CN112756237A - Antibacterial furniture paint surface treatment method - Google Patents
Antibacterial furniture paint surface treatment method Download PDFInfo
- Publication number
- CN112756237A CN112756237A CN202011594346.0A CN202011594346A CN112756237A CN 112756237 A CN112756237 A CN 112756237A CN 202011594346 A CN202011594346 A CN 202011594346A CN 112756237 A CN112756237 A CN 112756237A
- Authority
- CN
- China
- Prior art keywords
- parts
- furniture material
- furniture
- antibacterial
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antibacterial furniture paint surface treatment method, which comprises the following steps: (1) polishing and smoothing the surface of the furniture material; (2) after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying; (3) and (3) polishing and smoothing the surface of the dried furniture material again, removing dust on the surface of the furniture material, spraying the antibacterial paint on the surface of the furniture material again, and drying. The furniture material manufactured by the method is nontoxic, has excellent antibacterial performance and lasting antibacterial effect, and is suitable for large-scale popularization and use.
Description
Technical Field
The invention relates to the technical field of coatings, in particular to an antibacterial furniture paint surface treatment method.
Background
Furniture refers to a large category of appliances and facilities essential for human beings to maintain normal life, engage in production practice and develop social activities. Furniture is continuously developed and innovated following the foot steps of the times, has various doors, different materials, complete varieties and different purposes, and is an important foundation for establishing working and living spaces. The furniture is composed of four factors of materials, structures, appearance forms and functions, wherein the functions are the leading factors and the power for promoting the development of the furniture; the structure is a main frame and is the basis for realizing the functions, and the four factors are mutually related and mutually restricted. Furniture also has material and appearance form factors, as it is designed and manufactured to meet certain material needs and use purposes. Common bacteria and viruses such as fungi, escherichia coli, golden grape balls, hepatitis B viruses and the like are easily bred or attached to the surfaces of some solid wood furniture, so that the surfaces of the furniture are mildewed, discolored and damaged by worms, the appearance performance and the service life of the solid wood furniture are influenced, meanwhile, diseases are propagated and transmitted by bacteria, the health of human bodies is threatened, and the furniture which is frequently contacted becomes a main transmission medium of the bacteria and the microorganisms.
Most of the existing wood furniture is coated with paint on the surface, which plays roles of water resistance, mildew resistance, bacterial proliferation inhibition and the like, and can also make the furniture look beautiful. The varnish used by many furniture is alkyd paint, but the alkyd paint has low drying speed, limited antibacterial effect, low sterilization rate and easy growth of mould, and the alkyd paint slows down the construction speed of painters, thereby not only affecting the beauty of the furniture, but also affecting the daily life of people.
Disclosure of Invention
The invention aims to provide an antibacterial furniture paint surface treatment method, and the manufactured furniture material is nontoxic, has excellent antibacterial performance and lasting antibacterial effect.
In order to achieve the purpose, the invention adopts the following technical scheme:
the invention aims to provide an antibacterial furniture paint surface treatment method, which comprises the following steps:
(1) polishing and smoothing the surface of the furniture material;
(2) after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying;
(3) and (3) polishing and smoothing the surface of the dried furniture material again, removing dust on the surface of the furniture material, spraying the antibacterial paint on the surface of the furniture material again, and drying.
In a specific embodiment of the invention, the antibacterial paint comprises the following components in parts by weight: 6-15 parts of nano silver particles, 20-30 parts of nano talcum powder, 4-10 parts of tung oil, 2-6 parts of rosin oil, 0.5-2 parts of lithium carbonate, 5-12 parts of a film forming agent, 4-10 parts of polyvinylpyrrolidone, 1-5 parts of a thickening agent, 1-3 parts of a defoaming agent and 30-60 parts of distilled water.
In a specific embodiment of the invention, the antibacterial paint comprises the following components in parts by weight: 6-10 parts of nano silver particles, 20-25 parts of nano talcum powder, 7-10 parts of tung oil, 2-4 parts of rosin oil, 0.5-1 part of lithium carbonate, 5-8 parts of film forming agent, 4-7 parts of polyvinylpyrrolidone, 2-4 parts of thickening agent, 2-3 parts of defoaming agent and 40-50 parts of distilled water.
In a specific embodiment of the invention, the antibacterial paint comprises the following components in parts by weight: 10 parts of nano silver particles, 20 parts of nano talcum powder, 7 parts of tung oil, 2 parts of rosin oil, 0.5 part of lithium carbonate, 5 parts of film forming agent, 7 parts of polyvinylpyrrolidone, 2 parts of thickening agent, 2 parts of defoaming agent and 40 parts of distilled water.
Further, the silver content of the nano silver particles is 0.02-1%, and preferably 0.05%.
Further, the film forming agent is selected from one or more of propylene glycol, methoxy butanol, ethylene glycol monobutyl ether, propylene glycol butyl ether, dipropylene glycol dimethyl ether, diethylene glycol monoethyl ether and tripropylene glycol butyl ether.
Further, the thickening agent is selected from one of hydroxyethyl cellulose ether and microcrystalline cellulose.
Further, the thickener is selected from microcrystalline cellulose.
Further, the defoaming agent is tributyl phosphate.
In a specific embodiment of the present invention, the drying conditions are: the temperature is 35-45 ℃, and the drying time is 1.5-2.5 h.
Compared with the prior art, the invention has the following beneficial effects:
the antibacterial paint disclosed by the invention is reasonable in component preparation, and after the antibacterial paint is sprayed on the surface of furniture through the matching action among the components in the antibacterial paint, the antibacterial paint can actively resist and kill the acquired common bacteria attached to the wood furniture, plays a good protection role on a human body, and can effectively inhibit and/or kill bacteria and mildew-eaten existing in the wood furniture, so that the wood furniture is comprehensively protected from inside to outside; the manufactured furniture material has excellent bacteriostatic and antibacterial properties, has a lasting antibacterial effect, is non-toxic, odorless, non-irritant, pollution-free, green, environment-friendly, safe and reliable, and is suitable for large-scale popularization and use.
Detailed Description
The technical solutions of the present invention are described clearly and completely below, and it is obvious that the described embodiments are some, not all embodiments of the present invention. All other embodiments, which can be obtained by a person skilled in the art without any inventive step based on the embodiments of the present invention, are within the scope of the present invention.
Example 1
(1) Preparing the antibacterial paint vehicle according to the weight parts of 10 parts of nano-silver particles, 20 parts of nano-talcum powder, 7 parts of tung oil, 2 parts of rosin oil, 0.5 part of lithium carbonate, 5 parts of propylene glycol, 7 parts of polyvinylpyrrolidone, 2 parts of microcrystalline cellulose, 2 parts of tributyl phosphate and 40 parts of distilled water, wherein the silver content of the nano-silver particles is 0.05%, and placing for later use after the preparation is completed.
(2) Slightly wiping the surface of the furniture material to remove dust and other pollutants adhered to the surface of the furniture material, and grinding and smoothing the surface of the furniture material after the surface of the furniture is dried.
(3) And after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying for 2.5 hours at the temperature of 35 ℃.
(4) And (3) polishing and smoothing the surface of the furniture material sprayed with the antibacterial paint again, removing dust on the surface of the furniture material after polishing the surface of the furniture material, spraying the antibacterial paint on the surface of the furniture material again for one time, and drying for 1.5 hours at 35 ℃ after spraying to obtain the required antibacterial furniture material product.
Example 2
(1) Preparing the antibacterial paint vehicle according to the weight parts of 15 parts of nano-silver particles, 30 parts of nano-talcum powder, 10 parts of tung oil, 6 parts of rosin oil, 2 parts of lithium carbonate, 12 parts of methoxybutanol, 10 parts of polyvinylpyrrolidone, 5 parts of microcrystalline cellulose, 3 parts of tributyl phosphate and 60 parts of distilled water, wherein the silver content of the nano-silver particles is 1%, and after the preparation is finished, placing for later use.
(2) Slightly wiping the surface of the furniture material to remove dust and other pollutants adhered to the surface of the furniture material, and grinding and smoothing the surface of the furniture material after the surface of the furniture is dried.
(3) And after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying for 2 hours at the temperature of 40 ℃.
(4) And (3) polishing and smoothing the surface of the furniture material sprayed with the antibacterial paint again, removing dust on the surface of the furniture material after polishing the surface of the furniture material, spraying the antibacterial paint on the surface of the furniture material again for one time, and drying for 1.5 hours at 35 ℃ after spraying to obtain the required antibacterial furniture material product.
Example 3
(1) Preparing the antibacterial paint vehicle according to the weight parts of 6 parts of nano-silver particles, 20 parts of nano-talcum powder, 4 parts of tung oil, 2 parts of rosin oil, 0.5 part of lithium carbonate, 5 parts of ethylene glycol monobutyl ether, 4 parts of polyvinylpyrrolidone, 1 part of microcrystalline cellulose, 1 part of tributyl phosphate and 30 parts of distilled water, wherein the silver content of the nano-silver particles is 0.02%, and placing for later use after the preparation is completed.
(2) Slightly wiping the surface of the furniture material to remove dust and other pollutants adhered to the surface of the furniture material, and grinding and smoothing the surface of the furniture material after the surface of the furniture is dried.
(3) And after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying for 1.5h at the temperature of 35 ℃.
(4) And (3) polishing and smoothing the surface of the furniture material sprayed with the antibacterial paint again, removing dust on the surface of the furniture material after polishing the surface of the furniture material, spraying the antibacterial paint on the surface of the furniture material again for one time, and drying for 1.5 hours at 35 ℃ after spraying to obtain the required antibacterial furniture material product.
Example 4
(1) Preparing the antibacterial paint vehicle according to the weight parts of 10 parts of nano-silver particles, 25 parts of nano-talcum powder, 10 parts of tung oil, 4 parts of rosin oil, 1 part of lithium carbonate, 8 parts of diethylene glycol monoethyl ether, 7 parts of polyvinylpyrrolidone, 4 parts of microcrystalline cellulose, 3 parts of tributyl phosphate and 50 parts of distilled water, wherein the silver content of the nano-silver particles is 1%, and placing for later use after the preparation is completed.
(2) Slightly wiping the surface of the furniture material to remove dust and other pollutants adhered to the surface of the furniture material, and grinding and smoothing the surface of the furniture material after the surface of the furniture is dried.
(3) And after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying for 2 hours at the temperature of 35 ℃.
(4) And (3) polishing and smoothing the surface of the furniture material sprayed with the antibacterial paint again, removing dust on the surface of the furniture material after polishing the surface of the furniture material, spraying the antibacterial paint once again on the surface of the furniture material, and drying for 2 hours at 45 ℃ after spraying to obtain the required antibacterial furniture material product.
Example 5
(1) Preparing the antibacterial paint vehicle according to the weight parts of 8 parts of nano-silver particles, 22 parts of nano-talcum powder, 8 parts of tung oil, 5 parts of rosin oil, 1 part of lithium carbonate, 6 parts of tripropylene glycol butyl ether, 4 parts of polyvinylpyrrolidone, 2 parts of hydroxyethyl cellulose ether, 1 part of tributyl phosphate and 40 parts of distilled water, wherein the silver content of the nano-silver particles is 0.08%, and placing for later use after the preparation is completed.
(2) Slightly wiping the surface of the furniture material to remove dust and other pollutants adhered to the surface of the furniture material, and grinding and smoothing the surface of the furniture material after the surface of the furniture is dried.
(3) And after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying for 1.5h at the temperature of 35 ℃.
(4) And (3) polishing and smoothing the surface of the furniture material sprayed with the antibacterial paint again, removing dust on the surface of the furniture material after polishing the surface of the furniture material, spraying the antibacterial paint on the surface of the furniture material again for one time, and drying for 1.5 hours at 45 ℃ after spraying to obtain the required antibacterial furniture material product.
Example 6
(1) Preparing the antibacterial paint vehicle according to the weight parts of 9 parts of nano-silver particles, 20 parts of nano-talcum powder, 8 parts of tung oil, 5 parts of rosin oil, 0.5 part of lithium carbonate, 6 parts of tripropylene glycol butyl ether, 4 parts of hydroxyethyl cellulose ether, 2 parts of thickening agent, 1 part of tributyl phosphate and 40 parts of distilled water, wherein the silver content of the nano-silver particles is 0.06%, and placing for later use after the preparation is completed.
(2) Slightly wiping the surface of the furniture material to remove dust and other pollutants adhered to the surface of the furniture material, and grinding and smoothing the surface of the furniture material after the surface of the furniture is dried.
(3) And after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying for 1.5h at the temperature of 40 ℃.
(4) And (3) polishing and smoothing the surface of the furniture material sprayed with the antibacterial paint again, removing dust on the surface of the furniture material after polishing the surface of the furniture material, spraying the antibacterial paint once again on the surface of the furniture material, and drying for 1.5h at 40 ℃ after spraying to obtain the required antibacterial furniture material product.
Example 7
(1) Preparing the antibacterial paint vehicle according to the weight parts of 10 parts of nano-silver particles, 22 parts of nano-talcum powder, 8 parts of tung oil, 5 parts of rosin oil, 1 part of lithium carbonate, 5 parts of tripropylene glycol butyl ether, 4 parts of polyvinylpyrrolidone, 2 parts of hydroxyethyl cellulose ether, 1 part of defoaming agent and 50 parts of distilled water, wherein the silver content of the nano-silver particles is 0.02-1%, and placing for later use after the preparation is completed.
(2) Slightly wiping the surface of the furniture material to remove dust and other pollutants adhered to the surface of the furniture material, and grinding and smoothing the surface of the furniture material after the surface of the furniture is dried.
(3) And after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying for 2.5 hours at the temperature of 35 ℃.
(4) And (3) polishing and smoothing the surface of the furniture material sprayed with the antibacterial paint again, removing dust on the surface of the furniture material after polishing the surface of the furniture material, spraying the antibacterial paint once again on the surface of the furniture material, and drying for 2.5 hours at 40 ℃ after spraying to obtain the required antibacterial furniture material product.
The antibacterial performance tests of the examples 1 to 7 are carried out according to GB/T21866-; performing mildew resistance tests according to the evaluation standards of DB 44/T2043-2017, wherein the mildew resistance grades are all 0 grade; and the antibacterial effect is lasting, and the disinfectant is non-toxic, free of pungent odor, pollution-free and environment-friendly.
Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that changes, modifications, substitutions and alterations can be made in these embodiments without departing from the principles and spirit of the invention, the scope of which is defined in the appended claims and their equivalents.
Claims (10)
1. An antibacterial furniture paint surface treatment method is characterized by comprising the following steps:
(1) polishing and smoothing the surface of the furniture material;
(2) after the surface of the furniture material is subjected to smoothing treatment, uniformly spraying antibacterial paint on the surface of the furniture material, and drying;
(3) and (3) polishing and smoothing the surface of the dried furniture material again, removing dust on the surface of the furniture material, spraying the antibacterial paint on the surface of the furniture material again, and drying.
2. The process according to claim 1, characterized in that the antimicrobial paint comprises the following components in parts by weight: 6-15 parts of nano silver particles, 20-30 parts of nano talcum powder, 4-10 parts of tung oil, 2-6 parts of rosin oil, 0.5-2 parts of lithium carbonate, 5-12 parts of a film forming agent, 4-10 parts of polyvinylpyrrolidone, 1-5 parts of a thickening agent, 1-3 parts of a defoaming agent and 30-60 parts of distilled water.
3. The treatment according to claim 2, characterized in that the antimicrobial paint comprises the following components in parts by weight: 6-10 parts of nano silver particles, 20-25 parts of nano talcum powder, 7-10 parts of tung oil, 2-4 parts of rosin oil, 0.5-1 part of lithium carbonate, 5-8 parts of film forming agent, 4-7 parts of polyvinylpyrrolidone, 2-4 parts of thickening agent, 2-3 parts of defoaming agent and 40-50 parts of distilled water.
4. The treatment according to claim 3, characterized in that the antimicrobial paint comprises the following components in parts by weight: 10 parts of nano silver particles, 20 parts of nano talcum powder, 7 parts of tung oil, 2 parts of rosin oil, 0.5 part of lithium carbonate, 5 parts of film forming agent, 7 parts of polyvinylpyrrolidone, 2 parts of thickening agent, 2 parts of defoaming agent and 40 parts of distilled water.
5. The treatment according to any one of claims 2 to 4, wherein the silver content of the nano-silver particles is 0.02 to 1%, preferably 0.05%.
6. The treatment method according to any one of claims 2 to 4, wherein the film forming agent is one or more selected from propylene glycol, methoxybutanol, ethylene glycol monobutyl ether, propylene glycol butyl ether, dipropylene glycol dimethyl ether, diethylene glycol monoethyl ether and tripropylene glycol butyl ether.
7. The method according to any one of claims 2 to 4, wherein the thickener is one selected from the group consisting of hydroxyethyl cellulose ether and microcrystalline cellulose.
8. The treatment method according to claim 7, characterized in that the thickening agent is chosen from microcrystalline cellulose.
9. The process according to any one of claims 2 to 4, wherein the defoaming agent is tributyl phosphate.
10. The process according to claim 1, characterized in that the drying conditions are: the temperature is 35-45 ℃, and the drying time is 1.5-2.5 h.