comprising a glass fiber cloth layer; each of the upper face and lower face of the glass fiber cloth layer is provided with a bottom layer and a Teflon layer from inside to outside; each bottom layer is formed by mixing and dipping a Teflon emulsion, a hydrophilic nanosilicon dioxide, an organic thickener and a silane coupling agent; the Teflon layer on the upper surface of the glass fiber cloth layer is coated with a surface layer which is formed by mixing and dipping the Teflon emulsion, BIO-PRUF, Nano-TiO2 and a dispersing agent; the Teflon layer on the lower surface of the glass fiber cloth layer is orderly coated with a PTFE (Polytetrafluoroethylene) surface treating agent, an environment friendly hybrid adhesive and a release paper layer. The width of the membrane material is 0.53-4.2m; the thickness is 0.13-0.35mm; the strength of extension (longitude/latitude) is not less than 4500/3800 (N/5cm); the peel strength is not less than 40/30 (N/5cm); and the fireproof self-cleaning wall cloth membrane material disclosed by the invention is integrated with architectonics, structural mechanics, fine chemical engineering and material science.
Description
Technical field
The present invention relates to a kind of decorative wall cloth film material, is that a kind of polytetrafluoroethylene (PTFE) is prevented fires self-cleaning wall paper film material specifically.
Background technology
Self-cleaning wall paper of preventing fires is a kind of Decorative watch facial mask material that in ornament materials, latest development is got up, particularly the requirement of structural fire protection to ornament materials is more and more higher, fireproof wall cloth application obtains swift and violent development, prevent fires self-cleaning wall paper with its fire prevention, antibacterial, waterproof, energy-saving and environmental protection, anti-aging, self-cleaning, daylighting, the excellent properties such as high-strength, easy for installation, be widely used in the public building furnishing fields such as aerodrome, high ferro, high-grade club, hospital, exhibition hall.But there is the shortcomings such as tensile strength is low, light transmittance is low, application life is short in the wallpaper generally used at present, PVC wallpaper decoration film material.
Summary of the invention
The self-cleaning wall paper film material that the object of the present invention is to provide that one is self-cleaning, antibacterial, high strength, light transmittance are high, polytetrafluoroethylene (PTFE) that is long service life is prevented fires.
The technical solution used in the present invention is: a kind of polytetrafluoroethylene (PTFE) is prevented fires self-cleaning wall paper film material, comprise fiberglass cloth, it is characterized in that: described fiberglass cloth upper, be equipped with bottom and polytetrafluoroethylene floor from inside to outside below, bottom is by ptfe emulsion, hydrophilic nano silica, organic thickening agent, silane coupler mixing dip-coating forms, polytetrafluoroethylene floor above fiberglass cloth is coated with surface course, surface course is by ptfe emulsion, BIO-PRUF, nano titanium oxide and dispersant dip-coating form, coated with PTFE surface treatment agent layer successively on polytetrafluoroethylene floor below fiberglass cloth, environment-friendly type mixes mucigel and off-style paper layer.
Further, described glass fabric layer thickness 0.08-0.8mm, underlayer thickness 0.02-0.1mm, polytetrafluoroethylene (PTFE) layer thickness 0.05-1.2mm; Surface layer thickness is 0.01-0.05mm; It is 0.05-0.1mm that blade coating environment-friendly type mixes viscose thickness.
Further, organic thickening agent is homopolymers or both mixtures formation of polyacrylate acrylic or methacrylic acid.
Further, described dispersing agent is mixtures of calgon or neopelex or one or more formations of PEG2000 or H5040.
Again further, described fiberglass cloth is the glass fabric after processing of singing.
The beneficial effect that the present invention reaches is: intermediate layer is fiberglass cloth, the adhesive power of polytetrafluoroethylene (PTFE) is improved after process of singing, bottom mixes by ptfe emulsion, hydrophilic nano silica, organic thickening agent, silane coupler the pliability that the bottom formed improves glass fabric, enhances PTFE to prevent fires the tensile strength of self-cleaning wall paper by polytetrafluoroethylene floor; Add nano titanium oxide in surface course, utilize its photo-catalysis function further to improve self-cleaning function; PTFE surface treatment agent layer increases prevent fires self-cleaning wall paper back side hydrophily and environment-friendly type of PTFE and mixes viscose adhesiveness; Back side blade coating environment-friendly type mixes mucigel, easy construction; Off-style paper layer, protection painting is scraped environment-friendly type and is mixed gummed surface.
The present invention has tension, tear-proof, antibacterial, self-cleaning, fire-retardant, ageing-resistant, smooth surface, the excellent properties such as reflecting sunlight, refraction photosensitiveness are good, long service life, its fabric width: 0.53-4.2m, thickness: 0.13-0.35mm, tensile strength (warp/latitude)≤4500/3800(N/5cm), Bao is from Qiang Du≤40/30(N/5cm), integrate the fire prevention self-cleaning wall paper decorating film material of architecture, structural mechanics, fine chemistry industry and material science.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention.
In figure: fiberglass cloth 1, bottom 2,3, polytetrafluoroethylene floor 4,5, surface course 6, PTFE surface treatment agent layer 7, environment-friendly type mixes mucigel 8, off-style paper layer 9.
Detailed description of the invention
Below in conjunction with accompanying drawing, the invention will be further described.
Shown in Fig. 1, a kind of polytetrafluoroethylene (PTFE) is prevented fires self-cleaning wall paper film material, comprise fiberglass cloth 1, fiberglass cloth 1 upper, be equipped with bottom 2 from inside to outside below, 3 and polytetrafluoroethylene floor 4, 5, bottom is by ptfe emulsion, hydrophilic nano silica, organic thickening agent, silane coupler mixing dip-coating forms, polytetrafluoroethylene floor above fiberglass cloth is coated with surface course 6, surface course is by ptfe emulsion, BIO-PRUF, nano titanium oxide and dispersant dip-coating form, coated with PTFE surface treatment agent layer 7 successively on polytetrafluoroethylene floor 5 below fiberglass cloth, environment-friendly type mixes mucigel 8 and off-style paper layer 9, described glass fabric layer thickness 0.08-0.8mm, underlayer thickness 0.02-0.1mm, polytetrafluoroethylene (PTFE) layer thickness 0.05-1.2mm, surface layer thickness is 0.01-0.05mm, it is 0.05-0.1mm that blade coating environment-friendly type mixes viscose thickness, described organic thickening agent is homopolymers or both mixtures formation of the acid of polyacrylate acrylic or methacrylic, described dispersing agent is mixtures of calgon or neopelex or one or more formations of PEG2000 or H5040, described fiberglass cloth is the glass fabric after processing of singing.
Claims (5)
1. a polytetrafluoroethylene (PTFE) is prevented fires self-cleaning wall paper film material, comprise fiberglass cloth, it is characterized in that: described fiberglass cloth upper, be equipped with bottom from inside to outside below, polytetrafluoroethylene floor, bottom is by ptfe emulsion, hydrophilic nano silica, organic thickening agent, silane coupler mixing dip-coating forms, polytetrafluoroethylene floor above fiberglass cloth is coated with surface course, surface course is by ptfe emulsion, BIO-PRUF, nano titanium oxide and dispersant dip-coating form, coated with PTFE surface treatment agent layer successively on polytetrafluoroethylene floor below fiberglass cloth, environment-friendly type mixes mucigel and off-style paper layer.
2. to prevent fires self-cleaning wall paper film material according to a kind of polytetrafluoroethylene (PTFE) described in claim 1, it is characterized in that: described glass fabric layer thickness 0.08-0.8mm, underlayer thickness 0.02-0.1mm, polytetrafluoroethylene (PTFE) layer thickness 0.05-1.2mm; Surface layer thickness is 0.01-0.05mm; It is 0.05-0.1mm that blade coating environment-friendly type mixes viscose thickness.
3. to prevent fires self-cleaning wall paper film material according to a kind of polytetrafluoroethylene (PTFE) described in claim 1, it is characterized in that: described organic thickening agent is that the homopolymers of polyacrylate acrylic or methacrylic acid or both mixtures are formed.
4. to prevent fires self-cleaning wall paper film material according to a kind of polytetrafluoroethylene (PTFE) described in claim 1, it is characterized in that: described dispersing agent is calgon or neopelex or one or more mixtures formed of PEG2000 or H5040.
5. to prevent fires self-cleaning wall paper film material according to a kind of polytetrafluoroethylene (PTFE) described in claim 1, it is characterized in that: described fiberglass cloth is the glass fabric of singing after process.