CN103924759A - Polyterafluoroethylene fireproof self-cleaning wall cloth film - Google Patents
Polyterafluoroethylene fireproof self-cleaning wall cloth film Download PDFInfo
- Publication number
- CN103924759A CN103924759A CN201410148424.2A CN201410148424A CN103924759A CN 103924759 A CN103924759 A CN 103924759A CN 201410148424 A CN201410148424 A CN 201410148424A CN 103924759 A CN103924759 A CN 103924759A
- Authority
- CN
- China
- Prior art keywords
- layer
- ptfe
- glass fiber
- polyterafluoroethylene
- polytetrafluoroethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a polyterafluoroethylene fireproof self-cleaning wall cloth film which comprises a glass fiber cloth layer. Base layers and polyterafluoroethylene layers are respectively arranged on the upper surface and the lower surface of the glass fiber cloth layer from the inside to the outside, polyterafluoroethylene emulsion, hydrophilic nanometer silicon dioxide, organic thickeners and silane coupling agents are mixed with one another and are subjected to dip-coating to form the base layers, a surface layer is coated on the polyterafluoroethylene layer on the upper surface of the glass fiber cloth layer, polyterafluoroethylene emulsion, BIO-PRUE, nanometer silicon dioxide and dispersing agents are mixed with one another and are subjected to dip-coating to form the surface layer, and a PTFE (polyterafluoroethylene) surface treating agent layer, an environment-friendly mixed adhesive layer and a release paper layer are sequentially coated on the polyterafluoroethylene layer on the lower surface of the glass fiber cloth layer. The polyterafluoroethylene fireproof self-cleaning wall cloth film has the advantages that the width of the film ranges from 0.53m to 4.2m, the thickness of the film ranges from 0.13mm to 0.35mm, the tensile strength (warp/weft) of the film is higher than or equal to 4500/3800(N/5cm), the peel strength of the film is higher than or equal to 40/30(N/5cm), and accordingly architecture, structural mechanics, fine chemicals and material science are integrated on the decorative fireproof self-cleaning wall cloth film.
Description
Technical field
The present invention relates to a kind of decorative wall cloth film material, is a kind of polytetrafluoroethylene (PTFE) self-cleaning wall paper film material of preventing fires specifically.
Background technology
The self-cleaning wall paper of preventing fires be in ornament materials
newlya kind of Decorative watch facial mask material growing up, particularly
structural fire protection pairthe requirement of ornament materials is more and more higher,
fire prevention wall paperapplication obtains swift and violent development,
prevent fires self-cleaning wall paper with its fire prevention,
antibacterial, waterproof, energy-saving and environmental protection, anti-aging, self-cleaning, daylighting, high-strength,
the excellent properties such as easy for installation, is widely used in the public buildings such as aerodrome, high ferro, high-grade club, hospital, exhibition hall and decorates field.But there is the shortcomings such as tensile strength is low, light transmittance is low, application life is short in the wallpaper, the PVC wallpaper decoration film material that generally use at present.
Summary of the invention
The object of the present invention is to provide one self-cleaning, antibacterial, high strength, light transmittance polytetrafluoroethylene (PTFE) high, long service life the self-cleaning wall paper film material of preventing fires.
The technical solution used in the present invention is: a kind of polytetrafluoroethylene (PTFE) self-cleaning wall paper film material of preventing fires, comprise glass fiber layer of cloth, it is characterized in that: described glass fiber layer of cloth upper, be equipped with from inside to outside bottom and polytetrafluoroethylene floor below, bottom is by ptfe emulsion, hydrophilic nano silica, organic thickening agent, silane coupler mixing dip-coating forms, on polytetrafluoroethylene floor above glass fiber layer of cloth, be coated with surface course, surface course is by ptfe emulsion, BIO-PRUF, nano titanium oxide and dispersant dip-coating form, coated with PTFE surface conditioning agent layer successively on polytetrafluoroethylene floor below glass fiber layer of cloth, the mixed mucigel of environment-friendly type and off-style paper layer.
Further, described glass fiber ply gage 0.08-0.8mm, underlayer thickness 0.02-0.1mm, polytetrafluoroethylene (PTFE) layer thickness 0.05-1.2mm; Surface layer thickness is 0.01-0.05mm; The mixed viscose thickness of blade coating environment-friendly type is 0.05-0.1mm.
Further, organic thickening agent is homopolymers or both mixtures formation of polyacrylate acrylic or methacrylic acid.
Further, described dispersing agent is the mixture of calgon or neopelex or PEG2000 or one or more formations of H5040.
Again further, described glass fiber layer of cloth is the glass fabric after treatment of singing.
The beneficial effect that the present invention reaches is: intermediate layer is glass fiber layer of cloth, after processing through singing, improve the adhesive power of polytetrafluoroethylene (PTFE), bottom is mixed the bottom forming and is improved the pliability of glass fabric by ptfe emulsion, hydrophilic nano silica, organic thickening agent, silane coupler, strengthened PTFE by polytetrafluoroethylene floor
the self-cleaning wall paper of preventing firestensile strength; In surface course, add nano titanium oxide, utilize its photo-catalysis function further to improve self-cleaning function; PTFE surface conditioning agent layer increases the PTFE mixed viscose adhesiveness of self-cleaning wall paper back side hydrophily and environment-friendly type of preventing fires; Back side blade coating environment-friendly type is mixed mucigel, easy construction; Off-style paper layer, protection is coated with scrapes the mixed viscose of environment-friendly type surface.
The present invention has tension, tear-proof, antibacterial, self-cleaning, fire-retardant, ageing-resistant, smooth surface, reflect daylight, reflect the excellent properties such as photosensitiveness is good, long service life, its fabric width: 0.53-4.2m, thickness: 0.13-0.35mm, tensile strength (warp/latitude)≤4500/3800(N/5cm), Bao is from Qiang Du≤40/30(N/5cm), integrate architecture, structural mechanics, fine chemistry industry and material science
the self-cleaning wall paper of preventing firesdecorating film material.
Brief description of the drawings
Fig. 1 is structural representation of the present invention.
In figure: glass fiber layer of cloth 1,
bottom 2,3, polytetrafluoroethylene floor 4,5, surface course 6, PTFE surface conditioning agent layer 7, environment-friendly type is mixed mucigel 8, off-style paper layer 9.
Detailed description of the invention
Below in conjunction with accompanying drawing, the invention will be further described.
Shown in Fig. 1, a kind of polytetrafluoroethylene (PTFE) self-cleaning wall paper film material of preventing fires, comprises glass fiber layer of cloth 1, and all establish from inside to outside the above and below of glass fiber layer of cloth 1
there are bottom 2,3 and polytetrafluoroethylene floor 4,5, bottom is formed by ptfe emulsion, hydrophilic nano silica, organic thickening agent, silane coupler mixing dip-coating, on polytetrafluoroethylene floor above glass fiber layer of cloth, be coated with surface course 6, surface course is formed by ptfe emulsion, BIO-PRUF, nano titanium oxide and dispersant dip-coating, coated with PTFE surface conditioning agent layer 7, the mixed mucigel 8 of environment-friendly type and off-style paper layer 9 successively on the polytetrafluoroethylene floor 5 below glass fiber layer of cloth;described glass fiber ply gage 0.08-0.8mm, underlayer thickness 0.02-0.1mm, polytetrafluoroethylene (PTFE) layer thickness 0.05-1.2mm; Surface layer thickness is 0.01-0.05mm; The mixed viscose thickness of blade coating environment-friendly type is 0.05-0.1mm; Described organic thickening agent is that homopolymers or both mixtures of polyacrylate acrylic or methacrylic acid forms; Described dispersing agent is the mixture of calgon or neopelex or PEG2000 or one or more formations of H5040; Described glass fiber layer of cloth is the glass fabric after treatment of singing.
Claims (5)
1. the polytetrafluoroethylene (PTFE) self-cleaning wall paper film material of preventing fires, comprises glass fiber layer of cloth, it is characterized in that: the above and below of described glass fiber layer of cloth is equal from inside to outside
be provided with bottom, polytetrafluoroethylene floor,bottom is formed by ptfe emulsion, hydrophilic nano silica, organic thickening agent, silane coupler mixing dip-coating, on polytetrafluoroethylene floor above glass fiber layer of cloth, be coated with surface course, surface course is formed by ptfe emulsion, BIO-PRUF, nano titanium oxide and dispersant dip-coating, coated with PTFE surface conditioning agent layer, the mixed mucigel of environment-friendly type and off-style paper layer successively on the polytetrafluoroethylene floor below glass fiber layer of cloth.
2. a kind of polytetrafluoroethylene (PTFE) according to claim 1 self-cleaning wall paper film material of preventing fires, is characterized in that: described glass fiber ply gage 0.08-0.8mm, underlayer thickness 0.02-0.1mm, polytetrafluoroethylene (PTFE) layer thickness 0.05-1.2mm; Surface layer thickness is 0.01-0.05mm; The mixed viscose thickness of blade coating environment-friendly type is 0.05-0.1mm.
3. a kind of polytetrafluoroethylene (PTFE) according to claim 1 self-cleaning wall paper film material of preventing fires, is characterized in that: described organic thickening agent is
polyacrylate acrylic acid ormethacrylic acid
homopolymers or both mixtures form.
4. a kind of polytetrafluoroethylene (PTFE) according to claim 1 self-cleaning wall paper film material of preventing fires, is characterized in that: described dispersing agent is the mixture of calgon or neopelex or PEG2000 or one or more formations of H5040.
5. a kind of polytetrafluoroethylene (PTFE) according to claim 1 self-cleaning wall paper film material of preventing fires, is characterized in that: described glass fiber layer of cloth is the glass fabric after treatment of singing.