CN104893369A - 一种防火保温涂料 - Google Patents

一种防火保温涂料 Download PDF

Info

Publication number
CN104893369A
CN104893369A CN201410079555.XA CN201410079555A CN104893369A CN 104893369 A CN104893369 A CN 104893369A CN 201410079555 A CN201410079555 A CN 201410079555A CN 104893369 A CN104893369 A CN 104893369A
Authority
CN
China
Prior art keywords
parts
coating
insulation coating
heat insulation
thermo
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410079555.XA
Other languages
English (en)
Other versions
CN104893369B (zh
Inventor
顾国清
胡文双
姜世杰
王兴全
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410079555.XA priority Critical patent/CN104893369B/zh
Publication of CN104893369A publication Critical patent/CN104893369A/zh
Application granted granted Critical
Publication of CN104893369B publication Critical patent/CN104893369B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明提供一种防火保温涂料其特征在于：主要组成的质量比为：无机纳米复合粘合剂15-30，海泡石5-10，空心陶瓷微球10-15，纳米硅气溶胶18-25，纳米陶瓷纤维15-22，稀土4-8，助剂1-2，水10-15。本发明提供的防火保温涂料，其优点在于：本产品涂层厚24mm时在符合GB14907-2002钢结构防火保温涂料的情况下防火极限达到了4小时；导热系数在0.030W/(m·K)以内，于储油罐来说，是一种新型的绝热保温材料，达到了节能的作用；线膨胀系数大，在冷热交替的情况下，产品不开裂、不脱落机械性能稳定；在发生火灾情况下，能抗住爆炸时产生的冲击波而使漆膜不被破坏。

Description

一种防火保温涂料
技术领域
本发明涉及涂料。
背景技术
油田储油罐及管线发生火灾时升温速度快，易发生爆炸，爆炸时能产生较大的冲击波，针对这种现状，目前应用的防火涂料多为室外厚型防火涂料，目前此种防火涂料的防火极限标准定为2小时，市面上销售的此类型防火保温涂料的防火极限最高为3小时，对于油田灭火形式复杂，不易扑灭的特性防火极限为3小时的时间就显得不太够用。油田储油罐及管线本身有一定的温度，冬夏季温差大，线膨胀系数大，因此在表面涂刷的防火涂料易开裂及脱落，为避免此类不足，在施工中要挂网，增加了施工的难度，对于油田储油罐及管线的复杂结构来说，挂网就更加难施工。油田储油罐及管线需要保温，在涂刷普通防火涂料的内层要进行保温处理，这就增加其施工工序，更增加了成本。
发明内容
本发明的目的在于提供一种防火极限高于3小时的防火保温涂料。
本发明提供一种防火保温涂料其特征在于：主要组成的质量比为：
无机纳米复合粘合剂     15-30，
海泡石                 5-10，
空心陶瓷微球           10-15，
纳米硅气溶胶           18-25，
纳米陶瓷纤维           15-22，
稀土                   4-8，
助剂                   1-2，
水                     10-15。
导热系数极低的纳米硅气凝胶及纳米陶瓷纤维材料，在防火保温涂料中按一定的比例添加并代替一定量的传统防火保温涂料的阻燃材料（如膨胀珍珠岩、海泡石及苯乙烯空心聚合物球体等），在防火保温涂料中按一定比例添加稀土使其内部结构发生质的变化，这样此产品不但弥补了传统防火保温涂料的不足，更起到了绝热保温的作用。
本发明提供的防火保温涂料，其空心陶瓷微球的直径为50～100μm。
本发明提供的防火保温涂料，其稀土的成分为纳米氧化铈。
本发明提供的防火保温涂料，其助剂的成分为为润湿剂WK-2037、分散剂WK-2034、消泡剂VG-108，质量比为（0.7-1.2）：（7-12）：（4-6）。
本发明提供的防火保温涂料，其优点在于：本产品涂层厚24mm时在符合GB 14907-2002钢结构防火保温涂料的情况下防火极限达到了4小时，可给救援争取了更多的时间；可做新型的保温绝热材料，导热系数在0.030W/(m·K)以内，是传统材料的2～3倍，于储油罐来说，是一种新型的绝热保温材料，达到了节能的作用；线膨胀系数大，在冷热交替的情况下，产品不开裂、不脱落机械性能稳定，因此施工时不用挂网，节省了劳动强度；在发生火灾情况下，能抗住爆炸时产生的冲击波而使漆膜不被破坏；所选的无机纳米复合粘结剂具有优良的粘结性能，对钢铁和水泥都能有很好的润湿作用，并且不含有腐蚀钢铁和水泥的离子及有害的重金属，因此本产品不但适合钢结构的表面，更能完全适用于预应力混凝土楼板、防火堤等水泥制品表面。
具体实施方式
实施例1
防火保温涂料的组成（质量比）为：
无机纳米复合粘合剂             15，
海泡石                         5，
空心陶瓷微球，直径为50～100μm 10，
纳米硅气溶胶                   18，
纳米陶瓷纤维                   15，
稀土，纳米氧化铈               4，
助剂                           1，
其中：润湿剂WK-2037    0.7，
分散剂WK-2034          7，
消泡剂VG-108           4，
水                     10。
防火极限达到了4.5小时，导热系数为0.027W/(m·K)，在冷热交替的情况下，产品不开裂、不脱落机械性能稳定，能抗住爆炸时产生的冲击波。
实施例2
防火保温涂料的组成（质量比）为：
无机纳米复合粘合剂               30，
海泡石                           10，
空心陶瓷微球，直径为50～100μm   15，
纳米硅气溶胶                   25，
纳米陶瓷纤维                   22，
纳米氧化铈                     8，
其中：润湿剂WK-2037            1.2，
分散剂WK-2034，                12，
消泡剂VG-108                   6，
助剂                           2，
水                             15。
防火极限达到了4.5小时，导热系数为0.028 W/(m·K)，在冷热交替的情况下，产品不开裂、不脱落机械性能稳定，能抗住爆炸时产生的冲击波。
实施例3
防火保温涂料的组成（质量比）为：
无机纳米复合粘合剂             15，
海泡石                         10，
空心陶瓷微球，直径为50～100μm 10，
纳米硅气溶胶                   25，
纳米陶瓷纤维                   15，
纳米氧化铈                     8，
助剂                           1，
其中：润湿剂WK-2037            1.2，
分散剂WK-2034，                7，
消泡剂VG-108                   6，
水                             10。
防火极限达到了4.1小时，导热系数为0.030W/(m·K)，在冷热交替的情况下，产品不开裂、不脱落机械性能稳定，能抗住爆炸时产生的冲击波。
实施例4
防火保温涂料的组成（质量比）为：
无机纳米复合粘合剂              30，
海泡石                          5，
空心陶瓷微球，直径为50～100μm  15，
纳米硅气溶胶                    18，
纳米陶瓷纤维                    22，
纳米氧化铈                      8，
助剂                            2，
其中：润湿剂WK-2037             0.7，
分散剂WK-2034                   12，
消泡剂VG-108                    4，
水                              15。
防火极限达到了4小时，导热系数为0.029W/(m·K)，在冷热交替的情况下，产品不开裂、不脱落机械性能稳定，能抗住爆炸时产生的冲击波。

Claims (5)

1.一种防火保温涂料，其特征在于：主要组成的质量比为：
无机纳米复合粘合剂     15-30，
海泡石                 5-10，
空心陶瓷微球           10-15，
纳米硅气溶胶           18-25，
纳米陶瓷纤维           15-22，
稀土                   4-8，
助剂                   1-2，
水                     10-15。
2.按照权利要求1所述的防火保温涂料，其特征在于：所述空心陶瓷微球的直径为直径为50～100μm。
3.按照权利要求1所述的防火保温涂料，其特征在于：所述稀土的成分为纳米氧化铈。
4.按照权利要求2所述的防火保温涂料，其特征在于：所述稀土的成分为纳米氧化铈。
5.按照权利要求1～4之一所述的防火保温涂料，其特征在于：所述助剂的成分为润湿剂WK-2037、分散剂WK-2034、消泡剂VG-108，质量比为（0.7-1.2）：（7-12）：（4-6）。
CN201410079555.XA 2014-03-06 2014-03-06 一种防火保温涂料 Active CN104893369B (zh)