CN105058937A - Heat-insulation anticorrosive polytetrafluoroethylene membrane - Google Patents
Heat-insulation anticorrosive polytetrafluoroethylene membrane Download PDFInfo
- Publication number
- CN105058937A CN105058937A CN201510463856.7A CN201510463856A CN105058937A CN 105058937 A CN105058937 A CN 105058937A CN 201510463856 A CN201510463856 A CN 201510463856A CN 105058937 A CN105058937 A CN 105058937A
- Authority
- CN
- China
- Prior art keywords
- ptfe
- heat insulating
- polytetrafluoroethylene
- film material
- corrosion film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a heat-insulation anticorrosive polytetrafluoroethylene membrane. The thickness of the heat-insulation anticorrosive membrane is 0.34-0.80mm, and contains a four-layer structure sequentially comprising a fiber cloth, a bottom layer, a structure layer and a surface layer from inside to outside. The fiber cloth is one of a glass fiber woven cloth, a carbon fiber woven cloth, a basalt fiber woven cloth, an aramid fiber woven cloth and a polyimide fiber woven cloth, and the thickness of the fiber cloth is 0.18-0.30mm. The membrane can be used for making heat insulation sleeves of detachable pipelines, valves and other pipe fittings, mechanical devices and instruments, and can also be used for making heat insulation layer outer protection materials of the pipelines, valves and other pipe fittings, mechanical devices and instruments.
Description
Technical field
The invention belongs to field of material technology, be specifically related to a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material and preparation method thereof, be mainly used in detachable heat-insulation collet, pipeline, pipe fitting, the heat insulation external protective material of insulation of equipment.
Background technology
At the pipe fitting of cold and hot media flow as elbow, flange, valve, instrument, equipment such as the thermal part such as rubber and plastic extruder, injector, thermoelectricity nuclear steam turbine group can not adopt conventional heat preserving method, and use detachable muff, this muff is made up of heat insulation inner core and protective coat, protective coat generally adopts the fabric of glass fabric or glass fabric coating silicon rubber, glass fabric heat insulation effect is poor, intensity is low, non-watertight, glass fibre easily damages human body; Glass fabric coating silicon rubber fabric intensity is low, ageing-resistant performance and corrosion-resistant, easily get wet, be stained with oil, be stained with ash.On the pipeline of cold and hot media flow, usually need, on surface, insulation material is installed, effectively reduce heat loss.The protective layer that tradition uses mainly contains the materials such as fiberglass, plastics, aluminium alloy plate, corrosion resistant plate; such material mostly needs to customize in advance according to line size; inside also must arrange watertight composition, and manufacturing cost is high, transports, installs inconvenience, waterproof effect is poor, perishable; and its hardness is larger; after once mounting uses, be unfavorable for dismantling Reusability, and fiberglass, plastics loss of properties on aging; metal material is perishable, and service life is all lower.At present good solution is not yet proposed.
Summary of the invention
For the deficiencies in the prior art, the invention provides a kind of excellent performance, polytetrafluoroethylene (PTFE) heat insulating and corrosion film material easy to process and preparation method thereof.
The technical solution used in the present invention is: a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material, described heat insulating and corrosion film material thickness 0.34-0.80 ㎜, altogether containing four-layer structure, is followed successively by fiber cloth, bottom, structure sheaf, superficial layer from the inside to surface.
Further, described fiber cloth is any one in glass fiber textile cloth, carbon fiber textile cloth, basalt fibre woven fabric, aramid fiber woven fabric, polyimide fiber woven fabric, and fiber cloth thickness is 0.18-0.30 ㎜.
Further, described underlayer thickness is 0.05-0.15 ㎜, and bottom comprises PTFE emulsion 10-50%, coupling agent 0.2-1%, deionized water 49-89.8% by weight percentage.
Further, described coupling agent is silane coupling agent, titante coupling agent, aluminate coupling agent, one or more mixtures of Borate Ester as Coupling.
Further, described Laminate construction thickness is 0.10-0.30 ㎜, and structure sheaf comprises PTFE emulsion 80-90%, inorganic thickening agent 2-8%, organic thickening agent 1-5%, 4 microns of hollow glass micropearl 1-2%, pigment 0.5-2%, deionized water 1-15.5% by weight percentage.
Further, described inorganic thickening agent is silica, bentonite, alumina silicate, one or more mixtures of sepiolite.
Further, described organic thickening agent is polyacrylic.
Further, described surface layer thickness is 0.01-0.05 ㎜, and superficial layer comprises PTFE emulsion 90-95%, deionized water 5-10% by weight percentage.
A preparation method for polytetrafluoroethylene (PTFE) heat insulating and corrosion film material, comprises the following steps: (1) bottom preparation:
1. PTFE bottom dispersion liquid preparation, gets PTEE emulsion, coupling agent and deionized water, and low rate mixing is to even;
2. single-side impregnated process forms bottom, fiber cloth is entered in impregnating equipment with the linear velocity of 0.5-6 m/min, fiber cloth one side is immersed in bottom dispersion liquid flood, enter baking oven again, batch after being dried by one, two baking zones of baking oven successively, one district's bake out temperature is 80-120 DEG C, and two district's bake out temperatures are 100-240 DEG C, forms in the one side of fiber cloth the bottom that dipping thickness is 0.05-0.15 ㎜;
(2) structure sheaf preparation:
1. structure sheaf slurry preparation, gets inorganic thickening agent, 4 microns of hollow glass micropearls, pigment and deionized waters, and after rapid stirring is extremely even, added in PTFE emulsion, low rate mixing is even, leaves standstill 1 hour; Re-start low rate mixing, slowly add organic thickening agent simultaneously, place 1 hour after stirring, measurement viscosity is 0.5-2Pa.s;
2. one side coating processing forms structure sheaf, the fiber cloth of dipping bottom is entered in coating equipment with the linear velocity of 0.5-6 m/min, at bottom coated structure layer slurry, enter baking oven again, batch after being dried by one, two baking zones of baking oven successively, one district's bake out temperature is 100-150 DEG C, and two district's bake out temperatures are 120-280 DEG C, and fiber cloth bottom is formed the structure sheaf that thickness is 0.10-0.30 ㎜;
(3) superficial layer preparation:
1. PTFE superficial layer dispersion liquid preparation, gets PTEE emulsion and deionized water, and low rate mixing is to even;
2. single-side impregnated process forms superficial layer, to enter in impregnating equipment with the linear velocity of 1-8 m/min through the above-mentioned fiber cloth being coated with structure sheaf, the one side being coated with structure sheaf is immersed in superficial layer dispersion liquid flood, enter baking oven again, successively by one of baking oven, two, three baking zones batch after drying, one district's bake out temperature is 80-120 DEG C, two district's bake out temperatures are 100-240 DEG C, three district's bake out temperatures are 280-380 DEG C, fiber cloth structure sheaf is formed the superficial layer that dipping thickness is 0.01-0.05 ㎜, after impregnation surface layer, a high temperature sintering plasticizing finished product is polytetrafluoroethylene (PTFE) heat insulating and corrosion film material.
Again further, described PTFE emulsion solid content is 45-65%.
In polytetrafluoroethylene (PTFE) heat insulating and corrosion film material design process of the present invention, the mechanical property of material, thermodynamic property, water resistance are considered.The present invention, by adding coupling agent in PTFE bottom dispersion liquid, improves very thin and wetting effect that is PTFE resin, effectively improves the stripping performance of product; Adopt inorganic thickening agent and organic thickening agent with the use of, overcome excessive, the single organic thickening agent of single inorganic thickening agent addition and decompose the defect affecting properties of product at processing temperatures, inorganic thickening agent can also reduce product thermal conductivity factor, improves effect of heat insulation; PTFE superficial layer dispersion liquid adopts PTFE emulsion to add deionized water dilution, and ensure product surface compactness, good water-proof effect, surface smoothness is high; After dipping bottom, coated structure layer, do not carry out high temperature sintering plastify completely, and be in half plastifying state, a high temperature sintering plasticizing after impregnation surface layer, make ensure that structure sheaf intensity, make again structure sheaf there is microbubble structure, reduce thermal conductivity factor.The present invention, without the need to the process equipment of additional configuration complexity, only simply improves existing impregnating equipment and coating equipment.
Polytetrafluoroethylene (PTFE) heat insulating and corrosion film material through this method manufacture gives full play to polytetrafluoroethylplastic plastic king performance and fiber cloth strengthens synergy, and have high insulating effect, under normal temperature, thermal conductivity factor only has 0.025W/MK-0.055W/MK; High-low temperature resistant, high temperature resistant 280 DEG C, low temperature resistant negative 70 DEG C; Chemical stability is good, resistance to various chemical attack, and Anti-moth-eating is anti-mildew; Fire protection flame retarding, fire prevention A level-do not fire; Ageing-resistant performance is good, more than 20 years service life; Self-cleaning property is good, does not get wet, oily dirt free; Waterproof, be 118 degree with the contact angle of water, hydrophobicity is good; Intensity is high, and softness is flexible again, flexible wrapping, is easily cut into various shape.
The present invention has high-low temperature resistant, heat insulation, chemical stability is good, corrosion-resistant, fire protection flame retarding, Vermins-proof mildew-proof, ageing-resistant, uvioresistant, mechanical strength is high, waterproof, grease proofing, the feature such as there is self-cleaning function, softness, flexible, folding is flexible, can repeatedly dismantle, reuse, can be widely used in making pipe fitting, plant equipment, the instrument and meter thermal insulation separation hot jackets such as detachable pipeline, valve; Also can be used for the pipe fitting such as pipeline, valve, plant equipment, instrument and meter heat-insulation layer external protective material.
Detailed description of the invention
Below with reference to embodiment, the present invention is described in detail.
Embodiment one
(1) single-side impregnated process forms bottom.PTFE bottom dispersion liquid components by weight percentage: the PTFE emulsion 10% of solid content 60%, KH550 silane coupler 0.5%, deionized water 89.5%.Add in container by PTEE emulsion, silane coupler and deionized water, mixing speed 80 revs/min, is stirred to each component disperses even; PTFE bottom dispersion liquid is added in impregnating equipment hopper, again the glass fabric of thickness 0.2 ㎜ is wound on the power transmission shaft of impregnating equipment, then partly wrap on the dip roll in hopper, fiber cloth one side is contacted with PTFE bottom dispersion liquid and carries out single-side impregnated process, after controlling bottom dipping thickness by thickness dancer rools, enter baking oven, successively by one, two district of baking oven, 100 DEG C, baking oven design temperature first district, 220 DEG C, the secondth district, batch after baking oven removing moisture content and auxiliary agent with the linear velocity of 3.5 ms/min, bottom dipping thickness is 0.06 ㎜.(2) one side coating processing forms structure sheaf.Structure sheaf slurry components by weight percentage: PTFE emulsion 90%, silica 3%, water soluble acrylic acid thickener 2%, 4 microns of hollow glass micropearls 2%, water-based gray paint mill base 1%, deionized water 2%; Silica, 4 microns of hollow glass micropearls, water-based gray paint mill base and deionized waters are added in container, mixing speed 1000-2000 rev/min, stir 1 little after evenly, then add PTFE emulsion, mixing speed 80 revs/min, stir 0.5 hour and leave standstill after 1 hour, slowly add water soluble acrylic acid thickener while stirring, mixing speed 80 revs/min, be stirred to each component disperses evenly without sinking to the bottom, phenomenon of condensing, leave standstill 1 hour, viscosity is 1.4Pa.s; Structure sheaf slurry is added in coating equipment hopper, again the glass fabric of dipping bottom is wound on the power transmission shaft of coating equipment, adopt scraper or method of roll coating at bottom coated structure layer slurry, enter baking oven, successively by one, two district of baking oven, 120 DEG C, baking oven design temperature first district, 260 DEG C, the secondth district, batch after baking oven removing moisture content and auxiliary agent with the linear velocity of 3 ms/min, and structure sheaf dipping thickness is 0.2 ㎜.(3) single-side impregnated process forms superficial layer.PTFE superficial layer dispersion liquid components by weight percentage: PTFE emulsion 90%, deionized water 10%.Add in container by PTEE emulsion, deionized water, mixing speed 80 revs/min, is stirred to each component disperses even, PTFE superficial layer dispersion liquid is added in impregnating equipment hopper, again the glass fabric of coated structure layer is wound on the power transmission shaft of impregnating equipment, then partly wrap on the dip roll in hopper, fiber cloth structure sheaf one side is contacted with PTFE superficial layer dispersion liquid and carries out single-side impregnated process, after thickness dancer rools control table surface layer dipping thickness, enter baking oven, successively by one of baking oven, two, three districts, 100 DEG C, baking oven design temperature first district, second 240 DEG C, district, 3rd 360 DEG C, district, moisture content is removed through baking oven with the linear velocity of 3 ms/min, batch after auxiliary agent and sintering, inspection, superficial layer dipping thickness is 0.02 ㎜, finished product is polytetrafluoroethylene (PTFE) heat insulating and corrosion film material.
Embodiment two
(1) single-side impregnated process forms bottom.PTFE bottom dispersion liquid components by weight percentage: the PTFE emulsion 20% of solid content 60%, KH550 silane coupler 0.8%, JTW titanate coupling agent 1%, deionized water 78.2%.Add in container by PTEE emulsion, coupling agent and deionized water, mixing speed 80 revs/min, is stirred to each component disperses even; PTFE bottom dispersion liquid is added in impregnating equipment hopper, again the very thin cloth of plain weave carbon of thickness 0.2 ㎜ is wound on the power transmission shaft of impregnating equipment, then partly wrap on the dip roll in hopper, fiber cloth one side is contacted with PTFE bottom dispersion liquid and carries out single-side impregnated process, after controlling bottom dipping thickness by thickness dancer rools, enter baking oven, successively by one, two district of baking oven, 110 DEG C, baking oven design temperature first district, 240 DEG C, the secondth district, batch after baking oven removing moisture content and auxiliary agent with the linear velocity of 3 ms/min, bottom dipping thickness is 0.04 ㎜.(2) one side coating processing forms structure sheaf.Structure sheaf slurry components by weight percentage: PTFE emulsion 85%, silica 1 %, sepiolite 3%, water soluble acrylic acid thickener 1%, 4 microns of hollow glass micropearls 1%, aqueous white dispersible pigment color paste 0.5%, deionized waters 8.5%; Silica, sepiolite, 4 microns of hollow glass micropearls, aqueous white dispersible pigment color paste and deionized waters are added in container, mixing speed 1000-2000 rev/min, stir 1 little after evenly, then add PTFE emulsion, mixing speed 80 revs/min, stir 0.5 hour and leave standstill after 1 hour, slowly add water soluble acrylic acid thickener while stirring, mixing speed 80 revs/min, be stirred to each component disperses evenly without sinking to the bottom, phenomenon of condensing, leave standstill 1 hour, viscosity is 1.8Pa.s; Structure sheaf slurry is added in coating equipment hopper, again the fiber cloth of dipping bottom is wound on the power transmission shaft of coating equipment, adopt scraper or method of roll coating at bottom coated structure layer slurry, enter baking oven, successively by one, two district of baking oven, 150 DEG C, baking oven design temperature first district, 280 DEG C, the secondth district, batch after baking oven removing moisture content and auxiliary agent with the linear velocity of 4 ms/min, and structure sheaf dipping thickness is 0.18 ㎜.(3) single-side impregnated process forms superficial layer.PTFE superficial layer dispersion liquid components by weight percentage: PTFE emulsion 90%, deionized water 10%.Add in container by PTEE emulsion, deionized water, mixing speed 80 revs/min, is stirred to each component disperses even, PTFE superficial layer dispersion liquid is added in impregnating equipment hopper, again the fiber cloth of coated structure layer is wound on the power transmission shaft of impregnating equipment, then partly wrap on the dip roll in hopper, fiber cloth structure sheaf one side is contacted with PTFE superficial layer dispersion liquid and carries out single-side impregnated process, after thickness dancer rools control table surface layer dipping thickness, enter baking oven, successively by one of baking oven, two, three districts, 90 DEG C, baking oven design temperature first district, second 220 DEG C, district, 3rd 380 DEG C, district, moisture content is removed through baking oven with the linear velocity of 4 ms/min, batch after auxiliary agent and sintering, inspection, superficial layer dipping thickness is 0.03 ㎜, finished product is polytetrafluoroethylene (PTFE) heat insulating and corrosion film material.Embodiment three
(1) single-side impregnated process forms bottom.PTFE bottom dispersion liquid components by weight percentage: the PTFE emulsion 25% of solid content 60%, KH550 silane coupler 0.2%, JTW18 aluminate coupling agent 0.3%, deionized water 74.5%.Add in container by PTEE emulsion, coupling agent and deionized water, mixing speed 80 revs/min, is stirred to each component disperses even; PTFE bottom dispersion liquid is added in impregnating equipment hopper, again the glass fabric of thickness 0.25 ㎜ is wound on the power transmission shaft of impregnating equipment, then partly wrap on the dip roll in hopper, fiber cloth one side is contacted with PTFE bottom dispersion liquid and carries out single-side impregnated process, after controlling bottom dipping thickness by thickness dancer rools, enter baking oven, successively by one, two district of baking oven, 110 DEG C, baking oven design temperature first district, 235 DEG C, the secondth district, batch after baking oven removing moisture content and auxiliary agent with the linear velocity of 4 ms/min, bottom dipping thickness is 0.08 ㎜.(2) one side coating processing forms structure sheaf.Structure sheaf slurry components by weight percentage: PTFE emulsion 80%, bentonite 4%, alumina silicate 2%, water soluble acrylic acid thickener 3%, 4 microns of hollow glass micropearls 1%, water-based gray paint mill base 1%, deionized water 9%; Bentonite, alumina silicate, 4 microns of hollow glass micropearls, water-based gray paint mill base and deionized waters are added in container, mixing speed 1000-2000 rev/min, stir 1 little after evenly, then add PTFE emulsion, mixing speed 80 revs/min, stir 0.5 hour and leave standstill after 1 hour, slowly add water soluble acrylic acid thickener while stirring, mixing speed 80 revs/min, be stirred to each component disperses evenly without sinking to the bottom, phenomenon of condensing, leave standstill 1 hour, viscosity is 1.55Pa.s; Structure sheaf slurry is added in coating equipment hopper, again the glass fabric of dipping bottom is wound on the power transmission shaft of coating equipment, adopt scraper or method of roll coating at bottom coated structure layer slurry, enter baking oven, successively by one, two district of baking oven, 130 DEG C, baking oven design temperature first district, 280 DEG C, the secondth district, batch after baking oven removing moisture content and auxiliary agent with the linear velocity of 3 ms/min, and structure sheaf dipping thickness is 0.25 ㎜.(3) single-side impregnated process forms superficial layer.PTFE superficial layer dispersion liquid components by weight percentage: PTFE emulsion 95%, deionized water 5%.Add in container by PTEE emulsion, deionized water, mixing speed 80 revs/min, is stirred to each component disperses even, PTFE superficial layer dispersion liquid is added in impregnating equipment hopper, again the glass fabric of coated structure layer is wound on the power transmission shaft of impregnating equipment, then partly wrap on the dip roll in hopper, fiber cloth structure sheaf one side is contacted with PTFE superficial layer dispersion liquid and carries out single-side impregnated process, after thickness dancer rools control table surface layer dipping thickness, enter baking oven, successively by one of baking oven, two, three districts, 100 DEG C, baking oven design temperature first district, second 220 DEG C, district, 3rd 380 DEG C, district, moisture content is removed through baking oven with the linear velocity of 4 ms/min, batch after auxiliary agent and sintering, inspection, superficial layer dipping thickness is 0.02 ㎜, finished product is polytetrafluoroethylene (PTFE) heat insulating and corrosion film material.
After tested, by embodiment one, embodiment two, embodiment three manufacture polytetrafluoroethylene (PTFE) heat insulating and corrosion film material index as following table:
Patent application protection domain of the present invention is not limited to the embodiment provided.
Claims (8)
1. a polytetrafluoroethylene (PTFE) heat insulating and corrosion film material, is characterized in that: described heat insulating and corrosion film material thickness 0.34-0.80 ㎜, altogether containing four-layer structure, is followed successively by fiber cloth, bottom, structure sheaf, superficial layer from the inside to surface.
2. a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material according to claim 1, it is characterized in that: described fiber cloth is any one in glass fiber textile cloth, carbon fiber textile cloth, basalt fibre woven fabric, aramid fiber woven fabric, polyimide fiber woven fabric, and fiber cloth thickness is 0.18-0.30 ㎜.
3. a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material according to claim 1, it is characterized in that: described underlayer thickness is 0.05-0.15 ㎜, bottom comprises PTFE emulsion 10-50%, coupling agent 0.2-1%, deionized water 49-89.8% by weight percentage.
4. a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material according to claim 3, is characterized in that: described coupling agent is silane coupling agent, titante coupling agent, aluminate coupling agent, one or more mixtures of Borate Ester as Coupling.
5. a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material according to claim 1, it is characterized in that: described Laminate construction thickness is 0.10-0.30 ㎜, structure sheaf comprises PTFE emulsion 80-90%, inorganic thickening agent 2-8%, organic thickening agent 1-5%, 4 microns of hollow glass micropearl 1-2%, pigment 0.5-2%, deionized water 1-15.5% by weight percentage.
6. a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material according to claim 5, is characterized in that: described inorganic thickening agent is silica, bentonite, alumina silicate, one or more mixtures of sepiolite.
7. a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material according to claim 5, is characterized in that: described organic thickening agent is polyacrylic.
8. a kind of polytetrafluoroethylene (PTFE) heat insulating and corrosion film material according to claim 1, is characterized in that: described surface layer thickness is 0.01-0.05 ㎜, and superficial layer comprises PTFE emulsion 90-95%, deionized water 5-10% by weight percentage.