CN104910725A - Application method of nano antibacterial primer - Google Patents
Application method of nano antibacterial primer Download PDFInfo
- Publication number
- CN104910725A CN104910725A CN201510340230.7A CN201510340230A CN104910725A CN 104910725 A CN104910725 A CN 104910725A CN 201510340230 A CN201510340230 A CN 201510340230A CN 104910725 A CN104910725 A CN 104910725A
- Authority
- CN
- China
- Prior art keywords
- nano
- parts
- antibacterial
- priming paint
- nano antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a using method of a nano antibacterial primer, which comprises the steps of fully and uniformly stirring the nano antibacterial primer, adding a proper amount of diluent to dilute the nano antibacterial primer to the required viscosity by 20-30%, and coating 15-18 kg/m of nano antibacterial primer per liter by calculating a 50 mu m dry paint film2Then, drying for 15-25 minutes by self, and curing to obtain a coating; the nano antibacterial primer is prepared from 30-40 parts of modified acrylic resin, 10-20 parts of a nano antibacterial agent, 2-10 parts of titanium dioxide, 5-15 parts of a nano filler, 2-8 parts of a thickening agent, 3-9 parts of a film forming assistant, 3-12 parts of an anti-settling agent and 25-35 parts of deionized water. The paint film formed by the using method of the invention has strong and durable antibacterial performance and the bacteria killing rate reachesMore than 95 percent, low VOC content, no toxicity, no pollution and good weather resistance, and is suitable for the coating fields of houses, vehicles, ships and the like.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of using method of nano-antibacterial priming paint.
Background technology
In house ornamentation and building operation, on wall before brushing finish paint, preferably will be coated with priming, priming paint has good sticking power, makes metope more smooth.And the brushing of more convenient finish paint, improve construction quality, also save the usage quantity of finish paint, saved construction cost.
At present, priming paint is at building, vehicle, military affairs, decoration, shipbuilding industry consumption greatly, closely bound up with the life of people, but most priming paint itself does not have sterilization, antibacterial, easy breed bacteria, becomes the contagium of germ, affects HUMAN HEALTH.
Summary of the invention
The object of the invention is to the deficiency overcoming the existence of above-mentioned prior art, provide a kind of using method of nano-antibacterial priming paint, utilize using method of the present invention, the anti-microbial property excellence of the coating of preparation, good weatherability, VOC content are low.
For achieving the above object, the present invention is achieved by the following technical solutions:
A using method for nano-antibacterial priming paint, stirs nano-antibacterial priming paint, adds appropriate thinner 20 ~ 30% and is diluted to required viscosity, calculates often liter of nano-antibacterial prime 15 ~ 18kg/m with 50 μm of dry paints
2, then from dry 15 ~ 25 minutes, solidification obtains coating;
Described nano-antibacterial priming paint is made up of following raw material according to ratio of weight and number: acrylic resin modified 30 ~ 40 parts, nano antibacterial agent 10 ~ 20 parts, titanium dioxide 2 ~ 10 parts, Nano filling 5 ~ 15 parts, thickening material 2 ~ 8 parts, film coalescence aid 3 ~ 9 parts, anti-settling agent 3 ~ 12 parts, deionized water 25 ~ 35 parts.
Preferably, described acrylic resin modified be any one in organosilicon modified crylic acid resin, epoxy modified acrylic resin, polyester modification acrylic resin.
Preferably, described nano antibacterial agent is any one in nano titanium oxide, nanometer silver, nano-sized magnesium hydroxide.
Preferably, described Nano filling is any one in nano-calcium carbonate, nanomete talc powder, nano mica powder.
Preferably, described thickening material is any one in polyvinyl alcohol, polyvinylpyrrolidone, polyoxyethylene.
Preferably, described film coalescence aid is any one in propylene glycol monomethyl ether, dipropylene glycol propyl ether, alcohol ester 12.
Preferably, described anti-settling agent is any one in aerosil, polyolefin-wax, polyamide wax.
Beneficial effect of the present invention:
By the paint film that using method of the present invention is formed, anti-microbial property is strong and lasting, and bacterial inactivation rate reaches more than 95%, and VOC content is low, nontoxic, pollution-free, good weatherability, is applicable to the coating fields such as house, vehicle, boats and ships.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in detail.Following examples will contribute to those skilled in the art and understand the present invention further, but not limit the present invention in any form.It should be pointed out that to those skilled in the art, without departing from the inventive concept of the premise, some distortion and improvement can also be made.These all belong to protection scope of the present invention.
A kind of using method of nano-antibacterial priming paint: stirred by nano-antibacterial priming paint, adds appropriate thinner 20 ~ 30% and is diluted to required viscosity, calculates often liter of nano-antibacterial prime 15 ~ 18kg/m with 50 μm of dry paints
2, then from dry 15 ~ 25 minutes, solidification obtains coating;
Described nano-antibacterial priming paint is made up of following raw material according to ratio of weight and number: acrylic resin modified 30 ~ 40 parts, nano antibacterial agent 10 ~ 20 parts, titanium dioxide 2 ~ 10 parts, Nano filling 5 ~ 15 parts, thickening material 2 ~ 8 parts, film coalescence aid 3 ~ 9 parts, anti-settling agent 3 ~ 12 parts, deionized water 25 ~ 35 parts.
The using method of nano-antibacterial priming paint of the present invention, utilizes using method of the present invention, and the anti-microbial property excellence of the coating of preparation, good weatherability, VOC content are low.
Embodiment 1
The using method of nano-antibacterial priming paint of the present invention: stirred by nano-antibacterial priming paint, adds appropriate thinner 20% and is diluted to required viscosity, calculates often liter of nano-antibacterial prime 15kg/m with 50 μm of dry paints
2, then from dry 15 minutes, solidification obtains coating;
Nano-antibacterial priming paint is made up of following raw material according to ratio of weight and number: organosilicon modified crylic acid resin 40 parts, nano titanium oxide 10 parts, titanium dioxide 2 parts, nano-calcium carbonate 15 parts, polyvinyl alcohol 2 parts, propylene glycol monomethyl ether 9 parts, aerosil 3 parts, deionized water 25 parts.
Embodiment 2
The using method of nano-antibacterial priming paint of the present invention: stirred by nano-antibacterial priming paint, adds appropriate thinner 30% and is diluted to required viscosity, calculates often liter of nano-antibacterial prime 18kg/m with 50 μm of dry paints
2, then from dry 25 minutes, solidification obtains coating;
Nano-antibacterial priming paint is made up of following raw material according to ratio of weight and number: epoxy modified acrylic resin, polyester modification acrylic resin 30 parts, nanometer silver 20 parts, titanium dioxide 10 parts, nanomete talc powder 5 parts, polyvinylpyrrolidone 8 parts, dipropylene glycol propyl ether 3 parts, polyolefin-wax 12 parts, deionized water 35 parts.
Embodiment 3
The using method of nano-antibacterial priming paint of the present invention: stirred by nano-antibacterial priming paint, adds appropriate thinner 25% and is diluted to required viscosity, calculates often liter of nano-antibacterial prime 16kg/m with 50 μm of dry paints
2, then from dry 18 minutes, solidification obtains coating;
Nano-antibacterial priming paint is made up of following raw material according to ratio of weight and number: polyester modification acrylic resin 35 parts, nano-sized magnesium hydroxide 14 parts, titanium dioxide 6 parts, 9 parts, nano mica powder, polyoxyethylene 5 parts, alcohol ester 12 parts, polyamide wax 8 parts, deionized water 30 parts.
Embodiment 4
The using method of nano-antibacterial priming paint of the present invention: stirred by nano-antibacterial priming paint, adds appropriate thinner 22% and is diluted to required viscosity, calculates often liter of nano-antibacterial prime 18kg/m with 50 μm of dry paints
2, then from dry 22 minutes, solidification obtains coating;
Nano-antibacterial priming paint is made up of following raw material according to ratio of weight and number: organosilicon modified crylic acid resin 36 parts, nanometer silver 16 parts, titanium dioxide 10 parts, 8 parts, nano mica powder, polyoxyethylene 7 parts, alcohol ester 12 parts, aerosil 5 parts, deionized water 28 parts.
Performance test
Basic mechanical design feature of the present invention is as shown in Table 1 and Table 2:
Table 1
Table 2
From Table 1 and Table 2, the using method of nano-antibacterial priming paint of the present invention, utilizes using method of the present invention, and the anti-microbial property of the coating of preparation is excellent, and good weatherability, VOC content are low.
Above specific embodiments of the invention are described.It is to be appreciated that the present invention is not limited to above-mentioned particular implementation, those skilled in the art can make various distortion or amendment within the scope of the claims, and this does not affect flesh and blood of the present invention.
Claims (7)
1. a using method for nano-antibacterial priming paint, is characterized in that: stirred by nano-antibacterial priming paint, adds appropriate thinner 20 ~ 30% and is diluted to required viscosity, calculates often liter of nano-antibacterial prime 15 ~ 18kg/m with 50 μm of dry paints
2, then from dry 15 ~ 25 minutes, solidification obtains coating;
Described nano-antibacterial priming paint is made up of following raw material according to ratio of weight and number: acrylic resin modified 30 ~ 40 parts, nano antibacterial agent 10 ~ 20 parts, titanium dioxide 2 ~ 10 parts, Nano filling 5 ~ 15 parts, thickening material 2 ~ 8 parts, film coalescence aid 3 ~ 9 parts, anti-settling agent 3 ~ 12 parts, deionized water 25 ~ 35 parts.
2. the using method of nano-antibacterial priming paint according to claim 1, is characterized in that: described acrylic resin modified be organosilicon modified crylic acid resin, epoxy modified acrylic resin, any one in polyester modification acrylic resin.
3. the using method of nano-antibacterial priming paint according to claim 1, is characterized in that: described nano antibacterial agent is any one in nano titanium oxide, nanometer silver, nano-sized magnesium hydroxide.
4. the using method of nano-antibacterial priming paint according to claim 1, is characterized in that: described Nano filling is any one in nano-calcium carbonate, nanomete talc powder, nano mica powder.
5. the using method of nano-antibacterial priming paint according to claim 1, is characterized in that: described thickening material is any one in polyvinyl alcohol, polyvinylpyrrolidone, polyoxyethylene.
6. the using method of nano-antibacterial priming paint according to claim 1, is characterized in that: described film coalescence aid is any one in propylene glycol monomethyl ether, dipropylene glycol propyl ether, alcohol ester 12.
7. the using method of nano-antibacterial priming paint according to claim 1, is characterized in that: described anti-settling agent is any one in aerosil, polyolefin-wax, polyamide wax.