CN205890049U - Compound color painted steel strip of two -sided PCM - Google Patents
Compound color painted steel strip of two -sided PCM Download PDFInfo
- Publication number
- CN205890049U CN205890049U CN201620906851.7U CN201620906851U CN205890049U CN 205890049 U CN205890049 U CN 205890049U CN 201620906851 U CN201620906851 U CN 201620906851U CN 205890049 U CN205890049 U CN 205890049U
- Authority
- CN
- China
- Prior art keywords
- steel plate
- steel sheet
- parts
- layer
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a compound color painted steel strip of two -sided PCM, substrate include first steel sheet and second steel sheet, the back of first steel sheet, second steel sheet is equipped with engaged with interlock tooth, the junction coating of first steel sheet, second steel sheet has the adhesive linkage, the front of first steel sheet, second steel sheet coated respectively first priming paint layer, second priming paint layer, it has first finish paint layer, second finish paint layer to coat respectively on first priming paint layer, the second priming paint layer. The utility model discloses having organic polymer and sheet metal substrate advantage between them concurrently, having fine temperature resistant, resistantly wait, acidproof, alkaline -resisting, can resist strong ultraviolet photolysis, coating loss when having reduced the application has reduced the pollution to the environment, makes production process optimization: environmental protection, low carbon can two -sidedly use to reduce and synthesize manufacturing cost, be fit for as various decorations, decoration and household appliances.
Description
Technical field
This utility model is related to composite board technical field, the composite coloured coated steel sheet of more particularly, to a kind of two-sided pcm.
Background technology
Application ratio in industry and life for the various steel plates is wide, such as automobile, refrigerator, washing machine, top-grade furniture, kitchen
Equipment, industry and civil buildings etc. are required for using, but in use, can only using wherein one side, another side attractive in appearance
Property has much room for improvement, and its weatherability, thermostability, lower temperature resistance, chemical proofing are all not satisfactory.The application of nanotechnology
It is the mark of world technology, nanotechnology, in the application of coating industry and development, promotes coating to update, is that coating becomes true
Positive Green Product has started breakthrough new era.Nano paint has been identified as the special of Olympic Village's architectural engineering
With product, show using value in building field for the nano paint, the unique physics of nano material, chemistry, biological nature
Development for paint field provides new opportunity.
Utility model content
The purpose of this utility model is to solve shortcoming present in prior art, and a kind of two-sided pcm proposing is multiple
Close color painted steel strip.
To achieve these goals, this utility model adopts the technical scheme that
A kind of composite coloured coated steel sheet of two-sided pcm, base material includes the first steel plate and the second steel plate, described first steel plate,
The back side of the second steel plate is provided with the tooth engaged being meshed, and described first steel plate, the junction of the second steel plate are coated with adhesive linkage, institute
State the first steel plate, the front of the second steel plate has been respectively coated with the first prime coat, the second prime coat, described first prime coat, second
First top coat layer, the second top coat layer have been respectively coated with prime coat.
Preferably, described first steel plate, the front of the second steel plate are respectively formed with first surface process layer, at second surface
Reason layer, described first surface process layer is coated with the first prime coat, described second surface process layer is coated with the second priming paint
Layer.
Preferably, described first top coat layer, be covered with the first protection film layer, the second protection film layer respectively on the second top coat layer.
Preferably, the coating that the first described top coat layer, the second top coat layer are used, its raw material includes by weight: poly-
20～40 parts of carbamate resins, 20～40 parts of acrylic resin, 4～8 parts of pigment, 0.5～2 part of diluent, drier 1～
2 parts, 0.5～2 part of set agent, 0.4～1 part of levelling agent, 1～3 part of defoamer, 1～3 part of stabilizer, 2～4 parts of filler, nanometer
1～2 part of zinc oxide, 1～2 part of nano-calcium carbonate, 1～2 part of nano-sized iron oxide, 15～35 parts of water.
Preferably, the coating that the first described top coat layer, the second top coat layer are used, its raw material includes by weight: poly-
25～35 parts of carbamate resins, 25～35 parts of acrylic resin, 6～7 parts of pigment, 1～1.5 part of diluent, drier 1.2
～1.8 parts, 0.8～1.8 part of set agent, 0.6～0.8 part of levelling agent, 1.5～2.5 parts of defoamer, 1.5～2.5 parts of stabilizer,
2.5～3.5 parts of filler, 1.2～1.8 parts of nano zine oxide, 1.2～1.8 parts of nano-calcium carbonate, nano-sized iron oxide 1.2～1.8
Part, 20～30 parts of water.
Preferably, the coating that the first described top coat layer, the second top coat layer are used, its raw material includes by weight: poly-
30 parts of carbamate resins, 30 parts of acrylic resin, 6.5 parts of pigment, 1.2 parts of diluent, 1.5 parts of drier, set agent 1.2
Part, 0.7 part of levelling agent, 2 parts of defoamer, 2 parts of stabilizer, 3 parts of filler, 1.5 parts of nano zine oxide, 1.5 parts of nano-calcium carbonate,
1.5 parts of nano-sized iron oxide, 25 parts of water.
Preferably, described diluent is acetone, butanone, Ketohexamethylene, benzene,toluene,xylene, n-butyl alcohol, styrene, vinegar
One or more of acetoacetic ester, methanol, ethanol, ethylene glycol, butyl glycol ether.
Preferably, described drier adopts rare earth drier, is formed with liquid carboxylic acid with rare earth chloride.
Preferably, described set agent is vinyl triamine, and described levelling agent is esters of acrylic acid levelling agent, described defoamer
For polypropylene glycerol aether, described stabilizer is zinc stearate.
Preferably, described set agent is vinyl triamine, and described levelling agent is esters of acrylic acid levelling agent, described filler
Including precipitated calcium carbonate, Pulvis Talci, wollastonite, Kaolin, barite, mica powder, melamine phosphate.
In this utility model, the composite coloured coated steel sheet of two-sided pcm has the excellent of organic polymer and thin plate base material concurrently
Point, the good coloring of existing organic polymer, mouldability, corrosion resistance, dicoration have high intensity and the easy processing of thin plate again
Property, can easily carry out being punched, bend, deep-draw, the processing such as welding, it is excellent that this just makes the product that this composite is made have
Practicality, dicoration, processability, durability, and the first steel plate, the second steel plate are made using the structure that tooth engaged is meshed
The composite coloured coated steel sheet of pcm is two-sided available, and is detachably used alone, and the nano zine oxide of particle diameter 60nm is to wavelength 300-
The ultraviolet of 400nm has the scattering process of good absorption, as the age-inhibiting addition of coating, and can improve antioxidation
Performance, has anti-microbial property, nano-calcium carbonate as loading pigment, have the advantages that exquisiteness, uniformly, whiteness high, strengthen
The transparency of coating, thixotropy and levelability, increase the thermal insulation of coating, and nano-sized iron oxide can have well as pigment
Heatproof, weather-proof, acidproof, alkaline-resisting and brilliant idea colourity, the strong premium properties absorbing ultraviolet, can resist intense UV rays
Photolysises, reduce coating loss during application, decrease the pollution to environment, make production process optimization: environmental protection, low-carbon (LC),
Two-sided can use, and reduce comprehensive production cost, be suitable as various decorations, decoration and household appliances.
Brief description
Fig. 1 be the utility model proposes the composite coloured coated steel sheet of a kind of two-sided pcm structural representation.
In figure: 1 first steel plate, 2 second steel plates, 3 tooth engaged, 4 first prime coats, 5 second prime coats, 6 first top coat layers,
7 second top coat layers, 8 first surface process layers, 9 second surface process layers, 10 first protection film layers, 11 second protection film layers.
Specific embodiment
Below in conjunction with the accompanying drawing in this utility model embodiment, the technical scheme in this utility model embodiment is carried out
Clearly and completely description is it is clear that described embodiment is only a part of embodiment of this utility model rather than whole
Embodiment.
Embodiment one:
With reference to Fig. 1, a kind of composite coloured coated steel sheet of two-sided pcm, base material includes the first steel plate 1 and the second steel plate 2, and first
Steel plate 1, the back side of the second steel plate 2 are provided with the tooth engaged 3 being meshed, and the first steel plate 1, the junction of the second steel plate 2 are coated with viscous
Connect layer, the first steel plate 1, the front of the second steel plate 2 have been respectively coated with the first prime coat 4, the second prime coat 5, the first prime coat 4,
First top coat layer 6, the second top coat layer 7, the first steel plate 1, the front difference of the second steel plate 2 have been respectively coated with the second prime coat 5
It is formed with first surface process layer 8, second surface process layer 9, first surface process layer 8 is coated with the first prime coat 4, second
Second prime coat 5 is coated with surface-treated layer 9, the first top coat layer 6, the second top coat layer 7 are covered with the first protection film layer respectively
10th, the second protection film layer 11.
The coating that described the first top coat layer 6, the second top coat layer 7 are used, its raw material includes by weight: poly- amino first
20 parts of acid ester resin, 20 parts of acrylic resin, 4 parts of pigment, 0.5 part of diluent, 1 part of drier, 0.5 part of set agent, levelling agent
0.4 part, 1 part of defoamer, 1 part of stabilizer, 2 parts of filler, 1 part of nano zine oxide, 1 part of nano-calcium carbonate, nano-sized iron oxide 1
Part, 15 parts of water.
Diluent is acetone, butanone, Ketohexamethylene, benzene,toluene,xylene, n-butyl alcohol, styrene, ethyl acetate, first
Alcohol, ethanol, ethylene glycol, drier adopts rare earth drier, is formed, set with liquid carboxylic acid with rare earth chloride
Agent is vinyl triamine, and levelling agent is esters of acrylic acid levelling agent, and defoamer is polypropylene glycerol aether, and stabilizer is stearic acid
Zinc, filler includes precipitated calcium carbonate, Pulvis Talci, wollastonite, Kaolin, barite, mica powder, melamine phosphate.
Embodiment two:
With reference to Fig. 1, a kind of composite coloured coated steel sheet of two-sided pcm, base material includes the first steel plate 1 and the second steel plate 2, and first
Steel plate 1, the back side of the second steel plate 2 are provided with the tooth engaged 3 being meshed, and the first steel plate 1, the junction of the second steel plate 2 are coated with viscous
Connect layer, the first steel plate 1, the front of the second steel plate 2 have been respectively coated with the first prime coat 4, the second prime coat 5, the first prime coat 4,
First top coat layer 6, the second top coat layer 7, the first steel plate 1, the front difference of the second steel plate 2 have been respectively coated with the second prime coat 5
It is formed with first surface process layer 8, second surface process layer 9, first surface process layer 8 is coated with the first prime coat 4, second
Second prime coat 5 is coated with surface-treated layer 9, the first top coat layer 6, the second top coat layer 7 are covered with the first protection film layer respectively
10th, the second protection film layer 11.
The coating that described the first top coat layer 6, the second top coat layer 7 are used, its raw material includes by weight: poly- amino first
25 parts of acid ester resin, 25 parts of acrylic resin, 6 parts of pigment, 1 part of diluent, 1.2 parts of drier, 0.8 part of set agent, levelling agent
0.6 part, 1.5 parts of defoamer, 1.5 parts of stabilizer, 2.5 parts of filler, 1.2 parts of nano zine oxide, 1.2 parts of nano-calcium carbonate, receive
1.2 parts of ferrum oxide of rice, 20 parts of water.
Diluent is acetone, butanone, Ketohexamethylene, benzene,toluene,xylene, n-butyl alcohol, styrene, ethyl acetate, first
One or more of alcohol, ethanol, ethylene glycol, butyl glycol ether, drier adopts rare earth drier, by liquid carboxylic
Acid is coordinated with rare earth chloride and is formed, and set agent is vinyl triamine, and levelling agent is esters of acrylic acid levelling agent, and defoamer is poly-
Oxypropylene glycerin ether, stabilizer is zinc stearate, and filler includes precipitated calcium carbonate, Pulvis Talci, wollastonite, Kaolin, weight crystalline substance
Stone, mica powder, melamine phosphate.
Embodiment three:
With reference to Fig. 1, a kind of composite coloured coated steel sheet of two-sided pcm, base material includes the first steel plate 1 and the second steel plate 2, and first
Steel plate 1, the back side of the second steel plate 2 are provided with the tooth engaged 3 being meshed, and the first steel plate 1, the junction of the second steel plate 2 are coated with viscous
Connect layer, the first steel plate 1, the front of the second steel plate 2 have been respectively coated with the first prime coat 4, the second prime coat 5, the first prime coat 4,
First top coat layer 6, the second top coat layer 7, the first steel plate 1, the front difference of the second steel plate 2 have been respectively coated with the second prime coat 5
It is formed with first surface process layer 8, second surface process layer 9, first surface process layer 8 is coated with the first prime coat 4, second
Second prime coat 5 is coated with surface-treated layer 9, the first top coat layer 6, the second top coat layer 7 are covered with the first protection film layer respectively
10th, the second protection film layer 11.
The coating that described the first top coat layer 6, the second top coat layer 7 are used, its raw material includes by weight: poly- amino first
30 parts of acid ester resin, 30 parts of acrylic resin, 6.5 parts of pigment, 1.2 parts of diluent, 1.5 parts of drier, 1.2 parts of set agent, stream
0.7 part of flat agent, 2 parts of defoamer, 2 parts of stabilizer, 3 parts of filler, 1.5 parts of nano zine oxide, 1.5 parts of nano-calcium carbonate, nanometer
1.5 parts of ferrum oxide, 25 parts of water.
Diluent is acetone, butanone, Ketohexamethylene, benzene,toluene,xylene, n-butyl alcohol, styrene, ethyl acetate, first
One or more of alcohol, ethanol, ethylene glycol, butyl glycol ether, drier adopts rare earth drier, by liquid carboxylic
Acid is coordinated with rare earth chloride and is formed, and set agent is vinyl triamine, and levelling agent is esters of acrylic acid levelling agent, and defoamer is poly-
Oxypropylene glycerin ether, stabilizer is zinc stearate, and filler includes precipitated calcium carbonate, Pulvis Talci, wollastonite, Kaolin, weight crystalline substance
Stone, mica powder, melamine phosphate.
Example IV:
With reference to Fig. 1, a kind of composite coloured coated steel sheet of two-sided pcm, base material includes the first steel plate 1 and the second steel plate 2, and first
Steel plate 1, the back side of the second steel plate 2 are provided with the tooth engaged 3 being meshed, and the first steel plate 1, the junction of the second steel plate 2 are coated with viscous
Connect layer, the first steel plate 1, the front of the second steel plate 2 have been respectively coated with the first prime coat 4, the second prime coat 5, the first prime coat 4,
First top coat layer 6, the second top coat layer 7, the first steel plate 1, the front difference of the second steel plate 2 have been respectively coated with the second prime coat 5
It is formed with first surface process layer 8, second surface process layer 9, first surface process layer 8 is coated with the first prime coat 4, second
Second prime coat 5 is coated with surface-treated layer 9, the first top coat layer 6, the second top coat layer 7 are covered with the first protection film layer respectively
10th, the second protection film layer 11.
The coating that described the first top coat layer 6, the second top coat layer 7 are used, its raw material includes by weight: poly- amino first
35 parts of acid ester resin, 35 parts of acrylic resin, 7 parts of pigment, 1.5 parts of diluent, 1.8 parts of drier, 1.8 parts of set agent, levelling
0.8 part of agent, 2.5 parts of defoamer, 2.5 parts of stabilizer, 3.5 parts of filler, 1.8 parts of nano zine oxide, 1.8 parts of nano-calcium carbonate,
1.8 parts of nano-sized iron oxide, 30 parts of water.
Diluent is dimethylbenzene, and drier adopts rare earth drier, formed with liquid carboxylic acid with rare earth chloride, becomes
Determining agent is vinyl triamine, and levelling agent is esters of acrylic acid levelling agent, and defoamer is polypropylene glycerol aether, and stabilizer is Hard Fat
Sour zinc, filler includes precipitated calcium carbonate, Pulvis Talci, wollastonite, Kaolin, barite, mica powder, melamine phosphate.
Embodiment five:
With reference to Fig. 1, a kind of composite coloured coated steel sheet of two-sided pcm, base material includes the first steel plate 1 and the second steel plate 2, and first
Steel plate 1, the back side of the second steel plate 2 are provided with the tooth engaged 3 being meshed, and the first steel plate 1, the junction of the second steel plate 2 are coated with viscous
Connect layer, the first steel plate 1, the front of the second steel plate 2 have been respectively coated with the first prime coat 4, the second prime coat 5, the first prime coat 4,
First top coat layer 6, the second top coat layer 7, the first steel plate 1, the front difference of the second steel plate 2 have been respectively coated with the second prime coat 5
It is formed with first surface process layer 8, second surface process layer 9, first surface process layer 8 is coated with the first prime coat 4, second
Second prime coat 5 is coated with surface-treated layer 9, the first top coat layer 6, the second top coat layer 7 are covered with the first protection film layer respectively
10th, the second protection film layer 11.
The coating that described the first top coat layer 6, the second top coat layer 7 are used, its raw material includes by weight: poly- amino first
40 parts of acid ester resin, 40 parts of acrylic resin, 8 parts of pigment, 2 parts of diluent, 2 parts of drier, 2 parts of set agent, 1 part of levelling agent,
3 parts of defoamer, 3 parts of stabilizer, 4 parts of filler, 2 parts of nano zine oxide, 2 parts of nano-calcium carbonate, 2 parts of nano-sized iron oxide, water 35
Part.
Diluent be benzene,toluene,xylene, n-butyl alcohol, styrene, ethyl acetate, methanol, ethanol, ethylene glycol,
Butyl glycol ether, drier adopts rare earth drier, is formed with liquid carboxylic acid with rare earth chloride, and set agent is ethylene
Base triamine, levelling agent is esters of acrylic acid levelling agent, and defoamer is polypropylene glycerol aether, and stabilizer is zinc stearate, filling
Agent includes precipitated calcium carbonate, Pulvis Talci, wollastonite, Kaolin, barite, mica powder, melamine phosphate.
The composite coloured coated steel sheet of the two-sided pcm of this utility model has the advantage of organic polymer and thin plate base material concurrently,
The good coloring of existing organic polymer, mouldability, corrosion resistance, dicoration have high intensity and the workability of thin plate, energy again
Easily carry out being punched, bend, deep-draw, the processing such as welding, this just makes the product that this composite is made have excellent reality
With property, dicoration, processability, durability, and the first steel plate, the second steel plate make pcm multiple using the structure that tooth engaged is meshed
Close color painted steel strip two-sided available, and be detachably used alone, the nano zine oxide of particle diameter 60nm is to wavelength 300-400nm
Ultraviolet have the scattering process of good absorption, as the age-inhibiting addition of coating, and can improve antioxygenic property,
There is anti-microbial property, nano-calcium carbonate as loading pigment, have the advantages that exquisiteness, uniformly, whiteness high, strengthen coating
The transparency, thixotropy and levelability, increase the thermal insulation of coating, and nano-sized iron oxide can have good heatproof, resistance to as pigment
Time, acidproof, alkaline-resisting and brilliant idea colourity, the strong premium properties absorbing ultraviolet, can resist the photolysis of intense UV rays
With, reduce coating loss during application, decrease the pollution to environment, make production process optimization: environmental protection, low-carbon (LC), can be two-sided
Use, and reduce comprehensive production cost, be suitable as various decorations, decoration and household appliances.
The above, only this utility model preferably specific embodiment, but protection domain of the present utility model is not
Be confined to this, any those familiar with the art in the technical scope that this utility model discloses, according to this practicality
New technical scheme and its utility model design in addition equivalent or change, all should cover in protection model of the present utility model
Within enclosing.
Claims (3)
1. a kind of composite coloured coated steel sheet of two-sided pcm it is characterised in that: base material includes the first steel plate and the second steel plate, described
First steel plate, the back side of the second steel plate are provided with the tooth engaged being meshed, and described first steel plate, the junction of the second steel plate are coated with
Adhesive linkage, described first steel plate, the front of the second steel plate have been respectively coated with the first prime coat, the second prime coat, described first bottom
First top coat layer, the second top coat layer have been respectively coated with enamelled coating, the second prime coat.
2. a kind of composite coloured coated steel sheet of two-sided pcm according to claim 1 it is characterised in that: described first steel plate,
The front of the second steel plate is respectively formed with first surface process layer, second surface process layer, and described first surface process layer applies
It is covered with the first prime coat, described second surface process layer is coated with the second prime coat.
3. a kind of composite coloured coated steel sheet of two-sided pcm according to claim 1 it is characterised in that: described first finish paint
It is covered with the first protection film layer, the second protection film layer respectively on layer, the second top coat layer.