CN104893675A - 一种化学冰袋及其制备方法 - Google Patents
一种化学冰袋及其制备方法 Download PDFInfo
- Publication number
- CN104893675A CN104893675A CN201510376633.7A CN201510376633A CN104893675A CN 104893675 A CN104893675 A CN 104893675A CN 201510376633 A CN201510376633 A CN 201510376633A CN 104893675 A CN104893675 A CN 104893675A
- Authority
- CN
- China
- Prior art keywords
- parts
- solution
- sodium
- sulfate dodecahydrate
- ammonium nitrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种化学冰袋及其制备方法,所述的化学冰袋由以下重量份配比的各组分制成:硝酸铵40~50份,十二水硫酸铝钾70~80份,羧甲基纤维素钠2~5份,乙醇4~9份,氯化钠15~30份,氢氧化钠1~4份。所述的化学冰袋制备方法是按上述重量份配比称重,先将称好的羧甲基纤维素钠加入到一半十二水硫酸铝钾中搅拌,搅拌速度为200~300r/min,并加热至80~90℃,当溶液呈现透明后,停止加热,让其自然冷却至室温,得到溶液A;然后在搅拌状态下依次加入硝酸铵,另一半十二水硫酸铝钾,乙醇到溶液A中,使其搅拌均匀,得到溶液B;最后在溶液B中,依次加入氢氧化钠和氯化钠搅拌均匀后,用袋封装。本发明所公开的化学冰袋制冷时间长。
Description
技术领域
本发明涉及一种化学冰袋及其制备方法,属于化学技术领域。
背景技术
化学冰袋是利用某些化学物质(如铵盐)在溶解过程中会吸收热量,而使袋内的温度迅速下降的原理而制成。其主要应用在医疗保健(如冷敷消肿),或是食品保鲜,或是药品(如疫苗)冷藏等等,都有良好的效果。总之,化学冰袋在日常生活中扮演着一个比较重要的角色。
通常人们使用冰块来实现降温的目的,但是使用冰块带来很大不便,如冰块是固体,接触面积不大,降温不均匀,难以实现预期的效果。化学冰袋与冰块相比,化学冰袋具有体积小、质量轻、冷却温度低、生产成本低、使用方便等特点。由于其具有这些特点,化学冰袋越来越吸引人们的眼球。
近年来,随着冰袋的使用范围越来越广,人们对化学冰袋投入很大的研究,并取得一定的研究成果。如中国专利文献公开了一种名称为“一种冰袋”(公开号:CN 1308922 A,公开日:2001年8月22日)。其公开了一种能迅速降温至26℃的冰袋,主要应用在外伤冰敷、疲劳提神及外出冷藏。其的冷却剂是由硝酸铵、羧甲基纤维素钠、氯化钠等物质制成的颗粒状物。虽然这种方法能有效地降低温度,但由于制备过程中的水使其存在着这样的问题:盐在水中的溶解速度很快,温度会变化很快,但是制冷时间不长。此外,制成的冰袋是颗粒状物,颗粒与颗粒之间是不连续的,这也不利于维持长时间制冷效果。因此,开发一种新的化学冰袋对人们医疗保健起到非常重要的作用。
发明内容
针对上述现有技术的不足,本发明所要解决的技术问题是提出了一种制冷时间长的化学冰袋及其制备方法。
本发明为解决上述问题所采取的技术方案为:
一种化学冰袋,由以下重量份配比的各组分制成:硝酸铵40~50份,十二水硫酸铝钾70~80份,羧甲基纤维素钠2~5份,乙醇4~9份,氯化钠15~30份,氢氧化钠1~4份。
其重量份配比如下:
硝酸铵45份,十二水硫酸铝钾75份,羧甲基纤维素钠4份,乙醇6份,氯化钠23份,氢氧化钠3份。
本发明中,所述的硝酸铵溶解热是吸热,而且是吸热比较大的化合物,可以迅速地溶于水,吸收大量的热量,使周围温度发生骤降。十二水硫酸铝钾替代水,能够减缓硝酸铵在水中溶解速度,增加制冷时间。此外,硫酸铝钾能够发生水解形成吸附能力很强的氢氧化铝胶体,能够有效地减缓能量传递。羧甲基纤维素钠具有缓凝,增稠和保持水分的作用。乙醇容易水同样是吸热,当硝酸铵溶解完,可以继续维持制冷,增加制冷时间。氯化钠是防冻剂,通过添加不同量的氯化钠来改变化学冰袋的冰点。氢氧化钠,一方面可以促进形成氢氧化铝胶体,另一方面可以放热来调节化学冰袋的温度。
所述化学冰袋的制备方法,包括如下步骤:
(1)按各组分重量份配比准确称重,将称好的羧甲基纤维素钠加入到一半十二水硫酸铝钾中搅拌,搅拌速度为200~300r/min,并加热至80~90℃,当溶液呈现透明后,停止加热,让其自然冷却至室温,得到溶液A;
(2)在搅拌状态下依次加入硝酸铵,另一半十二水硫酸铝钾,乙醇到溶液A中,使其搅拌均匀,得到溶液B;
(3)在溶液B中,先加入氢氧化钠搅拌均匀后,再加氯化钠,当搅拌均匀并使其成透明状时,用袋封装,即可得到化学冰袋。
本发明的有益效果是:
本发明所公开的化学冰袋特点:通过硝酸铵和乙醇制冷,同时应用了胶体的吸附作用,大大地增加制冷时间和冰袋使用寿命;十二水硫酸铝钾能够减缓硝酸铵在水中溶解速度,增加制冷的时间;添加氢氧化钠可以调节化学冰袋的温度,使化学冰袋更有灵活性。
具体实施方式
实施例1
一种化学冰袋,由以下重量份配比的各组分制成:硝酸铵45份,十二水硫酸铝钾75份,羧甲基纤维素钠4份,乙醇6份,氯化钠23份,氢氧化钠3份。
所述化学冰袋的制备方法,包括如下步骤:
(1)按各组分重量份配比准确称重,将称好的羧甲基纤维素钠加入到一半十二水硫酸铝钾中搅拌,搅拌速度为250r/min,并加热至85℃,当溶液呈现透明后,停止加热,让其自然冷却至室温,得到溶液A;
(2)在搅拌状态下依次加入硝酸铵,另一半十二水硫酸铝钾,乙醇到溶液A中,使其搅拌均匀,得到溶液B;
(3)在溶液B中,先加入氢氧化钠搅拌均匀后,再加氯化钠,当搅拌均匀并使其成透明状时,用袋封装,即可得到化学冰袋。
实施例2
一种化学冰袋,由以下重量份配比的各组分制成:硝酸铵40份,十二水硫酸铝钾70份,羧甲基纤维素钠2份,乙醇9份,氯化钠30份,氢氧化钠4份。
所述化学冰袋的制备方法,包括如下步骤:
(1)按各组分重量份配比准确称重,将称好的羧甲基纤维素钠加入到一半十二水硫酸铝钾中搅拌,搅拌速度为200r/min,并加热至80℃,当溶液呈现透明后,停止加热,让其自然冷却至室温,得到溶液A;
(2)在搅拌状态下依次加入硝酸铵,另一半十二水硫酸铝钾,乙醇到溶液A中,使其搅拌均匀,得到溶液B;
(3)在溶液B中,先加入氢氧化钠搅拌均匀后,再加氯化钠,当搅拌均匀并使其成透明状时,用袋封装,即可得到化学冰袋。
实施例3
一种化学冰袋,由以下重量份配比的各组分制成:硝酸铵50份,十二水硫酸铝钾80份,羧甲基纤维素钠5份,乙醇4份,氯化钠15份,氢氧化钠1份。
所述化学冰袋的制备方法,包括如下步骤:
(1)按各组分重量份配比准确称重,将称好的羧甲基纤维素钠加入到一半十二水硫酸铝钾中搅拌,搅拌速度为300r/min,并加热至90℃,当溶液呈现透明后,停止加热,让其自然冷却至室温,得到溶液A;
(2)在搅拌状态下依次加入硝酸铵,另一半十二水硫酸铝钾,乙醇到溶液A中,使其搅拌均匀,得到溶液B;
(3)在溶液B中,先加入氢氧化钠搅拌均匀后,再加氯化钠,当搅拌均匀并使其成透明状时,用袋封装,即可得到化学冰袋。
实施例4
一种化学冰袋,由以下重量份配比的各组分制成:硝酸铵43份,十二水硫酸铝钾73份,羧甲基纤维素钠3份,乙醇5份,氯化钠20份,氢氧化钠2份。
所述化学冰袋的制备方法,包括如下步骤:
(1)按各组分重量份配比准确称重,将称好的羧甲基纤维素钠加入到一半十二水硫酸铝钾中搅拌,搅拌速度为225r/min,并加热至83℃,当溶液呈现透明后,停止加热,让其自然冷却至室温,得到溶液A;
(2)在搅拌状态下依次加入硝酸铵,另一半十二水硫酸铝钾,乙醇到溶液A中,使其搅拌均匀,得到溶液B;
(3)在溶液B中,先加入氢氧化钠搅拌均匀后,再加氯化钠,当搅拌均匀并使其成透明状时,用袋封装,即可得到化学冰袋。
实施例5
一种化学冰袋,由以下重量份配比的各组分制成:硝酸铵47份,十二水硫酸铝钾77份,羧甲基纤维素钠3份,乙醇8份,氯化钠27份,氢氧化钠2份。
所述化学冰袋的制备方法,包括如下步骤:
(1)按各组分重量份配比准确称重,将称好的羧甲基纤维素钠加入到一半十二水硫酸铝钾中搅拌,搅拌速度为275r/min,并加热至87℃,当溶液呈现透明后,停止加热,让其自然冷却至室温,得到溶液A;
(2)在搅拌状态下依次加入硝酸铵,另一半十二水硫酸铝钾,乙醇到溶液A中,使其搅拌均匀,得到溶液B;
(3)在溶液B中,先加入氢氧化钠搅拌均匀后,再加氯化钠,当搅拌均匀并使其成透明状时,用袋封装,即可得到化学冰袋。
我们对化学冰袋的制冷效果进行测试,结果如表1所示。
表1化学冰袋制冷效果测试结果
当然,上面只是本发明优选的具体实施方式作了详细描述,并非以此限制本发明的实施范围,凡依本发明的原理、构造以及结构所作的等效变化,均应涵盖于本发明的保护范围内。
Claims (3)
1.一种化学冰袋,其特征是:由以下重量份配比的各组分制成:硝酸铵40~50份,十二水硫酸铝钾70~80份,羧甲基纤维素钠2~5份,乙醇4~9份,氯化钠15~30份,氢氧化钠1~4份。
2.根据权利要求1所述的化学冰袋,其特征是:其重量份配比如下:硝酸铵45份,十二水硫酸铝钾75份,羧甲基纤维素钠4份,乙醇6份,氯化钠23份,氢氧化钠3份。
3.权利要求1所述的化学冰袋的制备方法,其特征是:包括如下步骤:
(1)按各组分重量份配比准确称重,将称好的羧甲基纤维素钠加入到一半十二水硫酸铝钾中搅拌,搅拌速度为200~300r/min,并加热至80~90℃,当溶液呈现透明后,停止加热,让其自然冷却至室温,得到溶液A;
(2)在搅拌状态下依次加入硝酸铵,另一半十二水硫酸铝钾,乙醇到溶液A中,使其搅拌均匀,得到溶液B;
(3)在溶液B中,先加入氢氧化钠搅拌均匀后,再加氯化钠,当搅拌均匀并使其成透明状时,用袋封装,即可得到化学冰袋。