CN104909814A - 一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料及其制备方法 - Google Patents

一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料及其制备方法 Download PDF

Info

Publication number
CN104909814A
CN104909814A CN201510305147.6A CN201510305147A CN104909814A CN 104909814 A CN104909814 A CN 104909814A CN 201510305147 A CN201510305147 A CN 201510305147A CN 104909814 A CN104909814 A CN 104909814A
Authority
CN
China
Prior art keywords
micro mist
heat
expanded perlite
phenolic resin
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510305147.6A
Other languages
English (en)
Inventor
武子静
袁学红
赵雨昕
陈劲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hefei Hean Machinery Manufacturing Co Ltd
Original Assignee
Hefei Hean Machinery Manufacturing Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hefei Hean Machinery Manufacturing Co Ltd filed Critical Hefei Hean Machinery Manufacturing Co Ltd
Priority to CN201510305147.6A priority Critical patent/CN104909814A/zh
Publication of CN104909814A publication Critical patent/CN104909814A/zh
Pending legal-status Critical Current

Abstract

本发明涉及排气管用隔热材料，具体涉及一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料及其制备方法，本发明在制备过程中先对掺混了中间相炭微球、羰基铁粉的酚醛树脂进行发泡处理，这样制备得到的改性酚醛树脂泡沫粉体在后续的炭化过程中炭化过程更高效，炭化材料结构更为紧致，强度更高，导热系数更低，而掺混有硅溶胶的复合膨胀珍珠岩微粉胶黏剂不仅具有良好的粘接能力，还能提高材料的高温稳定性，炭化处理后的材料结构均匀紧致，这种材料具有轻质、隔热、环保等优点，以这种材料制备的隔热板、隔热套等成品隔热效果卓越，高效耐用，有效的改善了叉车发动机工作环境。

Description

一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料及其制备方法
技术领域
本发明涉及排气管用隔热材料，具体涉及一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料及其制备方法。
背景技术
在叉车的连续运行过程中，发动机排气管部位会产生大量的热，由于热量的循环，最终使得排气管温度极高，若是不进行隔热处理势必会严重影响到排气系统周围零部件的正常工作，常见的处理方法是在排气管外面包裹由具有隔热效果的材料制成的隔热罩，组成隔热罩的常见隔热材料主要包括金属铝板和石棉布、玻璃纤维布等，然而这些材料存在一些缺点，比如铝材料虽然隔热效果较好，但是生产成本相对较高，延伸率有限，而石棉布、玻璃纤维布存在使用寿命短、易损坏、不够环保、需频繁更换维修等缺点，因此急需研制一类更为高效的复合隔热材料。
发明内容
本发明的目的在于，提供一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料及其制备方法，以改善传统隔热材料的缺陷，达到高效、环保、经济的隔热效果，为了实现上述目的，本发明采用的技术方案如下：
一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料，其特征在于，本发明材料由以下重量份的原料制成：羰基铁粉1-2、纳米二氧化锡1-2、固含量为20-30%的硅溶胶8-10、400-500目膨胀珍珠岩微粉10-12、铝粉4-5、酚醛树脂30-40、三聚磷酸铝1-2、中间相炭微球4-5、波美度为40°的水玻璃16-20、十二烷基磺酸钠0.1-0.2、碳酸氢钠0.2-0.3、水25-30。
所述的一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料的制备方法，其特征在于，其制备方法如下：
（1）制备改性酚醛树脂泡沫微粉：将酚醛树脂投入有机溶剂中，使其完全溶解即可，随后将中间相炭微球、羰基铁粉投入溶液中，充分搅拌使其在溶液中分散均匀，随后将混合物料进行发泡处理，制成改性泡沫酚醛树脂，再将改性酚醛树脂泡沫粉碎，制成粒径为250-300目的微粉，即得；
（2）制备复合膨胀珍珠岩微粉胶黏剂：将膨胀珍珠岩微粉与水混合研磨40-50min，随后将所得浆料与水玻璃、硅溶胶、纳米二氧化锡混合，继续搅拌混合均匀，即得复合膨胀珍珠岩微粉胶黏剂；
（3）将改性酚醛树脂泡沫微粉与复合膨胀珍珠岩微粉胶黏剂及其它剩余成分混合，混合均匀后送料入模具中压制成型，再将所得模型送入炭化炉中，以氮气作为保护气体，以5-8℃/min的速率升温至650-700℃，达到最高温度时恒温1.5-2h，炭化结束后在氮气氛围下冷却至室温后取出，随后进行切割、分装，即得所述隔热材料。
本发明先对掺混了中间相炭微球、羰基铁粉的酚醛树脂进行发泡处理，这样制备得到的改性酚醛树脂泡沫粉体在后续的炭化过程中炭化过程更高效，炭化材料结构更为紧致，强度更高，导热系数更低，而掺混有硅溶胶的复合膨胀珍珠岩微粉胶黏剂不仅具有良好的粘接能力，还能提高材料的高温稳定性，炭化处理后的材料结构均匀紧致，这种材料具有轻质、隔热、环保等优点，以这种材料制备的隔热板、隔热套等成品隔热效果卓越，高效耐用，有效的改善了叉车发动机工作环境。
具体实施方式
实施例
本实施例的隔热材料由以下重量份原料制成：羰基铁粉1.5、纳米二氧化锡1.5、固含量为25%的硅溶胶8、400目膨胀珍珠岩微粉10、铝粉4、酚醛树脂35、三聚磷酸铝1.5、中间相炭微球4、波美度为40°的水玻璃16、十二烷基磺酸钠0.1、碳酸氢钠0.2、水25。
所述的一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料的制备方法如下：
（1）制备改性酚醛树脂泡沫微粉：将酚醛树脂投入有机溶剂中，使其完全溶解即可，随后将中间相炭微球、羰基铁粉投入溶液中，充分搅拌使其在溶液中分散均匀，随后将混合物料进行发泡处理，制成改性泡沫酚醛树脂，再将改性酚醛树脂泡沫粉碎，制成粒径为300目的微粉，即得；
（2）制备复合膨胀珍珠岩微粉胶黏剂：将膨胀珍珠岩微粉与水混合研磨45min，随后将所得浆料与水玻璃、硅溶胶、纳米二氧化锡混合，继续搅拌混合均匀，即得复合膨胀珍珠岩微粉胶黏剂；
（3）将改性酚醛树脂泡沫微粉与复合膨胀珍珠岩微粉胶黏剂及其它剩余成分混合，混合均匀后送料入模具中压制成型，再将所得模型送入炭化炉中，以氮气作为保护气体，以5℃/min的速率升温至650℃，达到最高温度时恒温2h，炭化结束后在氮气氛围下冷却至室温后取出，随后进行切割、分装，即得所述隔热材料。
本实施例所制得的材料根据相关标准测试得到的性能指标如下：
密度:0.11g/cm3；孔隙率45%；抗压强度25.2MPa；导热系数0.10W/（m.k），发动机室平均温度降低30.5℃。

Claims (2)

1.一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料，其特征在于，该隔热材料由以下重量份的原料制成：羰基铁粉1-2、纳米二氧化锡1-2、固含量为20-30%的硅溶胶8-10、400-500目膨胀珍珠岩微粉10-12、铝粉4-5、酚醛树脂30-40、三聚磷酸铝1-2、中间相炭微球4-5、波美度为40°的水玻璃16-20、十二烷基磺酸钠0.1-0.2、碳酸氢钠0.2-0.3、水25-30。
2.如权利要求1所述的一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料的制备方法，其特征在于，所述的制备方法如下：
（1）制备改性酚醛树脂泡沫微粉：将酚醛树脂投入有机溶剂中，使其完全溶解即可，随后将中间相炭微球、羰基铁粉投入溶液中，充分搅拌使其在溶液中分散均匀，随后将混合物料进行发泡处理，制成改性泡沫酚醛树脂，再将改性酚醛树脂泡沫粉碎，制成粒径为250-300目的微粉，即得；
（2）制备复合膨胀珍珠岩微粉胶黏剂：将膨胀珍珠岩微粉与水混合研磨40-50min，随后将所得浆料与水玻璃、硅溶胶、纳米二氧化锡混合，继续搅拌混合均匀，即得复合膨胀珍珠岩微粉胶黏剂；
（3）将改性酚醛树脂泡沫微粉与复合膨胀珍珠岩微粉胶黏剂及其它剩余成分混合，混合均匀后送料入模具中压制成型，再将所得模型送入炭化炉中，以氮气作为保护气体，以5-8℃/min的速率升温至650-700℃，达到最高温度时恒温1.5-2h，炭化结束后在氮气氛围下冷却至室温后取出，随后进行切割、分装，即得所述隔热材料。
CN201510305147.6A 2015-06-04 2015-06-04 一种叉车发动机排气管用复合改性膨胀珍珠岩-炭化发泡酚醛树脂基隔热材料及其制备方法 Pending CN104909814A (zh)