CN104910664A - 磁性涂料及其制备方法 - Google Patents

磁性涂料及其制备方法 Download PDF

Info

Publication number
CN104910664A
CN104910664A CN201510308649.4A CN201510308649A CN104910664A CN 104910664 A CN104910664 A CN 104910664A CN 201510308649 A CN201510308649 A CN 201510308649A CN 104910664 A CN104910664 A CN 104910664A
Authority
CN
China
Prior art keywords
parts
magnetic coating
tensio
active agent
methacrylic anhydride
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510308649.4A
Other languages
English (en)
Inventor
翟红波
杨振枢
韦洪屹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Polymer New Materials Technology Co Ltd
Original Assignee
Suzhou Polymer New Materials Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Polymer New Materials Technology Co Ltd filed Critical Suzhou Polymer New Materials Technology Co Ltd
Priority to CN201510308649.4A priority Critical patent/CN104910664A/zh
Publication of CN104910664A publication Critical patent/CN104910664A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种磁性涂料及其制备方法，涂料包括以下重量份计的原料：硝基纤维素20~50份、表面活性剂5~10份、氧化铁30~80份、甲基异丁基酮45~65份、二氧化钛20~50份、甲基丙烯酸酐60~90份、丙烯酸丁酯50~80份、氧化铁黑30~50份、二甲苯80~120份、氧化铝40~60份。其制备方法：将各组分混合均匀，加入甲基丙烯酸酐、丙烯酸丁酯、氧化铁黑、二甲苯、氧化铝，混合均匀。本发明的磁性涂料可用于录像磁带，具有较强的粘度。

Description

磁性涂料及其制备方法
技术领域
    本发明涉及磁性涂料及其制备方法。
背景技术
磁粉，一种硬磁性的单畴颗粒。它与粘合剂、溶剂等制成磁浆，涂布在塑料或金属片基（支持体）的表面，就可制成磁带、磁盘、磁性卡片等磁记录材料。磁粉，是磁性涂料的核心组成，是决定磁记录介质磁特性的主要因素。它应有足够的矫顽力，以便有效地提高去磁作用，但又不能高到难以消磁的程度，它的磁化强度应和铁磁性金属有同一量级，以便对磁头提供足够的磁通量；颗粒要均匀，无烧结块体，结晶完整；应具有良好的分散性，填充密度高；它的磁性特性应该稳定，不受时间、温湿度和压力的影响，但是容易脱落。
发明内容
本发明针对现有技术的不足，提供一种磁性涂料及其制备方法，粘度大，不易脱落。
本发明采用以下技术方案：
磁性涂料，包括以下重量份计的原料：硝基纤维素20~50份、表面活性剂5~10份、氧化铁30~80份、甲基异丁基酮45~65份、二氧化钛20~50份、甲基丙烯酸酐60~90份、丙烯酸丁酯50~80份、氧化铁黑30~50份、二甲苯80~120份、氧化铝40~60份。
作为优选，磁性涂料，包括以下重量份计的原料：硝基纤维素35份、表面活性剂8份、氧化铁55份、甲基异丁基酮55份、二氧化钛35份、甲基丙烯酸酐75份、丙烯酸丁酯65份、氧化铁黑40份、二甲苯100份、氧化铝50份。
作为优选，表面活性剂为烷基二甲基磺乙基甜菜碱、六亚甲基四胺、十二烷基氨基丙酸钠、羧酸盐型咪唑啉中的至少一种。
作为优选，氧化铁的粒径为100~500微米。
上述磁性涂料的制备方法，包括以下步骤：将硝基纤维素、表面活性剂、氧化铁、甲基异丁基酮、二氧化钛混合均匀，加入甲基丙烯酸酐、丙烯酸丁酯、氧化铁黑、二甲苯、氧化铝，混合均匀，即可。
有益效果
本发明的磁性涂料可用于录像磁带，具有较强的粘度，不加甲基丙烯酸酐的磁性涂料粘度仅0.8Pa·s，甲基丙烯酸酐明显提高了本发明的粘度，使粘度达到1.3~1.4Pa·s。
具体实施方式
    下面结合具体实施例对本发明作进一步详细介绍。
实施例1
磁性涂料，包括以下重量份计的原料：硝基纤维素35份、表面活性剂8份、氧化铁55份、甲基异丁基酮55份、二氧化钛35份、甲基丙烯酸酐75份、丙烯酸丁酯65份、氧化铁黑40份、二甲苯100份、氧化铝50份。
表面活性剂为质量比1：:1的烷基二甲基磺乙基甜菜碱、六亚甲基四胺。
氧化铁的粒径为300微米。
上述磁性涂料的制备方法，包括以下步骤：将硝基纤维素、表面活性剂、氧化铁、甲基异丁基酮、二氧化钛混合均匀，加入甲基丙烯酸酐、丙烯酸丁酯、氧化铁黑、二甲苯、氧化铝，混合均匀，即可。
实施例2
磁性涂料，包括以下重量份计的原料：硝基纤维素20份、表面活性剂5份、氧化铁30份、甲基异丁基酮45份、二氧化钛20份、甲基丙烯酸酐60份、丙烯酸丁酯50份、氧化铁黑30份、二甲苯80份、氧化铝40份。
表面活性剂为质量比1：1的十二烷基氨基丙酸钠和羧酸盐型咪唑啉。
氧化铁的粒径为100微米。
上述磁性涂料的制备方法，包括以下步骤：将硝基纤维素、表面活性剂、氧化铁、甲基异丁基酮、二氧化钛混合均匀，加入甲基丙烯酸酐、丙烯酸丁酯、氧化铁黑、二甲苯、氧化铝，混合均匀，即可。
实施例3
磁性涂料，包括以下重量份计的原料：硝基纤维素50份、表面活性剂10份、氧化铁80份、甲基异丁基酮65份、二氧化钛50份、甲基丙烯酸酐90份、丙烯酸丁酯80份、氧化铁黑50份、二甲苯120份、氧化铝60份。
表面活性剂为质量比1：1：1的六亚甲基四胺、十二烷基氨基丙酸钠、羧酸盐型咪唑啉。
氧化铁的粒径为500微米。
上述磁性涂料的制备方法，包括以下步骤：将硝基纤维素、表面活性剂、氧化铁、甲基异丁基酮、二氧化钛混合均匀，加入甲基丙烯酸酐、丙烯酸丁酯、氧化铁黑、二甲苯、氧化铝，混合均匀，即可。
对比例1
    与实施例1相同，不同在于：不加甲基丙烯酸酐。
性能测试
将实施例1~3和对比例1的产品进行性能测试，结果见表1。
表1
  实施例1 实施例2 实施例3 对比例1
粘度Pa·s 1.4 1.4 1.3 0.8
结论：本发明的磁性涂料可用于录像磁带，具有较强的粘度，不加甲基丙烯酸酐的磁性涂料粘度仅0.8Pa·s，甲基丙烯酸酐明显提高了本发明的粘度，使粘度达到1.3~1.4Pa·s。

Claims (5)

1.磁性涂料，其特征在于，包括以下重量份计的原料：硝基纤维素20~50份、表面活性剂5~10份、氧化铁30~80份、甲基异丁基酮45~65份、二氧化钛20~50份、甲基丙烯酸酐60~90份、丙烯酸丁酯50~80份、氧化铁黑30~50份、二甲苯80~120份、氧化铝40~60份。
2.根据权利要求1所述的磁性涂料，其特征在于，包括以下重量份计的原料：硝基纤维素35份、表面活性剂8份、氧化铁55份、甲基异丁基酮55份、二氧化钛35份、甲基丙烯酸酐75份、丙烯酸丁酯65份、氧化铁黑40份、二甲苯100份、氧化铝50份。
3.根据权利要求1所述的磁性涂料，其特征在于，表面活性剂为烷基二甲基磺乙基甜菜碱、六亚甲基四胺、十二烷基氨基丙酸钠、羧酸盐型咪唑啉中的至少一种。
4.根据权利要求1所述的磁性涂料，其特征在于，氧化铁的粒径为100~500微米。
5.基于权利要求1所述的磁性涂料的制备方法，其特征在于，包括以下步骤：将硝基纤维素、表面活性剂、氧化铁、甲基异丁基酮、二氧化钛混合均匀，加入甲基丙烯酸酐、丙烯酸丁酯、氧化铁黑、二甲苯、氧化铝，混合均匀，即可。
CN201510308649.4A 2015-06-08 2015-06-08 磁性涂料及其制备方法 Pending CN104910664A (zh)